S T E L L I T E 21 ALLOY
MMA WELD DEPOSITION
TIG WELD DEPOSITION
T E C H N I C A L D ATA
MIG WELD DEPOSITION
PTA & LASER WELD DEPOSITION
Hvof & Plasma Spray Deposition
Nominal Composition (mass %) and Physical Properties
Co
Cr
Mo
Ni
Base
26-29
4.5-6. 0
0.20-0.35
2.0-3. 0
Others
Hardness**
Fe, Si, Mn
Density
27-40 HRC**
8.33 g/cm 3
290-430 HV**
0.301 lb/in 3
Melting Range
2360-2615 F
1295-1435 C
** Higher values indicate a typical work hardened surface. Stellite 21 can work harden up to 550HV (48HRC).
Stellite 21 (previously known as Stellite 8) was developed in the mid 1930s as a corrosion resistant CoCr alloy,
and rapidly found application as a biocompatible hip implant and denture alloy. Many of the alloys currently used
in medical applications are variants of the original Stellite
21 composition. It was also one of the first heat-resistant
alloys trialled for use in jet engines.
Stellite 21 consists of a CoCrMo alloy matrix containing dispersed hard carbides which strengthen the alloy
and increase its hardness, but also decrease the ductility.
The type, shape, size, and distribution of the carbides is
strongly influenced by the processing history of the alloy,
and for this reason the mechanical properties of Stellite
21 are very dependent upon the manufacturing route and
any subsequent heat treatments.
Optical Micrograph of a Stellite 21 investment casting (as-cast, etched,
200X). The carbides in Stellite 21 are usually of the type (Cr,Mo,Co)23C6.
Due to the low volume fraction of carbides, the Co-based
alloy matrix dominates the wear and corrosion properties. Stellite 21 has excellent cavitation, galling and metal-tometal sliding wear resistance, but is not recommended for severe hard particle abrasion. The surface can work harden
considerably during wear or even during machining, and the use of correct machining tools and techniques is important
to achieve optimal results.
Stellite 21 has excellent resistance to thermal and mechanical shock. Optimum high temperature strength is obtained
by solution heat treatments at 1200-1240C (2190 - 2265F) followed by quenching, and aging in the temperature
range 700-1150C (1290-2100F).
Stellite 21 can be cast, powder metallurgically processed, or applied as a weld hardfacing. It is recommended for applications involving cavitation, erosion, corrosion and/or high temperatures, such as valve trim for petrochemical and power
generation. Due to its good impact resistance, it has been widely used in the building up of forging or hot stamping dies.
The oxyacetylene weld deposition method is not recommended for this alloy.
Corrosion Resistance
Stellite 21 is resistant to oxidizing and reducing gaseous atmospheres up to 1150C (2100F). Because its ternary alloying element is Mo and not W, it has higher resistance to reducing or complex environments (e.g. sulphuric acid,
hydrochloric acid, and sour gas) than CoCrW alloys such as Stellite 6. The typical electrode potential in sea water at room
temperature is approx. -0.3 V (SCE). Like stainless steels, Stellite 21 corrodes primarily by a pitting mechanism and not by
general mass loss in seawater and chloride solutions. More information regarding corrosion resistance can be provided
on request.
Productivity through filler metal selection
exocor.com
Nominal Thermal Expansion Coefficient (from 20C to stated temperature)
100 C
(212F)
200 C
(392F)
300 C
(572F)
400 C
(752F)
500 C
(932F)
600C
(1112F)
700C
(1292F)
800C
(1472F)
900 C
(1652F)
m/m.K
11. 0
11. 2
12. 0
12.65
13. 1
13. 6
14. 3
14. 7
15.21
-inch/inch-F
6. 1
6. 2
6. 7
7. 0
7. 3
7. 6
7. 9
8. 2 32.2 8.45
Nominal Tensile Properties at Room Temperature
Note: The Mechanical properties of Stellite
21 are very dependent upon the manufacturing route and heat treatment.
Ultimate Tensile Strength Rm
Investment Castings or
undiluted weld metal
Stellite HS-21 (*)
Yield Stress Rp(0.2% )
ksi
MPa
ksi
MPa
103
710
145
1000
82
87
Elongation
Elastic Modulus
565
A(%)
9
psi
36.2x10
GPa
650
20
35.5x10
250
245
(*) HS = HIP -consolidated from the powder form.
Nominal Hot Hardness (DHP) of undiluted weld deposit
20 C
(68F)
100 C
(212F)
200 C
(392F)
300 C
(572F)
400 C
(752F)
500 C
(932F)
600 C
(1112F)
700 C
(1292F)
800 C
(1472F)
347
279
248
228
208
197
181
153
123
900 C
(1652F)
92
Nominal Thermal and Electrical Properties
Approximate value at Room Temperature
T
Thermal conductivity
Electrical resistivity
100.5 Btu-in/hr/ft/F
14.5 W/m.K
87.38 -ohm.cm
34.4 -ohm.inch
Product Forms and Cross Reference Specifications
SPECIFICATION
PRODUCT FORM
SPECIFICATION
PRODUCT FORM
UNS R30021
Rod, Castings
AWS A5.21 / ASME BPVC IIC SFA 5.21 ERCoCr- E
Rod
UNS W73041
Wire
AWS A5.21 / ASME BPVC IIC SFA 5.21 ERCCoCr- E
Wire
UNS W73021
Electrode
AWS A5.13 / ASME BPVC IIC SFA 5.13 ECoCr- E
E lectrode
AMS 5385
Castings
SAE J467
HIP - Consolidated
AMS 5819
Rod, Wire
Stellite is a registered Trade Name of Deloro Stellite.
Deloro Stellite manufactures sophisticated alloys in the form of
castings, powders, coatings, consumables, and machined parts
that resist wear, corrosion, and abrasion. Information provided in this document is intended only for general guidance
about Deloro Stellite products and is the best information in
our possession at the time. Product users may request information about their individual use of our products, but Deloro
Stellite does not warrant or guarantee this information in any
way. Selection and purchase of Deloro Stellite products is the
sole responsibility of the product user based on the suitability
of each use. Individual applications must be fully evaluated
by the user, including compliance with applicable laws, regulations, and non-infringement. Deloro Stellite cannot know
or anticipate the many variables that affect individual product
use and individual performance results may vary. For these
reasons, Deloro Stellite does not warrant or guarantee advice
or information in this document, assumes no liability regarding the same, and expressly disclaims any warranty of any kind,
including any warranty of fitness for a particular purpose, regarding the same.
UK SALES OFFICE
US SALES OFFICE
CHINA SALES OFFICE
Deloro Stellite
Cheney Manor Industrial Estate
Swindon SN2 2PW
UK
Stellite Coatings
1201 Eisenhower Drive North
Goshen, Indiana 46526
USA
Shanghai Stellite Co. Ltd.
1799 Bao Jia Road
Jia ding district, 201800
Shanghai, Peoples Republic of China
Tel: (+44) 1793-498500
Fax: (+44) 1793-498501
Tel: (+1) 574-534-2585
Fax: (+1) 574-534-3417
E-Mail: [email protected]
E-Mail: [email protected]
Literature Number: DS-2149
Copyright 2007 Deloro Stellite
Printed in USA
www.stellite.com
Productivity through filler metal selection
exocor.com