Designation: B103/B103M 15

Standard Specification for

Phosphor Bronze Plate, Sheet, Strip, and Rolled Bar1
This standard is issued under the fixed designation B103/B103M; the number immediately following the designation indicates the year
of original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.
A superscript epsilon () indicates an editorial change since the last revision or reapproval.
This standard has been approved for use by agencies of the U.S. Department of Defense.

1. Scope* 1.3 The following safety hazard caveat pertains only to the
1.1 This specification establishes the requirements for test method(s) described in this specification.
copper-tin alloy (phosphor bronze), copper-tin-lead alloy 1.3.1 This standard does not purport to address all of the
(leaded phosphor bronze), and copper-tin-lead-zinc alloy (bear- safety concerns, if any, associated with its use. It is the
ing bronze), plate, sheet, strip, and rolled bar. The phosphor responsibility of the user of this standard to establish appro-
bronzes commonly are used for deep drawing into bellows and priate safety and health practices and determine the applica-
stamping and forming into spring devices and into terminals bility of regulatory limitations prior to use.
and connectors for electrical apparatus because they combine
2. Referenced Documents
high strength with high elongation. The leaded phosphor
bronzes are used where strength, corrosion resistance, and 2.1 ASTM Standards:3
machinability are required. The bearing bronze is used in B248 Specification for General Requirements for Wrought
bushings, bearings, and load-bearing thrust washers. The Copper and Copper-Alloy Plate, Sheet, Strip, and Rolled
following alloys are covered: Bar
Copper Alloy Nominal Composition, % Previously Used
B248M Specification for General Requirements for Wrought
UNS No.2 Copper Tin Zinc Lead Designation Copper and Copper-Alloy Plate, Sheet, Strip, and Rolled
Bar (Metric)
C51000 95 5 . .. . .. A1
C51100 96 4 . .. . .. A
B601 Classification for Temper Designations for Copper and
C51180 96 4 . .. . .. ... Copper AlloysWrought and Cast
C51900 94 6 . .. . .. B846 Terminology for Copper and Copper Alloys
C52100A 92 8 . .. . .. C
C52180 92 8 . .. . .. ...
E8/E8M Test Methods for Tension Testing of Metallic Ma-
C52400 90 10 . .. . .. D terials
C53400 94 5 . .. 1 B1 E62 Test Methods for Chemical Analysis of Copper and
C54400 88 4 3 4 B2
Copper Alloys (Photometric Methods) (Withdrawn 2010)4
A
SAE Specification CA 521 conforms to the requirements of UNS No. C52100.
E75 Test Methods for Chemical Analysis of Copper-Nickel
and Copper-Nickel-Zinc Alloys (Withdrawn 2010)4
NOTE 1All of the above alloys contain small amounts of phosphorus, E255 Practice for Sampling Copper and Copper Alloys for
used as a deoxidant in melting, and to enhance the mechanical properties.
the Determination of Chemical Composition
1.2 The values stated in either inch-pound units or SI units E478 Test Methods for Chemical Analysis of Copper Alloys
are to be regarded separately as standard. Within the text, SI E527 Practice for Numbering Metals and Alloys in the
units are shown in brackets. The values stated in each system Unified Numbering System (UNS)
may not be exact equivalents; therefore, each system shall be
used independently of the other. Combining values from the 3. General Requirements
two systems may result in non-conformance with the standard. 3.1 The following sections of Specifications B248 and
B248M constitute a part of this specification.
1
3.1.1 Terminology,
This specification is under the jurisdiction of ASTM Committee B05 on Copper
and Copper Alloys and is the direct responsibility of Subcommittee B05.01 on Plate,
3.1.2 Materials and Manufacturing,
Sheet, and Strip.
Current edition approved May 15, 2015. Published June 2015. Originally
3
approved in 1936. Last previous edition approved in 2010 as B103/B103M 10. For referenced ASTM standards, visit the ASTM website, www.astm.org, or
DOI: 10.1520/B0103_B0103M-15. contact ASTM Customer Service at [email protected]. For Annual Book of ASTM
2
The UNS system for copper and copper alloys (see Practice E527) is a simple Standards volume information, refer to the standards Document Summary page on
expansion of the former standard designation system accomplished by the addition the ASTM website.
4
of a prefix C and a suffix 00. The suffix can be used to accommodate The last approved version of this historical standard is referenced on
composition variations of the base alloy. www.astm.org.

*A Summary of Changes section appears at the end of this standard

Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States
Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
1
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
3.1.3 Workmanship, Finish, and Appearance, 6. Materials and Manufacture
3.1.4 Sampling, Except for Chemical Analysis, 6.1 Materials:
3.1.5 Number of Tests and Retests, 6.1.1 The material of manufacture shall be a cast bar, cake,
3.1.6 Specimen Preparation, slab, of Copper Alloy UNS No. C51000, C51100, C51180,
3.1.7 Test Methods, Except for Chemical Analysis, C51900, C52100, C52180, C52400, C53400, or C54400 of
3.1.8 Significance of Numerical Limits, such purity and soundness as to be suitable for processing into
3.1.9 Inspection, the products prescribed herein.
3.1.10 Rejection and Rehearing, 6.1.2 When specified in the contract or purchase order, that
3.1.11 Certification, heat identification or traceability is required, the purchaser
3.1.12 Test Reports, shall specify the details desired.
3.1.13 Packaging and Package Marking, and
3.1.14 Supplementary Requirements. NOTE 2Due to the discontinuous nature of the processing of castings
into wrought products, it is not always practical to identify a specific
3.2 In addition, when a section with a title identical to that casting analysis with a specific quantity of finished material.
referenced in 5.1 appears in this specification, it contains 6.2 Manufacture:
additional requirements, which supplement those appearing in 6.2.1 The product shall be manufactured by such hot
Specifications B248 and B248M working, cold working, and annealing processes as to produce
4. Terminology a uniform wrought structure in the finished product.
6.2.2 The product shall be hot or cold worked to the finished
4.1 DefinitionsFor definitions of terms used in this size and subsequently annealed, when required, to meet the
specification, refer to Terminology B846. temper properties specified.
6.2.3 EdgesSlit edges shall be furnished unless otherwise
5. Ordering Information
specified in the contract or purchase order.
5.1 Include the following specified choices when placing
orders for product under this specification, as applicable: 7. Chemical Composition
5.1.1 ASTM designation and year of issue (for example, 7.1 The materials shall conform to the chemical composi-
B103/B103M 04); tion requirements specified in Table 1 for the copper alloy UNS
5.1.2 Copper [Alloy] UNS No. designation (for example, No. designation specified in the ordering information.
C51000);
5.1.3 Temper; 7.2 These composition limits do not preclude the presence
5.1.4 Dimensions: thickness, width, length, and so forth; of other elements. By agreement between the manufacturer and
5.1.5 Form: plate, sheet, strip, or rolled bar; purchaser, limits may be established and analysis required for
5.1.6 How furnished: coils, specific length or stock lengths, unnamed elements.
with or without ends; 7.3 Copper, specified as the remainder, may be taken as
5.1.7 Quantity: total weight each form, temper, and size; the difference between the sum of results of all the elements
and, determined and 100 %. When all the elements in Table 1 are
5.1.8 When material is purchased for agencies of the U.S. determined, the sum of results for each alloy shall be 99.5 %
Government. min.
5.2 The following options are available but may not be
included unless specified at the time of placing of the order 8. Temper
when required; 8.1 The standard tempers for products described in this
5.2.1 Type of edge: slit, sheared, sawed, square corners, specification are given in Table 2.
round corners, rounded edges, or full rounded edges; 8.1.1 M20 (as Hot-Rolled Material)The standard temper
5.2.2 Width and straightness tolerances; of sheet and plate produced by hot rolling as designated in
5.2.3 Heat identification or traceability details; Table 2.
5.2.4 Certification, and 8.1.2 H (Rolled Material)The standard tempers of rolled
5.2.5 Mill Test Report. material are as designated in Table 2 with prefix H. Former

TABLE 1 Chemical Requirements

Composition, %
Element Copper Alloy UNS No.
C51000 C51100 C51180 C51900 C52100 C52180 C52400 C53400A C54400A
Tin 4.2-5.8 3.5-4.9 3.5-4.9 5.0-7.0 7.0-9.0 7.0-9.0 9.0-11.0 3.5-5.8 3.5-4.5
Phosphorus 0.03-0.35 0.03-0.35 0.01-0.35 0.03-0.35 0.03-0.35 0.01-0.35 0.03-0.35 0.03-0.35 0.01-0.50
Iron, max 0.10 0.10 0.05-0.20 0.10 0.10 0.05-0.20 0.10 0.10 0.10
Lead 0.05 max 0.05 max 0.05 max 0.05 max 0.05 max 0.05 max 0.05 max 0.8-1.2 3.0-4.0
Zinc 0.30 max 0.30 max 0.30 max 0.30 max 0.20 max 0.30 max 0.20 max 0.30 max 1.5-4.5
Nickel ... ... 0.05-0.20 ... ... 0.05-0.20 ... ... ...
Copper remainder remainder remainder remainder remainder remainder remainder remainder remainder
A
When specified for bearings, the phosphorus content shall be maintained from 0.01 to 0.15 %.

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
2
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
TABLE 2 Tensile Strength Requirements and Approximate Rockwell Hardness Values
NOTE 1Plate is generally available in only the as hot-rolled (M20) temper. Required properties for other tempers shall be agreed upon between the
manufacturer purchaser at the time of placing the order.
Tensile Strength,
Temper DesignationA Approximate Rockwell Hardness
Thickness, in. [mm] ksiB [MPa]
Code Name Min Max B Scale Superficial 30T
Copper Alloy UNS No. C51000
M20 as hot-rolled Over 0.188 [4.775] 40 [275] 60 [415] ... ...
O60 soft Over 0.039 [0.991] 43 [295] 58 [400] 16-64 ...
Over 0.029 [0.737] ... 32-59
Over 0.020 [0.508] to 0.039 [0.991] incl 12-60 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 24-53
0.003 [0.076] to 0.010 [0.254] incl
H02 half-hard Over 0.039 [0.991] 58 [400] 73 [505] 64-85 ...
Over 0.029 [0.737] ... 59-73
Over 0.02 [0.508] to 0.039 [0.991] incl 60-82 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 53-69
0.003 [0.076] to 0.010 [0.254] incl
H04 hard Over 0.039 [0.991] 76 [525] 91 [625] 86-93 ...
Over 0.029 [0.737] ... 73-78
Over 0.020 [0.508] to 0.039 [0.991] incl 84-91 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 71-75
0.003 [0.076] to 0.010 [0.254] incl
H06 extra-hard Over 0.039 [0.991] 88 [605] 103 [710] 92-96 ...
Over 0.029 [0.737] ... 77-81
Over 0.020 [0.508] to 0.039 [0.991] incl 89-95 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 74-78
0.003 [0.076] to 0.010 [0.254] incl
H08 spring Over 0.039 [0.991] 95 [655] 110 [760] 94-98 ...
Over 0.029 [0.737] ... 79-82
Over 0.020 [0.508] to 0.039 [0.991] incl 92-97 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 76-80
0.003 [0.076] to 0.010 [0.254] incl
H10 extra-spring Over 0.039 [0.991] 100 [690] 114 [785] 96-99 ...
Over 0.029 [0.737] ... 80-83
Over 0.020 [0.508] to 0.039 [0.991] incl 94-98 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 77-81
0.003 [0.076] to 0.010 [0.254] incl
Copper Alloy UNS Nos. C51100, C53400, and C54400
M20 as hot-rolled Over 0.188 [4.775] 40 [275] 58 [400] ... ...
O60 soft Over 0.039 [0.991] 40 [275] 55 [380] 7-50 ...
Over 0.029 [0.737] ... 24-50
Over 0.020 [0.508] to 0.039 [0.991] incl 0-45 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 16-46
H02 half-hard Over 0.039 [0.991] 55 [380] 70 [485] 60-81 ...
Over 0.029 [0.737] ... 57-73
Over 0.020 [0.508] to 0.039 [0.991] incl 53-78 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 52-71
H04 hard Over 0.039 [0.991] 72 [495] 87 [600] 82-90 ...
Over 0.029 [0.737] ... 71-77
Over 0.020 [0.506] to 0.039 [0.991] incl 80-86 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 69-75
H06 extra-hard Over 0.039 [0.991] 84 [580] 99 [685] 88-94 ...
Over 0.029 [0.737] ... 75-80
Over 0.020 [0.506] to 0.039 [0.991] incl 86-92 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 73-78
H08 spring Over 0.039 [0.991] 91 [625] 106 [730] 90-98 ...
Over 0.029 [0.737] ... 77-81
Over 0.020 [0.508] to 0.039 [0.991] incl 86-94 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 75-79
H10 extra-spring Over 0.039 [0.991] 96 [660] 108 [745] 92-97 ...
Over 0.029 [0.737] ... 78-82
Over 0.020 [0.508] to 0.039 [0.991] incl 89-94 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 76-80
Copper Alloy UNS No. C51180
H02 half-hard Over 0.039 [0.991] 69 [475] 84 [580] 80-90
Over 0.029 [0.737] 69-75
Over 0.020 [0.508] to 0.039 [0.991] incl 78-88
Over 0.010 [0.254] to 0.029 [0.737] incl 67-73
H03 -hard
34 Over 0.039 [0.991] 80 [550] 92 [635] 84-92
Over 0.029 [0.737] 71-77
Over 0.020 [0.508] to 0.039 [0.991] incl 80-88
Over 0.010 [0.254] to 0.029 [0.737] incl 69-75
H04 hard Over 0.039 [0.991] 85 [585] 100 [690] 88-95
Over 0.029 [0.737] 74-80

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
3
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
TABLE 2 Continued
Tensile Strength,
Temper DesignationA Approximate Rockwell Hardness
Thickness, in. [mm] ksiB [MPa]
Code Name Min Max B Scale Superficial 30T
Over 0.020 [0.508] to 0.039 [0.991] incl 85-93
Over 0.010 [0.254] to 0.029 [0.737] incl 71-78
H06 extra-hard Over 0.039 [0.991] 97 [670] 112 [770] 89-97
Over 0.029 [0.737] 76-81
Over 0.020 [0.508] to 0.039 [0.991] incl 87-95
Over 0.010 [0.254] to 0.029 [0.737] incl 74-79
H08 spring Over 0.039 [0.991] 105 [725] 119 [820] 94-100
Over 0.029 [0.737] 77-82
Over 0.020 [0.508] to 0.039 [0.991] incl 92-98
Over 0.010 [0.254] to 0.029 [0.737] incl 74-80
H10 extra-spring Over 0.039 [0.991] 110 [760] 122 [840] 96-104
Over 0.029 [0.737] 78-82
Over 0.020 [0.508] to 0.039 [0.991] incl 94-102
Over 0.010 [0.254] to 0.029 [0.737] incl 76-80
Copper Alloy UNS No. C51900
O60 soft Over 0.039 [0.991] 48 [330] 63 [435] 22-66 ...
Over 0.029 [0.737] ... 35-64
Over 0.020 [0.508] to 0.039 [0.991] incl 18-63 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 25-57
H02 half-hard Over 0.039 [0.991] 64 [440] 79 [545] 70-88 ...
Over 0.029 [0.737] ... 63-76
Over 0.020 [0.508] to 0.039 [0.991] incl 65-85 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 58-72
H04 hard Over 0.039 [0.991] 80 [550] 96 [660] 89-95 ...
Over 0.029 [0.737] ... 74-80
Over 0.020 [0.508] to 0.039 [0.991] incl 86-93 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 72-78
Copper Alloy UNS No. C52100
M20 as hot-rolled Over 0.188 [4.775] 50 [345] 78 [540] ... ...
O60 soft Over 0.039 [0.991] 53 [365] 67 [460] 29-70 ...
Over 0.029 [0.737] ... 38-68
Over 0.020 [0.508] to 0.039 [0.991] incl 20-66 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 27-62
H02 half-hard Over 0.039 [0.991] 69 [475] 84 [580] 76-91 ...
Over 0.029 [0.737] ... 67-78
Over 0.020 [0.508] to 0.039 [0.991] incl 69-88 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 63-75
H04 hard Over 0.039 [0.991] 85 [585] 100 [690] 91-97 ...
Over 0.029 [0.737] ... 76-81
Over 0.020 [0.508] to 0.039 [0.991] incl 89-95 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 73-80
H06 extra-hard Over 0.039 [0.991] 97 [670] 112 [770] 95-100 ...
Over 0.029 [0.737] ... 78-83
Over 0.020 [0.508] to 0.039 [0.991] incl 93-98 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 77-82
H08 spring Over 0.039 [0.991] 105 [725] 119 [820] 97-102 ...
Over 0.029 [0.737] ... 79-84
Over 0.020 [0.508] to 0.039 [0.991] incl 95-100 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 78-83
H10 extra-spring Over 0.039 [0.991] 110 [760] 122 [840] 98-103 ...
Over 0.029 [0.737] ... 80-84
Over 0.020 [0.508] to 0.039 [0.991] incl 96-101 ...
Over 0.010 [0.254] to 0.029 [0737] incl ... 79-83
Copper Alloy UNS No. C52180
H02 half-hard Over 0.039 [0.991] 90 [620] 105 [725] 90-100
Over 0.029 [0.737] 77-83
Over 0.020 [0.508] to 0.039 [0.991] incl 93-99
Over 0.010 [0.254] to 0.029 [0.737] incl 72-81
H03 hard
34 Over 0.039 [0.991] 97 [670] 112 [770] ... ...
Over 0.029 [0.737] ... ...
Over 0.020 [0.508] to 0.039 [0.991] incl ... ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... ...
H04 hard Over 0.039 [0.991] 105 [725] 120 [825] 94-102
Over 0.029 [0.737] 78-84
Over 0.020 [0.508] to 0.039 [0.991] incl 92-98
Over 0.010 [0.254] to 0.029 [0.737] incl 77-82
H06 extra-hard Over 0.039 [0.991] 108 [745] 125 [860] 97-103
Over 0.029 [0.737] 79-85
Over 0.020 [0.508] to 0.039 [0.991] incl 96-103
Over 0.010 [0.254] to 0.029 [0.737] incl 78-84
H08 spring Over 0.039 [0.991] 115 [795] 132 [910] 98-105
Over 0.029 [0.737] 80-86

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
4
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
TABLE 2 Continued
Tensile Strength,
Temper DesignationA Approximate Rockwell Hardness
Thickness, in. [mm] ksiB [MPa]
Code Name Min Max B Scale Superficial 30T
Over 0.020 [0.508] to 0.039 [0.991] incl 98-104
Over 0.010 [0.254] to 0.029 [0.737] incl 79-84
H10 extra-spring Over 0.039 [0.991] 120 [825] 140 [965] 100 min
Over 0.029 [0.737] 82 min
Over 0.020 [0.508] to 0.039 [0.991] incl 98 min
Over 0.010 [0.254] to 0.029 [0.737] incl 80 min
Copper Alloy UNS No. C52400
M20 as hot-rolled Over 0.188 [4.775] 55 [380] 75 [515] ... ...
O60 soft Over 0.039 [0.991] 58 [400] 73 [505] 35-75 ...
Over 0.029 [0.737] ... 40-78
Over 0.020 [0.508] to 0.039 [0.991] incl 25-71 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 29-84
H02 half-hard Over 0.039 [0.991] 76 [525] 91 [625] 78-96 ...
Over 0.029 [0.737] ... 67-80
Over 0.020 [0.508] to 0.039 [0.991] incl 74-93 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 63-77
H04 hard Over 0.039 [0.991] 94 [650] 109 [750] 94-101 ...
Over 0.029 [0.737] ... 78-82
Over 0.020 [0.508] to 0.039 [0.991] incl 92-100 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 75-81
H06 extra-hard Over 0.039 [0.991] 107 [740] 122 [840] 98-103 ...
Over 0.029 [0.737] ... 80-84
Over 0.020 [0.508] to 0.039 [0.991] incl 97-102 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 79-83
H08 spring Over 0.039 [0.991] 115 [795] 129 [890] 99-104 ...
Over 0.029 [0.737] ... 81-85
Over 0.020 [0.508] to 0.039 [0.991] incl 98-103 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 80-84
H10 extra-spring Over 0.039 [0.991] 120 [825] 133 [915] 100-106 ...
Over 0.029 [0.737] ... 82-86
Over 0.020 [0.508] to 0.039 [0.991] incl 99-104 ...
Over 0.010 [0.254] to 0.029 [0.737] incl ... 81-85
A
Standard designations defined in Classification B601.
B
ksi = 1000 psi.

designations and the standard designations as defined in 10.1.4 The tension test specimens shall be taken so the
Classification B601 are shown. longitudinal axis of the specimens is parallel to direction of
rolling.
NOTE 3The properties of special and nonstandard tempers are subject
to agreement between the manufacture and purchaser. 10.2 Rockwell Hardness:
8.1.3 O60 (Annealed)The standard temper is O60 (soft), 10.2.1 The approximate Rockwell hardness values given in
as indicated in Table 2. Table 2 are for general information and assistance in testing,
and shall not be used as a basis for product rejection.
9. Grain Size of Annealed Tempers NOTE 4The Rockwell hardness test offers a quick and convenient
9.1 Other than O60 (soft) temper, as indicated in Table 2, method of checking for general conformity to the specification require-
annealed tempers are special, and the material shall conform to ments for temper, tensile strength, and grain size.
grain size requirements agreed upon between manufacturer and
11. Other Requirements
purchaser as defined in Classification B601.
11.1 Purchases for U.S. Government AgenciesWhen iden-
10. Mechanical Property Requirements tified in the contract or purchase order, product purchased for
10.1 Tensile Strength Requirements: agencies of the U.S. Government shall conform to the special
10.1.1 Product furnished under this specification in inch- government requirements stipulated in the supplemental re-
pound units shall conform to tensile requirements prescribed in quirements given in Specifications B248 and B248M.
ksi units in Table 2, when tested in accordance with Test
Methods E8/E8M. 12. Dimensions, Mass, and Permissible Variations
10.1.2 Product furnished under this specification in SI units 12.1 The dimensions and tolerances for product described
shall conform to tensile requirements prescribed in MPa units by this specification shall be as specified in Specification B248
in Table 2, when tested in accordance with Test Methods and B248M with particular reference to the following tables
E8/E8M. and related paragraphs.
10.1.3 Acceptance or rejection based upon mechanical 12.1.1 Thickness:
properties shall depend only on the tensile strength. 12.1.1.1 TolerancesSee Table 1.

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
5
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
12.1.2 Width: 13.1.3.2 When sampled from the semi-finished product, at
12.1.2.1 Tolerances for Slit Metal and Slit Metal with Rolled least one sample shall be taken to represent each 10 000 lb, or
Edges. fraction thereof, except that not more than one sample shall be
12.1.2.2 Tolerances for Square-Sheared Metal. required per piece.
12.1.2.3 Tolerances for Sawed Metal. 13.1.3.3 Only one sample need be taken from the semi-
12.1.3 Length: finished product of one cast bar from a single furnace melt
12.1.3.1 Tolerances for Straight Lengths. charge continuously processed.
13.1.3.4 When the material is cast in the horizontal continu-
12.1.3.2 Schedule of Minimum Lengths with Ends.
ous casting mode, at least one sample will be taken to represent
12.1.3.3 Tolerances for Squared-Sheared Metal.
the composition of the holder per cast coil.
12.1.3.4 Tolerances for Sawed Metal.
12.1.4 Straightness: 14. Test Methods
12.1.4.1 Tolerances for Slit Metal or Slit Metal Either 14.1 Chemical Analysis:
Straightened or Edge-Rolled. 14.1.1 In case of disagreement, test methods for chemical
12.1.4.2 Tolerances for Squared Sheared Metal. analysis shall be subject to agreement upon between the
12.1.4.3 Tolerance for Squared Sheared Metal. manufacturer or supplier and purchaser. The following table is
12.1.5 Edges: a list of published methods, some of which may no longer be
12.1.5.1 Tolerances for Radius of Square Edges. viable, which along with others not listed, may be used subject
12.1.5.2 Tolerances for Radius of Rounded Corners. to agreement:
12.1.5.3 Tolerances for Radius of Rounded Edges. Element Test Method

12.1.5.4 Tolerances for Radius of Full-Rounded Edges. Copper E478

Iron E75 (AA)
Lead E478 (AA)
13. Sampling Phosphorus E62
Tin E478 (Photometric)
13.1 Chemical Analysis: Zinc E478 (AA)
13.1.1 The sample for chemical analysis shall be taken from
14.1.2 Test methods(s) used for the determination of ele-
the pieces selected and combined into one composite sample in
ment(s) required by contractual or purchase order agreement
accordance with Practice E255 for product in its final form.
shall be as agreed upon between the manufacturer and the
The minimum weight of the composite sample shall be 150 g.
purchaser.
13.1.2 Instead of sampling in accordance with Practice
E255, the manufacturer shall have the option of taking samples 15. Keywords
at the time the castings are poured or by taking samples from 15.1 copper-tin alloy plate; copper-tin alloy rolled bar;
the semi-finished product. copper-tin alloy sheet; copper-tin alloy strip; copper-tin-lead
13.1.2.1 When composition of the material has been deter- alloy plate; copper-tin-lead alloy rolled bar; copper-tin-lead
mined during the course of manufacture, sampling of the alloy sheet; copper-tin-lead alloy strip; copper-tin-lead-zinc
finished product by the manufacturer is not required. alloy plate; copper-tin-lead-zinc alloy rolled bar; copper-tin-
13.1.3 The number of samples to be taken for determination lead-zinc alloy sheet; copper-tin-lead-zinc alloy strip; copper-
of chemical composition shall be as follows. tin-lead-zinc-iron alloy sheet; copper-tin-lead-zinc-iron alloy
13.1.3.1 When sampled at the time the castings are poured, strip; UNS No. C51000; UNS No. C51100; UNS No. C51180;
at least one sample shall be taken for each group of castings UNS No. C51900; UNS No. C52100; UNS No. C52180; UNS
poured from the same source of molten metal. No. C52400; UNS No. C53400; UNS No. C54400

SUMMARY OF CHANGES

Committee B05 has identified the principal changes to this specification that have been incorporated since the
2010 issue as follows (Approved May 15, 2015):

(1) Rewrote Sections 1, 3, 4, 5, 6, 7, 8, 10, 12, and 15 to (2) Changed the nominal zinc value in 1.1 from 4 to 3.
incorporate the format of Guide B950.

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
6
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.
 B103/B103M 15
ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentioned
in this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the risk
of infringement of such rights, are entirely their own responsibility.

This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years and
if not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standards
and should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of the
responsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you should
make your views known to the ASTM Committee on Standards, at the address shown below.

This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,
United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the above
address or at 610-832-9585 (phone), 610-832-9555 (fax), or [email protected] (e-mail); or through the ASTM website
(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222
Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http://www.copyright.com/

Copyright by ASTM Int'l (all rights reserved); Thu Jun 23 10:52:43 EDT 2016
7
Downloaded/printed by
Pontificia Universidad Catolica del Peru (Pontificia Universidad Catolica del Peru) pursuant to License Agreement. No further reproductions authorized.