Materials for long service life

Bearing technology | Plain bearing | iglidur® Endurance runner

Materials for long service life Temperature [°C] 123) +180 – +

Surface pressure [MPa] 124) 75 – +
Every iglidur plain bearing is naturally optimised for wear, but the materials in this group are characterised by very low
® iglidur® W360
Coefficient of friction [µ] 125) 0.07 – +
rates of wear and therefore the ability to provide a long service life. Endurance runner up to +180°C Wear [µm/km] 125) 0.24 – +
Besides the absolute service life and price level, they differ inter alia in terms of potential temperature and load ranges, Price index ​ – +
and the suitability in conjunction with special shaft materials.
Temperature [°C] 123) +90 – +
Online product finder Online service life calculation Surface pressure [MPa] 124) 45 – +
www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert iglidur® L250
Coefficient of friction [µ] 125) 0.18 – +
For fast rotating applications Wear [µm/km] 125) 0.20 – +
Price index ​ – +

Temperature [°C] 123) +90 – + Temperature [°C] 123) +180 – +

Surface pressure [MPa] 124) 35 – + Surface pressure [MPa] 124) 59 – +
iglidur® J iglidur® L350
Coefficient of friction [µ] 125) 0.16 – + Coefficient of friction [µ] 125) 0.12 – +
The versatile endurance runner Wear [µm/km] 125) 0.29 – +
For high rotational speeds Wear [µm/km] 125) 1.50 – +
Price index ​ – + Price index ​ – +

Temperature [°C] 123) +90 – + Temperature [°C] 123) +250 – +

iglidur® W300 Surface pressure [MPa] 124) 60 – + Surface pressure [MPa] 124) 70 – +
iglidur® L500
The classic endurance runner Coefficient of friction [µ] 125) 0.18 – + Coefficient of friction [µ] 125) 0.19 – +
Wear [µm/km] 125) – +
For extreme rotational speeds Wear [µm/km] 125) – +
up to 30MPa 0.33 1.00

Price index ​ – + Price index ​ – +

iglidur® J3 Temperature [°C] 123) +90 – + Temperature [°C] 123) +90 – +

Surface pressure [MPa] 124) 45 – + Surface pressure [MPa] 124) 23 – +
The new endurance runner: iglidur® R
Coefficient of friction [µ] 125) 0.13 – + Coefficient of friction [µ] 125) 0.20 – +
specialist for pivoting applications Wear [µm/km] 125) 0.07 – +
Low-cost Wear [µm/km] 125) 0.95 – +
and pulsating loads Price index ​ – + Price index ​ – +

Temperature [°C] 123) +90 – + Temperature [°C] 123) +90 – +

Surface pressure [MPa] 124) 44 – + Surface pressure [MPa] 124) 23 – +
iglidur® J3B iglidur® D
Coefficient of friction [µ] 125) 0.17 – + Coefficient of friction [µ] 125) 0.25 – +
Proven long-life material in black Wear [µm/km] 125) 0.07 – +
Low-cost with silicone Wear [µm/km] 125) 1.91 – +
Price index ​ – +

iglidur® J350 Temperature [°C] 123) +180 – + Temperature [°C] 123) +90 – +
Surface pressure [MPa] 124) 60 – + Surface pressure [MPa] 124) 23 – +
Endurance runner with high iglidur® J200
Coefficient of friction [µ] 125) 0.16 – + Coefficient of friction [µ] 125) 0.15 – +
dimensional stability at high Wear [µm/km] 125) 1.14 – +
Specialist for linear movement Wear [µm/km] 125) 1.30 – +
temperatures Price index ​ – + Price index ​ – +

Temperature [°C] 123) +120 – + Temperature [°C] 123) +70 – +

Surface pressure [MPa] 124) 40 – + Surface pressure [MPa] 124) 18 – +
iglidur® J260 iglidur® E7
Coefficient of friction [µ] 125) 0.16 – + Coefficient of friction [µ] 125) 0.13 – +
Ideal for plastic shafts Wear [µm/km] 125) 0.11 – +
Ideal for pivoting movement Wear [µm/km] 125) 0.14 – +
Price index ​ – + Price index ​ – +

123)
max. long-term application temperature 124)
max. recommended surface pressure at +20°C 125)
best combination for p = 1MPa,
v = 0.3m/s, rotating

156 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 157
 The versatile endurance runner
Wear resistance on (almost) all shafts,
very low coefficient of friction
iglidur J ®

When to use it?

●● For high speeds
●● When highest wear resistance at low to medium pressures is required
●● Low wear against different shafts
●● When a low coefficient of friction in dry operation is requested
●● For vibration dampening
●● When good chemical resistance is required
●● For best performance with soft shaft materials
●● Low moisture absorption

When not to use?

●● When high pressures occur
iglidur® G, iglidur® W300
●● When short-term temperatures higher than +120°C occur
iglidur® G, iglidur® Z
●● When a cost-effective plain bearing for occasional movements is necessary
iglidur® G

158
iglidur® J iglidur® J
+90°C +90°C
35MPa 35MPa
Bearing technology | Plain bearing | iglidur® J Technical data
General properties​ Testing method

Density g/cm³ 1.49 ​ –50°C up to

Ø +90°C
1.5 – Colour yellow ​
120.0mm Max. moisture absorption at +23°C and 50% r.h. % weight 0.3 DIN 53495
Max. moisture absorption % weight 1.3 ​
Coefficient of friction, dynamic, against steel µ 0.06 – 0.18 ​ 35MPa
pv value, max. (dry) MPa · m/s 0.34 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,400 DIN 53457
The versatile endurance runner Flexural strength at +20°C MPa 73 DIN 53452

Bar stock,
Wear resistance on (almost) all shafts, very low Compressive strength MPa 60 ​
Max. recommended surface pressure (+20°C) MPa 35 ​
round bar
Page 674 coefficient of friction Shore D hardness 74 DIN 53505
Physical and thermal properties
One main advantage of iglidur® J plain bearings is the combination of a low coefficient of friction in dry Max. application temperature long-term °C +90 ​
operation and the low stickslip tendency. With a maximum recommended surface pressure of 35MPa, FOOD
Max. application temperature short-term °C +120 ​
iglidur® J plain bearings are not suitable for extreme loads. Min. application temperature °C –50 ​
Bar stock, ●● Over 250 sizes available from stock Thermal conductivity W/m · K 0.25 ASTM C 177
plate ●● High wear resistance
Page 684 Coefficient of thermal expansion (at +23°C) K–1 · 10–5 10 DIN 53752
●● Low coefficient of friction Electrical properties
●● Vibration-dampening Specific contact resistance Ωcm > 1013 DIN IEC 93
●● High chemical resistance Surface resistance Ω > 1012 DIN 53482
●● Recommended for soft shafts
Table 01: Material properties
●● Low moisture absorption
tribo-tape liner
Page 691
One main advantage of iglidur® J plain bearings is the Resistance to weathering
Typical application areas
combination of a low coefficient of friction in dry operation iglidur® J plain bearings are resistant to weathering. The
●● Automation
and the low stickslip tendency. material properties are slightly affected. Discoloration
●● Printing industry
occurs.
●● Beverage industry
Moisture absorption
●● Aerospace engineering
Under standard climatic conditions, the moisture absorption Mechanical properties
Piston rings ●● Cleanroom
Page 584 of iglidur® J plain bearings is approximately 0.3% weight. With increasing temperatures, the compressive strength of
The saturation limit in water is 1.3% weight. These values iglidur® J plain bearings decreases. Diagram 02 shows this
Descriptive technical specifications are so low that a moisture expansion need to be considered inverse relationship. However, at the long-term maximum
Wear resistance at +23°C – + only in extreme cases. temperature of +90°C the permissible surface pressure
is around 20MPa. The maximum recommended surface
Wear resistance at +90°C – +
Vacuum pressure is a mechanical material parameter. No conclusions
Two hole Wear resistance at +150°C – + In vacuum, any present moisture is released as vapour. regarding the tribological properties can be drawn from this.
flange
bearings Use in vacuum is only possible with dehumidified iglidur® J With a maximum recommended surface pressure of
Page 603 Low coefficient of friction – +
bearings. 35MPa, iglidur® J plain bearings are not suitable for
Low moisture absorption – + extreme loads. Diagram 03 shows the elastic deformation
Radiation resistance of iglidur® J at radial loads.
Wear resistance under water – +
Plain bearings made from iglidur® J are resistant up to a Surface pressure, page 41
Moulded High media resistance – + radiation intensity of 3 · 10²Gy.
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 848 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

160 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 161
iglidur® J iglidur® J
+90°C +90°C
35MPa 35MPa
Bearing technology | Plain bearing | iglidur® J Technical data
Permissible surface speeds Installation tolerances 100.0 0.30

The low coefficient of friction and the very low stick iglidur ® J plain bearings are standard bearings for 0.25
10.0

Coefficient of friction [µ]

slip tendency of iglidur® J plain bearings are particularly shafts with h tolerance (recommended minimum h9). 0.20
important at very low speeds. However, iglidur® J can also The bearings are designed for press-fit into a housing 1.0 0.15

Pressure [MPa]
be used for high speeds of over 1m/s. In both cases the machined to a H7 tolerance. After being assembled into a 0.10
static friction is very low and stick slip does not occur. The nominal size housing, in standard cases the inner diameter 0.1
0.05
maximum values shown in table 03 can only be achieved automatically adjusts to the E10 tolerances. For particular
0.01 0.00
at low pressures. At the given speeds, friction can cause dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 5 10 15 20 25 30 35
a temperature increase to maximum permissible levels. In thickness (please see product range table).
Surface speed [m/s] Load [MPa]
practice, though, this level is rarely reached due to varying Testing methods, page 57
application conditions. Diagram 01: Permissible pv values for iglidur® J plain Diagram 05: Coefficient of friction as a function of the load,
Surface speed, page 44 bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
Temperature Alcohols +
iglidur® J plain bearings can be used between –50°C and Diluted acids 0 up to – 120 1.2
+90°C; the short-term maximum permissible temperature Diluted alkalines +
100 1.0

Cf53, hard-chromed
is +120°C. Wear increases significantly at temperatures Fuels +

304 stainless steel

Free cutting steel
80 0.8

High grade steel

HR carbon steel
above +80°C. For temperatures over +60°C an additional Greases, oils without additives +

H.a. aluminium
60 0.6
securing is required. Hydrocarbons +

Wear [µm/km]
Application temperatures, page 49 Strong acids – 40 0.4

Load [MPa]

Cf53
Additional securing, page 49 Strong alkalines + up to 0 20 0.2
All information given at room temperature [+20°C] 0 0.0
Friction and wear Table 02: Chemical resistance 20 30 40 50 60 70 80 90
Similar to wear resistance, the coefficient of friction µ also Chemical table, page 1636 Temperature [°C]
changes with the surface speed and load (diagrams 04 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
and 05). ​ ​ Rotating Oscillating linear function of temperature (35MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
Coefficient of friction and surfaces, page 47 long-term m/s 1.5 1.1 8.0
Wear resistance, page 50 short-term m/s 3.0 2.1 10.0 12.5 3.5
Table 03: Maximum surface speeds rotating
3.0 oscillating
10.0
Shaft materials +23°C 2.5
The friction and wear are also dependent, to a large ​ Dry Greases Oil Water 7.5 +60°C
2.0
degree, on the shaft material. With increasing shaft surface Coefficient of friction µ 0.06 – 0.18 0.09 0.04 0.04

Deformation [%]
5.0 1.5

Wear [µm/km]
finish, the coefficient of friction also increases. For iglidur® J Table 04: Coefficient of friction against steel (Ra = 1μm, 1.0
2.5
a ground surface with an average surface finish Ra 50HRC) 0.5
= 0.1 – 0.3µm is recommended. Diagrams 06 and 07 0.0 0.0
show the test results of iglidur® J plain bearings running ​ Housing Plain bearing Shaft 0.0 12.5 25.0 37.5 50.0 Cf53 hard 304SS HR carbon
chromed steel
against various shaft materials. When compared to most Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa]
iglidur® materials, iglidur® J plain bearings have very low 0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for rotating and oscillating applications
wear results at low loads compared with all shaft materials >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with different shaft materials, p = 2MPa
tested. Also, for increasing loads up to 5MPa, the wear > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
resistance of iglidur® J is excellent. If the shaft material you > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 0.4

plan on using is not shown in these test results, please > 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
Coefficient of friction [µ]

contact us. > 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 0.3
Shaft materials, page 52 > 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
0.2
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
Table 05: Important tolerances for plain bearings according
0.1
to ISO 3547-1 after press-fit
0.05 0.10 0.15 0.20 0.25 0.30 0.35
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

162 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 163
iglidur® J iglidur® J
+90°C +90°C
35MPa 35MPa
Bearing technology | Plain bearing | iglidur® J Product range
Sleeve bearing (form S) d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.
Tolerance3) h13 Tolerance3) h13
f1

30°
[mm] [mm] [mm] [mm] [mm] [mm]
12.0 14.0 6.0 JSM-1214-06 20.0 +0.020 23.0 25.0 JSM-2023-25
12.0 14.0 8.0 JSM-1214-08 20.0 +0.104 23.0 30.0 JSM-2023-30

d1

d2
0.5
12.0 14.0 9.0 JSM-1214-09 20.0 26.0 6.0 JSM-2026-06
+0.032
12.0 14.0 10.0 JSM-1214-10 20.0 +0.065 26.0 20.0 JSM-2026-20

30°
+0.102
b1 12.0 14.0 12.0 JSM-1214-12 20.0 +0.195 26.0 25.0 JSM-2026-25
12.0 14.0 15.0 JSM-1214-15 20.0 26.0 30.0 JSM-2026-30
12.0 14.0 20.0 JSM-1214-20 21.0 24.0 12.0 JSM-2124-12
2)
Thickness < 0.6mm: Chamfer = 20° 12.0 +0.050 16.0 12.0 JSM-1216-12 22.0 25.0 15.0 JSM-2225-15
Chamfer in relation to d1 12.0 +0.160 16.0 17.0 JSM-1216-17 22.0 25.0 20.0 JSM-2225-20
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and 13.0 15.0 10.0 JSM-1315-10 22.0 25.0 25.0 JSM-2225-25
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions 13.0 15.0 20.0 JSM-1315-20 22.0 25.0 30.0 JSM-2225-30
13.0 16.0 18.5 JSM-1316-185 23.0 26.0 12.0 JSM-2326-12
Order example: JSM-0104-02 – no minimum order quantity. 14.0 16.0 5.0 JSM-1416-05 24.0 27.0 15.0 JSM-2427-15
J iglidur® material S Sleeve bearing M Metric 01 Inner Ø d1 04 Outer Ø d2 02 Total length b1 14.0 +0.032 16.0 8.0 JSM-1416-08 24.0 27.0 20.0 JSM-2427-20
+0.040
14.0 +0.102 16.0 10.0 JSM-1416-10 24.0 27.0 25.0 JSM-2427-25
+0.124
14.0 16.0 15.0 JSM-1416-15 24.0 27.0 30.0 JSM-2427-30
d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No. 14.0 16.0 20.0 JSM-1416-20 24.0 27.0 46.0 JSM-2427-46
Tolerance3) h13 Tolerance3) h13 14.0 16.0 25.0 JSM-1416-25 25.0 28.0 12.0 JSM-2528-12
[mm] [mm] [mm] [mm] [mm] [mm] 14.0 18.0 18.0 JSM-1418-18 25.0 28.0 15.0 JSM-2528-15
1.5 +0.014 4.0 2.0 JSM-0104-02 +0.020 +0.050 25.0 28.0 20.0 JSM-2528-20
6.0 8.0 10.0 JSM-0608-10 14.0 20.0 20.0 JSM-1420-20
2.0 +0.054 3.5 7.0 JSM-0203-07 +0.068 +0.160 25.0 28.0 25.0 JSM-2528-25
2.0 +0.020 5.0 2.5 JSM-0205-02 6.0 +0.030 9.0 6.0 JSM-0609-06 15.0 17.0 6.0 JSM-1517-06 25.0 28.0 30.0 JSM-2528-30
2.5 +0.080 6.0 2.5 JSM-0206-02 6.0 +0.105 10.0 10.0 JSM-0610-10 15.0 17.0 10.0 JSM-1517-10 25.0 28.0 60.0 JSM-2528-60
3.0 +0.014 4.5 5.0 JSM-0304-05 7.0 9.0 5.0 JSM-0709-05 15.0 17.0 12.0 JSM-1517-12 25.0 30.0 40.0 JSM-2530-40
3.0 +0.054 4.5 9.0 JSM-0304-09 7.0 9.0 7.0 JSM-0709-07 15.0 17.0 15.0 JSM-1517-15 25.0 32.0 25.0 JSM-2532-25
+0.065
3.0 5.0 4.0 JSM-0305-04 7.0 9.0 9.0 JSM-0709-09 15.0 17.0 20.0 JSM-1517-20 25.0 32.0 32.0 JSM-2532-32
+0.195
3.0 +0.020 7.0 14.0 JSM-0307-14 7.0 9.0 12.5 JSM-0709-125 15.0 +0.032 17.0 25.0 JSM-1517-25 25.0 32.0 35.0 JSM-2532-35
3.0 +0.080 8.0 4.0 JSM-0308-04 8.0 10.0 3.0 JSM-0810-03 15.0 +0.102 18.0 10.0 JSM-1518-10 26.0 30.0 20.0 JSM-2630-20
+0.025
3.0 8.0 5.0 JSM-0308-05 8.0 10.0 4.0 JSM-0810-04 16.0 18.0 10.0 JSM-1618-10 +0.040
+0.083 27.0 30.0 20.0 JSM-2730-20
4.0 5.5 4.0 JSM-0405-04 8.0 10.0 6.0 JSM-0810-06 16.0 18.0 12.0 JSM-1618-12 +0.124
4.0 5.5 6.0 JSM-0405-06 8.0 10.0 8.0 JSM-0810-08 16.0 18.0 15.0 JSM-1618-15 28.0 32.0 20.0 JSM-2832-20
+0.065
4.0 5.5 8.0 JSM-0405-08 8.0 10.0 10.0 JSM-0810-10 16.0 18.0 20.0 JSM-1618-20 28.0 32.0 25.0 JSM-2832-25
+0.020 +0.195
5.0 7.0 4.6 JSM-0507-046 8.0 10.0 12.0 JSM-0810-12 16.0 18.0 25.0 JSM-1618-25 28.0 32.0 30.0 JSM-2832-30
+0.068
5.0 7.0 5.0 JSM-0507-05 8.0 10.0 16.0 JSM-0810-16 16.0 20.0 16.0 JSM-1620-16 30.0 34.0 20.0 JSM-3034-20
+0.050
5.0 7.0 10.0 JSM-0507-10 8.0 +0.040 12.0 10.0 JSM-0812-10 16.0 22.0 16.0 JSM-1622-16 30.0 +0.040 34.0 25.0 JSM-3034-25
+0.160
5.0 7.0 14.0 JSM-0507-14 8.0 +0.130 12.0 12.0 JSM-0812-12 16.0 22.0 20.0 JSM-1622-20 30.0 +0.124 34.0 30.0 JSM-3034-30
+0.020 9.0 11.0 10.0 JSM-0911-10 17.0 19.0 6.0 JSM-1719-06 30.0 34.0 40.0 JSM-3034-40
5.0 7.0 15.0 JSM-0507-15
+0.080 10.0 12.0 5.0 JSM-1012-05 18.0 20.0 10.0 JSM-1820-10 +0.065
30.0 38.0 40.0 JSM-3038-40
+0.030 10.0 12.0 6.0 JSM-1012-06 18.0 +0.032 20.0 15.0 JSM-1820-15 +0.195
5.0 8.0 5.0 JSM-0508-05
+0.105 10.0 12.0 8.0 JSM-1012-08 18.0 +0.102 20.0 20.0 JSM-1820-20 32.0 36.0 20.0 JSM-3236-20
+0.025
6.0 7.0 3.0 JSM-0607-03 10.0 12.0 10.0 JSM-1012-10 18.0 20.0 25.0 JSM-1820-25 32.0 36.0 30.0 JSM-3236-30
+0.083
6.0 7.0 5.0 JSM-0607-05 10.0 12.0 11.0 JSM-1012-11 19.0 22.0 14.0 JSM-1922-14 32.0 36.0 40.0 JSM-3236-40
+0.010
6.0 7.0 8.0 JSM-0607-08 10.0 12.0 12.0 JSM-1012-12 20.0 22.0 20.0 JSM-2022-20 32.0 37.0 25.0 JSM-3237-25
+0.058 +0.050
6.0 7.0 12.5 JSM-0607-12.5 10.0 12.0 15.0 JSM-1012-15 20.0 22.0 30.0 JSM-2022-30 32.0 38.0 50.0 JSM-3238-50
+0.040 +0.150
6.0 7.0 14.0 JSM-0607-14 10.0 12.0 20.0 JSM-1012-20 20.0 23.0 10.0 JSM-2023-10 35.0 39.0 20.0 JSM-3539-20
+0.124
6.0 8.0 4.3 JSM-0608-043 10.0 +0.040 14.0 10.0 JSM-1014-10 20.0 23.0 15.0 JSM-2023-15 35.0 39.0 30.0 JSM-3539-30
+0.020
6.0 8.0 6.0 JSM-0608-06 10.0 +0.130 14.0 16.0 JSM-1014-16 20.0 23.0 20.0 JSM-2023-20 35.0 39.0 40.0 JSM-3539-40
+0.068
6.0 8.0 8.0 JSM-0608-08 35.0 39.0 50.0 JSM-3539-50
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

164 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 165
iglidur® J iglidur® J
+90°C +90°C
35MPa 35MPa
Bearing technology | Plain bearing | iglidur® J Bearing technology | Plain bearing | iglidur® J
d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No. Flange bearing (form F)
.5
.0
Tolerance3) h13 Tolerance3) h13 ax
f1

30
rm

°
[mm] [mm] [mm] [mm] [mm] [mm]
36.0 40.0 45.0 JSM-3640-45 50.0 55.0 20.0 JSM-5055-20
40.0 44.0 20.0 JSM-4044-20 50.0 55.0 30.0 JSM-5055-30

d2
d3

d1
+0.050
40.0 +0.050 44.0 30.0 JSM-4044-30 50.0 55.0 40.0 JSM-5055-40
+0.150
40.0 +0.150 44.0 35.0 JSM-4044-35 50.0 55.0 50.0 JSM-5055-50
40.0 44.0 40.0 JSM-4044-40 50.0 55.0 60.0 JSM-5055-60 b2

40.0 44.0 50.0 JSM-4044-50 55.0 60.0 60.0 JSM-5560-60 b1

+0.080 60.0 65.0 60.0 JSM-6065-60

42.0 46.0 73.0 JSM-4246-73
+0.240 65.0 70.0 50.0 JSM-6570-50 2)
Thickness < 0.6mm: Chamfer = 20°
+0.060
45.0 50.0 20.0 JSM-4550-20 70.0 75.0 60.0 JSM-7075-60 Chamfer in relation to d1
+0.180
45.0 +0.025 50.0 30.0 JSM-4550-30 75.0 80.0 60.0 JSM-7580-60 d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and
45.0 +0.125 50.0 40.0 JSM-4550-40 80.0 85.0 100.0 JSM-8085-100 f1 [mm] 0.3 0.5 0.8 1.2 special dimensions
45.0 50.0 50.0 JSM-4550-50 80.0 86.0 60.0 JSM-8086-60
100.0 +0.072 105.0 100.0 JSM-100105-100 Order example: JFM-0304-03 – no minimum order quantity.
110.0 +0.212 115.0 60.0 JSM-110115-60 J iglidur® material F Flange bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 03 Total length b1
3)
After press-fit. Testing methods, page 57

d1 d1 d2 d3 b1 b2 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) d133) h13 h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
3.0 4.5 7.5 3.0 0.75 JFM-0304-03 8.0 12.0 16.0 9.0 2.00 JFM-0812-09
+0.014
3.0 4.5 7.5 4.5 0.75 JFM-0304-045 10.0 12.0 18.0 5.0 1.00 JFM-1012-05
+0.054
3.0 4.5 7.5 5.0 0.75 JFM-0304-05 10.0 12.0 18.0 7.0 1.00 JFM-1012-07
+0.020 10.0 12.0 18.0 9.0 1.00 JFM-1012-09
3.0 6.0 9.0 10.0 1.50 JFM-0306-10
+0.080 10.0 12.0 18.0 10.0 1.00 JFM-1012-10
4.0 5.5 9.5 3.0 0.75 JFM-0405-03 10.0 +0.025 12.0 18.0 12.0 1.00 JFM-1012-12
4.0 5.5 9.5 6.0 0.75 JFM-0405-06 10.0 +0.083 12.0 18.0 15.0 1.00 JFM-1012-15
5.0 6.0 10.0 5.0 0.50 JFM-0506-05 10.0 12.0 18.0 17.0 1.00 JFM-1012-17
5.0 7.0 11.0 3.0 1.00 JFM-0507-03 10.0 12.0 18.0 18.0 1.00 JFM-1012-18
+0.020
5.0 7.0 11.0 5.0 1.00 JFM-0507-05 10.0 12.0 15.0 3.5 1.00 JFM-101215-035
+0.068
6.0 8.0 12.0 4.0 1.00 JFM-0608-04 10.0 14.0 17.5 14.0 1.00 JFM-1014-14
6.0 8.0 12.0 6.0 1.00 JFM-0608-06 10.0 16.0 22.0 16.0 3.00 JFM-1016-16
6.0 8.0 12.0 8.0 1.00 JFM-0608-08 11.0 13.0 18.0 5.0 1.00 JFM-1113-05
6.0 8.0 12.0 10.0 1.00 JFM-0608-10 12.0 14.0 20.0 4.0 1.00 JFM-1214-04
+0.030 12.0 14.0 20.0 5.0 1.00 JFM-1214-05
6.0 10.0 14.0 10.0 2.00 JFM-0610-10
+0.105 12.0 14.0 20.0 7.0 1.00 JFM-1214-07
8.0 10.0 15.0 3.8 1.00 JFM-0810-038 12.0 +0.032 14.0 20.0 9.0 1.00 JFM-1214-09
8.0 10.0 15.0 5.0 1.00 JFM-0810-05 12.0 +0.102 14.0 20.0 12.0 1.00 JFM-1214-12
Available from stock Ordering note 8.0 10.0 15.0 6.0 1.00 JFM-0810-06 12.0 14.0 20.0 15.0 1.00 JFM-1214-15
Detailed information about delivery time online. Our prices are scaled according to order 8.0 10.0 15.0 7.0 1.00 JFM-0810-07 12.0 14.0 20.0 17.0 1.00 JFM-1214-17
www.igus.eu/24 quantities, current prices can be found online. 8.0 10.0 15.0 8.0 1.00 JFM-0810-08 12.0 14.0 18.0 4.5 1.00 JFM-121418-045
Online ordering 8.0 +0.025 10.0 15.0 9.5 1.00 JFM-0810-09 12.0 14.0 18.0 10.0 1.00 JFM-121418-10
Discount scaling 8.0 +0.083 10.0 15.0 10.0 1.00 JFM-0810-10 12.0 18.0 24.0 8.0 3.00 JFM-1218-08
Including delivery times, prices, online tools +0.050
1–9 50 – 99 500 – 999 8.0 10.0 12.0 16.0 1.00 JFM-081012-16 12.0 18.0 24.0 12.0 3.00 JFM-1218-12
www.igus.eu/J +0.160
10 – 24 100 – 199 1,000 – 2,499 8.0 10.0 12.5 10.0 1.00 JFM-0810125-10 12.0 18.0 22.0 20.0 3.00 JFM-1218-20
25 – 49 200 – 499 2,500 – 4,999 8.0 10.0 14.0 10.0 1.00 JFM-081014-10 14.0 16.0 22.0 3.0 1.00 JFM-1416-03
+0.032
No minimum order value. 8.0 10.0 16.0 11.0 2.00 JFM-081016-11 14.0 16.0 22.0 10.0 1.00 JFM-1416-10
+0.102
No low-quantity surcharges. 8.0 12.0 16.0 6.0 2.00 JFM-0812-06 14.0 16.0 22.0 12.0 1.00 JFM-1416-12
Free shipping within Germany for orders 3)
After press-fit. Testing methods, page 57
above €150.

166 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 167
iglidur® J iglidur® J
+90°C +90°C
35MPa 35MPa
Bearing technology | Plain bearing | iglidur® J Bearing technology | Plain bearing | iglidur® J
d1 d1 d2 d3 b1 b2 Part No. d1 d1 d2 d3 b1 b2 Part No. Thrust washer (form T)
d1
Tolerance3) d133) h13 h13 Tolerance3) d133) h13 h13

s
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
d2
14.0 16.0 22.0 17.0 1.00 JFM-1416-17 25.0 28.0 35.0 14.5 1.50 JFM-2528-14.5
14.0 18.0 22.0 20.0 2.00 JFM-141822-20 25.0 +0.040 28.0 35.0 21.5 1.50 JFM-2528-21
14.0 18.0 25.0 24.0 2.00 JFM-141825-24 25.0 +0.124 28.0 39.0 5.0 1.50 JFM-252839-05
15.0 +0.032 17.0 23.0 4.0 1.00 JFM-1517-04 25.0 28.0 39.0 7.5 1.50 JFM-252839-075
15.0 +0.102 17.0 23.0 5.5 1.00 JFM-1517-055 25.0 32.0 38.0 20.0 4.00 JFM-2532-20

d5
+0.065
15.0 17.0 23.0 9.0 1.00 JFM-1517-09 25.0 32.0 38.0 25.0 4.00 JFM-2532-25 d4
+0.195
15.0 17.0 23.0 12.0 1.00 JFM-1517-12 28.0 32.0 35.0 7.0 2.00 JFM-283235-07
15.0 17.0 23.0 17.0 1.00 JFM-1517-17 28.0 32.0 39.0 20.0 2.00 JFM-283239-20 d6

h
+0.050 30.0 32.0 40.0 12.0 1.00 JFM-303240-12
15.0 21.0 27.0 20.0 3.00 JFM-1521-20 +0.040
+0.160 30.0 34.0 42.0 16.0 2.00 JFM-3034-16 Dimensions according to ISO 3547-1 and
+0.124
16.0 18.0 24.0 6.0 1.00 JFM-1618-06 30.0 34.0 42.0 20.0 2.00 JFM-3034-20 special dimensions
16.0 +0.032 18.0 24.0 12.0 1.00 JFM-1618-12 30.0 34.0 42.0 26.0 2.00 JFM-3034-26
16.0 +0.102 18.0 24.0 16.0 1.00 JFM-1618-16 +0.080 Order example: JTM-1224-015 – no minimum order quantity.
30.0 38.0 44.0 20.0 4.00 JFM-3038-20
16.0 18.0 24.0 17.0 1.00 JFM-1618-17 +0.240 J iglidur® material T Thrust washer M Metric 12 Inner Ø d1 24 Outer Ø d2 015 Thickness s
16.0 +0.050 22.0 28.0 12.0 3.00 JFM-1622-12 30.0 +0.065 38.0 44.0 30.0 4.00 JFM-3038-30
16.0 +0.160 22.0 28.0 15.0 3.00 JFM-1622-15 30.0 +0.195 38.0 44.0 36.0 4.00 JFM-3038-36
17.0 19.0 25.0 9.0 1.00 JFM-1719-09 35.0 39.0 47.0 12.0 2.00 JFM-3539-12 d1 d2 d4 d5 h d6 s Part No.
17.0 19.0 25.0 21.0 1.00 JFM-1719-21 35.0 39.0 47.0 16.0 2.00 JFM-3539-16 +0.25 –0.25 –0.12 +0.375 +0.2/–0.2 +0.12 –0.05
+0.12 +0.125
18.0 20.0 26.0 4.0 1.00 JFM-1820-04 35.0 39.0 47.0 26.0 2.00 JFM-3539-26
18.0 20.0 26.0 12.0 1.00 JFM-1820-12 40.0 44.0 52.0 20.0 2.00 JFM-4044-20 [mm] [mm] [mm] [mm] [mm] [mm] [mm]
+0.032
18.0 20.0 26.0 17.0 1.00 JFM-1820-17 40.0 44.0 52.0 30.0 2.00 JFM-4044-30 12 24 18 1.5 1 24 1.5 JTM-1224-015
+0.102 +0.050
18.0 20.0 26.0 22.0 1.00 JFM-1820-22 40.0 44.0 52.0 40.0 2.00 JFM-4044-40 12 34 4) 4)
1 34 1.5 JTM-1234-015
+0.150
18.0 21.0 25.0 12.0 1.00 JFM-1821-12 45.0 50.0 58.0 12.0 2.00 JFM-4550-12 14 20 4) 4)
1 20 1.5 JTM-1420-015
19.0 22.0 26.0 23.0 1.00 JFM-1922-23 45.0 50.0 58.0 20.0 2.00 JFM-4550-20 20 36 28 3 1 36 1.5 JTM-2036-015
19.0 22.0 26.0 36.0 1.00 JFM-1922-36 45.0 50.0 58.0 50.0 2.00 JFM-4550-50 28 42 35 3 1 42 2 JTM-2842-020
20.0 23.0 30.0 11.5 1.50 JFM-2023-11 50.0 55.0 63.0 11.5 2.00 JFM-5055-115 30 39 4) 4)
1 39 1.5 JTM-3039-015
20.0 +0.040 23.0 30.0 15.5 1.50 JFM-2023-15.5 50.0 55.0 63.0 50.0 2.00 JFM-5055-50 56 70 4) 4)
0.7 70 1 JTM-5670-010
20.0 +0.124 23.0 30.0 16.5 1.50 JFM-2023-16 55.0 60.0 68.0 50.0 2.00 JFM-5560-50 139 188 4) 4)
1.5 188 2 JTM-139188-020
20.0 23.0 30.0 21.5 1.50 JFM-2023-21 60.0 65.0 73.0 37.0 2.00 JFM-6065-37 4)
Design without fixing hole
+0.060
20.0 26.0 32.0 15.0 3.00 JFM-2026-15 60.0 65.0 73.0 50.0 2.00 JFM-6065-50
+0.065 +0.180
20.0 26.0 32.0 20.0 3.00 JFM-2026-20 60.0 70.0 78.0 60.0 2.00 JFM-6570-60
+0.195
20.0 26.0 32.0 25.0 3.00 JFM-2026-25 70.0 75.0 83.0 50.0 2.00 JFM-7075-50
22.0 25.0 32.0 8.0 1.50 JFM-222532-08 90.0 95.0 103.0 100.0 2.50 JFM-9095-100
24.0 30.0 36.0 30.0 3.00 JFM-2430-30 100.0 +0.072 105.0 113.0 100.0 2.50 JFM-100105-100
+0.040
25.0 28.0 35.0 6.0 1.50 JFM-2528-06 110.0 +0.212 115.0 123.0 100.0 2.50 JFM-110115-100
+0.124
25.0 28.0 35.0 11.5 1.50 JFM-2528-11 120.0 125.0 133.0 100.0 2.50 JFM-120125-100
25.0 28.0 35.0 12.0 1.50 JFM-2528-12
Available from stock Ordering note
3)
After press-fit. Testing methods, page 57
Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online.

Online ordering
Discount scaling
Including delivery times, prices, online tools
1–9 50 – 99 500 – 999
www.igus.eu/J
10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999

No minimum order value.

No low-quantity surcharges.
Free shipping within Germany for orders
above €150.

168 3D CAD, finder and service life calculation ... www.igus.eu/J Lubrication-free made easy ... from stock ... no minimum order quantity 169
The classic endurance runner
up to 30MPa
Excellent wear resistance on (virtually)
all shafts
iglidur W300 ®

When to use it?

●● When especially high service life is necessary
●● When low coefficient of dynamic friction and high wear resistance are required
●● For use on 304 stainless steel shafts
●● For harsh environments and rough shafts
●● Dirt-resistant

When not to use?

●● For high loads starting at 50MPa
iglidur® Q
●● When continuous operating temperatures are higher than +90°C
iglidur® H, iglidur® X
●● For very wet environments
iglidur® P
●● When a cost-effective plain bearing is required
iglidur® G
iglidur® W300 iglidur® W300
+90°C +90°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® W300 Technical data
General properties​ Testing method

Density g/cm³ 1.24 ​ –40°C up to

Ø +90°C
2.0 – Colour yellow ​
120.0mm Max. moisture absorption at +23°C and 50% r.h. % weight 1.3 DIN 53495
Max. moisture absorption % weight 6.5 ​
Coefficient of friction, dynamic, against steel µ 0.08 – 0.23 ​ 60MPa
pv value, max. (dry) MPa · m/s 0.23 ​
Also available
as: Mechanical properties
Flexural modulus MPa 3,500 DIN 53457
The classic endurance runner up to 30MPa Flexural strength at +20°C MPa 125 DIN 53452

Bar stock,
Excellent wear resistance on (virtually) all shafts Compressive strength MPa 61 ​
round bar Max. recommended surface pressure (+20°C) MPa 60 ​
Page 674 Shore D hardness 77 DIN 53505
iglidur® W300 gives excellent wear resistance, even in harsh environments or when used with rough shafts.
Of all iglidur® materials, iglidur® W300 is the most resistant to these conditions. Physical and thermal properties
●● Over 400 sizes available from stock Max. application temperature long-term °C +90 ​
FOOD
●● Very long service life Max. application temperature short-term °C +180 ​
●● Low coefficient of friction Min. application temperature °C –40 ​
Bar stock, ●● Very wear-resistant Thermal conductivity W/m · K 0.24 ASTM C 177
plate
Page 683 ●● Suitable for applications with soft shafts Coefficient of thermal expansion (at +23°C) K–1 · 10–5 9 DIN 53752
●● Lubrication-free Electrical properties
●● Maintenance-free Specific contact resistance Ωcm > 1013 DIN IEC 93
Surface resistance Ω > 1012 DIN 53482
Typical application areas Table 01: Material properties
tribo-tape liner ●● Automation
Page 691
●● Printing industry iglidur® W300 gives excellent wear resistance, even in Resistance to weathering
●● Woodworking harsh environments or when used with rough shafts. This iglidur® W300 plain bearings have limited resistance to
●● Mechatronics material is the most tolerant of these external effects out weathering. The material properties are affected. Discoloration
●● Test engineering and quality assurance of all the iglidur® range. occurs. Practical tests under real application conditions
are recommended.
Moisture absorption
Piston rings
Page 584 Under standard climatic conditions, the moisture absorp- Mechanical properties
tion of iglidur® W300 plain bearings is approximately 1.3% With increasing temperatures, the compressive strength of
Descriptive technical specifications weight. The saturation limit in water is 6.5% weight. This iglidur® W300 plain bearings decreases. Diagram 02 shows
Wear resistance at +23°C – + must be taken into account for these types of applications. this inverse relationship. The maximum recommended
surface pressure is a mechanical material parameter. No
Wear resistance at +90°C – +
Vacuum conclusions regarding the tribological properties can be
Two hole Wear resistance at +150°C – + In vacuum, any present moisture is released as vapour. drawn from this.
flange
bearings The use in vacuum is only possible to a limited extent. iglidur® W300 presents a very high compressive strength
Page 603 Low coefficient of friction – +
in spite of its high elasticity. Diagram 03 shows the elastic
Low moisture absorption – + Radiation resistance deformation of iglidur ® W300 at radial loads. At the
Plain bearings made from iglidur® W300 are resistant up maximum recommended surface pressure of 60MPa the
Wear resistance under water – +
to a radiation intensity of 3 · 10²Gy. deformation is less than 3%.
Moulded High media resistance – + Surface pressure, page 41
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 845 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

172 3D CAD, finder and service life calculation ... www.igus.eu/W300 Lubrication-free made easy ... from stock ... no minimum order quantity 173
iglidur® W300 iglidur® W300
+90°C +90°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® W300 Technical data
Permissible surface speeds Installation tolerances 100.0 0.30

Even at higher surface speeds, the coefficient of friction of iglidur® W300 plain bearings are standard bearings for 0.25
10.0

Coefficient of friction [µ]

iglidur® W300 plain bearings remains the same. In relation shafts with h tolerance (recommended minimum h9). 0.20
to other materials, somewhat higher surface speeds can The bearings are designed for press-fit into a housing 1.0 0.15

Pressure [MPa]
be attained, for example, up to 1.5m/s rotating and up to machined to a H7 tolerance. After being assembled into a 0.10
6.0m/s linear. The wear remains low when used for long nominal size housing, in standard cases the inner diameter 0.1
0.05
periods at high speeds, due to exceptional wear resistance. automatically adjusts to the E10 tolerances. For particular
0.01 0.00
Relatively high speeds can be obtained with iglidur® W300 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 10 20 30 40 50 60
bearings on hardened shafts with the recommended thickness (please see product range table).
Surface speed [m/s] Load [MPa]
surface finish. Testing methods, page 57
Surface speed, page 44 Diagram 01: Permissible pv values for iglidur® W300 plain Diagram 05: Coefficient of friction as a function of the load,
bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Temperature Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
iglidur® W300 plain bearings retain their exceptional wear Alcohols + up to 0
resistance even up to the highest permissible application Diluted acids 0 up to – 120 1.6
temperatures and at the same time resist becoming brittle Diluted alkalines + 1.4
100

Cf53, hard-chromed
at low temperatures. For temperatures over +60°C an Fuels + 1.2

304 stainless steel

Free cutting steel
80

High grade steel

HR carbon steel
additional securing is required. Greases, oils without additives + 1.0

H.a. aluminium
60 0.8
Application temperatures, page 49 Hydrocarbons +
0.6

Wear [µm/km]
Additional securing, page 49 Strong acids – 40
0.4

Load [MPa]

Cf53
Strong alkalines 0 20 0.2
Friction and wear All information given at room temperature [+20°C] 0 0.0
Similar to wear resistance, the coefficient of friction μ Table 02: Chemical resistance 20 30 40 50 60 70 80 90
also changes with the load. In contrast to other iglidur® Chemical table, page 1636 Temperature [°C]
materials, the coefficient of friction of iglidur® W300 remains Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
consistently low at higher rotational speeds. ​ ​ Rotating Oscillating linear function of temperature (60MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
Coefficient of friction and surfaces, page 47 long-term m/s 1.0 0.7 4.0
Wear resistance, page 50 short-term m/s 1.5 1.8 6.0 70
Table 03: Maximum surface speeds 8 60 rotating
+23°C oscillating
Shaft materials +60°C 50
6
The friction and wear are also dependent, to a large ​ Dry Greases Oil Water 40
degree, on the shaft material. Shafts that are too smooth, Coefficient of friction µ 0.08 – 0.23 0.09 0.04 0.04 4

Deformation [%]
30

Wear [µm/km]
increase both the coefficient of friction and the wear of Table 04: Coefficient of friction against steel (Ra = 1μm, 20
2
the bearing. Smooth shafts have the danger of stick slip. 50HRC) 10
Squeaking as an effect of stick slip is usually the result of 0 0
shafts that are too smooth. Shaft surface finish of 0.4 – ​ Housing Plain bearing Shaft 0 15 30 45 60 0.25 0.75 2.00 5.00 10.00 45.00 76.00
0.5µm have proven to be the best. For iglidur® W300, the Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa] Load [MPa]
wear resistance is still excellent with this surface finish 0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
as the friction adopts the minimum value. Diagram 06 >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with shaft material Cf53 hardened and ground steel, as a
shows results of testing different shafts. Hardened shafts > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000 function of the load
are preferred for applications for higher loads. If the shaft > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 1.0

material you plan on using is not shown in these test > 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
Coefficient of friction [µ]

results, please contact us. > 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000
Shaft materials, page 52 > 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 1.0
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
Table 05: Important tolerances for plain bearings according
0.4
to ISO 3547-1 after press-fit
0.05 0.10 0.15 0.20 0.25 0.30 0.35
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

174 3D CAD, finder and service life calculation ... www.igus.eu/W300 Lubrication-free made easy ... from stock ... no minimum order quantity 175
iglidur® W300 iglidur® W300
+90°C +90°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® W300 Product range
Sleeve bearing (form S) d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.
Tolerance3) h13 Tolerance3) h13
f1

30°
[mm] [mm] [mm] [mm] [mm] [mm]
14.0 16.0 7.2 WSM-1416-07 22.0 25.0 30.0 WSM-2225-30
14.0 16.0 10.0 WSM-1416-10 24.0 27.0 15.0 WSM-2427-15

d1

d2
0.5
14.0 16.0 15.0 WSM-1416-15 24.0 27.0 20.0 WSM-2427-20
14.0 16.0 20.0 WSM-1416-20 24.0 27.0 25.0 WSM-2427-25

30°
b1 14.0 16.0 25.0 WSM-1416-25 24.0 27.0 30.0 WSM-2427-30
14.0 16.0 33.0 WSM-1416-33 25.0 28.0 12.0 WSM-2528-12
15.0 17.0 10.0 WSM-1517-10 25.0 28.0 14.0 WSM-2528-14
2)
Thickness < 0.6mm: Chamfer = 20° 15.0 17.0 15.0 WSM-1517-15 25.0 28.0 15.0 WSM-2528-15
Chamfer in relation to d1 15.0 17.0 20.0 WSM-1517-20 25.0 28.0 20.0 WSM-2528-20
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and 15.0 17.0 25.0 WSM-1517-25 25.0 28.0 25.0 WSM-2528-25
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions 16.0 18.0 7.0 WSM-1618-07 25.0 28.0 30.0 WSM-2528-30
16.0 18.0 8.0 WSM-1618-08 25.0 28.0 50.0 WSM-2528-50
Order example: WSM-0203-03 – no minimum order quantity. 16.0 +0.032 18.0 11.5 WSM-1618-11 26.0 30.0 16.0 WSM-2630-16
W300 iglidur® material S Sleeve bearing M Metric 02 Inner Ø d1 03 Outer Ø d2 03 Total length b1 16.0 +0.102 18.0 12.0 WSM-1618-12 26.0 30.0 25.0 WSM-2630-25
+0.040
16.0 18.0 15.0 WSM-1618-15 28.0 30.0 10.0 WSM-2830-10
+0.124
16.0 18.0 20.0 WSM-1618-20 28.0 31.0 10.0 WSM-2831-10
d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No. 16.0 18.0 25.0 WSM-1618-25 28.0 32.0 20.0 WSM-2832-20
Tolerance3) h13 Tolerance3) h13 16.0 18.0 30.0 WSM-1618-30 28.0 32.0 25.0 WSM-2832-25
[mm] [mm] [mm] [mm] [mm] [mm] 16.0 18.0 35.0 WSM-1618-35 28.0 32.0 30.0 WSM-2832-30
2.0 3.5 3.0 WSM-0203-03 8.0 10.0 15.0 WSM-0810-15 16.0 18.0 45.0 WSM-1618-45 30.0 34.0 16.0 WSM-3034-16
2.0 4.0 1.8 WSM-0204-018 8.0 10.0 16.0 WSM-0810-16 18.0 20.0 12.0 WSM-1820-12 30.0 34.0 20.0 WSM-3034-20
2.5 +0.014 4.0 3.0 WSM-0204-03 8.0 10.0 20.0 WSM-0810-20 18.0 20.0 15.0 WSM-1820-15 30.0 34.0 24.0 WSM-3034-24
3.0 +0.054 4.5 3.0 WSM-0304-03 8.0 10.0 21.0 WSM-0810-21 18.0 20.0 20.0 WSM-1820-20 30.0 34.0 25.0 WSM-3034-25
3.0 4.5 5.0 WSM-0304-05 9.0 11.0 6.0 WSM-0911-06 18.0 20.0 25.0 WSM-1820-25 30.0 34.0 30.0 WSM-3034-30
3.0 4.5 6.0 WSM-0304-06 10.0 12.0 4.0 WSM-1012-04 18.0 20.0 33.0 WSM-1820-33 30.0 34.0 36.0 WSM-3034-36
4.0 5.5 4.0 WSM-0405-04 10.0 12.0 6.0 WSM-1012-06 18.0 20.0 35.0 WSM-1820-35 30.0 34.0 38.0 WSM-3034-38
+0.025
4.0 5.5 6.0 WSM-0405-06 10.0 12.0 8.0 WSM-1012-08 19.0 22.0 28.0 WSM-1922-28 30.0 34.0 40.0 WSM-3034-40
+0.083
4.0 5.5 8.0 WSM-0405-08 10.0 12.0 9.0 WSM-1012-09 20.0 22.0 11.5 WSM-2022-11 30.0 34.0 45.0 WSM-3034-45
+0.020
4.0 5.5 10.0 WSM-0405-10 10.0 12.0 10.0 WSM-1012-10 20.0 22.0 12.0 WSM-2022-12 30.0 34.0 47.0 WSM-3034-47
+0.068
5.0 7.0 5.0 WSM-0507-05 10.0 12.0 12.0 WSM-1012-12 20.0 22.0 15.0 WSM-2022-15 32.0 36.0 20.0 WSM-3236-20
5.0 7.0 8.0 WSM-0507-08 10.0 12.0 15.0 WSM-1012-15 20.0 22.0 20.0 WSM-2022-20 32.0 36.0 25.0 WSM-3236-25
5.0 7.0 10.0 WSM-0507-10 10.0 12.0 17.0 WSM-1012-17 20.0 22.0 30.0 WSM-2022-30 32.0 36.0 30.0 WSM-3236-30
+0.010 10.0 12.0 20.0 WSM-1012-20 20.0 23.0 8.0 WSM-2023-08 32.0 36.0 40.0 WSM-3236-40
6.0 7.0 14.0 WSM-0607-14
+0.058 10.0 12.0 25.5 WSM-1012-25.5 20.0 23.0 10.0 WSM-2023-10 35.0 39.0 20.0 WSM-3539-20
6.0 8.0 6.0 WSM-0608-06 11.0 13.0 8.0 WSM-1113-08 20.0 23.0 12.0 WSM-2023-12 35.0 39.0 30.0 WSM-3539-30
6.0 8.0 8.0 WSM-0608-08 12.0 14.0 4.0 WSM-1214-04 20.0 23.0 15.0 WSM-2023-15 35.0 39.0 40.0 WSM-3539-40
6.0 +0.020 8.0 9.5 WSM-0608-09 12.0 14.0 5.0 WSM-1214-05 20.0 +0.040 23.0 20.0 WSM-2023-20 35.0 39.0 50.0 WSM-3539-50
6.0 +0.068 8.0 10.0 WSM-0608-10 12.0 14.0 6.0 WSM-1214-06 20.0 +0.124 23.0 23.0 WSM-2023-23 35.0 40.0 7.0 WSM-3540-07
+0.050
6.0 8.0 11.8 WSM-0608-11 12.0 14.0 8.0 WSM-1214-08 20.0 23.0 25.0 WSM-2023-25 40.0 44.0 20.0 WSM-4044-20
+0.150
6.0 8.0 13.8 WSM-0608-13 12.0 14.0 10.0 WSM-1214-10 20.0 23.0 30.0 WSM-2023-30 40.0 44.0 30.0 WSM-4044-30
7.0 9.0 9.0 WSM-0709-09 12.0 +0.032 14.0 12.0 WSM-1214-12 22.0 24.0 15.0 WSM-2224-15 40.0 44.0 40.0 WSM-4044-40
7.0 9.0 12.0 WSM-0709-12 12.0 +0.102 14.0 15.0 WSM-1214-15 22.0 24.0 20.0 WSM-2224-20 40.0 44.0 50.0 WSM-4044-50
7.0 9.0 12.5 WSM-0709-125 12.0 14.0 20.0 WSM-1214-20 22.0 24.0 30.0 WSM-2224-30 45.0 50.0 20.0 WSM-4550-20
8.0 +0.025 10.0 6.0 WSM-0810-06 12.0 14.0 25.0 WSM-1214-25 22.0 24.0 35.0 WSM-2224-35 45.0 50.0 30.0 WSM-4550-30
8.0 +0.083 10.0 8.0 WSM-0810-08 13.0 15.0 7.0 WSM-1315-07 22.0 24.0 45.0 WSM-2224-45 45.0 50.0 40.0 WSM-4550-40
8.0 10.0 10.0 WSM-0810-10 13.0 15.0 10.0 WSM-1315-10 22.0 25.0 15.0 WSM-2225-15 45.0 50.0 50.0 WSM-4550-50
8.0 10.0 12.0 WSM-0810-12 13.0 15.0 15.0 WSM-1315-15 22.0 25.0 20.0 WSM-2225-20 50.0 55.0 20.0 WSM-5055-20
8.0 10.0 13.8 WSM-0810-13 13.0 15.0 20.0 WSM-1315-20 22.0 25.0 25.0 WSM-2225-25 50.0 55.0 30.0 WSM-5055-30
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

176 3D CAD, finder and service life calculation ... www.igus.eu/W300 Lubrication-free made easy ... from stock ... no minimum order quantity 177
iglidur® W300 iglidur® W300
+90°C +90°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® W300 Bearing technology | Plain bearing | iglidur® W300
d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No. Flange bearing (form F)
.5
.0
Tolerance3) h13 Tolerance3) h13 ax
f1

30
rm

°
[mm] [mm] [mm] [mm] [mm] [mm]
50.0 55.0 40.0 WSM-5055-40 65.0 70.0 60.0 WSM-6570-60
50.0 +0.050 55.0 50.0 WSM-5055-50 70.0 75.0 60.0 WSM-7075-60

d2
d3

d1
+0.060
50.0 +0.150 55.0 55.0 WSM-5055-55 75.0 80.0 100.0 WSM-7580-100
+0.180
50.0 55.0 60.0 WSM-5055-60 80.0 85.0 100.0 WSM-8085-100
55.0 60.0 40.0 WSM-5560-40 80.0 85.0 20.0 WSM-8085-20 b2

55.0 +0.060 60.0 60.0 WSM-5560-60 90.0 +0.072 95.0 100.0 WSM-9095-100 b1

60.0 +0.180 65.0 30.0 WSM-6065-30 100.0 +0.212 105.0 100.0 WSM-100105-100
60.0 65.0 60.0 WSM-6065-60 2)
Thickness < 0.6mm: Chamfer = 20°
3)
After press-fit. Testing methods, page 57 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions

Order example: WFM-0204-03 – no minimum order quantity.

W300 iglidur® material F Flange bearing M Metric 02 Inner Ø d1 04 Outer Ø d2 03 Total length b1

d1 d1 d2 d3 b1 b2 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) d133) h13 h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
2.5 4.0 6.5 3.0 0.75 WFM-0204-03 10.0 12.0 18.0 6.0 1.00 WFM-1012-06
+0.014
3.0 4.5 7.5 3.0 0.75 WFM-0304-03 10.0 12.0 18.0 7.0 1.00 WFM-1012-07
+0.054
3.0 4.5 7.5 5.0 0.75 WFM-0304-05 10.0 12.0 18.0 9.0 1.00 WFM-1012-09
+0.025
4.0 5.5 9.5 3.0 0.75 WFM-0405-03 10.0 12.0 18.0 10.0 1.00 WFM-1012-10
+0.020 +0.083
4.0 5.5 9.5 4.0 0.75 WFM-0405-04 10.0 12.0 18.0 12.0 1.00 WFM-1012-12
+0.068
4.0 5.5 9.5 6.0 0.75 WFM-0405-06 10.0 12.0 18.0 15.0 1.00 WFM-1012-15
+0.010 10.0 12.0 18.0 17.0 1.00 WFM-1012-17
5.0 6.0 10.0 8.0 0.50 WFM-0506-08
+0.040 12.0 14.0 20.0 4.0 1.00 WFM-1214-04
5.0 7.0 11.0 4.0 1.00 WFM-0507-04 12.0 14.0 20.0 4.4 1.00 WFM-1214-044
5.0 7.0 11.0 5.0 1.00 WFM-0507-05 12.0 14.0 20.0 6.0 1.00 WFM-1214-06
6.0 8.0 12.0 4.0 1.00 WFM-0608-04 12.0 14.0 20.0 7.0 1.00 WFM-1214-07
+0.020
6.0 8.0 12.0 6.0 1.00 WFM-0608-06 12.0 14.0 20.0 9.0 1.00 WFM-1214-09
+0.068
6.0 8.0 12.0 8.0 1.00 WFM-0608-08 12.0 14.0 20.0 10.0 1.00 WFM-1214-10
6.0 8.0 12.0 10.0 1.00 WFM-0608-10 12.0 14.0 20.0 11.0 1.00 WFM-1214-11
6.0 8.0 12.0 15.0 1.00 WFM-0608-15 12.0 14.0 20.0 12.0 1.00 WFM-1214-12
7.0 9.0 15.0 10.0 1.00 WFM-0709-10 12.0 14.0 20.0 15.0 1.00 WFM-1214-15
7.0 9.0 15.0 12.0 1.00 WFM-0709-12 12.0 14.0 20.0 17.0 1.00 WFM-1214-17
+0.032
8.0 10.0 15.0 2.7 1.00 WFM-0810-02 12.0 14.0 20.0 20.0 1.00 WFM-1214-20
Available from stock Ordering note +0.102
8.0 10.0 15.0 4.0 1.00 WFM-0810-04 13.0 15.0 22.0 6.0 1.00 WFM-1315-06
Detailed information about delivery time online. Our prices are scaled according to order 8.0 10.0 15.0 5.5 1.00 WFM-0810-05 14.0 16.0 22.0 4.0 1.00 WFM-1416-04
www.igus.eu/24 quantities, current prices can be found online. 8.0 10.0 15.0 7.5 1.00 WFM-0810-07 14.0 16.0 22.0 5.0 1.00 WFM-1416-05
+0.025
Online ordering 8.0 10.0 15.0 9.5 1.00 WFM-0810-09 14.0 16.0 22.0 8.0 1.00 WFM-1416-08
Discount scaling +0.083
Including delivery times, prices, online tools 8.0 10.0 15.0 10.0 1.00 WFM-0810-10 14.0 16.0 22.0 12.0 1.00 WFM-1416-12
1–9 50 – 99 500 – 999 8.0 10.0 15.0 23.0 1.00 WFM-0810-23 14.0 16.0 22.0 17.0 1.00 WFM-1416-17
www.igus.eu/W300
10 – 24 100 – 199 1,000 – 2,499 8.0 10.0 15.0 30.0 1.00 WFM-0810-30 14.0 16.0 22.0 29.0 1.00 WFM-1416-29
25 – 49 200 – 499 2,500 – 4,999 8.0 10.0 15.0 5.0 1.00 WFM-081015-05 15.0 17.0 23.0 9.0 1.00 WFM-1517-09
No minimum order value. 10.0 12.0 18.0 4.0 1.00 WFM-1012-04 15.0 17.0 23.0 12.0 1.00 WFM-1517-12
No low-quantity surcharges. 10.0 12.0 18.0 5.0 1.00 WFM-1012-05 15.0 17.0 23.0 17.0 1.00 WFM-1517-17
Free shipping within Germany for orders 3)
After press-fit. Testing methods, page 57
above €150.

178 3D CAD, finder and service life calculation ... www.igus.eu/W300 Lubrication-free made easy ... from stock ... no minimum order quantity 179
iglidur® W300 iglidur® W300
+90°C +90°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® W300 Bearing technology | Plain bearing | iglidur® W300
d1 d1 d2 d3 b1 b2 Part No. d1 d1 d2 d3 b1 b2 Part No. Thrust washer (form T)
d1
Tolerance3) d133) h13 h13 Tolerance3) d133) h13 h13

s
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
d2
15.0 17.0 23.0 20.0 1.00 WFM-1517-20 30.0 34.0 42.0 16.0 2.00 WFM-3034-16
+0.040
16.0 18.0 24.0 9.0 1.00 WFM-1618-09 30.0 34.0 42.0 26.0 2.00 WFM-3034-26
+0.124
16.0 18.0 24.0 12.0 1.00 WFM-1618-12 30.0 34.0 42.0 37.0 2.00 WFM-3034-37
16.0 18.0 24.0 17.0 1.00 WFM-1618-17 32.0 36.0 40.0 16.0 2.00 WFM-3236-16
17.0 19.0 25.0 12.0 1.00 WFM-1719-12 32.0 36.0 40.0 26.0 2.00 WFM-3236-26

d5
+0.032
17.0 19.0 25.0 18.0 1.00 WFM-1719-18 35.0 39.0 47.0 9.0 2.00 WFM-3539-09 d4
+0.102
17.0 19.0 25.0 25.0 1.00 WFM-1719-25 35.0 39.0 47.0 16.0 2.00 WFM-3539-16
18.0 20.0 26.0 6.0 1.00 WFM-1820-06 35.0 39.0 47.0 26.0 2.00 WFM-3539-26 d6

h
18.0 20.0 26.0 12.0 1.00 WFM-1820-12 35.0 +0.050 39.0 50.0 35.0 2.00 WFM-353950-35
18.0 20.0 26.0 17.0 1.00 WFM-1820-17 38.0 +0.150 42.0 50.0 22.0 2.00 WFM-3842-22 Dimensions according to ISO 3547-1 and
18.0 20.0 26.0 22.0 1.00 WFM-1820-22 40.0 44.0 52.0 30.0 2.00 WFM-4044-30 special dimensions
20.0 23.0 30.0 8.0 1.50 WFM-2023-08 40.0 44.0 52.0 40.0 2.00 WFM-4044-40
20.0 23.0 30.0 8.5 1.50 WFM-2023-085 45.0 50.0 58.0 50.0 2.00 WFM-4550-50 Order example: WTM-0509-006 – no minimum order quantity.
20.0 23.0 30.0 11.5 1.50 WFM-2023-11 50.0 55.0 63.0 40.0 2.00 WFM-5055-40 W300 iglidur® material T Thrust washer M Metric 05 Inner Ø d1 09 Outer Ø d2 006 Thickness s
20.0 23.0 30.0 14.5 1.50 WFM-2023-14 50.0 55.0 63.0 50.0 2.00 WFM-5055-50
20.0 23.0 30.0 16.5 1.50 WFM-2023-16 55.0 60.0 68.0 60.0 2.00 WFM-5560-60
20.0 23.0 30.0 21.5 1.50 WFM-2023-21 57.0 62.0 67.0 40.0 2.00 WFM-5762-40 d1 d2 d4 d5 h d6 s Part No.
24.0 +0.040 27.0 32.0 10.5 1.50 WFM-2427-10 60.0 65.0 73.0 60.0 2.00 WFM-6065-60 +0.25 –0.25 –0.12 +0.375 +0.2/–0.2 +0.12 –0.05
+0.060 +0.12 +0.125
25.0 +0.124 28.0 35.0 11.5 1.50 WFM-2528-11 65.0 70.0 78.0 60.0 2.00 WFM-6570-60
+0.180
25.0 28.0 35.0 16.5 1.50 WFM-2528-16 70.0 75.0 83.0 100.0 2.50 WFM-7075-100 [mm] [mm] [mm] [mm] [mm] [mm] [mm]
25.0 28.0 35.0 21.5 1.50 WFM-2528-21 75.0 80.0 88.0 100.0 2.50 WFM-7580-100 5 9.5 4) 4)
0.3 9.5 0.6 WTM-0509-006
25.0 28.0 32.0 30.0 1.50 WFM-2528-30 80.0 85.0 93.0 100.0 2.50 WFM-8085-100 6 20 13 1.5 1 20 1.5 WTM-0620-015
25.0 28.0 31.0 13.5 1.50 WFM-252831-13 90.0 95.0 103.0 100.0 2.50 WFM-9095-100 8 18 13 1.5 1 18 1.5 WTM-0818-015
+0.072
28.0 30.0 35.0 36.0 1.00 WFM-2830-36 100.0 105.0 113.0 100.0 2.50 WFM-100105-100 10 18 4) 4)
0.7 18 1 WTM-1018-010
+0.212
30.0 34.0 42.0 10.0 2.00 WFM-3034-10 120.0 125.0 133.0 100.0 2.50 WFM-120125-100 10 18 4) 4)
1 18 1.5 WTM-1018-015
3)
After press-fit. Testing methods, page 57 12 24 18 1.5 1 24 1.5 WTM-1224-015
14 26 20 2 1 26 1.5 WTM-1426-015
15 24 19.5 1.5 1 24 1.5 WTM-1524-015
16 30 23 2 1 30 1.5 WTM-1630-015
18 32 25 2 1 32 1.5 WTM-1832-015
18 44 30 7 1 44 1.5 WTM-1844-015
20 36 28 3 1 36 1.5 WTM-2036-015
22 38 30 3 1 38 1.5 WTM-2238-015
24 42 33 3 1 42 1.5 WTM-2442-015
26 44 35 3 1 44 1.5 WTM-2644-015
28 40 38 4 1 48 1.5 WTM-2840-015
28 48 38 4 1 48 1.5 WTM-2848-015
Available from stock Ordering note 32 54 43 4 1 54 1.5 WTM-3254-015
Detailed information about delivery time online. Our prices are scaled according to order 38 62 50 4 1 62 1.5 WTM-3862-015
www.igus.eu/24 quantities, current prices can be found online. 42 66 54 4 1 66 1.5 WTM-4266-015
Online ordering 48 74 61 4 1.5 74 2 WTM-4874-020
Discount scaling 52 78 65 4 1.5 78 2 WTM-5278-020
Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 62 90 76 4 1.5 90 2 WTM-6290-020
www.igus.eu/W300
10 – 24 100 – 199 1,000 – 2,499 82 110 4) 4)
1.5 110 2 WTM-82110-020
25 – 49 200 – 499 2,500 – 4,999 102 130 4) 4)
1.5 130 2 WTM-102130-020
No minimum order value. 120 150 4) 4)
1.5 150 2 WTM-120150-020
No low-quantity surcharges. 4)
Design without fixing hole
Free shipping within Germany for orders
above €150.

180 3D CAD, finder and service life calculation ... www.igus.eu/W300 Lubrication-free made easy ... from stock ... no minimum order quantity 181
The new endurance runner:
specialist for pivoting applications
and pulsating loads
Up to 10MPa, up to three times more
wear-resistant than iglidur J ®

iglidur J3 ®

When to use it?

●● When optimising wear resistance compared to iglidur® J
●● When very low coefficients of friction in dry operation are required
●● When high wear resistance at low loads is required
●● When low moisture absorption is fundamental
●● When good liquid media resistance is required

When not to use?

●● When a wear-resistant plain bearing for linear motion is required
iglidur® J
●● When continuous operating temperatures are higher than +90°C
iglidur® J260
●● When radial surface pressure is higher than 45MPa
iglidur® W300
iglidur® J3 iglidur® J3
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® J3 Technical data
General properties​ Testing method

Density g/cm³ 1.42 ​ –50°C up to

Ø +90°C
2.0 – 50.0mm Colour yellow ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.3 DIN 53495
Max. moisture absorption % weight 1.3 ​
Coefficient of friction, dynamic, against steel µ 0.06 – 0.20 ​ 45MPa
pv value, max. (dry) MPa · m/s 0.50 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,700 DIN 53457
The new endurance runner: specialist for Flexural strength at +20°C MPa 70 DIN 53452

Bar stock,
pivoting applications and pulsating loads Compressive strength MPa 60 ​
Max. recommended surface pressure (+20°C) MPa 45 ​
round bar
Page 675 Up to 10MPa, up to three times more Shore D hardness 73 DIN 53505
wear-resistant than iglidur® J Physical and thermal properties
Max. application temperature long-term °C +90 ​
FOOD
iglidur® J3 is a material with improved wear resistance at low to medium loads and high speed. The service Max. application temperature short-term °C +120 ​
life is up to 300% longer than iglidur® J – the proven top endurance runner material. Min. application temperature °C –50 ​
Bar stock, ●● Low coefficient of friction Thermal conductivity W/m · K 0.25 ASTM C 177
plate
Page 683 ●● High media resistance Coefficient of thermal expansion (at +23°C) K–1 · 10–5 13 DIN 53752
●● Low moisture absorption Electrical properties
●● PTFE-free Specific contact resistance Ωcm > 1012 DIN IEC 93
●● Lubrication-free Surface resistance Ω > 1012 DIN 53482
●● Maintenance-free Table 01: Material properties
tribo-tape liner
Page 691
Typical application areas With respect to its general mechanical and thermal Resistance to weathering
●● Automation specifications, iglidur® J3 is directly comparable to our iglidur® J3 plain bearings are resistant to weathering. The
●● Printing industry classic, iglidur® J. material properties are slightly affected. Discoloration
●● Beverage industry occurs.
●● Glass industry Moisture absorption
●● Aerospace engineering Under standard climatic conditions, the moisture absorption Mechanical properties
Piston rings
Page 584 of iglidur® J3 plain bearings is approximately 0.3% weight. With increasing temperatures, the compressive strength
The saturation limit in water is 1.3% weight. These values of iglidur® J3 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications are so low that a moisture expansion need to be considered this inverse relationship. The maximum recommended
Wear resistance at +23°C – + only in extreme cases. surface pressure is a mechanical material parameter. No
conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
Vacuum drawn from this.
Two hole Wear resistance at +150°C – + In vacuum, any present moisture is released as vapour. Use Diagram 03 shows the elastic deformation of iglidur® J3
flange
bearings in vacuum is only possible with dehumidified iglidur® J3 at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
bearings. pressure of 45MPa at room temperature the deformation
Low moisture absorption – + is less than 6%. A possible deformation could be, among
Radiation resistance others, dependant on the duty cycle of the load.
Wear resistance under water – +
Resistant to radiation up to an intensity of 1 · 10⁴Gy. Surface pressure, page 41
Moulded High media resistance – +
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

184 3D CAD, finder and service life calculation ... www.igus.eu/J3 Lubrication-free made easy ... from stock ... no minimum order quantity 185
iglidur® J3 iglidur® J3
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® J3 Technical data
Permissible surface speeds Installation tolerances 100.0 0.25

iglidur® J3 is also suitable for medium to high surface iglidur ® J3 plain bearings are standard bearings for
10.0

Coefficient of friction [µ]

speeds. The maximum values shown in table 03 can only shafts with h tolerance (recommended minimum h9). 0.20
be achieved at low pressures. At the given speeds, friction The bearings are designed for press-fit into a housing 1.0

Pressure [MPa]
can cause a temperature increase to maximum permissible machined to a H7 tolerance. After being assembled into a 0.15
levels. In practice, though, this level is rarely reached due nominal size housing, in standard cases the inner diameter 0.1
to varying application conditions. automatically adjusts to the E10 tolerances. For particular
0.01 0.10
Surface speed, page 44 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 15 25 35 45
thickness (please see product range table). In relation to
Surface speed [m/s] Load [MPa]
Temperature the installation tolerance, the inner diameter changes with
The temperatures prevailing in the bearing system also have the absorption of humidity. Diagram 01: Permissible pv values for iglidur® J3 plain Diagram 05: Coefficient of friction as a function of the load,
an influence on the wear. With increasing temperatures, Testing methods, page 57 bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
the wear increases and this effect is significant when a steel shaft, at +20°C, mounted in a steel housing
temperatures rise over +90°C. For temperatures over
+60°C an additional securing is required. Chemicals Resistance 90 1.6
Application temperatures, page 49 Alcohols + 80 1.4

Cf53, hard-chromed
Additional securing, page 49 Diluted acids 0 up to – 70 1.2

304 stainless steel

Free cutting steel
60

High grade steel

HR carbon steel
Diluted alkalines + 1.0

H.a. aluminium
50
0.8
Friction and wear Fuels + 40
0.6

Wear [µm/km]
Similar to wear resistance, the coefficient of friction µ also Greases, oils without additives + 30
0.4

Load [MPa]
20

Cf53
changes with the surface speed and load (diagrams 04 Hydrocarbons + 10 0.2
and 05). Strong acids – 0 0.0
Coefficient of friction and surfaces, page 47 Strong alkalines + up to 0 20 30 40 50 60 70 80 90
Wear resistance, page 50 All information given at room temperature [+20°C] Temperature [°C]
Table 02: Chemical resistance Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Shaft materials Chemical table, page 1636 function of temperature (45MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
The friction and wear are also dependent, to a large degree,
on the shaft material. Shafts that are too smooth, increase ​ ​ Rotating Oscillating linear 10 45
both the coefficient of friction and the wear of the bearing. long-term m/s 1.5 1.1 8.0 40 rotating
8 oscillating
short-term m/s 3.0 2.1 10.0 35
For iglidur® J3 a ground surface with an average surface +23°C 30
finish Ra = 0.1 – 0.3µm is recommended. The diagram Table 03: Maximum surface speeds 6 +60°C
25
06 shows that iglidur® J3 can be combined with various 20

Deformation [%]
4

Wear [µm/km]
shaft materials. Diagram 07 shows rotating and pivoting ​ Dry Greases Oil Water 15
2 10
applications in comparison. With higher load, the wear Coefficient of friction µ 0.06 – 0.20 0.09 0.04 0.04 5
increases more for rotating than for pivoting movements. Table 04: Coefficient of friction against steel (Ra = 1μm, 0 0
Shaft materials, page 52 50HRC) 0 5 10 15 20 25 30 35 40 45 0 5 10 15 20 25 30 35 40 45
Load [MPa] Load [MPa]
​ Housing Plain bearing Shaft Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] with shaft material Cf53 hardened and ground steel, as a
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 function of the load
>3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 0.25

> 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000

Coefficient of friction [µ]

> 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 0.20

> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000
0.15
> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
0.10
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
0.05 0.10 0.15 0.20 0.25 0.30 0.35
Table 05: Important tolerances for plain bearings according
Surface speed [m/s]
to ISO 3547-1 after press-fit
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa
​

186 3D CAD, finder and service life calculation ... www.igus.eu/J3 Lubrication-free made easy ... from stock ... no minimum order quantity 187
iglidur® J3 iglidur® J3
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® J3 Product range
Sleeve bearing (form S) d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.
Tolerance3) h13 Tolerance3) h13
f1

30°
[mm] [mm] [mm] [mm] [mm] [mm]
30.0 34.0 25.0 J3SM-3034-25 40.0 44.0 40.0 J3SM-4044-40
+0.040
30.0 34.0 30.0 J3SM-3034-30 40.0 44.0 50.0 J3SM-4044-50
+0.124

d1

d2
0.5
30.0 34.0 40.0 J3SM-3034-40 45.0 50.0 20.0 J3SM-4550-20
32.0 36.0 20.0 J3SM-3236-20 45.0 50.0 30.0 J3SM-4550-30

30°
b1 32.0 36.0 30.0 J3SM-3236-30 45.0 50.0 40.0 J3SM-4550-40
+0.050
32.0 36.0 40.0 J3SM-3236-40 45.0 50.0 50.0 J3SM-4550-50
+0.150
35.0 39.0 20.0 J3SM-3539-20 50.0 55.0 20.0 J3SM-5055-20
+0.050
2)
Thickness < 0.6mm: Chamfer = 20° 35.0 39.0 30.0 J3SM-3539-30 50.0 55.0 30.0 J3SM-5055-30
+0.150
Chamfer in relation to d1 35.0 39.0 40.0 J3SM-3539-40 50.0 55.0 40.0 J3SM-5055-40
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and 35.0 39.0 50.0 J3SM-3539-50 50.0 55.0 50.0 J3SM-5055-50
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions 40.0 44.0 20.0 J3SM-4044-20 50.0 55.0 60.0 J3SM-5055-60
40.0 44.0 30.0 J3SM-4044-30
Order example: J3SM-0304-05 – no minimum order quantity. 3)
After press-fit. Testing methods, page 57
J3 iglidur® material S Sleeve bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 05 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.

Tolerance3) h13 Tolerance3) h13
[mm] [mm] [mm] [mm] [mm] [mm]
+0.014 15.0 17.0 30.0 J3SM-1517-30
3.0 4.5 5.0 J3SM-0304-05
+0.054 16.0 18.0 15.0 J3SM-1618-15
4.0 5.5 4.0 J3SM-0405-04 16.0 18.0 20.0 J3SM-1618-20
4.0 5.5 6.0 J3SM-0405-06 16.0 +0.032 18.0 25.0 J3SM-1618-25
5.0 7.0 5.0 J3SM-0507-05 18.0 +0.102 20.0 15.0 J3SM-1820-15
+0.020
5.0 7.0 10.0 J3SM-0507-10 18.0 20.0 20.0 J3SM-1820-20
+0.068
6.0 8.0 6.0 J3SM-0608-06 18.0 20.0 25.0 J3SM-1820-25
6.0 8.0 8.0 J3SM-0608-08 18.0 21.0 25.0 J3SM-1821-25
6.0 8.0 10.0 J3SM-0608-10 20.0 23.0 10.0 J3SM-2023-10
8.0 10.0 8.0 J3SM-0810-08 20.0 23.0 15.0 J3SM-2023-15
8.0 10.0 10.0 J3SM-0810-10 20.0 23.0 20.0 J3SM-2023-20
8.0 10.0 12.0 J3SM-0810-12 20.0 23.0 25.0 J3SM-2023-25
10.0 +0.025 12.0 8.0 J3SM-1012-08 20.0 23.0 30.0 J3SM-2023-30
10.0 +0.083 12.0 10.0 J3SM-1012-10 22.0 25.0 15.0 J3SM-2225-15
10.0 12.0 12.0 J3SM-1012-12 22.0 25.0 20.0 J3SM-2225-20
10.0 12.0 15.0 J3SM-1012-15 22.0 25.0 25.0 J3SM-2225-25
10.0 12.0 20.0 J3SM-1012-20 22.0 25.0 30.0 J3SM-2225-30
12.0 14.0 10.0 J3SM-1214-10 24.0 27.0 15.0 J3SM-2427-15
+0.040 Available from stock Ordering note
12.0 14.0 12.0 J3SM-1214-12 24.0 27.0 20.0 J3SM-2427-20
+0.124 Detailed information about delivery time online. Our prices are scaled according to order
12.0 14.0 15.0 J3SM-1214-15 24.0 27.0 25.0 J3SM-2427-25
12.0 14.0 20.0 J3SM-1214-20 24.0 27.0 30.0 J3SM-2427-30 www.igus.eu/24 quantities, current prices can be found online.
13.0 15.0 10.0 J3SM-1315-10 25.0 28.0 15.0 J3SM-2528-15 Online ordering
13.0 +0.032 15.0 20.0 J3SM-1315-20 25.0 28.0 20.0 J3SM-2528-20 Discount scaling
Including delivery times, prices, online tools
14.0 +0.102 16.0 15.0 J3SM-1416-15 25.0 28.0 25.0 J3SM-2528-25 1–9 50 – 99 500 – 999
www.igus.eu/J3
14.0 16.0 20.0 J3SM-1416-20 25.0 28.0 30.0 J3SM-2528-30 10 – 24 100 – 199 1,000 – 2,499
14.0 16.0 25.0 J3SM-1416-25 28.0 32.0 20.0 J3SM-2832-20 25 – 49 200 – 499 2,500 – 4,999
15.0 17.0 15.0 J3SM-1517-15 28.0 32.0 25.0 J3SM-2832-25 No minimum order value.
15.0 17.0 20.0 J3SM-1517-20 28.0 32.0 30.0 J3SM-2832-30 No low-quantity surcharges.
15.0 17.0 25.0 J3SM-1517-25 30.0 34.0 20.0 J3SM-3034-20 Free shipping within Germany for orders
3)
After press-fit. Testing methods, page 57 above €150.

188 3D CAD, finder and service life calculation ... www.igus.eu/J3 Lubrication-free made easy ... from stock ... no minimum order quantity 189
iglidur® J3
+90°C
45MPa
Bearing technology | Plain bearing | iglidur® J3
Flange bearing (form F)
.5
.0
ax
f1

30
rm

°
d2
d3

d1
b2
b1

2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions

Order example: J3FM-0304-05 – no minimum order quantity.

J3 iglidur® material F Flange bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 05 Total length b1
Proven long-life material in black
d1 d1
Tolerance3)
d2 d3
d133)
b1
h13
b2 Part No.
h13
d1 d1
Tolerance3)
d2 d3
d133)
b1
h13
b2 Part No.
h13
Wear-resistant endurance runner
[mm]
2.0 +0.014
[mm] [mm] [mm] [mm]
3.5 5.0 5.0 0.75 J3FM-0203505-05 15.0
[mm]
17.0
[mm] [mm] [mm] [mm]
23.0 9.0 1.00 J3FM-1517-09 up to 10MPa
3.0 +0.054 4.5 7.5 5.0 0.75 J3FM-0304-05 15.0 17.0 23.0 12.0 1.00 J3FM-1517-12
5.0
6.0 +0.020
7.0
8.0
11.0
12.0
5.0
4.0
1.00 J3FM-0507-05
1.00 J3FM-0608-04
15.0
16.0
+0.032
+0.102
17.0
18.0
23.0
24.0
17.0
12.0
1.00 J3FM-1517-17
1.00 J3FM-1618-12
iglidur J3B ®

6.0 +0.068 8.0 12.0 6.0 1.00 J3FM-0608-06 16.0 18.0 24.0 17.0 1.00 J3FM-1618-17
6.0 8.0 12.0 8.0 1.00 J3FM-0608-08 18.0 20.0 26.0 12.0 1.00 J3FM-1820-12
8.0 10.0 15.0 5.5 1.00 J3FM-0810-05 18.0 20.0 26.0 17.0 1.00 J3FM-1820-17 When to use it?
8.0 10.0 15.0 7.5 1.00 J3FM-0810-07 18.0 20.0 26.0 22.0 1.00 J3FM-1820-22 ●● When optimising wear resistance compared to iglidur® J
8.0 10.0 15.0 9.5 1.00 J3FM-0810-09 18.0 21.0 25.0 12.0 1.00 J3FM-1821-12 ●● When low moisture absorption is fundamental
8.0 10.0 15.0 10.0 1.00 J3FM-0810-10 20.0 23.0 30.0 11.5 1.50 J3FM-2023-11 ●● When good liquid media resistance is required
+0.025
10.0 12.0 18.0 7.0 1.00 J3FM-1012-07 20.0 +0.040 23.0 30.0 16.5 1.50 J3FM-2023-16 ●● When high wear resistance at low loads is required
+0.083
10.0 12.0 18.0 9.0 1.00 J3FM-1012-09 20.0 +0.124 23.0 30.0 21.5 1.50 J3FM-2023-21 ●● When very low coefficients of friction in dry operation are required
10.0 12.0 18.0 10.0 1.00 J3FM-1012-10 25.0 28.0 35.0 11.5 1.50 J3FM-2528-11
10.0 12.0 18.0 12.0 1.00 J3FM-1012-12 25.0 28.0 35.0 16.5 1.50 J3FM-2528-16
10.0 12.0 18.0 17.0 1.00 J3FM-1012-17 25.0 28.0 35.0 21.5 1.50 J3FM-2528-21
12.0 14.0 20.0 7.0 1.00 J3FM-1214-07 30.0 34.0 42.0 16.0 2.00 J3FM-3034-16 When not to use?
12.0 14.0 20.0 9.0 1.00 J3FM-1214-09 30.0 34.0 42.0 26.0 2.00 J3FM-3034-26 ●● When a wear-resistant plain bearing for linear motion is required
12.0 +0.032 14.0 20.0 12.0 1.00 J3FM-1214-12 35.0 39.0 47.0 16.0 2.00 J3FM-3539-16 iglidur® J
12.0 +0.102 14.0 20.0 17.0 1.00 J3FM-1214-17 35.0 39.0 47.0 26.0 2.00 J3FM-3539-26 ●● When continuous operating temperatures are higher than +90°C
+0.050
14.0 16.0 22.0 12.0 1.00 J3FM-1416-12 40.0 44.0 52.0 30.0 2.00 J3FM-4044-30 iglidur® J260
+0.150
14.0 16.0 22.0 17.0 1.00 J3FM-1416-17 40.0 44.0 52.0 40.0 2.00 J3FM-4044-40 ●● When radial surface pressure is higher than 45MPa
45.0 50.0 58.0 50.0 2.00 J3FM-4550-50 iglidur® W300
3)
After press-fit. Testing methods, page 57

190 3D CAD, finder and service life calculation ... www.igus.eu/J3

iglidur® J3B iglidur® J3B
+90°C +90°C
44MPa 44MPa
Bearing technology | Plain bearing | iglidur® J3B Technical data
General properties​ Testing method

Density g/cm³ 1.42 ​ –50°C up to

Ø +90°C
6.0 – 20.0mm Colour black ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.3 DIN 53495
Max. moisture absorption % weight 1.3 ​
Coefficient of friction, dynamic, against steel µ 0.08 – 0.17 ​ 44MPa
pv value, max. (dry) MPa · m/s 0.50 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,895 DIN 53457
Proven long-life material in black Flexural strength at +20°C MPa 65 DIN 53452

Bar stock,
Wear-resistant endurance runner up to 10MPa Compressive strength MPa k. A. ​
round bar Max. recommended surface pressure (+20°C) MPa 44 ​
Page 657 Shore D hardness 76 DIN 53505
The proven long-life material iglidur® J3 is now available in black as well. The endurance runner is a
specialist for pivoting and pulsating loads and also media-resistant. Physical and thermal properties
●● Aesthetically suitable Max. application temperature long-term °C +90 ​
FOOD
●● Low coefficient of friction Max. application temperature short-term °C +110 ​
●● Is especially long-lasting in the most varied of applications Min. application temperature °C –50 ​
Bar stock, ●● Low moisture absorption Thermal conductivity W/m · K 0.30 ASTM C 177
plate
Page 683 Coefficient of thermal expansion (at +23°C) K–1 · 10–5 12.7 DIN 53752
Typical application areas Electrical properties
●● Furniture industry Specific contact resistance Ωcm > 1012 DIN IEC 93
●● Sports and leisure Surface resistance Ω > 1012 DIN 53482
●● Two-wheel technology Table 01: Material properties
tribo-tape liner
Page 691
With respect to its general mechanical and thermal Resistance to weathering
specifications, iglidur® J3B is directly comparable to our iglidur® J3B plain bearings have not yet been tested for
classic, iglidur® J. their resistance to weathering. Please consult igus ® if
you‘re planning to use them outdoors.
Moisture absorption
Under standard climatic conditions, the moisture absorp- Mechanical properties
Piston rings
Page 581 tion of iglidur® J3B plain bearings is approximately 0.3% With increasing temperatures, the compressive strength of
weight. The saturation limit in water is 1.3% weight. These iglidur® J3B plain bearings decreases. Diagram 02 shows
Descriptive technical specifications values are so low that a moisture expansion need to be this inverse relationship. The maximum recommended
Wear resistance at +23°C – + considered only in extreme cases. surface pressure is a mechanical material parameter. No
conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
Vacuum drawn from this.
Two hole Wear resistance at +150°C – + In vacuum, any present moisture is released as vapour. Use Diagram 03 shows the elastic deformation of iglidur® J3B
flange
bearings in vacuum is only possible with dehumidified iglidur® J3B at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
bearings. pressure of 44MPa at room temperature the deformation
Low moisture absorption – + is less than 6%. A possible deformation could be, among
Radiation resistance others, dependant on the duty cycle of the load.
Wear resistance under water – +
Resistant to radiation up to an intensity of 3 · 10²Gy. Surface pressure, page 41
Moulded High media resistance – +
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

192 3D CAD, finder and service life calculation ... www.igus.eu/J3B Lubrication-free made easy ... from stock ... no minimum order quantity 193
iglidur® J3B iglidur® J3B
+90°C +90°C
44MPa 44MPa
Bearing technology | Plain bearing | iglidur® J3B Technical data
Permissible surface speeds 100.0 0.25
Chemicals Resistance
iglidur® J3B is also suitable for medium to high surface Alcohols + 10.0

Coefficient of friction [µ]

speeds. The maximum values shown in table 03 can only Diluted acids 0 up to – 0.20
be achieved at low pressures. At the given speeds, friction Diluted alkalines + 1.0

Pressure [MPa]
can cause a temperature increase to maximum permissible Fuels + 0.15
levels. In practice, though, this level is rarely reached due 0.1
Greases, oils without additives +
to varying application conditions. Hydrocarbons +
0.01 0.10
Surface speed, page 44 Strong acids – 0.001 0.01 0.1 1.0 10.0 0 15 25 35 45
Strong alkalines + up to 0 Surface speed [m/s] Load [MPa]
Temperature
All information given at room temperature [+20°C]
The temperatures prevailing in the bearing system also Diagram 01: Permissible pv values for iglidur® J3B plain Diagram 05: Coefficient of friction as a function of the
Table 02: Chemical resistance
have an influence on the wear. For temperatures over bearings with a wall thickness of 1mm, dry operation against pressure, v = 0.01m/s
Chemical table, page 1636
+60°C an additional securing is required. a steel shaft, at +20°C, mounted in a steel housing
Application temperatures, page 49
​ ​ Rotating Oscillating linear
Additional securing, page 49 120 2.5
long-term m/s 1.5 1.1 8.0
short-term m/s 3.0 2.1 10.0 100

Cf53, hard-chromed
2.0
Friction and wear

304 stainless steel

Free cutting steel
Table 03: Maximum surface speeds 80

High grade steel

HR carbon steel
Similar to wear resistance, the coefficient of friction µ also 1.5

H.a. aluminium
60
changes with the surface speed and load (diagrams 04 1.0
​ Dry Greases Oil Water

Wear [µm/km]
and 05). 40
Coefficient of friction µ 0.08 – 0.17 0.09 0.04 0.04

Load [MPa]
0.5

Cf53
Coefficient of friction and surfaces, page 47 20
Table 04: Coefficient of friction against steel (Ra = 1μm,
Wear resistance, page 50 0 0.0
50HRC)
20 30 40 50 60 70 80
Shaft materials Temperature [°C]
​ Housing Plain bearing Shaft
The friction and wear are also dependent, to a large Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm]
degree, on the shaft material. Shafts that are too smooth, function of temperature (44MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000
increase both the coefficient of friction and the wear of the
>3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000
bearing. For iglidur® J3B a ground surface with an average 10 350
> 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
surface finish Ra = 0.1 – 0.3µm is recommended. Diagram 300 rotating
> 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 8
06 shows results of testing different shafts. Diagram 07 oscillating
> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000 +23°C 250
shows rotating and pivoting applications in comparison. 6 +60°C
> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 200
With higher load, the wear increases more for rotating than

Deformation [%]
4 150
> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000

Wear [µm/km]
for pivoting movements. 100
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000 2
Shaft materials, page 52 50
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
0 0
Table 05: Important tolerances for plain bearings according
Installation tolerances 0 5 10 15 20 25 30 35 40 45 0 1 2 5 10 20
to ISO 3547-1 after press-fit
iglidur® J3B plain bearings are standard bearings for Load [MPa] Load [MPa]
shafts with h tolerance (recommended minimum h9). Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
​
The bearings are designed for press-fit into a housing with shaft material Cf53 hardened and ground steel, as a
machined to a H7 tolerance. After being assembled into a function of the load
nominal size housing, in standard cases the inner diameter 0.25

automatically adjusts to the E10 tolerances. For particular

Coefficient of friction [µ]

dimensions the tolerance differs depending on the wall 0.20

thickness (please see product range table). In relation to
the installation tolerance, the inner diameter changes with 0.15
the absorption of humidity.
Testing methods, page 57
0.10
0.1 0.2 0.3 0.4 0.5
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

194 3D CAD, finder and service life calculation ... www.igus.eu/J3B Lubrication-free made easy ... from stock ... no minimum order quantity 195
iglidur® J3B iglidur® J3B
+90°C +90°C
44MPa 44MPa
Bearing technology | Plain bearing | iglidur® J3B Bearing technology | Plain bearing | iglidur® J3B
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: J3BSM-0608-06 – no minimum order quantity. Order example: J3BFM-0608-06 – no minimum order quantity.
J3B iglidur® material S Sleeve bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1 J3B iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
6.0 +0.020 +0.068 8.0 6.0 J3BSM-0608-06 6.0 +0.020 +0.068 8.0 12.0 8.0 1.00 J3BFM-0608-06
8.0 10.0 10.0 J3BSM-0810-10 8.0 10.0 15.0 9.5 1.00 J3BFM-0810-10
+0.025 +0.083 +0.025 +0.083
10.0 12.0 10.0 J3BSM-1012-10 10.0 12.0 18.0 9.0 1.00 J3BFM-1012-10
12.0 14.0 12.0 J3BSM-1214-12 12.0 14.0 20.0 12.0 1.00 J3BFM-1214-12
+0.032 +0.102 +0.032 +0.102
16.0 18.0 15.0 J3BSM-1618-15 16.0 18.0 24.0 17.0 1.00 J3BFM-1618-17
20.0 +0.040 +0.124 23.0 20.0 J3BSM-2023-20 20.0 +0.040 +0.124 23.0 30.0 21.5 1.50 J3BFM-2023-21
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/J3B www.igus.eu/J3B
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

196 3D CAD, finder and service life calculation ... www.igus.eu/J3B Lubrication-free made easy ... from stock ... no minimum order quantity 197
Endurance runner with high
dimensional stability at high
temperatures
Can be used with many kinds of shafts
and loads
iglidur J350 ®

When to use it?

●● When a wear-resistant bearing for rotational movement at medium and high loads is required
●● When a cost-effective plain bearing for high temperatures is required
●● When press-fit up to +150°C is necessary
●● When the bearing is exposed to shock loading

When not to use?

●● When continuous operating temperatures are higher than +180°C
iglidur® X
●● When the lowest friction is required
iglidur® J
●● When a cost-effective plain bearing with low friction is required
iglidur® D, iglidur® R
●● For high rotational speeds
iglidur® J
iglidur® J350 iglidur® J350
+180°C +180°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® J350 Technical data
​General properties Testing method

Density g/cm³ 1.44 ​ –100°C up to

Ø +180°C
4.0 – 50.0mm Colour yellow ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.3 DIN 53495
Max. moisture absorption % weight 1.6 ​
Coefficient of friction, dynamic, against steel µ 0.10 – 0.20 ​ 60MPa
pv value, max. (dry) MPa · m/s 0.45 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,000 DIN 53457
Endurance runner with high dimensional Flexural strength at +20°C MPa 55 DIN 53452

Bar stock,
stability at high temperatures Compressive strength MPa 60 ​
Max. recommended surface pressure (+20°C) MPa 60 ​
round bar
Page 675 Can be used with many kinds of shafts and loads Shore D hardness 80 DIN 53505
Physical and thermal properties
An outstanding plain bearing for rotating applications – and for a wide range of different shaft materials: Max. application temperature long-term °C +180 ​
with iglidur® J350 plain bearings, the service life can often be increased for applications between 2 and FOOD
Max. application temperature short-term °C +220 ​
50MPa. In addition, the high temperature resistance makes it a very versatile material. Min. application temperature °C –100 ​
Bar stock, ●● Recommended for steel shafts Thermal conductivity W/m · K 0.24 ASTM C 177
plate ●● Continuous operating temperatures up to +180°C
Page 683 Coefficient of thermal expansion (at +23°C) K–1 · 10–5 7 DIN 53752
●● Suitable for medium and high loads Electrical properties
●● Suitable for rotating applications Specific contact resistance Ωcm > 1013 DIN IEC 93
●● Lubrication-free Surface resistance Ω > 1010 DIN 53482
●● Maintenance-free
Table 01: Material properties
tribo-tape liner
Page 691 Typical application areas
iglidur® J350 blends universally good wear resistance, Resistance to weathering
●● Automation
flexibility and temperature resistance into a very versatile iglidur® J350 plain bearings are continuously resistant
●● Mechanical engineering
iglidur® material with a broad application spectrum. to weathering. The material properties are only slightly
●● Automotive
affected. Possible discolorations are only superficial.
●● Glass industry
Moisture absorption
The moisture absorption of iglidur® J350 is low and can be Mechanical properties
Piston rings
Page 584 ignored when using standard plain bearings. Even when With increasing temperatures, the compressive strength of
saturated with water, iglidur® J350 does not absorb more iglidur® J350 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications than 1.6% weight of water (by weight). this inverse relationship. The maximum recommended
Wear resistance at +23°C – + surface pressure is a mechanical material parameter. No
Vacuum conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
In vacuum, any present moisture is released as vapour. Use drawn from this.
Two hole Wear resistance at +150°C – + in vacuum is only possible with dehumidified iglidur® J350 iglidur® J350 plain bearings are adequate for medium and
flange
bearings bearings. high loads. Diagram 03 shows the elastic deformation
Page 603 Low coefficient of friction – +
of iglidur® J350 at radial loads. It shows the material
Low moisture absorption – + Radiation resistance behaviour submitted to a short-term load. The ambient
Plain bearings made from iglidur® J350 are resistant up to temperatures are only noticeable at 60MPa.
Wear resistance under water – +
a radiation intensity of 2 · 10²Gy. Surface pressure, page 41
Moulded High media resistance – +
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

200 3D CAD, finder and service life calculation ... www.igus.eu/J350 Lubrication-free made easy ... from stock ... no minimum order quantity 201
iglidur® J350 iglidur® J350
+180°C +180°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® J350 Technical data
Permissible surface speeds Installation tolerances 100.0 0.40

iglidur® J350 plain bearings are suitable for low and iglidur® J350 plain bearings are standard bearings for
10.0 0.30

Coefficient of friction [µ]

medium speeds in rotating and oscillating applications. shafts with h tolerance (recommended minimum h9).
The wear rates, however, are much better in the case The bearings are designed for press-fit into a housing 1.0 0.20

Pressure [MPa]
of rotating applications. iglidur® J350 is also excellent for machined to a H7 tolerance. After being assembled into a
linear movements. nominal size housing, in standard cases the inner diameter 0.1 0.10
Surface speed, page 44 automatically adjusts to the F10 tolerances. For particular
0.01 0.00
dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 10 20 30 40 50 60
Temperature thickness (please see product range table).
Surface speed [m/s] Load [MPa]
The temperatures prevailing in the bearing system also have Testing methods, page 57
an influence on the wear. The wear-rate of iglidur® J350 Diagram 01: Permissible pv values for iglidur® J350 plain Diagram 05: Coefficient of friction as a function of the load,
bearings changes very little at high temperatures. In some bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
cases, wear even decreases at +100°C. For temperatures Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
over +140°C an additional securing is required. Alcohols +
Application temperatures, page 49 Diluted acids + 80 0.40
Additional securing, page 49 Diluted alkalines +
0.35
Fuels +

Coefficient of friction [µ]

60
0.30
Friction and wear Greases, oils without additives +
40 0.25
The coefficient of friction of iglidur® J350 in dry operation Hydrocarbons + up to 0
against steel is very good. They decrease significantly Strong acids + up to 0 0.20
20

Load [MPa]
at higher surface speeds. This benefits the service life Strong alkalines + 0.15
of the plain bearings in continuous operations with high All information given at room temperature [+20°C] 0 0.00
surface speeds. Diagram 04 illustrates this relationship. Table 02: Chemical resistance 20 40 60 80 100 120 140 160 180 0.4 0.6 0.8 1.0 1.2 1.4 1.6
Especially with loads higher than 2MPa, the iglidur® J350 Chemical table, page 1636 Temperature [°C]
plain bearings are clearly superior to other bearings in Diagram 02: Maximum recommended surface pressure as a Diagram 06: Coefficient of friction as a function of the shaft
rotating applications. ​ ​ Rotating Oscillating linear function of temperature (60MPa at +20°C) surface (Cf53 shaft)
Coefficient of friction and surfaces, page 47 long-term m/s 1.3 1.0 4.0
Wear resistance, page 50 short-term m/s 3.0 2.3 8.0 6 3.0
Table 03: Maximum surface speeds
5 2.5

Cf53, hard-chromed
Shaft materials

304 stainless steel

Free cutting steel
4 +23°C 2.0

High grade steel

HR carbon steel
Diagrams 06 and 07 show the test results of iglidur® J350 ​ Dry Greases Oil Water +60°C

H.a. aluminium
3 1.5
plain bearings running against various shaft materials. Coefficient of friction µ 0.10 – 0.20 0.09 0.04 0.04

Deformation [%]

Wear [µm/km]
iglidur® J350 plain bearings can be combined with various Table 04: Coefficient of friction against steel (Ra = 1μm, 2 1.0

Cf53
shaft materials. One shaft – bearing combination stands out 50HRC) 1 0.5
when looking at the wear results of the test: iglidur® J350 0 0.0
with soft 304 stainless steel. Not many bearing materials ​ Housing Plain bearing Shaft 0 10 20 30 40 50 60
are suitable for use with this rather difficult soft stainless Ø d1 [mm] H7 [mm] F10 [mm] h9 [mm] Load [MPa]
steel material (304 stainless steel) and achieve good wear 0–3 +0.000 +0.010 +0.006 +0.046 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear, rotating with different shaft materials,
results. Also, good properties are reached with hard-anodised >3–6 +0.000 +0.012 +0.010 +0.058 –0.030 +0.000 pressure, p = 1MPa, v = 0.3m/s
aluminium shafts. If the shaft material you plan on using is > 6 – 10 +0.000 +0.015 +0.013 +0.071 –0.036 +0.000
not shown in these test results, please contact us. > 10 – 18 +0.000 +0.018 +0.016 +0.086 –0.043 +0.000 0.30

Shaft materials, page 52 > 18 – 30 +0.000 +0.021 +0.020 +0.104 –0.052 +0.000
0.25
Coefficient of friction [µ]

> 30 – 50 +0.000 +0.025 +0.025 +0.125 –0.062 +0.000

> 50 – 80 +0.000 +0.030 +0.030 +0.150 –0.074 +0.000 0.20
> 80 – 120 +0.000 +0.035 +0.036 +0.176 –0.087 +0.000
> 120 – 180 +0.000 +0.040 +0.043 +0.203 +0.000 +0.100 0.15
Table 05: Important tolerances for plain bearings according
0.10
to ISO 3547-1 after press-fit
0.10 0.15 0.20 0.25 0.30 0.35 0.40 0.45 0.50
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 1MPa

202 3D CAD, finder and service life calculation ... www.igus.eu/J350 Lubrication-free made easy ... from stock ... no minimum order quantity 203
iglidur® J350 iglidur® J350
+180°C +180°C
60MPa 60MPa
Bearing technology | Plain bearing | iglidur® J350 Product range
Sleeve bearing (form S) d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.
Tolerance3) h13 Tolerance3) h13
f1

30°
[mm] [mm] [mm] [mm] [mm] [mm]
+0.020 40.0 44.0 40.0 J350SM-4044-40
30.0 34.0 40.0 J350SM-3034-40
+0.104 40.0 44.0 50.0 J350SM-4044-50

d1

d2
0.5
32.0 36.0 20.0 J350SM-3236-20 45.0 50.0 20.0 J350SM-4550-20
32.0 36.0 30.0 J350SM-3236-30 45.0 50.0 30.0 J350SM-4550-30

30°
b1 32.0 36.0 40.0 J350SM-3236-40 45.0 50.0 40.0 J350SM-4550-40
+0.025
35.0 39.0 20.0 J350SM-3539-20 45.0 50.0 50.0 J350SM-4550-50
+0.025 +0.125
35.0 39.0 30.0 J350SM-3539-30 50.0 55.0 20.0 J350SM-5055-20
+0.125
2)
Thickness < 0.6mm: Chamfer = 20° 35.0 39.0 40.0 J350SM-3539-40 50.0 55.0 30.0 J350SM-5055-30
Chamfer in relation to d1 35.0 39.0 50.0 J350SM-3539-50 50.0 55.0 40.0 J350SM-5055-40
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and 40.0 44.0 20.0 J350SM-4044-20 50.0 55.0 50.0 J350SM-5055-50
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions 40.0 44.0 30.0 J350SM-4044-30 50.0 55.0 60.0 J350SM-5055-60
3)
After press-fit. Testing methods, page 57
Order example: J350SM-0405-04 – no minimum order quantity.
J350 iglidur® material S Sleeve bearing M Metric 04 Inner Ø d1 05 Outer Ø d2 04 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 b1 Part No.

Tolerance3) h13 Tolerance3) h13
[mm] [mm] [mm] [mm] [mm] [mm]
4.0 5.5 4.0 J350SM-0405-04 16.0 18.0 20.0 J350SM-1618-20
4.0 5.5 6.0 J350SM-0405-06 16.0 18.0 25.0 J350SM-1618-25
+0.016
5.0 7.0 5.0 J350SM-0507-05 18.0 20.0 15.0 J350SM-1820-15
+0.010 +0.086
5.0 7.0 10.0 J350SM-0507-10 18.0 20.0 20.0 J350SM-1820-20
+0.058
6.0 8.0 6.0 J350SM-0608-06 18.0 20.0 25.0 J350SM-1820-25
6.0 8.0 8.0 J350SM-0608-08 20.0 23.0 10.0 J350SM-2023-10
6.0 8.0 10.0 J350SM-0608-10 20.0 23.0 15.0 J350SM-2023-15
8.0 10.0 8.0 J350SM-0810-08 20.0 23.0 20.0 J350SM-2023-20
8.0 10.0 10.0 J350SM-0810-10 20.0 23.0 25.0 J350SM-2023-25
8.0 10.0 12.0 J350SM-0810-12 20.0 23.0 30.0 J350SM-2023-30
10.0 +0.013 12.0 8.0 J350SM-1012-08 22.0 25.0 15.0 J350SM-2225-15
10.0 +0.071 12.0 10.0 J350SM-1012-10 22.0 25.0 20.0 J350SM-2225-20
10.0 12.0 12.0 J350SM-1012-12 22.0 25.0 25.0 J350SM-2225-25
10.0 12.0 15.0 J350SM-1012-15 22.0 25.0 30.0 J350SM-2225-30
10.0 12.0 20.0 J350SM-1012-20 24.0 27.0 15.0 J350SM-2427-15
12.0 14.0 10.0 J350SM-1214-10 24.0 27.0 20.0 J350SM-2427-20
12.0 14.0 12.0 J350SM-1214-12 24.0 +0.020 27.0 25.0 J350SM-2427-25
12.0 14.0 15.0 J350SM-1214-15 24.0 +0.104 27.0 30.0 J350SM-2427-30
12.0 14.0 20.0 J350SM-1214-20 25.0 28.0 15.0 J350SM-2528-15 Available from stock Ordering note
13.0 15.0 10.0 J350SM-1315-10 25.0 28.0 20.0 J350SM-2528-20 Detailed information about delivery time online. Our prices are scaled according to order
13.0 15.0 20.0 J350SM-1315-20 25.0 28.0 25.0 J350SM-2528-25 www.igus.eu/24 quantities, current prices can be found online.
14.0 +0.016 16.0 15.0 J350SM-1416-15 25.0 28.0 30.0 J350SM-2528-30 Online ordering
14.0 +0.086 16.0 20.0 J350SM-1416-20 25.0 28.0 45.0 J350SM-2528-45 Discount scaling
Including delivery times, prices, online tools
14.0 16.0 25.0 J350SM-1416-25 28.0 32.0 20.0 J350SM-2832-20 1–9 50 – 99 500 – 999
www.igus.eu/J350
15.0 17.0 15.0 J350SM-1517-15 28.0 32.0 25.0 J350SM-2832-25 10 – 24 100 – 199 1,000 – 2,499
15.0 17.0 20.0 J350SM-1517-20 28.0 32.0 30.0 J350SM-2832-30 25 – 49 200 – 499 2,500 – 4,999
15.0 17.0 25.0 J350SM-1517-25 30.0 34.0 20.0 J350SM-3034-20 No minimum order value.
16.0 18.0 4.0 J350SM-1618-04 30.0 34.0 25.0 J350SM-3034-25 No low-quantity surcharges.
16.0 18.0 15.0 J350SM-1618-15 30.0 34.0 30.0 J350SM-3034-30 Free shipping within Germany for orders
3)
After press-fit. Testing methods, page 57 above €150.

204 3D CAD, finder and service life calculation ... www.igus.eu/J350 Lubrication-free made easy ... from stock ... no minimum order quantity 205
iglidur® J350
+180°C
60MPa
Bearing technology | Plain bearing | iglidur® J350
Flange bearing (form F)
.5
.0
ax
f1

30
rm

°
d2
d3

d1
b2
b1

2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions

Order example: J350FM-0608-04 – no minimum order quantity.

J350 iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 04 Total length b1
Ideal for plastic shafts
d1 d1
Tolerance3)
d2 d3
d133)
b1
h13
b2 Part No.
h13
d1 d1
Tolerance3)
d2 d3
d133)
b1
h13
b2 Part No.
h13
Wear-resistant at medium temperatures
[mm]
6.0
+0.010
[mm] [mm] [mm] [mm]
8.0 12.0 4.0 1.00 J350FM-0608-04 16.0
[mm]
18.0
[mm] [mm] [mm] [mm]
24.0 12.0 1.00 J350FM-1618-12 and loads
6.0 8.0 12.0 6.0 1.00 J350FM-0608-06 16.0 18.0 24.0 17.0 1.00 J350FM-1618-17
6.0
8.0
+0.058
8.0
10.0
12.0
15.0
8.0
5.5
1.00 J350FM-0608-08
1.00 J350FM-0810-05
18.0
18.0
+0.016
+0.086
20.0
20.0
26.0
26.0
12.0
17.0
1.00 J350FM-1820-12
1.00 J350FM-1820-17
iglidur J260 ®

8.0 10.0 15.0 7.5 1.00 J350FM-0810-07 18.0 20.0 26.0 22.0 1.00 J350FM-1820-22
8.0 10.0 15.0 9.5 1.00 J350FM-0810-09 20.0 23.0 30.0 11.5 1.50 J350FM-2023-11
8.0 10.0 15.0 10.0 1.00 J350FM-0810-10 20.0 23.0 30.0 16.5 1.50 J350FM-2023-16 When to use it?
+0.013
10.0 12.0 18.0 7.0 1.00 J350FM-1012-07 20.0 23.0 30.0 21.5 1.50 J350FM-2023-21 ●● When polymer shafts are used
+0.071
10.0 12.0 18.0 9.0 1.00 J350FM-1012-09 25.0 28.0 35.0 11.5 1.50 J350FM-2528-11 ●● When the temperature rating of iglidur® J is not sufficient
10.0 12.0 18.0 10.0 1.00 J350FM-1012-10 25.0 +0.020 28.0 35.0 16.5 1.50 J350FM-2528-16 ●● When a plain bearing with low coefficient of friction is required
10.0 12.0 18.0 12.0 1.00 J350FM-1012-12 25.0 +0.104 28.0 35.0 21.5 1.50 J350FM-2528-21 ●● When high wear resistance is required at medium loads
10.0 12.0 18.0 17.0 1.00 J350FM-1012-17 30.0 34.0 42.0 16.0 2.00 J350FM-3034-16 ●● When good liquid media resistance is required
12.0 14.0 20.0 7.0 1.00 J350FM-1214-07 30.0 34.0 42.0 22.0 2.00 J350FM-3034-22
12.0 14.0 20.0 9.0 1.00 J350FM-1214-09 30.0 34.0 42.0 26.0 2.00 J350FM-3034-26
12.0 14.0 20.0 12.0 1.00 J350FM-1214-12 30.0 34.0 42.0 37.0 2.00 J350FM-3034-37
12.0 14.0 20.0 17.0 1.00 J350FM-1214-17 35.0 39.0 47.0 16.0 2.00 J350FM-3539-16 When not to use?
+0.016
14.0 16.0 22.0 12.0 1.00 J350FM-1416-12 35.0 39.0 47.0 26.0 2.00 J350FM-3539-26 ●● When high surface pressures occur
+0.086 +0.025
14.0 16.0 22.0 17.0 1.00 J350FM-1416-17 40.0 44.0 52.0 30.0 2.00 J350FM-4044-30 iglidur® Z
+0.125
15.0 17.0 23.0 9.0 1.00 J350FM-1517-09 40.0 44.0 52.0 40.0 2.00 J350FM-4044-40 ●● When continuous operating temperatures are higher than +120°C
15.0 17.0 23.0 12.0 1.00 J350FM-1517-12 45.0 50.0 58.0 50.0 2.00 J350FM-4550-50 iglidur® J350
15.0 17.0 23.0 17.0 1.00 J350FM-1517-17 ●● When universal wear resistance is required
3)
After press-fit. Testing methods, page 57 iglidur® J

206 3D CAD, finder and service life calculation ... www.igus.eu/J350

iglidur® J260 iglidur® J260
+120°C +120°C
40MPa 40MPa
Bearing technology | Plain bearing | iglidur® J260 Technical data
General properties​ Testing method

Density g/cm³ 1.35 ​ –100°C up to

Ø +120°C
6.0 – 20.0mm Colour yellow ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.2 DIN 53495
Max. moisture absorption % weight 0.4 ​
Coefficient of friction, dynamic, against steel µ 0.06 – 0.20 ​ 40MPa
pv value, max. (dry) MPa · m/s 0.35 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,200 DIN 53457
Ideal for plastic shafts Flexural strength at +20°C MPa 60 DIN 53452

Bar stock,
Wear-resistant at medium temperatures and loads Compressive strength MPa 50 ​
round bar Max. recommended surface pressure (+20°C) MPa 40 ​
Page 676 Shore D hardness 77 DIN 53505
Time and again the iglidur® J260 material proves its worth where the maximum service life and best
coefficient of friction are required under special application conditions – particularly in connection with Physical and thermal properties
plastic shafts! Max. application temperature long-term °C +120 ​
FOOD
●● For low and medium loads Max. application temperature short-term °C +140 ​
●● High media resistance Min. application temperature °C –100 ​
Bar stock, ●● Slightly higher temperature rating than iglidur® J Thermal conductivity W/m · K 0.24 ASTM C 177
plate
Page 683 ●● Long service life - even on polymer shafts and other special cases Coefficient of thermal expansion (at +23°C) K–1 · 10–5 13 DIN 53752
Electrical properties
Typical application areas Specific contact resistance Ωcm > 1012 DIN IEC 93
●● Automation Surface resistance Ω > 1010 DIN 53482
●● Plant construction Table 01: Material properties
tribo-tape liner ●● Test engineering and quality assurance
Page 691
●● Robotics industry Similar to the classic, iglidur® J, iglidur ® J260 is an Resistance to weathering
●● Electronics industry endurance runner with outstanding wear behaviour, but iglidur® J260 plain bearings are continuously resistant
provides increased reserves at its long-term application to weathering. The material properties are only slightly
temperature of +120°C. affected. Possible discolorations are only superficial.

Moisture absorption Mechanical properties

Piston rings
Page 581 Under standard climatic conditions, the moisture absorption With increasing temperatures, the compressive strength of
of iglidur® J260 plain bearings is approximately 0.2% iglidur® J260 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications weight. The saturation limit in water is 0.4% weight. These this inverse relationship. The maximum recommended
Wear resistance at +23°C – + values are so low that a moisture expansion need to be surface pressure is a mechanical material parameter. No
considered only in extreme cases. conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
drawn from this.
Two hole Wear resistance at +150°C – + Vacuum Diagram 03 shows the elastic deformation of iglidur® J260
flange
bearings In vacuum, any present moisture is released as vapour. Use at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
in vacuum is only possible with dehumidified iglidur® J260 pressure of 40MPa at room temperature the deformation
Low moisture absorption – + bearings. is less than 2.5%. A possible deformation could be, among
others, dependant on the duty cycle of the load.
Wear resistance under water – +
Radiation resistance Surface pressure, page 41
Moulded High media resistance – + Resistant to radiation up to an intensity of 3 · 10²Gy.
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

208 3D CAD, finder and service life calculation ... www.igus.eu/J260 Lubrication-free made easy ... from stock ... no minimum order quantity 209
iglidur® J260 iglidur® J260
+120°C +120°C
40MPa 40MPa
Bearing technology | Plain bearing | iglidur® J260 Technical data
Permissible surface speeds Installation tolerances 100.0 0.25

iglidur® J260 has been developed for low to medium iglidur® J260 plain bearings are standard bearings for
10.0 0.20

Coefficient of friction [µ]

surface speeds. The maximum values shown in table shafts with h tolerance (recommended minimum h9).
03 can only be achieved at low pressures. At the given The bearings are designed for press-fit into a housing 1.0 0.15

Pressure [MPa]
speeds, friction can cause a temperature increase to machined to a H7 tolerance. After being assembled into a
maximum permissible levels. In practice, though, this level nominal size housing, in standard cases the inner diameter 0.1 0.10
is rarely reached due to varying application conditions. automatically adjusts to the E10 tolerances. For particular
0.01 0.00
Surface speed, page 44 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 10 20 30 40
thickness (please see product range table).
Surface speed [m/s] Load [MPa]
Temperature Testing methods, page 57
The temperatures prevailing in the bearing system also have Diagram 01: Permissible pv values for iglidur® J260 plain Diagram 05: Coefficient of friction as a function of the load,
an influence on the wear. With increasing temperatures, bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
the wear increases and this effect is significant when Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
temperatures rise over +80°C. For temperatures over Alcohols + up to 0
+80°C an additional securing is required. Diluted acids – 60 3.0
Application temperatures, page 49 Diluted alkalines + up to 0
50 2.5

Cf53, hard-chromed
Additional securing, page 49 Fuels –

304 stainless steel

Free cutting steel
40 2.0

High grade steel

HR carbon steel
Greases, oils without additives 0 up to –

H.a. aluminium
30 1.5
Friction and wear Hydrocarbons +

Wear [µm/km]
Similar to wear resistance, the coefficient of friction μ also Strong acids – 20 1.0

Load [MPa]

Cf53
changes with the load. The coefficient of friction decreases Strong alkalines + up to 0 10 0.5
considerably with increasing pressures, whereas a slight All information given at room temperature [+20°C] 0 0.0
increase in surface speed causes an increase of the coefficient Table 02: Chemical resistance 20 30 40 50 60 70 80 90 100 110 120
of friction (diagrams 04 and 05). Chemical table, page 1636 Temperature [°C]
Coefficient of friction and surfaces, page 47 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Wear resistance, page 50 ​ ​ Rotating Oscillating linear function of temperature (40MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
long-term m/s 1.0 0.7 3.0
Shaft materials short-term m/s 2.0 1.4 4.0 4 120
The friction and wear are also dependent, to a large degree, Table 03: Maximum surface speeds
100 rotating
oscillating
on the shaft material. Shafts that are too smooth, increase 3
+23°C 80
both the coefficient of friction and the wear of the bearing. ​ Dry Greases Oil Water +60°C
2 60
For iglidur® J260 a ground surface with an average surface Coefficient of friction µ 0.06 – 0.20 0.09 0.04 0.04

Deformation [%]

Wear [µm/km]
finish Ra = 0.8µm is recommended. Diagram 06 shows the Table 04: Coefficient of friction against steel (Ra = 1μm, 40
1
test results of iglidur® J260 plain bearings running against 50HRC) 20
various shaft materials. It is important to notice that with 0 0
increasing loads, the recommended hardness of the shaft ​ Housing Plain bearing Shaft 0.0 12.5 25.0 37.5 50.0 0 5 10 15 20 25 30 35 40
increases. The "soft" shafts tend to wear more easily and thus Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa] Load [MPa]
increase the wear of the overall system, if the loads exceed 0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
2MPa. The comparison of rotating and pivoting movements >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with shaft material Cf53 hardened and ground steel, as a
in diagram 07 makes it very clear that iglidur® J260 plain > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000 function of the load
bearings are most suited for rotating operation. > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 0.25

Shaft materials, page 52 > 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
Coefficient of friction [µ]

> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 0.20

> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
0.15
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
Table 05: Important tolerances for plain bearings according
0.10
to ISO 3547-1 after press-fit
0.05 0.10 0.15 0.20 0.25 0.30 0.35
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

210 3D CAD, finder and service life calculation ... www.igus.eu/J260 Lubrication-free made easy ... from stock ... no minimum order quantity 211
iglidur® J260 iglidur® J260
+120°C +120°C
40MPa 40MPa
Bearing technology | Plain bearing | iglidur® J260 Bearing technology | Plain bearing | iglidur® J260
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: J260SM-0608-06 – no minimum order quantity. Order example: J260FM-0608-06 – no minimum order quantity.
J260 iglidur® material S Sleeve bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1 J260 iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
6.0 +0.020 +0.068 8.0 6.0 J260SM-0608-06 6.0 +0.020 +0.068 8.0 12.0 6.0 1.00 J260FM-0608-06
8.0 10.0 6.0 J260SM-0810-06 8.0 10.0 15.0 10.0 1.00 J260FM-0810-10
+0.025 +0.083
8.0 +0.025 +0.083 10.0 10.0 J260SM-0810-10 10.0 12.0 18.0 10.0 1.00 J260FM-1012-10
10.0 12.0 10.0 J260SM-1012-10 12.0 14.0 20.0 12.0 1.00 J260FM-1214-12
+0.032 +0.102
12.0 14.0 12.0 J260SM-1214-12 16.0 18.0 24.0 17.0 1.00 J260FM-1618-17
12.0 14.0 15.0 J260SM-1214-15 20.0 +0.040 +0.124 23.0 30.0 21.5 1.50 J260FM-2023-21
16.0 18.0 13.5 J260SM-1618-135 3)
After press-fit. Testing methods, page 57
+0.032 +0.102
16.0 18.0 15.0 J260SM-1618-15
18.0 20.0 12.0 J260SM-1820-12
18.0 20.0 20.0 J260SM-1820-20
20.0 +0.040 +0.124 23.0 20.0 J260SM-2023-20
3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/J260 www.igus.eu/J260
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

212 3D CAD, finder and service life calculation ... www.igus.eu/J260 Lubrication-free made easy ... from stock ... no minimum order quantity 213
Endurance runner up to +180°C
For applications that are clean and dry
iglidur W360 ®

When to use it?

●● When an extremely wear-resistant plain bearing is required for medium loads
●● When a low coefficient of friction at higher temperatures is required
●● When continuous operating temperatures are higher than +90°C

When not to use?

●● When a wear-resistant plain bearing is sought for the standard temperature range and low to medium loads
iglidur® J
●● When the maximum temperature resistance and high wear resistance is required
iglidur® Z, iglidur® J350, iglidur® V400
●● When the highest wear resistance under water is required
iglidur® UW, iglidur® H370
iglidur® W360 iglidur® W360
+180°C +180°C
75MPa 75MPa
Bearing technology | Plain bearing | iglidur® W360 Technical data
General properties​ Testing method

Density g/cm³ 1.34 ​ –40°C up to

Ø +180°C
6.0 – 20.0mm Colour yellow ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.2 DIN 53495
Max. moisture absorption % weight 1.6 ​
Coefficient of friction, dynamic, against steel µ 0.07 – 0.21 ​ 75MPa
pv value, max. (dry) MPa · m/s 0.35 ​
Also available
as: Mechanical properties
Flexural modulus MPa 3,829 DIN 53457
Endurance runner up to +180°C Flexural strength at +20°C MPa 119 DIN 53452

Bar stock,
For applications that are clean and dry Compressive strength MPa 75 ​
round bar Max. recommended surface pressure (+20°C) MPa 75 ​
Page 657 Shore D hardness 80 DIN 53505
The new iglidur® material combines outstanding endurance running properties with excellent temperature
resistance, reduced moisture absorption and good value for money – a real all-rounder in the endurance Physical and thermal properties
field. Max. application temperature long-term °C +180 ​
FOOD
●● High wear resistance Max. application temperature short-term °C +200 ​
●● Temperature-resistant up to +180°C Min. application temperature °C –40 ​
Bar stock, ●● Suitable for wet environments Thermal conductivity W/m · K 0.24 ASTM C 177
plate
Page 683 ●● Good price-performance ratio Coefficient of thermal expansion (at +23°C) K–1 · 10–5 6 DIN 53752
●● Lubrication-free Electrical properties
●● Maintenance-free Specific contact resistance Ωcm > 1013 DIN IEC 93
Surface resistance Ω > 1012 DIN 53482
Typical application areas Table 01: Material properties
tribo-tape liner ●● Material handling
Page 691
●● Automation Low moisture absorption and high temperature resistance Resistance to weathering
●● Two-wheel technology result in an extremely broad range of uses for this extremely iglidur® W360 plain bearings are resistant to weathering.
●● Electromobility wear-resistant material. The material properties are slightly affected. Discoloration
occurs.
Moisture absorption
The moisture absorption of iglidur® W360 is low and can Mechanical properties
Piston rings
Page 581 be disregarded when used in a humid environment. With With increasing temperatures, the compressive strength
a full saturation of 1.6% weight, however, underwater use of iglidur® W360 plain bearings decreases. Diagram 02
Descriptive technical specifications is only possible to a very restricted extent. shows this inverse relationship. However, at the long-term
Wear resistance at +23°C – + maximum temperature of +180°C the permissible surface
Vacuum pressure is around 10MPa. The maximum recommended
Wear resistance at +90°C – +
In vacuum, any present moisture is released as vapour. Use surface pressure is a mechanical material parameter. No
Two hole Wear resistance at +150°C – + in vacuum is only possible with dehumidified iglidur® W360 conclusions regarding the tribological properties can be
flange
bearings bearings. drawn from this.
Page 603 Low coefficient of friction – +
iglidur® W360 plain bearings are suitable for a broad
Low moisture absorption – + Radiation resistance range of loads. Diagram 03 shows the deformation under
Plain bearings made from iglidur® W360 are resistant up temperature. It shows the material behaviour submitted
Wear resistance under water – +
to a radiation intensity of 2 · 10²Gy. to a short-term load.
Moulded High media resistance – + Surface pressure, page 41
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

216 3D CAD, finder and service life calculation ... www.igus.eu/W360 Lubrication-free made easy ... from stock ... no minimum order quantity 217
iglidur® W360 iglidur® W360
+180°C +180°C
75MPa 75MPa
Bearing technology | Plain bearing | iglidur® W360 Technical data
Permissible surface speeds 100.0 0.25
Chemicals Resistance
iglidur® W360 plain bearings are suitable for low and Alcohols 0 up to – 0.20
10.0

Coefficient of friction [µ]

medium speeds in rotating and oscillating applications. Diluted acids 0 up to – 0.15
The wear rates, however, are much better in the case of Diluted alkalines + 1.0
0.10

Pressure [MPa]
rotating applications. iglidur® W360 is also excellent for Fuels +
linear movements. 0.1
Greases, oils without additives + 0.05
Surface speed, page 44 Hydrocarbons +
0.01 0.00
Strong acids 0 up to – 0.001 0.01 0.1 1.0 10.0 0 10 20 30 40 50 60 70
Temperature Strong alkalines + Surface speed [m/s] Load [MPa]
The temperature resistance makes iglidur® W360 a
All information given at room temperature [+20°C]
universal material for plain bearings in different industries. Diagram 01: Permissible pv values for iglidur® W360 plain Diagram 05: Coefficient of friction as a function of the load,
Table 02: Chemical resistance
Short-term application temperatures up to +200°C are bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Chemical table, page 1636
permitted. For temperatures over +90°C an additional a steel shaft, at +20°C, mounted in a steel housing
securing is required.
​ ​ Rotating Oscillating linear
Application temperatures, page 49 80 0.20
long-term m/s 1.2 0.9 3.0
Additional securing, page 49
short-term m/s 2.7 2.0 5.0 0.16

Coefficient of friction [µ]

60
Table 03: Maximum surface speeds
Friction and wear 0.12
40
The coefficient of friction of iglidur® W360 in dry operation 0.08
​ Dry Greases Oil Water
against steel is very good. They constantly remain at a
Coefficient of friction µ 0.07 – 0.21 0.09 0.04 0.04 20

Load [MPa]
0.04
low level regardless of the speed. Diagram 04 illustrates
Table 04: Coefficient of friction against steel (Ra = 1μm,
this relationship. As the load increases, the coefficient of 0 0.00
50HRC)
friction decreases. The correlation is especially strong up 20 40 60 80 100 120 140 160 180 0.4 0.6 0.8 1.0 1.2 1.4 1.6
to approximately 15MPa (diagram 05). Temperature [°C]
​ Housing Plain bearing Shaft
Coefficient of friction and surfaces, page 47 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Coefficient of friction as a function of the shaft
Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm]
Wear resistance, page 50 function of temperature (75MPa at +20°C) surface (Cf53 shaft)
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000
>3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000
Shaft materials 4.0 5
> 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
In the case of iglidur® W360, the shaft’s surface finish has
> 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000

Cf53, hard-chromed
4
practically no effect on the coefficient of friction in the range 3.0

304 stainless steel

Free cutting steel
> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000

High grade steel

HR carbon steel
+23°C
of up to 1.6MPa (diagram 06). Diagram 07 shows results 3

H.a. aluminium
> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 +60°C
2.0
of testing different shafts. iglidur® W360 plain bearings are

Deformation [%]
> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 2

Wear [µm/km]
suitable for all sliding surfaces. During rotation with a load 1.0
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000 1

Cf53
of 1MPa, all HC aluminium, Cf53 and stainless steel shafts
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
stand out. A similar picture also exists with other loads 0.0 0
Table 05: Important tolerances for plain bearings according
or pivoting movements. If the shaft material you plan on 0 25 50 75 100 125 150
to ISO 3547-1 after press-fit
using is not shown in these test results, please contact us. Load [MPa]
Shaft materials, page 52 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear, rotating with different shaft materials,
​
p = 1MPa, v = 0.3m/s
Installation tolerances
iglidur® W360 plain bearings are standard bearings for 0.25

shafts with h tolerance (recommended minimum h9). 0.20

Coefficient of friction [µ]

The bearings are designed for press-fit into a housing

0.15
machined to a H7 tolerance. After being assembled into a
nominal size housing, in standard cases the inner diameter 0.10

automatically adjusts to the E10 tolerances. 0.05

Testing methods, page 57
0.00
0.0 0.3 0.6 0.9 1.2 1.5
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 1MPa

218 3D CAD, finder and service life calculation ... www.igus.eu/W360 Lubrication-free made easy ... from stock ... no minimum order quantity 219
iglidur® W360 iglidur® W360
+180°C +180°C
75MPa 75MPa
Bearing technology | Plain bearing | iglidur® W360 Bearing technology | Plain bearing | iglidur® W360
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: W360SM-0608-06 – no minimum order quantity. Order example: W360FM-0608-06 – no minimum order quantity.
W360 iglidur® material S Sleeve bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1 W360 iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
6.0 +0.020 +0.068 8.0 6.0 W360SM-0608-06 6.0 +0.020 +0.068 8.0 12.0 6.0 1.00 W360FM-0608-06
8.0 10.0 10.0 W360SM-0810-10 8.0 10.0 15.0 10.0 1.00 W360FM-0810-10
+0.025 +0.083 +0.025 +0.083
10.0 12.0 10.0 W360SM-1012-10 10.0 12.0 18.0 10.0 1.00 W360FM-1012-10
12.0 14.0 12.0 W360SM-1214-12 12.0 14.0 20.0 12.0 1.00 W360FM-1214-12
+0.032 +0.102 +0.032 +0.102
16.0 18.0 15.0 W360SM-1618-15 16.0 18.0 24.0 17.0 1.00 W360FM-1618-17
20.0 +0.040 +0.124 23.0 20.0 W360SM-2023-20 20.0 +0.040 +0.124 23.0 30.0 21.5 1.50 W360FM-2023-21
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/W360 www.igus.eu/W360
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

220 3D CAD, finder and service life calculation ... www.igus.eu/W360 Lubrication-free made easy ... from stock ... no minimum order quantity 221
For fast rotating applications
Low coefficient of friction under low load
iglidur L250 ®

When to use it?

●● For rotating applications at high speed
●● When the highest service life is required
●● For low load applications
●● When a low noise level is required
●● For very low coefficient of friction

When not to use?

●● When high pressure occurs
iglidur® Q, iglidur® W300
●● When continuous operating temperatures are higher than +90°C
iglidur® V400
●● When low moisture absorption is required
iglidur® H1, iglidur® J
iglidur® L250 iglidur® L250
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® L250 Technical data
​General properties Testing method

Density g/cm³ 1.50 ​ –40°C up to

Ø +90°C
6.0 – 20.0mm Colour beige ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.7 DIN 53495
Max. moisture absorption % weight 3.9 ​
Coefficient of friction, dynamic, against steel µ 0.08 – 0.19 ​ 45MPa
pv value, max. (dry) MPa · m/s 0.40 ​
Also available
as: Mechanical properties
Flexural modulus MPa 1,950 DIN 53457
For fast rotating applications Flexural strength at +20°C MPa 67 DIN 53452

Bar stock,
Low coefficient of friction under low load Compressive strength MPa 47 ​
round bar Max. recommended surface pressure (+20°C) MPa 45 ​
Page 657 Shore D hardness 68 DIN 53505
Plain bearings for high speed rotation applications, especially for fans and motors.
●● Suitable for high rotating speeds Physical and thermal properties
●● Very low coefficients of friction Max. application temperature long-term °C +90 ​
FOOD
●● Very wear-resistant Max. application temperature short-term °C +180 ​
●● Lubrication-free Min. application temperature °C –40 ​
Bar stock, ●● Maintenance-free Thermal conductivity W/m · K 0.24 ASTM C 177
plate
Page 683 Coefficient of thermal expansion (at +23°C) K–1 · 10–5 10 DIN 53752
Typical application areas Electrical properties
●● Automotive industry Specific contact resistance Ωcm > 1010 DIN IEC 93
●● Electronics industry Surface resistance Ω > 1011 DIN 53482
●● Mechatronics Table 01: Material properties
tribo-tape liner ●● Optical industry
Page 691
●● Test engineering and quality assurance iglidur® L250 is a bearing material for high rotation speeds Resistance to weathering
and low coefficient of friction. The iglidur® L250 material iglidur® L250 plain bearings have limited resistance to
can feature these advantages particularly with low weathering. The material properties are affected. Discoloration
loads. Applications which feature these advantages are occurs. Practical tests under real application conditions
fans, small motors, fast-running sensors or the magnet are recommended.
technology.
Piston rings
Page 581 Mechanical properties
Moisture absorption With increasing temperatures, the compressive strength of
Descriptive technical specifications With regard to applications where the smallest bearing iglidur® L250 plain bearings decreases. Diagram 02 shows
Wear resistance at +23°C – + clearances are concerned, please take the moisture this inverse relationship. The maximum recommended
absorption into consideration. surface pressure is a mechanical material parameter. No
Wear resistance at +90°C – +
conclusions regarding the tribological properties can be
Two hole Wear resistance at +150°C – + Vacuum drawn from this.
flange
bearings In vacuum, any present moisture is released as vapour. Use Diagram 03 shows the elastic deformation of iglidur® L250
Page 603 Low coefficient of friction – +
in vacuum is only possible with dehumidified iglidur® L250 at radial loads. At the maximum recommended surface
Low moisture absorption – + bearings. pressure of 45MPa at room temperature the deformation
is less than 3%. A plastic deformation can be negligible
Wear resistance under water – +
Radiation resistance up to this value. It is however also dependent on the duty
Moulded High media resistance – + Plain bearings made from iglidur® L250 are resistant up to cycle of the load.
special parts
Page 624 a radiation intensity of 3 · 10⁴Gy. Higher radiation weakens Surface pressure, page 41
Resistant to edge pressures – +
the material and may result in a significant decrease in
Suitable for shock and impact loads – + mechanical properties.

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

224 3D CAD, finder and service life calculation ... www.igus.eu/L250 Lubrication-free made easy ... from stock ... no minimum order quantity 225
iglidur® L250 iglidur® L250
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® L250 Technical data
Permissible surface speeds 100.0 0.7
Chemicals Resistance
0.6
iglidur® L250 has been developed especially for high Alcohols + up to 0 10.0

Coefficient of friction [µ]

0.5
surface speeds with low loads. Besides the physical limit, Diluted acids 0 up to –
0.4
which is pre-set by the heating of the bearing, the coefficient Diluted alkalines + 1.0
0.3

Pressure [MPa]
of wear also acts limiting if rapidly high glide paths emerge Fuels +
0.1 0.2
at high peripheral speeds and the permitted wear limit is Greases, oils without additives +
0.1
thus reached earlier. The maximum speeds are shown Hydrocarbons +
0.01 0.0
in table 03. Strong acids – 0.001 0.01 0.1 1.0 10.0 0 10 20 30 40 50 60 70 80
Surface speed, page 44 Strong alkalines 0 Surface speed [m/s] Load [MPa]
All information given at room temperature [+20°C]
Temperature Diagram 01: Permissible pv values for iglidur® L250 plain Diagram 05: Coefficient of friction as a function of the load,
Table 02: Chemical resistance
The iglidur® L250 plain bearings can be used in short-term bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Chemical table, page 1636
temperatures up to +180°C. Note that a mechanical a steel shaft, at +20°C, mounted in a steel housing
securing of the bearing is recommended from temperatures
​ ​ Rotating Oscillating linear
of +55°C. Higher temperatures can also cause the plain 120 0.6
long-term m/s 1.0 0.7 2.0
bearing to lose its press-fit and move in the hole.
short-term m/s 1.5 1.1 3.0 100 0.5

Cf53, hard-chromed
Application temperatures, page 49

304 stainless steel

Free cutting steel
Table 03: Maximum surface speeds 80 0.4

High grade steel

HR carbon steel
Additional securing, page 49

H.a. aluminium
60 0.3
​ Dry Greases Oil Water

Wear [µm/km]
Friction and wear 40 0.2
Coefficient of friction µ 0.08 – 0.19 0.09 0.04 0.04

Load [MPa]

Cf53
In the best pairing (with 304 stainless steel shafts), coefficient 20 0.1
Table 04: Coefficient of friction against steel (Ra = 1μm,
of friction of 0.14µ is already reached with low loads. 0 0.0
50HRC)
Coefficient of friction under 0.1 was measured already 20 30 40 50 60 70 80 90
below 10MPa (diagrams 04 and 05). Temperature [°C]
​ Housing Plain bearing Shaft
Coefficient of friction and surfaces, page 47 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm]
Wear resistance, page 50 function of temperature (45MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000
>3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000
Shaft materials 200
> 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
As seen in diagram 06, many shafts are recommendable 180 rotating
> 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 10 oscillating
160
for low loads and low rotations. The low coefficient 140
> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000 +23°C
of friction is additionally retained over a wide range of +60°C 120
> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 100
recommendable shaft surfaces finish. For loads higher

Deformation [%]
> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 5 80

Wear [µm/km]
than 1MPa, particular attention should be paid to the 60
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000 40
shaft material used. 20
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
Shaft materials, page 52 0 0
Table 05: Important tolerances for plain bearings according
0 15 30 45 0 5 10 15 20 25 30 35 40 45
to ISO 3547-1 after press-fit
Installation tolerances Load [MPa] Load [MPa]
iglidur® L250 plain bearings are standard bearings for Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
​
shafts with h tolerance (recommended minimum h9). with shaft material Cf53 hardened and ground steel, as a
The bearings are designed for press-fit into a housing function of the load
machined to a H7 tolerance. After being assembled into a 0.5

nominal size housing, in standard cases the inner diameter

0.4
Coefficient of friction [µ]

automatically adjusts to the E10 tolerances. For particular

dimensions the tolerance differs depending on the wall 0.3
thickness (please see product range table).
Testing methods, page 57 0.2

0.1
0.05 0.10 0.15 0.20 0.25 0.30
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

226 3D CAD, finder and service life calculation ... www.igus.eu/L250 Lubrication-free made easy ... from stock ... no minimum order quantity 227
iglidur® L250 iglidur® L250
+90°C +90°C
45MPa 45MPa
Bearing technology | Plain bearing | iglidur® L250 Bearing technology | Plain bearing | iglidur® L250
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: L250SM-0608-06 – no minimum order quantity. Order example: L250FM-0608-06 – no minimum order quantity.
L250 iglidur® material S Sleeve bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1 L250 iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
6.0 +0.020 +0.068 8.0 6.0 L250SM-0608-06 6.0 +0.020 +0.068 8.0 12.0 6.0 1.00 L250FM-0608-06
8.0 10.0 10.0 L250SM-0810-10 8.0 10.0 15.0 10.0 1.00 L250FM-0810-10
+0.025 +0.083 +0.025 +0.083
10.0 12.0 10.0 L250SM-1012-10 10.0 12.0 18.0 10.0 1.00 L250FM-1012-10
12.0 14.0 12.0 L250SM-1214-12 12.0 14.0 20.0 12.0 1.00 L250FM-1214-12
+0.032 +0.102 +0.032 +0.102
16.0 18.0 15.0 L250SM-1618-15 16.0 18.0 24.0 17.0 1.00 L250FM-1618-17
20.0 +0.040 +0.124 23.0 20.0 L250SM-2023-20 20.0 +0.040 +0.124 23.0 30.0 21.5 1.50 L250FM-2023-21
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/L250 www.igus.eu/L250
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

228 3D CAD, finder and service life calculation ... www.igus.eu/L250 Lubrication-free made easy ... from stock ... no minimum order quantity 229
For high rotational speeds
High performance at lower cost
iglidur L350 ®

When to use it?

●● For rotating applications at high speed
●● When the highest service life is required
●● For high pv values with low loads
●● At operating temperatures up to +180°C (long-term, short-term up to max. +210°C)

When not to use?

●● When a universal bearing for high temperatures is required
iglidur® X
●● When medium to high pressures occur
iglidur® G, iglidur® Q
●● For oscillating applications
iglidur® W300, iglidur® J350
iglidur® L350 iglidur® L350
+180°C +180°C
59MPa 59MPa
Bearing technology | Plain bearing | iglidur® L350 Technical data
General properties​ Testing method

Density g/cm³ 1.54 ​ –100°C up to

Ø +180°C
3.0 – 10.0mm Colour dark grey ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.4 DIN 53495
Max. moisture absorption % weight 1.4 ​
Coefficient of friction, dynamic, against steel µ 0.07 – 0.18 ​ 59MPa
pv value, max. (dry) MPa · m/s 3.00 ​
Also available
as: Mechanical properties
Flexural modulus MPa 15,882 DIN 53457
For high rotational speeds Flexural strength at +20°C MPa 210 DIN 53452

Bar stock,
High performance at lower cost Compressive strength MPa 210 ​
round bar Max. recommended surface pressure (+20°C) MPa 59 ​
Page 657 Shore D hardness 80 DIN 53505
iglidur® L350 is extremely long-lasting. Developed for the best coefficient of wear and friction at speeds
of 1.5m/s and more, this material outperforms classic plain bearings in high-speed rotation operation. Physical and thermal properties
●● Up to 3.5m/s rotating Max. application temperature long-term °C +180 ​
FOOD
●● Temperature-resistant up to +210°C in continuous use Max. application temperature short-term °C +210 ​
●● Low moisture absorption Min. application temperature °C –100 ​
Bar stock, ●● Good price-performance ratio Thermal conductivity W/m · K 0.61 ASTM C 177
plate
Page 683 ●● Extremely wear-resistant Coefficient of thermal expansion (at +23°C) K–1 · 10–5 7 DIN 53752
●● Lubrication and maintenance-free Electrical properties
●● Standard range from stock Specific contact resistance Ωcm > 105 DIN IEC 93
Surface resistance Ω > 105 DIN 53482
Typical application areas Table 01: Material properties
tribo-tape liner ●● Electric motors
Page 691
●● Fans With iglidur® L350, another lubrication and maintenance-free Resistance to weathering
●● Household appliances material is now available, which is designed for continuous iglidur® L350 plain bearings have not yet been tested for
high speeds. Due to the low thermal expansion and low their resistance to weathering. Please consult igus ® if
moisture absorption, bearings can be manufactured with you‘re planning to use them outdoors.
minimal potential to expand. iglidur® L350 is especially
suitable for use in fans, blowers or electric motors – and Mechanical properties
Piston rings
Page 581 the costs are also lower. With increasing temperatures, the compressive strength of
iglidur® L350 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications Moisture absorption this inverse relationship. The maximum recommended
Wear resistance at +23°C – + The very low moisture absorption of 0.4% weight in surface pressure is a mechanical material parameter. No
standard climatic conditions and 1.4% weight at maximum conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
water absorption also enables continuous operation in high drawn from this.
Two hole Wear resistance at +150°C – + humidity or in liquid media. Diagram 03 shows the elastic deformation of iglidur® L350
flange
bearings at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
Vacuum pressure of 59MPa at room temperature the deformation
Low moisture absorption – + In vacuum, the moisture content is released as vapour. Due is less than 2.5%. A plastic deformation can be negligible
to its low moisture absorption, use in a vacuum is possible. up to this value. It is however also dependent on the duty
Wear resistance under water – +
cycle of the load.
Moulded High media resistance – + Radiation resistance Surface pressure, page 41
special parts
Page 624 Plain bearings made from iglidur® L350 are resistant up to
Resistant to edge pressures – +
a radiation intensity of 2 · 10²Gy. Higher radiation affects
Suitable for shock and impact loads – + the material and may result in a significant decrease in
mechanical properties.
Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

232 3D CAD, finder and service life calculation ... www.igus.eu/L350 Lubrication-free made easy ... from stock ... no minimum order quantity 233
iglidur® L350 iglidur® L350
+180°C +180°C
59MPa 59MPa
Bearing technology | Plain bearing | iglidur® L350 Technical data
Permissible surface speeds 100.0 5
Chemicals Resistance iglidur® L350
iglidur® L350 has been developed especially for high Alcohols + 4 iglidur® L500
10.0 Sintered
surface speeds with low loads. Due to the high temperature Diluted acids + bearing
3
resistance of iglidur® L350, the limit of the bearing has been

Wear rate [µm/km]

Diluted alkalines + 1.0
2

Pressure [MPa]
increased significantly. In addition, the extremely low wear Fuels +
allows the high acceleration speeds to be reached and 0.1
Greases, oils without additives + 1
maintained.The maximum speeds are shown in table 03. Hydrocarbons + up to 0
0.01 0
Surface speed, page 44 Strong acids + 0.001 0.01 0.1 1.0 10.0 0 1 2 3 4
Strong alkalines + Surface speed [m/s] Surface speed [m/s]
Temperature
All information given at room temperature [+20°C]
The iglidur® L350 plain bearings can be used in temperatures Diagram 01: Permissible pv values for iglidur® L350 plain Diagram 05: Rotating wear against Cf53, p = 0.25MPa,
Table 02: Chemical resistance
up to +210°C for the short-term. Note that a mechanical bearings with a wall thickness of 1mm, dry operation against T = +23°C
Chemical table, page 1636
securing of the bearing is recommended from temperatures a steel shaft, at +20°C, mounted in a steel housing
of +140°C. Higher temperatures can sometimes cause the
​ ​ Rotating Oscillating linear
plain bearings to lose their press-fit and move in the housing. 80 1.8
long-term m/s 3.0 1.5 4.0
Application temperatures, page 49 70
short-term m/s 4.0 3.0 6.0 1.5

Cf53, hard-chromed
Additional securing, page 49 60

304 stainless steel

Free cutting steel
Table 03: Maximum surface speeds 1.2

High grade steel

HR carbon steel
50

H.a. aluminium
40 0.9
Friction and wear
​ Dry Greases Oil Water 30

Wear [µm/km]
The very low coefficient of friction remains, even at high 0.6
Coefficient of friction µ 0.07 – 0.18 0.06 0.04 0.03 20

Load [MPa]

Cf53
speeds. Diagram 04 shows this relationship on a steel 0.3
10
Table 04: Coefficient of friction against steel (Ra = 1μm,
shaft at 0.75MPa surface pressure. 0 0.0
50HRC)
Coefficient of friction and surfaces, page 47 20 40 60 80 100 120 140 160 180
Wear resistance, page 50 Temperature [°C]
​ Housing Plain bearing Shaft
Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Ø d1 [mm] H7 [mm] F10 [mm] h9 [mm]
Shaft materials function of temperature (59MPa at +20°C) p = 1MPa, v = 0.3m/s
0–3 +0.000 +0.010 +0.006 +0.046 –0.025 +0.000
Diagram 05 compares the wear of a sintered bearing with
>3–6 +0.000 +0.012 +0.010 +0.058 –0.030 +0.000
that of bearings made of the materials iglidur® L500 and 4.0 0.20
> 6 – 10 +0.000 +0.015 +0.013 +0.071 –0.036 +0.000
L350. At a surface speed of 1.5m/s or more, the wear of iglidur® L350
> 10 – 18 +0.000 +0.018 +0.016 +0.086 –0.043 +0.000 iglidur® L500
the sintered bearing increases exponentially whereas the 3.0 0.15

Coefficient of friction [µ]

> 18 – 30 +0.000 +0.021 +0.020 +0.104 –0.052 +0.000 +23°C
wear of the iglidur® plain bearings almost remains the same +60°C
> 30 – 50 +0.000 +0.025 +0.025 +0.125 –0.062 +0.000 2.0 0.10
up to a speed of more than 3m/s.

Deformation [%]
> 50 – 80 +0.000 +0.030 +0.030 +0.150 –0.074 +0.000
Shaft materials, page 52 1.0 0.05
> 80 – 120 +0.000 +0.035 +0.036 +0.176 –0.087 +0.000
> 120 – 180 +0.000 +0.040 +0.043 +0.203 +0.000 +0.100
Installation tolerances 0.0 0.00
Table 05: Important tolerances for plain bearings according
iglidur® L350 plain bearings are standard bearings for 0 10 20 30 40 50 60 1.0 1.5 2.0 2.5 3.0 3.5 4.0
to ISO 3547-1 after press-fit
shafts with h tolerance (recommended minimum h9). Load [MPa] Surface speed [m/s]
The bearings are designed for press-fit into a housing Diagram 03: Deformation under pressure and temperature Diagram 07: Rotating coefficient of friction - "High speed"
​
machined to a H7 tolerance. After being assembled into a against Cf53, p = 1MPa (except for iglidur® L250), T = +23°C
nominal size housing, in standard cases the inner diameter
automatically adjusts to the F10 tolerances. For particular 0.20

dimensions the tolerance differs depending on the wall

Coefficient of friction [µ]
0.15
thickness (please see product range table).
Testing methods, page 57 0.10

0.05

0.00
0.0 0.5 1.0 1.5 2.0 2.5 3.0
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

234 3D CAD, finder and service life calculation ... www.igus.eu/L350 Lubrication-free made easy ... from stock ... no minimum order quantity 235
iglidur® L350 iglidur® L350
+180°C +180°C
59MPa 59MPa
Bearing technology | Plain bearing | iglidur® L350 Bearing technology | Plain bearing | iglidur® L350
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 special dimensions f1 [mm] 0.3 0.5 special dimensions

Order example: L350SM-0304-03 – no minimum order quantity. Order example: L350FM-0304-05 – no minimum order quantity.
L350 iglidur® material S Sleeve bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 03 Total length b1 L350 iglidur® material F Flange bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 05 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
3.0 +0.006 +0.046 4.5 3.0 L350SM-0304-03 3.0 +0.006 +0.046 4.5 7.5 5.0 0.75 L350FM-0304-05
4.0 5.5 4.0 L350SM-0405-04 4.0 5.5 9.5 6.0 0.75 L350FM-0405-06
5.0 +0.010 +0.058 7.0 5.0 L350SM-0507-05 5.0 +0.010 +0.058 7.0 11.0 7.0 1.00 L350FM-0507-07
6.0 8.0 6.0 L350SM-0608-06 6.0 8.0 12.0 8.0 1.00 L350FM-0608-08
8.0 10.0 10.0 L350SM-0810-10 8.0 10.0 15.0 9.0 1.00 L350FM-0810-09
+0.013 +0.071 +0.013 +0.071
10.0 12.0 10.0 L350SM-1012-10 10.0 12.0 18.0 9.0 1.00 L350FM-1012-09
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/L350 www.igus.eu/L350
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

236 3D CAD, finder and service life calculation ... www.igus.eu/L350 Lubrication-free made easy ... from stock ... no minimum order quantity 237
For extreme rotational speeds
Temperature-resistant and
media-resistant
iglidur L500 ®

When to use it?

●● For rotating applications at high speed
●● When the highest service life is required
●● For high pv values with low loads
●● At continuous operating temperatures up to +250°C (short-term up to max. +350°C)

When not to use?

●● When a universal plain bearing for high temperatures is required
iglidur® X
●● When medium to high pressures occur
iglidur® G, iglidur® Q
●● For oscillating applications
iglidur® W300, iglidur® J350
iglidur® L500 iglidur® L500
+250°C +250°C
70MPa 70MPa
Bearing technology | Plain bearing | iglidur® L500 Technical data
General properties​ Testing method

Density g/cm³ 1.53 ​ –100°C up to

Ø +250°C
3.0 – 10.0mm Colour black ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.1 DIN 53495
Max. moisture absorption % weight 0.3 ​
Coefficient of friction, dynamic, against steel µ 0.08 – 0.15 ​ 70MPa
pv value, max. (dry) MPa · m/s 4.00 ​
Also available
as: Mechanical properties
Flexural modulus MPa 12,015 DIN 53457
For extreme rotational speeds Flexural strength at +20°C MPa 201 DIN 53452

Bar stock,
Temperature-resistant and media-resistant Compressive strength MPa 70 ​
round bar Max. recommended surface pressure (+20°C) MPa 70 ​
Page 657 Shore D hardness 81 DIN 53505
Specially developed for fast continuous operation under low loads, iglidur® L500, inter alia, is intended
for fan and electric motor applications. Physical and thermal properties
●● Temperature-resistant up to +250°C Max. application temperature long-term °C +250 ​
FOOD
●● For rotational movements with surface speeds up to 5m/s Max. application temperature short-term °C +315 ​
●● Very wear-resistant Min. application temperature °C –100 ​
Bar stock, ●● Low moisture absorption Thermal conductivity W/m · K 0.45 ASTM C 177
plate
Page 683 ●● Low thermal expansion Coefficient of thermal expansion (at +23°C) K–1 · 10–5 6 DIN 53752
●● Lubrication-free Electrical properties
●● Maintenance-free Specific contact resistance Ωcm > 1010 DIN IEC 93
Surface resistance Ω > 1012 DIN 53482
Typical application areas Table 01: Material properties
tribo-tape liner ●● Cooling fans
Page 691
●● Electric motors iglidur® L500 is a plain bearing material for high speeds Resistance to weathering
●● Fans, etc. and fast sliding movements with low loads. Due to the iglidur® L500 plain bearings are continuously resistant
low thermal expansion and low moisture absorption, to weathering. The material properties are only slightly
bearings can be manufactured with minimal potential to affected. Possible discolorations are only superficial.
expand. Applications which feature these advantages are
fans, small motors, fast-running sensors or the magnet Mechanical properties
Piston rings
Page 581 technology. With increasing temperatures, the compressive strength of
iglidur® L500 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications Moisture absorption this inverse relationship. The maximum recommended
Wear resistance at +23°C – + The very low moisture absorption of 0.1% weight in surface pressure is a mechanical material parameter. No
standard climatic conditions and 0.3% weight at maximum conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
water absorption also enables continuous operation in high drawn from this.
Two hole Wear resistance at +150°C – + humidity or in liquid media. Diagram 03 shows the elastic deformation of iglidur® L500
flange
bearings at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
Vacuum pressure of 70MPa at room temperature the deformation
Low moisture absorption – + In vacuum, any present moisture is released as vapour. is less than 2.5%. A plastic deformation can be negligible
The use in vacuum is generally possible. up to this value. It is however also dependent on the duty
Wear resistance under water – +
cycle of the load.
Moulded High media resistance – + Radiation resistance Surface pressure, page 41
special parts
Page 624 Plain bearings made from iglidur® L500 are resistant up to
Resistant to edge pressures – +
a radiation intensity of 3 · 10²Gy. Higher radiation weakens
Suitable for shock and impact loads – + the material and may result in a significant decrease in
mechanical properties.
Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

240 3D CAD, finder and service life calculation ... www.igus.eu/L500 Lubrication-free made easy ... from stock ... no minimum order quantity 241
iglidur® L500 iglidur® L500
+250°C +250°C
70MPa 70MPa
Bearing technology | Plain bearing | iglidur® L500 Technical data
Permissible surface speeds 100.0 0.20
Chemicals Resistance
iglidur® L500 has been developed especially for high Alcohols + 10.0 0.15

Coefficient of friction [µ]

surface speeds with low loads. Due to the high temperature Diluted acids +
resistance of iglidur® L500, the limit of the bearing has been Diluted alkalines + 1.0 0.10

Pressure [MPa]
increased significantly. In addition, the extremely low wear Fuels +
allows the high acceleration speeds to be reached and 0.1 0.05
Greases, oils without additives +
maintained. The maximum speeds are shown in table 03. Hydrocarbons +
0.01 0.00
Surface speed, page 44 Strong acids + 0.001 0.01 0.1 1.0 10.0 0 10 20 30 40 50 60 70
Strong alkalines + Surface speed [m/s] Load [MPa]
Temperature
All information given at room temperature [+20°C]
The iglidur® L500 plain bearings can be used in short-term Diagram 01: Permissible pv values for iglidur® L500 plain Diagram 05: Coefficient of friction as a function of the load,
Table 02: Chemical resistance
temperatures up to +315°C. For temperatures over +135°C bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Chemical table, page 1636
an additional securing is required. Higher temperatures can a steel shaft, at +20°C, mounted in a steel housing
also cause the plain bearing to lose its press-fit and move
​ ​ Rotating Oscillating linear
in the hole. 80 3.0
long-term m/s 4.0 1.5 5.0
Application temperatures, page 49 70
short-term m/s 5.0 3.0 8.0 2.5

Cf53, hard-chromed
Additional securing, page 49 60

304 stainless steel

Free cutting steel
Table 03: Maximum surface speeds 2.0

High grade steel

HR carbon steel
50

H.a. aluminium
40 1.5
Friction and wear
​ Dry Greases Oil Water 30

Wear [µm/km]
The excellent coefficient of friction level of iglidur® L500 in 1.0
Coefficient of friction µ 0.08 – 0.15 0.09 0.04 0.04 20

Load [MPa]

Cf53
dry operation decreases considerably with speed. Diagram 0.5
10
Table 04: Coefficient of friction against steel (Ra = 1μm,
04 shows this with respect to a steel shaft. As the load 0 0.0
50HRC)
increases, the coefficient of friction decreases, especially 20 50 80 120 150 200 250
in the range up to 20MPa (diagram 05). Temperature [°C]
​ Housing Plain bearing Shaft
Coefficient of friction and surfaces, page 47 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Ø d1 [mm] H7 [mm] F10 [mm] h9 [mm]
Wear resistance, page 50 function of temperature (70MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
0–3 +0.000 +0.010 +0.006 +0.046 –0.025 +0.000
>3–6 +0.000 +0.012 +0.010 +0.058 –0.030 +0.000
Shaft materials 4.0 4
> 6 – 10 +0.000 +0.015 +0.013 +0.071 –0.036 +0.000
Diagram 07 shows the result of a comparison test between iglidur® L500
> 10 – 18 +0.000 +0.018 +0.016 +0.086 –0.043 +0.000 Sintered bearing
iglidur® L500 and a sintered bearing. The wear of the 3.0 3
> 18 – 30 +0.000 +0.021 +0.020 +0.104 –0.052 +0.000 +23°C
sintered bearing increases exponentially above 1.5m/s, +60°C
> 30 – 50 +0.000 +0.025 +0.025 +0.125 –0.062 +0.000 2.0 2
while the iglidur® L500 plain bearing retains a near constant

Deformation [%]
> 50 – 80 +0.000 +0.030 +0.030 +0.150 –0.074 +0.000

Wear [µm/km]
wear rate up to and above 4m/s. 1.0 1
> 80 – 120 +0.000 +0.035 +0.036 +0.176 –0.087 +0.000
Shaft materials, page 52
> 120 – 180 +0.000 +0.040 +0.043 +0.203 +0.000 +0.100
0.0 0
Table 05: Important tolerances for plain bearings according
Installation tolerances 0 10 20 30 40 50 60 70 0.0 0.5 1.0 1.5 2.0 2.5 3.0 3.5 4.0
to ISO 3547-1 after press-fit
iglidur® L500 plain bearings are standard bearings for Load [MPa] Surface speed [m/s]
shafts with h tolerance (recommended minimum h9). Diagram 03: Deformation under pressure and temperature Diagram 07: Rotating wear against Cf53, p = 0.25MPa,
​
The bearings are designed for press-fit into a housing T = +23°C
machined to a H7 tolerance. After being assembled into a
nominal size housing, in standard cases the inner diameter 0.20

automatically adjusts to the F10 tolerances. For particular

Coefficient of friction [µ]
0.15
dimensions the tolerance differs depending on the wall
thickness (please see product range table). 0.10
Testing methods, page 57
0.05

0.00
0.0 0.5 1.0 1.5 2.0 2.5 3.0
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

242 3D CAD, finder and service life calculation ... www.igus.eu/L500 Lubrication-free made easy ... from stock ... no minimum order quantity 243
iglidur® L500 iglidur® L500
+250°C +250°C
70MPa 70MPa
Bearing technology | Plain bearing | iglidur® L500 Bearing technology | Plain bearing | iglidur® L500
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 special dimensions f1 [mm] 0.3 0.5 special dimensions

Order example: L500SM-0304-03 – no minimum order quantity. Order example: L500FM-0304-05 – no minimum order quantity.
L500 iglidur® material S Sleeve bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 03 Total length b1 L500 iglidur® material F Flange bearing M Metric 03 Inner Ø d1 04 Outer Ø d2 05 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
3.0 +0.006 +0.046 4.5 3.0 L500SM-0304-03 3.0 +0.006 +0.046 4.5 7.5 5.0 0.75 L500FM-0304-05
4.0 5.5 4.0 L500SM-0405-04 4.0 5.0 9.5 4.0 0.75 L500FM-0405-04
5.0 +0.010 +0.058 7.0 5.0 L500SM-0507-05 5.0 +0.010 +0.058 7.0 11.0 7.0 1.00 L500FM-0507-07
6.0 8.0 6.0 L500SM-0608-06 6.0 8.0 12.0 8.0 1.00 L500FM-0608-08
8.0 10.0 10.0 L500SM-0810-10 8.0 10.0 15.0 9.5 1.00 L500FM-0810-09
+0.013 +0.071 +0.013 +0.071
10.0 12.0 10.0 L500SM-1012-10 10.0 12.0 18.0 9.5 1.00 L500FM-1012-09
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/L500 www.igus.eu/L500
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

244 3D CAD, finder and service life calculation ... www.igus.eu/L500 Lubrication-free made easy ... from stock ... no minimum order quantity 245
Low-cost
Abrasion-resistant
iglidur R ®

When to use it?

●● When high wear resistance at low loads is required
●● When a cost-effective plain bearing is required
●● When very low coefficients of friction in dry operation are required
●● When high edge loads occur
●● When you are looking for low water absorption
●● When PTFE and silicone are not allowed in your application

When not to use?

●● When high pressure occurs
iglidur® G
●● When continuous operating temperatures are higher than +90°C
iglidur® G, iglidur® P
●● When the best wear resistance is required
iglidur® J
iglidur® R iglidur® R
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® R Technical data
​General properties Testing method

Density g/cm³ 1.39 ​ –50°C up to

Ø +90°C
2.0 – 35.0mm Colour dark red ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.2 DIN 53495
Max. moisture absorption % weight 1.1 ​
Coefficient of friction, dynamic, against steel µ 0.09 – 0.25 ​ 23MPa
pv value, max. (dry) MPa · m/s 0.27 ​
Also available
as: Mechanical properties
Flexural modulus MPa 1,950 DIN 53457
Low-cost Flexural strength at +20°C MPa 70 DIN 53452

Bar stock,
Abrasion-resistant Compressive strength MPa 68 ​
round bar Max. recommended surface pressure (+20°C) MPa 23 ​
Page 676 Shore D hardness 77 DIN 53505
Low-cost material with low coefficient of friction and good wear resistance at low to medium loads.
●● High wear resistance Physical and thermal properties
●● Low coefficient of friction Max. application temperature long-term °C +90 ​
FOOD
●● Cost-effective Max. application temperature short-term °C +110 ​
●● Low moisture absorption Min. application temperature °C –50 ​
Bar stock, ●● Lubrication-free Thermal conductivity W/m · K 0.25 ASTM C 177
plate
Page 683 ●● Maintenance-free Coefficient of thermal expansion (at +23°C) K–1 · 10–5 11 DIN 53752
Electrical properties
Typical application areas Specific contact resistance Ωcm > 1012 DIN IEC 93
●● Sports and leisure Surface resistance Ω > 1012 DIN 53482
●● Model making Table 01: Material properties
tribo-tape liner ●● Furniture industry
Page 691
●● Mechatronics The development of the iglidur® R as a bearing material Resistance to weathering
focused on high performance and very low cost. Especially iglidur® R plain bearings are resistant to weathering. The
in the dry operation low coefficient of friction and wear material properties are slightly affected. Discoloration
were to be achieved. Plain bearings made from iglidur® R occurs.
are supported by a combination of solid lubricants. The
PTFE and silicon-free material achieves extremely low Mechanical properties
Piston rings
Page 581 coefficient of friction in dry operation and runs largely free With increasing temperatures, the compressive strength
of stick-slip effects. of iglidur® R plain bearings decreases. Diagram 02 shows
Descriptive technical specifications this inverse relationship. The maximum recommended
Wear resistance at +23°C – + Moisture absorption surface pressure is a mechanical material parameter. No
Under standard climatic conditions, the moisture absorp- conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
tion of iglidur® R plain bearings is approximately 0.2% drawn from this.
Two hole Wear resistance at +150°C – + weight. The saturation limit in water is 1.1% weight. This Diagram 03 shows the elastic deformation of iglidur® R
flange
bearings must be taken into account for these types of applications. at radial loads. At the maximum recommended surface
Page 603 Low coefficient of friction – +
pressure of 23MPa the deformation is about 4% at room
Low moisture absorption – + Vacuum temperature. A plastic deformation can be negligible up
In vacuum, any present moisture is released as vapour. to this value. However, it is also dependent on the service
Wear resistance under water – +
The use in vacuum is only possible to a limited extent. time.
Moulded High media resistance – + Surface pressure, page 41
special parts
Page 624 Radiation resistance
Resistant to edge pressures – +
Plain bearings made from iglidur® R are resistant up to a
Suitable for shock and impact loads – + radiation intensity of 3 · 10²Gy.

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 846 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

248 3D CAD, finder and service life calculation ... www.igus.eu/R Lubrication-free made easy ... from stock ... no minimum order quantity 249
iglidur® R iglidur® R
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® R Technical data
Permissible surface speeds Installation tolerances 100.0 0.35
0.30
iglidur® R plain bearings are suitable for high surface iglidur ® R plain bearings are standard bearings for
10.0

Coefficient of friction [µ]

0.25
speeds. Speeds of up to 5.0m/s are permitted in linear shafts with h tolerance (recommended minimum h9).
0.20
motions. The maximum values shown in table 03 can only The bearings are designed for press-fit into a housing 1.0
0.15

Pressure [MPa]
be achieved at low pressures. The specified values show machined to a H7 tolerance. After being assembled into a
0.1 0.10
the speed at which due to friction an increase in temperature nominal size housing, in standard cases the inner diameter
0.05
up to the long-term permitted value can occur. automatically adjusts to the E10 tolerances. For particular
0.01 0.00
Surface speed, page 44 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 5 10 15 20
thickness (please see product range table).
Surface speed [m/s] Load [MPa]
Temperature Testing methods, page 57
With increasing temperatures, the compressive strength Diagram 01: Permissible pv values for iglidur® R plain Diagram 05: Coefficient of friction as a function of the load,
of iglidur® R plain bearings decreases. Diagram 02 shows bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
this inverse relationship. The temperatures prevailing in Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
the bearing system also have an influence on the wear. Alcohols +
For temperatures over +50°C an additional securing is Diluted acids 0 up to – 25 4.0
required. Diluted alkalines + 3.5

Cf53, hard-chromed
20
Application temperatures, page 49 Fuels + 3.0

304 stainless steel

Free cutting steel

High grade steel

HR carbon steel
Additional securing, page 49 Greases, oils without additives + 15 2.5

H.a. aluminium
2.0
Hydrocarbons +
10 1.5

Wear [µm/km]
Friction and wear Strong acids –
1.0

Load [MPa]
5

Cf53
Similar to wear resistance, the coefficient of friction µ also Strong alkalines + up to 0 0.5
changes with the surface speed and load (diagrams 04 All information given at room temperature [+20°C] 0 0.0
and 05). iglidur® R is especially suitable for applications in Table 02: Chemical resistance 20 30 40 50 60 70 80 90
which high pv values are induced mainly through the high Chemical table, page 1636 Temperature [°C]
surface speed rather than surface pressure. Less distinct is Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
the dependency of the coefficient of friction of the iglidur® R ​ ​ Rotating Oscillating linear function of temperature (23MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
plain bearings on the shaft surface. long-term m/s 0.8 0.6 3.5
Coefficient of friction and surfaces, page 47 short-term m/s 1.2 1.0 5.0 10 10
Wear resistance, page 50 Table 03: Maximum surface speeds 9 rotating
8 8 oscillating
+23°C 7
Shaft materials ​ Dry Greases Oil Water 6 +60°C 6
5
Diagrams 06 and 07 show the test results of iglidur® R Coefficient of friction µ 0.09 – 0.25 0.09 0.04 0.04

Deformation [%]
4 4

Wear [µm/km]
plain bearings running against various shaft materials. At Table 04: Coefficient of friction against steel (Ra = 1μm, 3
2 2
0.3m/s and 1MPa, the high grade steel and Cf53 shafts 50HRC)
1
are the best materials. With increasing loads the iglidur® R 0 0
bearings feature the best wear behaviour with Cf53 and ​ Housing Plain bearing Shaft 0 4 8 12 16 20 24 Cf53 hard 304SS HR carbon
chromed steel
304 stainless steel shafts. In pivoting applications, the Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa]
hard-chromed shaft proves to be the ideal mating surface. 0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for rotating and oscillating applications
If the shaft material you plan on using is not shown in these >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with different shaft materials, p = 2MPa
test results, please contact us. > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
Shaft materials, page 52 > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 0.5

> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000

0.4
Coefficient of friction [µ]

> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000

> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 0.3
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000 0.2
Table 05: Important tolerances for plain bearings according
0.1
to ISO 3547-1 after press-fit
0.05 0.10 0.15 0.20 0.25 0.30 0.35
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

250 3D CAD, finder and service life calculation ... www.igus.eu/R Lubrication-free made easy ... from stock ... no minimum order quantity 251
iglidur® R iglidur® R
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® R Bearing technology | Plain bearing | iglidur® R
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Ø > 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 1.2 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: RSM-0203-07 – no minimum order quantity. Order example: RFM-0405-03 – no minimum order quantity.
R iglidur® material S Sleeve bearing M Metric 02 Inner Ø d1 03 Outer Ø d2 07 Total length b1 R iglidur® material F Flange bearing M Metric 04 Inner Ø d1 05 Outer Ø d2 03 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
2.0 +0.014 +0.054 3.6 7.0 RSM-0203-07 4.0 5.5 9.0 3.0 0.75 RFM-0405-03
4.0 5.5 4.0 RSM-0405-04 4.0 5.5 9.5 4.0 0.75 RFM-0405-04
+0.020 +0.068
5.0 +0.020 +0.068 7.0 5.0 RSM-0507-05 5.0 7.0 11.0 5.0 1.00 RFM-0507-05
6.0 8.0 6.0 RSM-0608-06 6.0 8.0 12.0 6.0 1.00 RFM-0608-06
8.0 10.0 10.0 RSM-0810-10 8.0 10.0 15.0 5.0 1.00 RFM-0810-05
10.0 12.0 5.0 RSM-1012-05 8.0 10.0 15.0 10.0 1.00 RFM-0810-10
+0.025 +0.083 +0.025 +0.083
10.0 12.0 10.0 RSM-1012-10 10.0 12.0 18.0 10.0 1.00 RFM-1012-10
10.0 12.0 15.0 RSM-1012-15 10.0 12.0 18.0 18.0 1.00 RFM-1012-18
12.0 14.0 12.0 RSM-1214-12 12.0 14.0 20.0 10.0 1.00 RFM-1214-10
14.0 16.0 15.0 RSM-1416-15 12.0 14.0 20.0 12.0 1.00 RFM-1214-12
15.0 +0.032 +0.102 17.0 15.0 RSM-1517-15 14.0 16.0 22.0 17.0 1.00 RFM-1416-17
+0.032 +0.102
16.0 18.0 15.0 RSM-1618-15 15.0 17.0 23.0 17.0 1.00 RFM-1517-17
18.0 20.0 25.0 RSM-1820-25 16.0 18.0 24.0 17.0 1.00 RFM-1618-17
20.0 23.0 15.0 RSM-2023-15 18.0 20.0 26.0 17.0 1.00 RFM-1820-17
20.0 23.0 20.0 RSM-2023-20 20.0 23.0 30.0 21.5 1.50 RFM-2023-21
25.0 28.0 25.0 RSM-2528-25 22.0 +0.040 +0.124 25.0 29.0 4.5 1.50 RFM-222529-045
+0.040 +0.124
28.0 32.0 12.0 RSM-2832-12 25.0 28.0 35.0 21.5 1.50 RFM-2528-21
30.0 34.0 25.0 RSM-3034-25 3)
After press-fit. Testing methods, page 57
30.0 34.0 30.0 RSM-3034-30
35.0 +0.050 +0.150 39.0 30.0 RSM-3539-30 Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order
3)
After press-fit. Testing methods, page 57
www.igus.eu/24 quantities, current prices can be found online.

Online ordering
Discount scaling
Including delivery times, prices, online tools
1–9 50 – 99 500 – 999
www.igus.eu/R
10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999

No minimum order value.

No low-quantity surcharges.
Free shipping within Germany for orders
above €150.

252 3D CAD, finder and service life calculation ... www.igus.eu/R Lubrication-free made easy ... from stock ... no minimum order quantity 253
Low-cost with silicone
Abrasion-resistant
iglidur D ®

When to use it?

●● When low coefficient of friction is required
●● For high speeds
●● For low load
●● When a cost-effective plain bearing is required

When not to use?

●● When high pressure occurs
iglidur® G
●● When the part should be free of silicone
iglidur® J, iglidur® R
●● When continuous operating temperatures are higher than +90°C
iglidur® G, iglidur® P
iglidur® D iglidur® D
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® D Technical data
​General properties Testing method

Density g/cm³ 1.40 ​ –50°C up to

Ø +90°C
​– ​ Colour green ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.3 DIN 53495
Max. moisture absorption % weight 1.1 ​
Coefficient of friction, dynamic, against steel µ 0.08 – 0.26 ​ 23MPa
pv value, max. (dry) MPa · m/s 0.27 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,000 DIN 53457
Low-cost with silicone Flexural strength at +20°C MPa 72 DIN 53452

Bar stock,
Abrasion-resistant Compressive strength MPa 70 ​
round bar Max. recommended surface pressure (+20°C) MPa 23 ​
Page 657 Shore D hardness 78 DIN 53505
Low-cost-material with low coefficient of friction and good wear resistance at low loads.
●● Low coefficient of friction Physical and thermal properties
●● For low loads Max. application temperature long-term °C +90 ​
FOOD
●● Cost-effective Max. application temperature short-term °C +110 ​
●● Vibration-dampening Min. application temperature °C –50 ​
Bar stock, ●● Very low moisture absorption Thermal conductivity W/m · K 0.25 ASTM C 177
plate
Page 683 ●● Lubrication-free Coefficient of thermal expansion (at +23°C) K–1 · 10–5 11 DIN 53752
●● Suitable for high surface speeds Electrical properties
Specific contact resistance Ωcm > 1014 DIN IEC 93
Typical application areas Surface resistance Ω > 1014 DIN 53482
●● Sports and leisure Table 01: Material properties
tribo-tape liner ●● Model making
Page 691
●● Furniture industry During the development process of iglidur® D as a bearing Resistance to weathering
●● Mechatronics material, high performance and low price were the top iglidur® D plain bearings are continuously resistant to
requirements. In particular, low coefficient of friction was weathering. The material properties are only slightly
required at high speeds in dry operation. This material affected. Possible discolorations are only superficial.
containing silicone achieves low coefficient of friction in dry
operation and runs with virtually no stick-slip. Mechanical properties
Piston rings
Page 581 With increasing temperatures, the compressive strength
Moisture absorption of iglidur® D plain bearings decreases. Diagram 02 shows
Descriptive technical specifications Under standard climatic conditions, the moisture absorp- this inverse relationship. The maximum recommended
Wear resistance at +23°C – + tion of iglidur® D plain bearings is approximately 0.3% surface pressure is a mechanical material parameter. No
weight. The saturation limit in water is 1.1% weight. This conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
low moisture absorption allows its use in wet environments. drawn from this.
Two hole Wear resistance at +150°C – + iglidur® D plain bearings were specially developed for low
flange
bearings Vacuum radial loads. Diagram 03 shows the elastic deformation of
Page 603 Low coefficient of friction – +
In vacuum, any present moisture is released as vapour. iglidur® D at radial loads. At the maximum recommended
Low moisture absorption – + The use in vacuum is only possible to a limited extent. surface pressure of 23MPa the deformation is less than
3%. A plastic deformation can be negligible up to this
Wear resistance under water – +
Radiation resistance value. However, it is also dependent on the service time.
Moulded High media resistance – + Plain bearings made from iglidur® D are resistant up to a Surface pressure, page 41
special parts
Page 624 radiation intensity of 3 · 10²Gy.
Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

256 3D CAD, finder and service life calculation ... www.igus.eu/D Lubrication-free made easy ... from stock ... no minimum order quantity 257
iglidur® D iglidur® D
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® D Technical data
Permissible surface speeds 100.0 0.35
Chemicals Resistance
0.30
iglidur® D plain bearings are suitable for high surface Alcohols + 10.0

Coefficient of friction [µ]

0.25
speeds. Speeds of up to 10.0m/s are permitted in linear Diluted acids 0 up to –
0.20
motions. The maximum values shown in table 03 can only Diluted alkalines + 1.0
0.15

Pressure [MPa]
be achieved at low pressures. The specified values show Fuels +
0.1 0.10
the speed at which due to friction an increase in temperature Greases, oils without additives +
0.05
up to the long-term permitted value can occur. Hydrocarbons +
0.01 0.00
Surface speed, page 44 Strong acids – 0.001 0.01 0.1 1.0 10.0 0 5 10 15 20
Strong alkalines + up to 0 Surface speed [m/s] Load [MPa]
Temperature
All information given at room temperature [+20°C]
With increasing temperatures, the compressive strength Diagram 01: Permissible pv values for iglidur® D plain Diagram 05: Coefficient of friction as a function of the load,
Table 02: Chemical resistance
of iglidur® D plain bearings decreases. Diagram 02 shows bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
Chemical table, page 1636
this inverse relationship. The temperatures prevailing in a steel shaft, at +20°C, mounted in a steel housing
the bearing system also have an influence on the wear.
​ ​ Rotating Oscillating linear
For temperatures over +50°C an additional securing is 30 8
long-term m/s 1.5 1.1 8.0
required. 7
short-term m/s 3.0 2.1 10.0

Cf53, hard-chromed
Application temperatures, page 49 6

304 stainless steel

Free cutting steel
Table 03: Maximum surface speeds 20

High grade steel

HR carbon steel
Additional securing, page 49 5

H.a. aluminium
4
​ Dry Greases Oil Water 3

Wear [µm/km]
Friction and wear 10
Coefficient of friction µ 0.08 – 0.26 0.09 0.04 0.04 2

Load [MPa]

Cf53
Similar to wear resistance, the coefficient of friction µ also 1
Table 04: Coefficient of friction against steel (Ra = 1μm,
changes with the surface speed and load (diagrams 04 and 0 0
50HRC)
05). In the Ra range between 0.4 – 0.6µm, the coefficient 20 30 40 50 60 70 80 90
of friction attains its optimum value. Temperature [°C]
​ Housing Plain bearing Shaft
Coefficient of friction and surfaces, page 47 Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm]
Wear resistance, page 50 function of temperature (23MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000
>3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000
Shaft materials 10 10
> 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000
Diagrams 06 and 07 show the test results of iglidur® D 9 rotating
> 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 8 8 oscillating
plain bearings running against various shaft materials. If +23°C 7
> 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
the shaft material you plan on using is not shown in these 6 +60°C 6
> 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 5
test results, please contact us.

Deformation [%]
> 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 4 4

Wear [µm/km]
Shaft materials, page 52 3
> 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000 2 2
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000 1
Installation tolerances 0 0
Table 05: Important tolerances for plain bearings according
iglidur ® D plain bearings are standard bearings for 0 4 8 12 16 20 24 Cf53 hard 304SS HR carbon
to ISO 3547-1 after press-fit chromed steel
shafts with h tolerance (recommended minimum h9). Load [MPa]
The bearings are designed for press-fit into a housing Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for rotating and oscillating applications
iglidur® D plain bearings are manufactured to special order.
machined to a H7 tolerance. After being assembled into a with different shaft materials, p = 2MPa
nominal size housing, in standard cases the inner diameter
automatically adjusts to the E10 tolerances. For particular 0.4

dimensions the tolerance differs depending on the wall

Coefficient of friction [µ]

thickness (please see product range table). 0.3

Testing methods, page 57
0.2

0.1
0.05 0.10 0.15 0.20 0.25 0.30 0.35 0.40
Surface speed [m/s]
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

258 3D CAD, finder and service life calculation ... www.igus.eu/D Lubrication-free made easy ... from stock ... no minimum order quantity 259
Specialist for linear movement
Low wear with low coefficient of friction
iglidur J200 ®

When to use it?

●● For applications with hard-anodised shafts
●● When lowest coefficient of friction is required
●● When long service life at low loads is required

When not to use?

●● For steel shafts
iglidur® J, iglidur® W300
●● When continuous operating temperatures are higher than +90°C
iglidur® V400
●● When a cost-effective universal plain bearing is required
iglidur® G, iglidur® P
iglidur® J200 iglidur® J200
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® J200 Technical data
​General properties Testing method

Density g/cm³ 1.72 ​ –50°C up to

Ø +90°C
​– ​ Colour matt grey ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.2 DIN 53495
Max. moisture absorption % weight 0.7 ​
Coefficient of friction, dynamic, against steel µ 0.11 – 0.17 ​ 23MPa
pv value, max. (dry) MPa · m/s 0.30 ​
Also available
as: Mechanical properties
Flexural modulus MPa 2,800 DIN 53457
Specialist for linear movement Flexural strength at +20°C MPa 58 DIN 53452

Bar stock,
Low wear with low coefficient of friction Compressive strength MPa 43 ​
round bar Max. recommended surface pressure (+20°C) MPa 23 ​
Page 677 Shore D hardness 70 DIN 53505
The specialist for low coefficient of friction and minimal wear with hard-anodised aluminium shafts.
●● Recommended for hard-anodised aluminium shafts Physical and thermal properties
●● Low coefficient of friction Max. application temperature long-term °C +90 ​
FOOD
●● High wear resistance Max. application temperature short-term °C +120 ​
●● For low and medium loads Min. application temperature °C –50 ​
Bar stock, ●● Lubrication-free Thermal conductivity W/m · K 0.24 ASTM C 177
plate
Page 683 ●● Maintenance-free Coefficient of thermal expansion (at +23°C) K–1 · 10–5 8 DIN 53752
Electrical properties
Typical application areas Specific contact resistance Ωcm > 108 DIN IEC 93
●● Automation Surface resistance Ω > 108 DIN 53482
●● Linear technology Table 01: Material properties
tribo-tape liner ●● Actuator
Page 691
iglidur® J200 is the result of the development of extremely Resistance to weathering
low friction plain bearing materials. When using plain iglidur® J200 plain bearings are resistant to weathering.
bearings in linear motion, friction can be critical. Many The material properties are slightly affected. Discoloration
materials can give low coefficient of friction under high occurs.
loads, but iglidur® J200 can give excellent friction values
even at low loads. Mechanical properties
Piston rings
Page 581 With increasing temperatures, the compressive strength of
Moisture absorption iglidur® J200 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications Under standard climatic conditions, the moisture absorption this inverse relationship. The maximum recommended
Wear resistance at +23°C – + of iglidur® J200 plain bearings is approximately 0.2% surface pressure is a mechanical material parameter. No
weight. The saturation limit in water is 0.7% weight. These conclusions regarding the tribological properties can be
Wear resistance at +90°C – +
values are so low that a moisture expansion need to be drawn from this.
Two hole Wear resistance at +150°C – + considered only in extreme cases. At the maximum permissible load of 23MPa, the deformation
flange
bearings is approximately 3.5% (diagram 03). A plastic deformation
Page 603 Low coefficient of friction – +
Vacuum can be negligible up to this value. However, it is also
Low moisture absorption – + In vacuum, any present moisture is released as vapour. dependent on the service time.
The use in vacuum is only possible to a limited extent. Surface pressure, page 41
Wear resistance under water – +

Moulded High media resistance – + Radiation resistance

special parts
Page 624 Plain bearings made from iglidur® J200 are resistant up to
Resistant to edge pressures – +
a radiation intensity of 3 · 10²Gy.
Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® spheri- Online product finder Online service life calculation

cal balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

262 3D CAD, finder and service life calculation ... www.igus.eu/J200 Lubrication-free made easy ... from stock ... no minimum order quantity 263
iglidur® J200 iglidur® J200
+90°C +90°C
23MPa 23MPa
Bearing technology | Plain bearing | iglidur® J200 Technical data
Permissible surface speeds Installation tolerances 100.0 0.70
0.60
iglidur® J200 attains high surface speeds due to its iglidur® J200 plain bearings are standard bearings for
10.0

Coefficient of friction [µ]

0.50
excellent coefficient of friction. Continuous rotation speeds shafts with h tolerance (recommended minimum h9).
0.40
of 1.0m/s are possible. The permitted speeds are clearly The bearings are designed for press-fit into a housing 1.0
0.30

Pressure [MPa]
higher yet in linear movements or in short-term operation. machined to a H7 tolerance. After being assembled into a
0.1 0.20
Speeds of over 15.0m/s have been successfully tested in nominal size housing, in standard cases the inner diameter
0.10
linear applications. automatically adjusts to the E10 tolerances. For particular
0.01 0.00
Surface speed, page 44 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 5 10 15 20
thickness (please see product range table).
Surface speed [m/s] Load [MPa]
Temperature Testing methods, page 57
The maximum permissible temperature of +120°C should Diagram 01: Permissible pv values for iglidur® J200 plain Diagram 05: Coefficient of friction as a function of the load,
not be exceeded. Therefore the ambient temperature bearings with a wall thickness of 1mm, dry operation against v = 0.01m/s
generated by friction has to be added. From +60°C Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
onward, the bearing should be mechanically retained, Alcohols +
so as to avoid the bearing moving out of the hole. The Diluted acids 0 up to – 25 5.0
wear resistance also decreases exponentially from +70°C Diluted alkalines + 4.5

Cf53, hard-chromed
20 4.0
upwards. Fuels +

304 stainless steel

3.5

Free cutting steel

High grade steel

HR carbon steel
Application temperatures, page 49 Greases, oils without additives + 15 3.0

H.a. aluminium
2.5
Additional securing, page 49 Hydrocarbons +
10 2.0

Wear [µm/km]
Strong acids – 1.5

Load [MPa]
5 1.0

Cf53
Friction and wear Strong alkalines + up to 0
0.5
Among all the iglidur® materials, iglidur® J200 exhibits All information given at room temperature [+20°C] 0 0.0
the lowest coefficient of friction. The average coefficient Table 02: Chemical resistance 20 30 40 50 60 70 80 90
of friction of all measurements, even with different shaft Chemical table, page 1636 Temperature [°C]
materials, is 0.11μ. The use of hard-anodised aluminium as Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
a shaft material is also of importance. The comparison with ​ ​ Rotating Oscillating linear function of temperature (23MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
the rest of the iglidur® materials shows that iglidur® J200 long-term m/s 1.0 0.7 10.0
plain bearings are suitable for rather low loads. The short-term m/s 1.5 1.1 15.0 10.0 80
influence of surface speed and load on the coefficient of Table 03: Maximum surface speeds 70 rotating
8.0 oscillating
friction is small. The change of the coefficient of friction at +23°C 60
high loads is in the normal range (diagrams 04 and 05). ​ Dry Greases Oil Water 6.0 +60°C 50
40
Surface finishes (Ra) of the shaft between 0.2 – 0.4µm Coefficient of friction µ 0.11 – 0.17 0.09 0.04 0.04

Deformation [%]
4.0 30

Wear [µm/km]
are ideal. The influence of the shaft material on the wear Table 04: Coefficient of friction against steel (Ra = 1μm,
20
2.0
resistance is significant. Even at low loads, we recommend 50HRC) 10
to have a closer look into the wear database. 0.0 0
Coefficient of friction and surfaces, page 47 ​ Housing Plain bearing Shaft 0 8 16 24 0 5 10 15 20 25
Wear resistance, page 50 Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa] Load [MPa]
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
Shaft materials >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with shaft material Cf53 hardened and ground steel, as a
The shaft material has a great impact on the wear resist- > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000 function of the load
0.5
ance. In fact, all shaft materials (smooth or hardened) are > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000
suitable for use with iglidur® J200, but the best results > 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
0.4
Coefficient of friction [µ]

are achieved with hard-anodised aluminium. In particular > 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000
when used in linear motion, this running surface has proven > 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000 0.3
its value. > 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
Shaft materials, page 52 > 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000 0.2
Table 05: Important tolerances for plain bearings according
0.1
to ISO 3547-1 after press-fit
0.05 0.10 0.15 0.20
Surface speed [m/s]
iglidur J200 plain bearings are manufactured to special
®
Diagram 04: Coefficient of friction as a function of the
order.
surface speed, p = 0.75MPa

264 3D CAD, finder and service life calculation ... www.igus.eu/J200 Lubrication-free made easy ... from stock ... no minimum order quantity 265
Ideal for pivoting movement
Vibration-dampening with low coefficient
of friction for low or medium loads
iglidur E7 ®

When to use it?

●● When good dampening properties and quiet operation are required
●● When a low coefficient of friction in a pivoting movement is required
●● When a tough material is required

When not to use?

●● When high pressures occur
iglidur® G, iglidur® Z
●● When continuous operating temperatures are higher than 70°C
iglidur® J350
●● When universal wear resistance is required
iglidur® J
iglidur® E7 iglidur® E7
+70°C +70°C
18MPa 18MPa
Bearing technology | Plain bearing | iglidur® E7 Technical data
General properties​ Testing method

Density g/cm³ 1.05 ​ –50°C up to

Ø +70°C
6.0 – 20.0mm Colour dark grey ​
Max. moisture absorption at +23°C and 50% r.h. % weight 0.1 DIN 53495
Max. moisture absorption % weight 0.1 ​
Coefficient of friction, dynamic, against steel µ 0.09 – 0.23 ​ 18MPa
pv value, max. (dry) MPa · m/s 0.22 ​
Also available
as: Mechanical properties
Flexural modulus MPa 1,477 DIN 53457
Ideal for pivoting movement Flexural strength at +20°C MPa 22 DIN 53452

Bar stock,
Vibration-dampening with low coefficient of friction Compressive strength MPa 18 ​
Max. recommended surface pressure (+20°C) MPa 18 ​
round bar
Page 677 for low or medium loads Shore D hardness 61 DIN 53505
Physical and thermal properties
For the first time, the material iglidur® E7, well-known from drylin® linear technology, is also available as Max. application temperature long-term °C +70 ​
a plain bearing. Plain bearings made of the material offer excellent coefficient of friction and wear with FOOD
Max. application temperature short-term °C +90 ​
low to medium loads. Min. application temperature °C –50 ​
Bar stock, ●● Noise-dampening Thermal conductivity W/m · K 0.24 ASTM C 177
plate ●● Very low coefficients of friction
Page 683 Coefficient of thermal expansion (at +23°C) K–1 · 10–5 25 DIN 53752
●● Lubrication-free Electrical properties
●● Corrosion-free Specific contact resistance Ωcm >109 DIN IEC 93
Surface resistance Ω >109 DIN 53482
Typical application areas
Table 01: Material properties
●● Packaging industry
tribo-tape liner
Page 691 ●● Textile industry
The material E7 offers good vibration-dampening properties. Resistance to weathering
●● Furniture/Industrial design
With low coefficient of friction at low and medium loads, the iglidur® E7 plain bearings are continuously resistant to
material is a suitable partner for almost all shaft materials. weathering. The material properties are only slightly
affected. Possible discolorations are only superficial.
Moisture absorption
Under standard climatic conditions, the moisture absorption Mechanical properties
Piston rings
Page 581 of iglidur® E7 plain bearings is approximately 0.1% weight. With increasing temperatures, the compressive strength of
The saturation limit in water is 0.1% weight. These values iglidur® E7 plain bearings decreases. Diagram 02 shows
Descriptive technical specifications are so low that a moisture expansion need to be consid- this inverse relationship. The maximum recommended
Wear resistance at +23°C – + ered only in extreme cases. surface pressure is a mechanical material parameter.
No conclusions regarding the tribological properties can
Wear resistance at +90°C – +
Vacuum be drawn from this. At the maximum permissible load of
Two hole Wear resistance at +150°C – + In vacuum, any present moisture is released as vapour. 18MPa, the deformation is approximately 6% (diagram 03).
flange
bearings The use in vacuum is generally possible. A plastic deformation can be negligible up to this value.
Page 603 Low coefficient of friction – +
However, it is also dependent on the service time.
Low moisture absorption – + Radiation resistance ​Surface pressure, page 41
Plain bearings made from iglidur® E7 are resistant up to a
Wear resistance under water – +
radiation intensity of 3 · 10²Gy.
Moulded High media resistance – +
special parts
Page 624 Resistant to edge pressures – +

Suitable for shock and impact loads – +

Resistant to dirt – +

igubal® Online product finder Online service life calculation

spherical balls
Page 841 www.igus.eu/iglidur-finder www.igus.eu/iglidur-expert

268 3D CAD, finder and service life calculation ... www.igus.eu/E7 Lubrication-free made easy ... from stock ... no minimum order quantity 269
iglidur® E7 iglidur® E7
+70°C +70°C
18MPa 18MPa
Bearing technology | Plain bearing | iglidur® E7 Technical data
Permissible surface speeds Installation tolerances 100.0 0.25

iglidur® E7 attains high surface speeds due to its excellent iglidur ® E7 plain bearings are standard bearings for
10.0

Coefficient of friction [µ]

coefficient of friction. Continuous rotation speeds of 0.5m/s shafts with h tolerance (recommended minimum h9). 0.20
are possible. The permitted speeds are clearly higher yet The bearings are designed for press-fit into a housing 1.0

Pressure [MPa]
in linear movements or in short-term operation. Speeds machined to a H7 tolerance. After being assembled into a 0.15
of over 3.0m/s have been successfully tested in linear nominal size housing, in standard cases the inner diameter 0.1
applications. automatically adjusts to the E10 tolerances. For particular
0.01 0.10
Surface speed, page 44 dimensions the tolerance differs depending on the wall
0.001 0.01 0.1 1.0 10.0 0 15 25 35 45
thickness (please see product range table).
Surface speed [m/s] Load [MPa]
Temperature Testing methods, page 57
The maximum permissible temperature of +90°C should Diagram 01: Permissible pv values for iglidur® E7 plain Diagram 05: Coefficient of friction as a function of the
not be exceeded. Therefore the ambient temperature bearings with a wall thickness of 1mm, dry operation against pressure, v = 0.01m/s
generated by friction has to be added. From +30°C Chemicals Resistance a steel shaft, at +20°C, mounted in a steel housing
onward, the bearing should be mechanically retained, Alcohols +
so as to avoid the bearing moving out of the hole. The Diluted acids 0 up to – 120 2.5
wear resistance also decreases exponentially from +90°C Diluted alkalines +
100

Cf53, hard-chromed
2.0
upwards. Fuels +

304 stainless steel

Free cutting steel
80

High grade steel

HR carbon steel
Application temperatures, page 49 Greases, oils without additives + 1.5

H.a. aluminium
60
Additional securing, page 49 Hydrocarbons +
1.0

Wear [µm/km]
Strong acids – 40

Load [MPa]
0.5

Cf53
Friction and wear Strong alkalines + up to 0 20
Among all the iglidur® materials, iglidur® E7 exhibits the All information given at room temperature [+20°C] 0 0.0
lowest coefficient of friction. The average coefficient of Table 02: Chemical resistance 20 30 40 50 60 70 80
friction of all measurements, even with different shaft Chemical table, page 1636 Temperature [°C]
materials, is 0.11μ. The use of hard-anodised aluminium Diagram 02: Maximum recommended surface pressure as a Diagram 06: Wear, rotating with different shaft materials,
as a shaft material is also of importance. The comparison ​ ​ Rotating Oscillating linear function of temperature (18MPa at +20°C) pressure, p = 1MPa, v = 0.3m/s
with the rest of the iglidur® materials shows that iglidur® E7 long-term m/s 0.5 0.4 2.0
plain bearings are suitable for rather low loads. The short-term m/s 0.8 0.6 3.0 10 350
influence of surface speed and load on the coefficient of Table 03: Maximum surface speeds 300 rotating
8 oscillating
friction is small. The change of the coefficient of friction at +23°C 250
high loads is in the normal range (diagrams 04 and 05). ​ Dry Greases Oil Water 6 +60°C
200
Surface finishes (Ra) of the shaft between 0.8µm are ideal. Coefficient of friction µ 0.09 – 0.23 0.09 0.04 0.04

Deformation [%]
4 150

Wear [µm/km]
The influence of the shaft material on the wear resistance Table 04: Coefficient of friction against steel (Ra = 1μm, 100
2
is significant. Even at low loads, we recommend to have 50HRC) 50
a closer look into the wear database. 0 0
Coefficient of friction and surfaces, page 47 ​ Housing Plain bearing Shaft 0 5 10 15 20 25 30 35 40 45 0 1 2 5 10 20
Wear resistance, page 50 Ø d1 [mm] H7 [mm] E10 [mm] h9 [mm] Load [MPa] Load [MPa]
0–3 +0.000 +0.010 +0.014 +0.054 –0.025 +0.000 Diagram 03: Deformation under pressure and temperature Diagram 07: Wear for oscillating and rotating applications
Shaft materials >3–6 +0.000 +0.012 +0.020 +0.068 –0.030 +0.000 with shaft material Cf53 hardened and ground steel, as a
The shaft material has a great impact on the wear resistance. > 6 – 10 +0.000 +0.015 +0.025 +0.083 –0.036 +0.000 function of the load
In fact, all shaft materials (smooth or hardened) are suitable > 10 – 18 +0.000 +0.018 +0.032 +0.102 –0.043 +0.000 0.25

for use with iglidur® E7, but the best results are achieved > 18 – 30 +0.000 +0.021 +0.040 +0.124 –0.052 +0.000
Coefficient of friction [µ]

with hard-anodised aluminium. In particular when used in > 30 – 50 +0.000 +0.025 +0.050 +0.150 –0.062 +0.000 0.20
linear motion, this running surface has proven its value. > 50 – 80 +0.000 +0.030 +0.060 +0.180 –0.074 +0.000
Shaft materials, page 52 > 80 – 120 +0.000 +0.035 +0.072 +0.212 –0.087 +0.000
0.15
> 120 – 180 +0.000 +0.040 +0.085 +0.245 –0.100 +0.000
Table 05: Important tolerances for plain bearings according
0.10
to ISO 3547-1 after press-fit
0.10 0.15 0.20 0.25 0.30
Surface speed [m/s]
​
Diagram 04: Coefficient of friction as a function of the
surface speed, p = 0.75MPa

270 3D CAD, finder and service life calculation ... www.igus.eu/E7 Lubrication-free made easy ... from stock ... no minimum order quantity 271
iglidur® E7 iglidur® E7
+70°C +70°C
18MPa 18MPa
Bearing technology | Plain bearing | iglidur® E7 Bearing technology | Plain bearing | iglidur® E7
Sleeve bearing (form S) Flange bearing (form F)
.5
.0
ax
f1

30
f1
rm

°
30°

d2
d3

d1
d1

d2
0.5

30°
b1 b2
b1

2)
Thickness < 0.6mm: Chamfer = 20° 2)
Thickness < 0.6mm: Chamfer = 20°
Chamfer in relation to d1 Chamfer in relation to d1
d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and d1 [mm] Ø 1 – 6 Ø 6 – 12 Ø 12 – 30 Dimensions according to ISO 3547-1 and
f1 [mm] 0.3 0.5 0.8 special dimensions f1 [mm] 0.3 0.5 0.8 special dimensions

Order example: E7SM-0608-06 – no minimum order quantity. Order example: E7FM-0608-06 – no minimum order quantity.
E7 iglidur® material S Sleeve bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1 E7 iglidur® material F Flange bearing M Metric 06 Inner Ø d1 08 Outer Ø d2 06 Total length b1

d1 d1 d2 b1 Part No. d1 d1 d2 d3 b1 b2 Part No.

Tolerance3) h13 Tolerance3) d133) h13 h13
[mm] [mm] [mm] [mm] [mm] [mm] [mm] [mm]
6.0 +0.020 +0.068 8.0 6.0 E7SM-0608-06 6.0 +0.020 +0.068 8.0 12.0 6.0 1.00 E7FM-0608-06
8.0 10.0 10.0 E7SM-0810-10 8.0 10.0 15.0 10.0 1.00 E7FM-0810-10
+0.025 +0.083 +0.025 +0.083
10.0 12.0 10.0 E7SM-1012-10 10.0 12.0 18.0 10.0 1.00 E7FM-1012-10
12.0 14.0 12.0 E7SM-1214-12 12.0 14.0 20.0 12.0 1.00 E7FM-1214-12
+0.032 +0.102 +0.032 +0.102
16.0 18.0 15.0 E7SM-1618-15 16.0 18.0 24.0 17.0 1.00 E7FM-1618-17
20.0 +0.040 +0.124 23.0 20.0 E7SM-2023-20 20.0 +0.040 +0.124 23.0 30.0 21.5 1.50 E7FM-2023-21
3)
After press-fit. Testing methods, page 57 3)
After press-fit. Testing methods, page 57

Available from stock Ordering note Available from stock Ordering note
Detailed information about delivery time online. Our prices are scaled according to order Detailed information about delivery time online. Our prices are scaled according to order
www.igus.eu/24 quantities, current prices can be found online. www.igus.eu/24 quantities, current prices can be found online.

Online ordering Online ordering

Discount scaling Discount scaling
Including delivery times, prices, online tools Including delivery times, prices, online tools
1–9 50 – 99 500 – 999 1–9 50 – 99 500 – 999
www.igus.eu/E7 www.igus.eu/E7
10 – 24 100 – 199 1,000 – 2,499 10 – 24 100 – 199 1,000 – 2,499
25 – 49 200 – 499 2,500 – 4,999 25 – 49 200 – 499 2,500 – 4,999

No minimum order value. No minimum order value.

No low-quantity surcharges. No low-quantity surcharges.
Free shipping within Germany for orders Free shipping within Germany for orders
above €150. above €150.

272 3D CAD, finder and service life calculation ... www.igus.eu/E7 Lubrication-free made easy ... from stock ... no minimum order quantity 273