261896
Technical Data Sheet
Terostat MS 930
20 July-2009
PRODUCT DESCRIPTION Volume change (acc. to DIN 52451), %: <2
Terostat MS 930 provides the following product UV resistance: no signif. changes
characteristics: UV source: Osram
Vitalux 300W,
Technology Silane-modified polymer dry UV
Distance to the specimen, cm: 25
Product Type Sealant
Test period, weeks: 6
Components One-component QUV resistance: no signif. changes
Cure Humidity QUV source: QUV
Application Assembly weatherometer acc.
Appearance White, Grey, Black to DIN 53384-A
Consistency Pasty, Thixotropic Test period, weeks: 6
Odor Characteristic Damp heat test durability **: given
Reference IEC 61215/61646 clause 10.13:
Test period, hours: 1,000
Terostat MS 930 is a gun-grade, one component sealant Application temperature, °C: 5 to 40
based on silane modified polymer, which cures by reaction In service temperature range, °C: -50 to +80
with moisture to a soft elastic product. The skin formation and Short exposure (up to 1 h), °C: 120
curing times are dependent on humidity and temperature, and * ISO 291 standard climate: 23°C, 50% relative
the curing time also depends on joint depth. By increasing the air humidity
temperature and moisture these times can be reduced; low **Damp heat conditions: 85°C, 85% relative
temperature as well as low moisture retard the process. air humidity
Terostat MS 930 is free of solvents, isocyanates, silicones
and PVC, and is odorless. It demonstrates good adhesion to
many substrates and is compatible with suitable paint
systems. The sealant also demonstrates good UV resistance DIRECTIONS OF USE
and can therefore be used for interior and exterior Preliminary statement:
applications. Terostat MS 930 allows accelerated curing as Prior to application it is necessary to read the Material Safety
two-component material. See separate data sheets Terostat Data Sheet for information about precautionary measures
MS Power & Speed Technology or Terostat MS and safety recommendations. Also, for chemical products
2c-Technology. exempt from compulsory labeling, the relevant precautions
should always be observed.
Application Areas:
Terostat MS 930 is used for the following applications: seam Pre-Treatment:
and joint sealing in vehicle body, railway carriage and The substrates must be clean, dry, oil- and grease free. Depending
container manufacture; ship and boat building; metal on the surface it can be necessary to roughen the surface or to use a
construction; the equipment, electrical, plastics, air primer/adhesion promoter to provide best adhesion. When
manufacturing plastics, external release agents are often used; these
conditioning and ventilation industries; for conventional
agents must be accurately removed prior to starting bonding or
vehicle window glazing between rubber profile and glass sealing. Due to the different compositions of paints, especially
(good adhesion to most rubber qualities, even on powder paints and the large number of different substrates,
EPDM-basis), for bonding of floor coverings in bus application trials before use are necessary. For cleaning, Cleaner +
manufacturing. Diluent A, FL or Terostat 450 from the Henkel portfolio are suitable.
When bonding and sealing PMMA, e.g. Plexiglas®, and
polycarbonate, e.g. Makrolon® or Lexan®, under tension, stress
TECHNICAL DATA corrosion cracking may occur. Application trials before use are
Density, g/cm³: approx. 1.5 necessary. There is no adhesion to polyethylene, polypropylene and
Sag resistance: no sagging (DIN PTFE. Substrates not mentioned above should be subject to trials.
profile 15 mm)
Skin formation time, min*: approx. 25 to 40
Cure rate, mm/24 hrs: approx. 4
Shore-A-hardness (ISO 868, Durometer A): approx. 30
Tensile strength (acc. to ISO 37), MPa: 1.0
Elongation at break (acc. to ISO 37, approx. 250
speed 200 mm/min),%:
Stress at 100 % elongation 0.7
(acc. to ISO 37), MPa:
______________________________________________________________________________________________________
Henkel AG & [Link]
40191 Düsseldorf. Germany
Phone: +49-211-797-0
[Link]
Application:
Application from 310 ml cartridges is made with the Teroson
Hand or Air Pressure Pistols, and from plastic wallets (310
and 570 ml) with the corresponding FK-Hand or FK-Air
Pressure Pistols. In the case of compressed air application a
pressure of 2 to 5 bar is required. Low material temperatures
of the sealant will lead to an increase of viscosity, resulting in
a lower extrusion rate. This can be avoided by bringing the
sealant up to room temperature prior to application. Terostat
MS 930 can also be applied from hobbocks or drums with
high pressure pumps with follower plates. See separate
application directions of Terostat MS products in hobbocks
and drums.
Cleaning:
For cleaning application equipment contaminated with
uncured Terostat MS 930 we recommend the use of
Cleaner+Diluent A, D or FL.
STORAGE
Frost-Sensitive No
Recommended Storage Temperature, °C 10 to 25
Shelf-life (in unopened original packaging), 12
months
ADDITIONAL INFORMATION
Disclaimer:
The Information provided herein, especially recommendations
for the usage and the application of our products, is based
upon our knowledge and experience. Due to different
materials used as well as to varying working conditions
beyond our control we strictly recommend to carry out
intensive trials to test the suitability of our products with
regard to the required processes and applications. We do not
accept any liability with regard to the above information or
with regard to any verbal recommendation, except for cases
where we are liable of gross negligence or false intention.
This datasheet replaces all former versions.
Reference 0.0
______________________________________________________________________________________________________
Henkel AG & [Link]
40191 Düsseldorf. Germany
Phone: +49-211-797-0
[Link]
261896
Powered by TCPDF ([Link])