Soldering, Brazing, and Braze Welding Explained

Brazing and soldering both use filler metals to join metal parts without melting the base metals. Brazing uses higher temperatures than soldering, with brazing filler metals melting above 450°C and below the melting point of the base metals. Common applications of brazing include joining automotive, electrical, and plumbing components where welding may damage the parts. Brazing provides strong joints between similar and dissimilar metals.

Uploaded by

Naram Appanna
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PPT, PDF, TXT or read online on Scribd
1K views25 pages

Soldering, Brazing, and Braze Welding Explained

Brazing and soldering both use filler metals to join metal parts without melting the base metals. Brazing uses higher temperatures than soldering, with brazing filler metals melting above 450°C and below the melting point of the base metals. Common applications of brazing include joining automotive, electrical, and plumbing components where welding may damage the parts. Brazing provides strong joints between similar and dissimilar metals.

Uploaded by

Naram Appanna
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PPT, PDF, TXT or read online on Scribd
  • Introduction to Soldering, Brazing, and Braze Welding: Provides an overview of soldering, brazing, and braze welding, focusing on their uses and differences.
  • Brazing Process and Principle: Describes the brazing process, highlighting the principle of not melting base metals, details of filler melting, and capillary action.
  • Advantages and Disadvantages of Brazing: Lists advantages such as applicability to various metals and limitations like joint strength and temperature sensitivity.
  • Industrial Applications of Brazing: Enumerates industries and uses for brazing, explaining its role in automotive, electronics, and other sectors.
  • Technical Specification of Joints: Discusses specifications for brazing joints, including clearance and surface preparation to ensure quality.
  • Braze Welding Differentiation: Examines how braze welding differs from other brazing processes, particularly in terms of joint formation and applications.
  • Introduction to Soldering: Defines soldering, focusing on the melting point of the filler metal and distribution techniques.
  • Applications of Soldering/Brazing: Covers soldering techniques and applications, including steps in sweat soldering and specific use cases.
  • Fluxes and Their Functions: Explains the role of fluxes in soldering and brazing, highlighting functions in oxide removal and wetting.
  • Soldering and Brazing Methods: Overviews different methods of applying heat in soldering and brazing, such as torch and induction methods.
  • Torch Soldering and Brazing: Discusses the pros and cons of torch soldering and brazing, emphasizing versatility and potential drawbacks.
  • Types of Filler Metals: Lists common solder alloys and their properties, including applications and melting temperatures.
  • Comparison of Joining Processes: Compares soldering, brazing, and welding based on parameters like temperature, joint type, and heat sources.

Soldering

Brazing
and
Braze Welding
• Brazing and soldering both use filler metals to
join and bond two (or more) metal parts to
provide a permanent joint.
• No melting of the base metals occurs, which is
similar to solid-state welding.
• Brazing and soldering are attractive compared
to welding under circumstances:
(1) the metals have poor weldability,
(2) dissimilar metals are to be joined,
(3) the intense heat of welding may damage the components being
joined,
(4) the geometry of the joint does not lend itself to any of the
welding methods,
(5) high strength is not a requirement.
• Brazing is a joining process in which a filler metal is
melted and distributed by capillary action between the
faying surfaces of the metal parts being joined.
• No melting of the base metals occurs in brazing; only the
filler melts.
• In brazing the filler metal (also called the brazing metal),
has a melting temperature (liquidus) that is above 450°C
but below the melting point (solidus) of the base
metal(s) to be joined.
• The metallurgical bonding that occurs between base and
filler metals
Figure 31-2 Capillary action pulls water into a thin tube.
Advantages
(1) Any metals can be joined, including dissimilar metals;
(2) Certain brazing methods can be performed quickly and
consistently, thus permitting high cycle rates and automated
production;
(3) Some methods allow multiple joints to be brazed
simultaneously;
(4) Brazing can be applied to join thin-walled parts that
cannot be welded;
(5) In general, less heat and power are required than in fusion
welding;
(6) Problems with the heat-affected zone in the base metal
near the joint are reduced;
(7) Joint areas that are inaccessible by many welding processes
can be brazed, since capillary action draws the molten filler
metal into the joint.
Disadvantages and limitations of brazing :
(1)Joint strength is generally less than that of a welded joint;

(2) Although strength of a good brazed joint is greater than


that of the filler metal, it is likely to be less than that of the base
metals;

(3) High service temperatures may weaken a brazed joint; and

(4) The color of the metal in the brazed joint may not match the
color of the base metal parts,
Brazing as a production process is widely used in a
variety of industries:
• Automotive (e.g., joining tubes and pipes)
• electrical equipment (e.g., joining wires and cables)
• cutting tools (e.g., brazing cemented carbide inserts to
shanks),
• Jewelry making.
• Chemical processing industry and plumbing
• Join metal pipes and tubes by brazing.
• It is used extensively for repair and
maintenance work in nearly all industries.
(a) Conventional butt joint, and adaptations of the butt joint
for brazing:
(b) scarf joint,
(c) stepped butt joint
, (d) increased cross section of the part at the joint.
• The clearance must be large enough so as not to restrict molten
filler metal from flowing throughout the entire interface.
• Typical brazing clearances in practice are 0.025 to 0.25mm
• Surfaces must be free of oxides, oils, and other contaminants in
order to promote wetting and capillary attraction during the
process
(a) torch and filler rod;
(b) ring of filler metal at Entrance of gap;
• Brazing fluxes serve a similar purpose as in
welding:

• They dissolve, combine with, and otherwise


inhibit the formation of oxides and other
unwanted byproducts in the brazing process.

• Flux is used in soldering, just as it is in brazing


and welding to clean the metal surfaces and
make it easy for the solder to flow over the
pieces to be joined.
Braze Welding
• This process differs from the other brazing processes
in the type of joint to which it is applied.
• A greater quantity of filler metal is deposited than in
brazing, and no capillary action occurs.
• In braze welding, the joint consists entirely of filler
metal;
• The base metal does not melt and is therefore not
fused into the joint as in a conventional fusion welding
process.
• The principal application of braze welding is repair
work.
SOLDERING
• It is similar to brazing

• Defined as a joining process in which a filler


metal with melting point (liquidus) not
exceeding 450°C (840F) is melted and
distributed by capillary action between the
faying surfaces of the metal parts being
joined.
HAND SOLDERING
• Hand soldering is performed manually using a
hot soldering iron.
• A bit, made of copper, is the working end of a
soldering iron.
• Its functions are
(1) to deliver heat to the parts being soldered.
(2) to melt the solder.
(3) to convey molten solder to the joint
(4) to withdraw excess solder. Most modern soldering
irons are heated by electrical resistance.
Soldering/Brazing
Applications
Steps in Sweat Soldering

1) Copper pipe is cleaned


2) Flux is applied
3) Heat is applied
4) Solder is added
5) Solder is drawn into
fitting via heat (capillary
Action)
6) Pipe is wiped cleaned
Fluxes
Fluxes used in soldering and brazing have three
major functions:
– Remove oxides that result from heating parts
– Promote wetting
– Aid in capillary action (if soldering or brazing)
Flux must be thin, when heated to its reacting
temperature
Fluxes are available in many forms
Paste
Liquid
Powder
Soldering and Brazing Methods
Grouped according to method of applying heat:
– Torch (TB)
– Furnace
– Induction
– Dip
Torch Soldering and
Torch Brazing
Advantages of using a torch:
– Versatility
– Portability
– Speed
Disadvantages of using a torch:
– Overheating
– Skill
– Fires
Tin-lead
Most popular solder
Least expensive
Most commonly used on electrical connections
Copper-zinc
Most popular brazing alloys
Available as regular and low-fuming alloys
Silver Brazing
Melting temperature for alloys is around 1400°
Fahrenheit
Copper pipe glows a dull red
Best types of flame to use:
– Air acetylene
– Air MAPP
– Air propane
– Any air fuel-gas mixture