CTD-101K Epoxy Resin Datasheet

CTD-101K is an epoxy resin system developed for cryogenic applications down to liquid helium temperatures and for resistance to high energy radiation. It has good handling characteristics with low viscosity and long pot-life, as well as low toxicity. The resin can be used for filament winding, resin transfer molding, vacuum pressure impregnation, and casting. It exhibits high strength and modulus even at cryogenic temperatures and maintains properties after high radiation doses.

Uploaded by

tsram90
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
1K views3 pages

CTD-101K Epoxy Resin Datasheet

CTD-101K is an epoxy resin system developed for cryogenic applications down to liquid helium temperatures and for resistance to high energy radiation. It has good handling characteristics with low viscosity and long pot-life, as well as low toxicity. The resin can be used for filament winding, resin transfer molding, vacuum pressure impregnation, and casting. It exhibits high strength and modulus even at cryogenic temperatures and maintains properties after high radiation doses.

Uploaded by

tsram90
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
  • Introduction and Applications
  • Shear and Combined Properties
  • Viscosity Profile

CTD-101K

Epoxy Resin System


High Performance Resins for Cryogenic and Radiation Applications

An anhydride cured epoxy system that was developed and tested for cryogenic applications down to
liquid helium temperatures (-269oC/-452oF) as well as for its resistance to high energy radiation.

Sets the performance standards in cryogenic and high radiation applications and is backed by
performance data that meet all applicable test specifications.

Good room temperature performance and handling characteristics: low viscosity and long pot-life.

Non-carcinogenic resin system with very low toxicity. It is a non-solvent based system, and will not
give off volatiles on cure.

Improved wetting and excellent impregnation of large coils with highly tortuous paths.

Cure:

1 1/2 hrs at 135 C; No Post Cure or


5 hrs at 110 C with a post cure of 16 hrs at 125 C
Process Compatibilities

Filament winding (FW)


Resin Transfer Molding (RTM)
Vacuum Pressure Impregnation (VPI)
Casting with or without filler

Material Advantages

Non-Carcinogenic
Low Toxicity
Long Pot-Life, 60 hours at 40 C
Low Viscosity, 400 cP at 40 C
Excellent adhesion to fibers and fillers
Specific Gravity 1.03 g/cc
Processing Temperature 40 - 60 C

Material Properties
Viscosity @
Glass
Linear
Dielectric Strength with S-2 Glass,
60o C
Transition
Shrinkage*
0.5 mm thick,
[cP]
Temp [oC]
[%]
at 76 K [KV/mm]
<100
113o
<1
76.3
*Neat resin linear cure shrinkage, cured 1.5 hrs at 135 C. Cure schedule will effect linear shrinkage.

CTD-101K, with 50% Vf satin weave S-2 Glass, Through Thickness: Unirradiated
Compressive Properties
Temperature
[K]
295
76
4

Compression Strength
[MPa]
790
1300
1360

Compression Modulus
[GPa]
12.9
16.7
19.7

2600 CAMPUS DRIVE, SUITE D | LAFAYETTE, CO 80026 | 303-664-0394 | FAX: 303-664-0392|

[Link]

Shear Properties
Temperature
[K]
76
4

Shear Strength
[MPa]
108.0
120.0

Flexural Modulus
[GPa]
27.9
34.1

Combined Shear/Compressive Properties


Temperature
[K]
76
76
76
76
4
4
4
4

Fixture
[deg.]
15
45
75
84
15
45
75
84

Shear Strength
[MPa]
101.5
175.8
247.5
127.1
104.1
178.3
277.2
125.0

Compressive Strength
[MPa]
29.6
175.8
933.2
1207.7
27.9
178.3
1034.3
1197.3

Irradiation Results
Irradiation
Temp
[K]

Dose
[Rads]

4
4
4
330
330
330
330

4.7E9
8.8E9
1.6E10
4.7E8
4.7E9
2.3E10

Compressive
Strength
at 76K
[GPa]
1.23
1.20
1.08
1.30
-

Compressive
Modulus
at 76K
[GPa]
19.5
13.0
13.5
16.7
-

Shear
Strength
at 76K
[MPa]
85.0
41.3
6.7
108.0
-

Flexural
Modulus
at 76K
[GPa]
27.5
20.6
15.6
27.9
-

Fracture
Resistance G1C
at 76K
[KN/m]
0.36
0.28
0.15
0.16

Coefficient of Thermal Expansion of CTD-101K, with 50% Vf satin weave S-2TM Glass
CTE

0.00

30.00

-0.10

% TE

-0.20

% TE Warp or
Fill
% TE Through
Thickness
CTE Warp or Fill

-0.30
-0.40

CTE Through
Thickness

-0.50

20.00
15.00
10.00

CTE (m/m-K)

25.00

5.00

-0.60
-0.70
0

50

100

150

200

Temp (K)

250

300

2600 CAMPUS DRIVE, SUITE D | LAFAYETTE, CO 80026 | 303-664-0394 | FAX: 303-664-0392|

0.00
350

[Link]

Viscosity Profile of CTD-101K at 60C


600.00

500.00

Viscosity [cP]

400.00

300.00

200.00

100.00

0.00
0.0

5.0

10.0

15.0

20.0

25.0

30.0

time [hr]

Disclaimer: The information and recommendations contained herein are based upon data believed to be accurate.
However, no guarantee or warranty of any kind expressed or implied is made with respect to the information
contained herein.
April 03

2600 CAMPUS DRIVE, SUITE D | LAFAYETTE, CO 80026 | 303-664-0394 | FAX: 303-664-0392|

[Link]