FEMPipe Tool When thermoplastic parts are being welded with a hot plate, the join partners are plasticized by means of a heat element and
then joined together under pressure. The parts can be plasticized either through contact with the heat element or by heat
Design radiation, without contact.
Joining Techniques
Processing
Downloads . . .
LANXESS Links
LANXESSone
LANXESS USA
LANXESS Global
LANXESS Press Center Intercooler manifold, Mercedes BR900 6-cylinder engine
Strengths
z Cost-effective process
z Large batch sizes possible
z Weld line can take heavy mechanical load
z Same strength as basic material can be attained
Basic principle of hot-plate welding process
When parts are being welded together by a hot plate, the join partners are clamped in place on the moving slides of the
machine and run up against the hot plate. The contact process is started under the warming-up pressure; the purpose of this is
to overcome the tolerance and attain a uniform contact surface at the hot plate. Once the preset travel distance has been
reached, the heating phase starts in which a melt cushion is created under virtually no pressure at all. Then the slides are run
back until the hot plate can be with-drawn completely freely, and then the welding process as such starts in which the melted
join partners are pressed together to form the join.
Diagram showing the sequence of hot plate welding
All Lanxess thermoplastic materials can be hot-plate-welded, but Durethan KU2-2140/30 was developed specifically for this
process. Its distinguishing features are a lower level of melting adhesion and a bigger welding-process window. This has been
achieved by increasing the melt viscosity.
[Link] 2010/8/17
TechCenter - TechServices - Joining Techniques 2 2
Limitations of Use
z 3-dimensional contours are easy to achieve with contour heating elements.
z Tight weld lines are easy to achieve, due to the high melt-layer density and consequent big welding displacement.
z Hard-soft combinations are basically possible as well, but a certain minimum dimensional stability must be ensured.
z The cycle time is very high, at least 40 seconds, or 10 to 15 seconds less in the case of high-temperature welding (over 400
C).
z The resultant melt flash can be covered with a flash trap.
z Due to the low welding force of small join areas, these can only be welded with special equipment.
z With certain materials, the melt adhesion at the heating element can result in stringing or even in a partial shearing-off of
the melt. It is possible to work with a Teflon non-stick coating at heating-element temperatures up to about 260 C.
Processing
Recommended setting parameters:
Resin Hot Plate Temperatures Joining Pressure
Centrex ASA 230 - 410 C 0,4 - 0,8 N/mm2
Durethan PA 6 and 66 280 - 450 C 0,1 - 1,0 N/mm2
Lustran ABS / Novodur 230 - 410 C 0,4 - 0,8 N/mm2
Pocan PBT 280 - 350 C 0,1 - 1,0 N/mm2
Triax PA+ABS 250 - 410 C 0,2 - 0,9 N/mm2
Various different types of drive technology are in use in hot plate welding machines:
z Electric motors (greatest accuracy, highest process speeds)
z Pneumatic (lowest-cost process variant)
z Hydraulic (greatest force and adequate accuracy)
The materials used for the heating element are aluminum-bronze alloys, or high-strength aluminum alloys for the lower
temperatures and steel for high-temperature welding.