Firelite® 95
Product Data Sheet
Product Description
A high purity castable with low iron and low silica content for service up to 1760°C (3200°F). It combines very high
refractoriness with low thermal conductivity. Recommended for burner blocks in thin walls and for special atmospheres;
particularly resistant to chemical attack in ammonia production processes where hydrogen atmospheres are encountered.
Conforms to class V of ASTM classification C-401-91.
Properties Firelite 95
Region of Manufacture Europe
Bond Type Hydraulic
Method of application Cast
Maximum Service Temperature, °C (°F) 1760 (3200)
ASTM C401-91 Classification V
Estimated weight of dry material/m3 of construction, kg (lb) 1690 (105.48)
Water addition, % by weight 16
Maximum grain size, mm 5
Packaging by weight, kg (lb) 25 (55)
The product(s) represented are intended for industrial refractory applications. The values and application information in this datasheet are
given for guidance only. The values and the information given are subject to normal manufacturing variation and may be subject to change
without notice. Morgan Advanced Materials – Thermal Ceramics makes no guarantees and gives no warranties about the suitability of a
product, and you should seek advice to confirm the product’s suitability for use with Morgan Advanced Materials.
Publication Date:01 January 2025 [Link]
Code: CA.27 Email: [Link]@[Link]
1 of 2 Thermal Ceramics is a business of Morgan Advanced Materials
Firelite® 95
Product Data Sheet
Density, kg/m3 (pcf), ASTM C134
oven dried, 110°C (230°F) 1730 (108.0)
after 5 hours firing, 815°C (1500°F) 1690 (105.5)
Cold crushing strength, MPa (psi), ASTM C133
oven dried, 110°C (230°C) 18.5 (2682.5)
after 5 hours firing, 815°C (1500°F) 11.3 (1638.5)
Permanent linear change, %, ASTM C113
after 5 hours firing, 815°C (1500°F) -0.1
After 5 hours firing, 1000°C (1832°F) -0.1
after 5 hours firing, 1200°C (2192°F) -0.2
after 5 hours firing, 1400°C (2550°F) -0.2
Thermal conductivity, W/m•K (BTU•in/hr•ft2•°F), ASTM C201/417
400°C (752°F) 0.93 (6.45)
600°C (1112°C) 0.84 (5.83)
800°C (1472°F) 0.79 (5.48)
1000°C (1832°F) 0.78 (5.41)
1200°C (2192°F) 0.77 (5.34)
Chemical composition, %
Alumina, Al2O3 95.4
Silica, SiO2 0.4
Calcium Oxide, CaO 4.9
Ferric Oxide, Fe2O3 0.1
Titanium Oxide, TiO2 0.06
Alkali as, MgO+K2O+Na2O 0.3
Ignition Loss 0.31
Storage and Shelf Life
• Should be stored in dry conditions, unopened packaging on pallets. Do not store on ground. Keep
out of rain and damp conditions.
• Shelf life is of twelve months with original packaging, double shrink film and dehydrating agent
provided if the monolithic is stored under these recommended conditions.
The product(s) represented are intended for industrial refractory applications. The values and application information in this datasheet are
given for guidance only. The values and the information given are subject to normal manufacturing variation and may be subject to change
without notice. Morgan Advanced Materials – Thermal Ceramics makes no guarantees and gives no warranties about the suitability of a
product, and you should seek advice to confirm the product’s suitability for use with Morgan Advanced Materials.
Publication Date:01 January 2025 [Link]
Code: CA.27 Email: [Link]@[Link]
2 of 2 Thermal Ceramics is a business of Morgan Advanced Materials