Technical Card Gruppo Lucefin Revision 2013 All Rights Reserved

This document provides technical specifications for a quenched and tempered steel. It includes chemical composition ranges, mechanical properties at different tempering temperatures, heat treatment process, and applications. Key information includes the steel being heat treated by quenching at 850°C in oil and tempering at 600°C, yielding a hardness of 40 HRC. Various properties are listed, such as tensile strength between 1020-900 MPa and elongation between 18-20% at a depth of 22mm.

Uploaded by

Arjun Prajapati
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
75 views1 page

Technical Card Gruppo Lucefin Revision 2013 All Rights Reserved

This document provides technical specifications for a quenched and tempered steel. It includes chemical composition ranges, mechanical properties at different tempering temperatures, heat treatment process, and applications. Key information includes the steel being heat treated by quenching at 850°C in oil and tempering at 600°C, yielding a hardness of 40 HRC. Various properties are listed, such as tensile strength between 1020-900 MPa and elongation between 18-20% at a depth of 22mm.

Uploaded by

Arjun Prajapati
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

Supply conditions:

According to standards EN ISO 4957: 2002 Quenched and Tempered


TECHNICAL CARD
GRUPPO LUCEFIN
Number REVISION 2013
ALL RIGHTS RESERVED


max max
0,350,45 0,200,40 1,301,60 0,035 0,035 1,802,10 0,150,25 0,901,20
0.03 0.03 0.08 + 0.005 + 0.005 0.07 0.03 0.07
Product deviations are allowed
Upon agreement, the sulphur content can be increased to 0,050,10%



1050850 850890 840860 860880 500600
air oil or polymer calm or forced air calm air
minimum cycles


710740 furnace cooling 50 under the 250300 500 furnace cooling
max 20 h to 600, then air temperature of
(HB max 235) tempering 705 795 215 20

Heat treatment: quenching at 850 C in oil, tempering at 600 C Sidermeccanica esperience KeyLos 2728
longitudinal J at the depth
N/mm2 1020 900 18 20 25 35 40 50 75 340 340 340 336 330 310 HB
0.2 N/mm2 900 760 mm
Test at

values at room temperature on round of 25 mm after quenching at 860 C in oil


512 512 504 482 475 468 448 432 409 390 353 319 286
52 52 51.5 50 49.5 49 47.5 46 44 42 38 34 30
N/mm2 1880 1880 1850 1760 1730 1700 1600 1520 1430 1340 1180 1050 950
+20 CJ 10 10 10 10 10 14 20 32
Tempering at
106 K1 12.8 13.0 13.4 13.8 14.0 14.2 14.2 14.5
long. GPa 210 196 177
tang. GPa 81 75 68
J/(KgK) 460
W/(mK) 32.0 31.1 30.0
Kg/dm3 7.83
Ohmmm2/m 0.19
Siemensm/mm2 5.26

The symbol indicates temperature between 20 C and 100 C, 20 C and 200 C

EN DIN GB JIS IS KS GOST AISI/SAE
40CrMnNiMo864 40CrMnNiMo861

it is obtained through a special production process which allows a high micropurity level
good suitability for nitriding, good wear resistance, excellent suitability for photoengraving and polishing
good weldability
applications: ,

extrusion:

The data contained herein are intended as reference only and are subject to constant change. Lucefin s.P.A. Disclaims any and all liability for any consequences that may result from their use.