Chemical admixtures are the ingredients in concrete other than portland cement, water, and
aggregate that are added to the mix immediately before or during mixing. Producers use
admixtures primarily to reduce the cost of concrete construction; to modify the properties of
hardened concrete; to ensure the quality of concrete during mixing, transporting, placing, and
curing; and to overcome certain emergencies during concrete operations.

Successful use of admixtures depends on the use of appropriate methods of batching and
concreting. Most admixtures are supplied in ready-to-use liquid form and are added to the
concrete at the plant or at the jobsite. Certain admixtures, such as pigments, expansive agents,
and pumping aids are used only in extremely small amounts and are usually batched by hand
from premeasured containers.

The effectiveness of an admixture depends on several factors including: type and amount of
cement, water content, mixing time, slump, and temperatures of the concrete and air.
Sometimes, effects similar to those achieved through the addition of admixtures can be achieved
by altering the concrete mixture-reducing the water-cement ratio, adding additional cement,
using a different type of cement, or changing the aggregate and aggregate gradation.

Five Functions

Admixtures are classed according to function. There are five distinct classes of chemical
admixtures: air-entraining, water-reducing, retarding, accelerating, and plasticizers
(superplasticizers). All other varieties of admixtures fall into the specialty category whose
functions include corrosion inhibition, shrinkage reduction, alkali-silica reactivity reduction,
workability enhancement, bonding, damp proofing, and coloring. Air-entraining admixtures,
which are used to purposely place microscopic air bubbles into the concrete, are discussed more
fully in Air-Entrained Concrete.

Water-reducing admixtures usually reduce the required water content for a concrete mixture by
about 5 to 10 percent. Consequently, concrete containing a water-reducing admixture needs less
water to reach a required slump than untreated concrete. The treated concrete can have a lower
water-cement ratio. This usually indicates that a higher strength concrete can be produced
without increasing the amount of cement. Recent advancements in admixture technology have
led to the development of mid-range water reducers. These admixtures reduce water content by
at least 8 percent and tend to be more stable over a wider range of temperatures. Mid-range
water reducers provide more consistent setting times than standard water reducers.

Retarding admixtures, which slow the setting rate of concrete, are used to counteract the
accelerating effect of hot weather on concrete setting. High temperatures often cause an
increased rate of hardening which makes placing and finishing difficult. Retarders keep concrete
workable during placement and delay the initial set of concrete. Most retarders also function as
water reducers and may entrain some air in concrete.

Accelerating admixtures increase the rate of early strength development, reduce the time
required for proper curing and protection, and speed up the start of finishing operations.
Accelerating admixtures are especially useful for modifying the properties of concrete in cold
weather.

Superplasticizers, also known as plasticizers or high-range water reducers (HRWR), reduce water
content by 12 to 30 percent and can be added to concrete with a low-to-normal slump and
water-cement ratio to make high-slump flowing concrete. Flowing concrete is a highly fluid but
workable concrete that can be placed with little or no vibration or compaction. The effect of
superplasticizers lasts only 30 to 60 minutes, depending on the brand and dosage rate, and is
followed by a rapid loss in workability. As a result of the slump loss, superplasticizers are usually
added to concrete at the jobsite.

Corrosion-inhibiting admixtures fall into the specialty admixture category and are used to slow
corrosion of reinforcing steel in concrete. Corrosion inhibitors can be used as a defensive
strategy for concrete structures, such as marine facilities, highway bridges, and parking garages,
that will be exposed to high concentrations of chloride. Other specialty admixtures include
shrinkage-reducing admixtures and alkali-silica reactivity inhibitors. The shrinkage reducers are
used to control drying shrinkage and minimize cracking, while ASR inhibitors control durability
problems associated with alkali-silica reactivity.

 About

 Associate Members

 Awards

 Bookstore

 Careers

 Design Aids

 Education Foundation
  Sustainability

 History

 Leadership

 Meetings

 Members

 Paving

 Privacy Policy

 Reference Library

 Staff

Portland Cement Association

 200 Massachusetts Ave NW, Suite 200

 Washington, DC 20001

 202.408.9494

© 2024 Portland Cement Association. All rights reserved. www.cement.org