DINXENGLISH 239L4PT*2 94 MM 279444 0038557 222 Me DEUTSCHE NORM, Seamless precision steel tubes Technical delivery conditions tes 23.040.10 ‘Supersedes July 1987 edition. Descriptors: Tube, stee! tube, precision tube, technical delivery conditions, Nahtlose Prazisionsstahirohre (mit besonderer Mafigenaugkelt); technische Lieferbedingungen In keeping with current practice in standards published by the International Organization for Standerdization (ISO), a ‘comma has been used throughout as the decimal marker. Dimensions in mm 1 Scope and field of application 1.1._This standard specifies technical delivery conditions {or cold finished seamless precision steel tubes of the di- Mentions iste in DIN Za¥1 Part 1, which are made from the steel grades listed In clause 4, Such tubes are mainly used where accuracy to size and, possibly, a smal! wall thickness, a particular surface condi- tion and specific mechanical properties are required, 4.2 This standard does not cover: = seamless circular unalloyed steel tubas subject to ‘special requirements (cf. DIN 1623}: = high performance seamless circular unalloyed steel tubes (cf. DIN 1630} ~ seamless circular steel tubes for structural steelwork (cf. DIN 17121); ~ swarntess circular fine grain steel tubes for structural ‘steolwork (ef. DIN 17124), = seamless circular tubes made from steel with low= temperature toughness (cf. DIN 17173), seamless tubes made from steel with elovated tam- porature properties (el. DIN 17170}, = seamless circular fine grain steel tubes subject to ‘special requirements (ef. DIN17 179), = seamless circular tubes made from steel for quench- Ing and tempering (cf DIN 17204), = seemless circular austenitic stalntess steel tubes subject to special requirements (cf. DIN 17458), = stesl pipes for conveying combustible liquids and (ases (cf. DIN 17172). Subject to agreement, tubes of dimensions speciiad in IN 2901 Part 1 and in compliance with one of the stand ards listed above may be ordered in quality grade C, 2 Quality grades ‘Tubes shall be supplied in the following quality grades: Copyright by the DIN Deutsches Insti Pur Normung KV Hed Sep 14 09:15:21 2005 {or precision steel tubes. that do not raquira an inspac- tion cerifcato and thus are not subject to special re quirements, grade A; for precision steel tubes subject to epecial require- ments, grade C. In accordance with the stated demands of the purchaser. ‘such special requirements and the relevant test methods shall be the subject of agreement. Table 10 lists possible additional raquieamante (lor grade C). 9 Order details and options ‘The following information shall be supplied by the pur- chase 2) the quantity, in metres; ) a reference to this standard; ©) the quality grade; 4d) the steal grad ©) the final supply condition; 4) the outside and inside diameters, or, where relevant, the outside diameter and wall thickness or inside dian eter and wall thickness; 9) the type of tube length to be supplied: h) any inspection document agreed upon. Designation for 100m seamless precision st made of 6136 ctec!, normalized (NBK) az specitied In DIN 2991 Part 1, of quailty grace ©, with an outside dlam- ter, D, of 100 mm and an inside diameter, D,, of 94 mr, in lexact iengins of 4000 mm, with type 3.1.8 iepection cer tificate as specified in DIN 50049: 1000 m tube DIN 2391 -C-St 35 NBK- 100 x 1D 94 x 4000- 3.1.8 Continued on pages 2 to 8. ‘September 1994DIN*ENGLISH 2392¥PT#2 Page2 DIN2301 Part? Unless otherwise specified, tubes shall be supplied In qual- ity orade A and in lengths as specified in subclause 9.3. 4 Materials ‘The tubes shall be manufactured from electric steel or ba~ sie oxygen stool, the melting and casting processes being at the discretion of the manulacture. 94M 275444b 0038558 bo a 5 Chemical composition 6.1 Ladle analycie ‘The chemical composition of the steels dealt with in this standard shall be as specitiag in table 2. Small departures, from these specifications are permissible i they do not impair the performance of the steel. 5.2 Product analysis When a product analysis is carried out on finished tubes, the permitted deviations given in table 3 shail apply to the ‘The steal shall be cast as killed steel, Table 1 lists rolevant Stee! grades. ladle analysis specified in table 2, Table 1: Steel grades ‘Steal grade Previous designation used JQvalty grade) ae in DINEN 10027Pankt | _as In PINFN1N027 Part? in Germany ‘s21sGsiT 1.0211 $1301 Sz15GAIT so2t2 8t30Al A s23sG2T 1.0308 St35 ‘S255CT 10408 Stas, ‘S355GT 11.0580 152 c ‘Al grades as for quality grade A, and any other steel grades. ‘Table 2: Chemical composition of steel grades shown on ladle analysis 1emical composition, a wentage by mass ‘toe! grade Chemical composition, as @ percentage by ce si Me Pp s symbol | Material number max ma max ma. 3081 1.0219 010 0380 =055 (0025) (0025) t30 AL 1.0212 010 005) S055 0.025 0025) St35) 1.0908 047, 035) 2040 0025 0025 345 1.0408 zt 035 S040 0035 0025 S152 1.0580 022 055 51,60 0925 0.925 | “The folowing alloying elements may be added: Nb: < 0,08 %; Ti: $0,039; V: $0,05%; Nb + Ti+ V: $0.05%. ‘Table 3: Permitted deviations of the product analysis from the specified ladle analysis Element Permitted deviation trom the specified limits of the adie analysts, a9 a percentage by mace +002 +003 +008 or -006 +0,005 +0005 +001 =|gz]o|~|z|2/o Copyright by the DIN Deutsches Insti Pur Normung KV Hed Sep 14 09:15:35 2005 +001 +002DINXENGLISH 2394*PTx2 94 MM 279444b 0038559 OTS Ml 6 Final supply conditions “Tubes are to be supplied in one ot te conditions specitied in table 4 7 Mechanical properties 7.4. Tho mechanical propertioe are a function of the final ‘supply condition (ef. table 4) and shall comply with table 6. 7.2. When tested a¢ desoribed in euboiauese 10.2.2.2 ang 40.2.2, tubes shall show no cracks. DIN 2391 Pan2 Pages 7.3. In the case of steel grades andlor final supply condi- tions other than those specified in tables 2 and 4. the re- ‘quired mechanical properties shall be subject to agree- ‘ment. Such tubes shall be supplied in quality grade C. 7.4 On the basis of their cnemical composition and the \ay they have been processed. the steels listed In table 2 are to be regarded as weldabie. It should, however, be ‘otad that the mechanical properties of tubes in the BK, BKW or BKS condition are modified in the zone of the tube ‘which has been subjected to heat (c. DIN 8528 Part 1). ‘Table 4: Final supply conditions Designation ‘eymbet Description (Cold finished (hard) BK ‘Tubes do not undergo heat treatment following the final cold forming and, thus, nave a rather high resistance to detormation. Cold finished (sort) BKW | The final heat treatment is followed by cold drawing involving limited deformation. Appropriate further processing allows. certain degree of cold forming (e.g. bending, expanding). Cold finished ana BKS | Heat treatment is applied following the last cold forming process. Subject to stress-rolieved appropriate processing conditions, the increase in the residual stresses involved enables both forming and machining to a certain deares. “Annealed G8K | The last cold forming process is followed by annealing in a controled atmosphere. Normalized NBK | The last cold forming process is followed by annealing above the upper transformation point in a controled atmosphere. ‘Table 5: Mechanical properties of tubes at ambient temperature et supp condition] Cold finished | Cold finished | Cold finished and | Annealed Normalized (NBK) (hard) (BK)") | (sont) (BKW))) | stress-relieved (BKS) | — (GBK)") formalized (NBK) Steel grade Me, Wn, i, Mn. in, Mn [elonge-} win. | donge-| mir. | Min | atnge-| Mir. | eoras-| renayy | Mme | eonge Material | syateat | 25% | tne | tesie | enat | tormie | yits | tonat | teste | tonat | Je vied | tonat ‘docig- | Mateo |eargi| tact, |erengin|tactun| erengey| event ones, | tac ration Ryn | Ajasa| Rain [Ayara| Ron | Raplt Raia |Apae Nin |percent-| Nin | percent] Win? | Nim? Nina? | percent saosi | razr | 430 | 8 | 380 | 12 | 380 | 250 290 toazo| 215 | 30 siaom | saziz | 430 | 8 | 380 | 12 | 50 | 200 | 16 | 280 | a0 | 200t04m| 215 | 90 | | | sas | 1308 | 40 | 6 | 420 | 1 | 420 | a5 | 14 | 318 | 25 | sato470| 235 | a5 sas | ina | sao | s | so] @ | sao | as | a2 | a0 | 2 | a4ntnsro| 255 | 21 sisz | 10580 | 640 | 4 | 520 | 7 | s90 | 420 | 10 | 490 | 22 | as0tosm| 55 | 22 +) The yield strength for the annealed (GBK) condition shall be equal to atleast $0% of the tensile strength. Depending (on the extent of deformation, the yield strength of tubes supplied in the cold finished (hard) (BK) and cold finished (soft) (GKW) conditions, may come close to reaching the tensile strength. Calculations should be based on a minimum value (f 80% of the tensile strength for the cold finished (hard) condition and of 70% for the cold finished (sot) cont ) For tubes with an outside dlamater of up ta 30 mm and 2 wall thickness up to 2.mm, the minimum yild strength may be 10 Nim? lowe Copyright by the DIN Deutsches Insti Pur Normung KV Hed Sep 14 09:15:36 2005DINXENGLISH 2393xPT#2 94 MH 2794446 0038560 617 ml Page4 DIN2991 Part 2 8 Appearance 8.1 Tubes shall have a smooth internal and external sur- face consistent with the cold working process. As a result, the arithmetical mean deviation of the profile, R,, will Be 6.3 um of less. Lower R, values shall be subject fo agree- rent for quality grade C tubes. NOTE: For wutwical reasons, It Is not alwayo poe jbo to obtain a smooth surface on tubes with an internal diameter of less than 15 mm, 8.2 Slight surface Imperfections such as scabs or ‘gouges, resulting from the manufacturing procece, are por- mitted provided the Inner and outer diameters, after dress- ing, continue to meet the specified requirements. Scabs, Taps or laminations are not permitted. It freedom from imperfections is of particular significance, an appropriate non-destructive test method (such as eddy Current oF ultrasonia testing) shall be agreed (ct. subclause 10.2.2.) 8.3 Asaresultof cold working, tubes that have not uncer- ‘done heat treatment, i.e. tubes Inthe BK or BKW concition, fre generally covered by a kbricant or grease flm on their inner anc outer surfaces. An agreement shall be made con- corning its removal ‘Tubes that have undergone heat treatment, ie. tubes in the BK, GBK of NBK conaition, may show signs of scorching, Dut snail De tree of ose sca. 18.4 Where, with rogard to cubsaquent surace treatment {such 2s galvanizing), special requirernents are to be met concering the surlace preparation grade of tubes, such fFequiroments shall be agreed upon at the time of ordering, 1&5. In compliance with commercial practice, the tubes shall De supplied with provisional corrosion protection. Ifa particular form of corrosion protection (e.g. galvanizing as Specified in DIN 80060 Part}, or none whatsoever, Isr ‘quested, this shall be stated in the order. 9 Dimensions and limit deviations 9.1 Diameter and wall thicknesses DIN 2391 Part 1 shall apply for the dimensions of seamless precision steel tubes. it one of the mit deviations for the diameter isto be 200, the limit doviation for the wall thickness shall be equal to 410% of the mean wall thickness calculated using the for- ‘muta given in clause 2 Of DIN 2981 Part + 9.2 Straightnesss ‘Tubes with an outside diameter exceeding 15 mm shall not deviate trom straightness by more than 0,259 ofthe total fengin, Tubes witn a ytd strength greater than 500 Nimm2 shall not deviate from straightness by more than 0,3% of the total length. Localized deviations shall not exceed Smm/m and shall be measured a6 the cistance between the tube surface and a chord linking two random points 1000 mm apart. ‘Tubes of exact lengths shall nt deviate from straightness ‘by more than 0,3% of the tube length. In compliance with commercial practice, tubes with an ‘outside diameter of up to 15 mm shall be supplied straight ened. As establishing the straightness of such tubes might prove to be aficul, tne stralghiness measuring procedure Shall be subject to agreement, More stringent requirements regarding straightness shall bbe subject to agreement and shall apply for quality grade C tubes. Copyright by the DIN Deutsches Insti Pur Normung KV Hed Sep 14 09:15:36 2005 9.3 Lengths Uniess ulerwise specified by the purchaser atthe time of ordering, tubes shall be supplied as random lengths be- ‘tween 4m and 7 m. “The number of tubes in lengths from 2 m to below 4 m shall not exceed 15% of the quantity ordered and shall be sup- plied in separate bundles. Cut lengths shall allow for deviations of + $00 mm of the length ordeted, short langths of 2000mm or more being SUpplod in separate buncles up ‘0 a maximum of 10% of tho quantity ordered. Exact lengths are aubject to the following limit deviations: for lengths up to 500 mm: 3 mm; {or lengths above 500.mm up to 2000 mm: "3 mm: for lengths above 2000 mm up to 5000 mm: °} mm; for lengths above 5000 up to 700mm: “"3 mm. For lengths areator than 7 000 mm, limit deviations shall be subject fo agreement. 9.4 Tube ends ‘Tube ends shall be cut nominally square to the tube axis and chall be fre from excessive burrs, as may result trom ‘tha cutting process. Such burrs may cause a change in diameter, exceeding the limit deviations specified in Bin 2391 Pert 7 ‘Agreement regarding the finishing of ends of tubes of exact length ie mandatory. 9.8 Divergence between quantity ordered and consignment Where tubes of exact length have baon ordered, deficient ‘supplies shall not ba permitted. However. excess supplies hall be permissible in compliance with the specifications, siven in table 7 Table 7: Excess supplies ‘Quantity ordered, Percentage deviation in metres Up to 500 +20 ‘Above 500 up to 2000 +18 ‘Above 2000 +10 10 Testing 40.1. Tubes to be cuppliod without inepection document (quality grade A) {As part of internal control, the manufacturer shall submit tubes to: ) a dimensional check; ) a surface inspection; ©) a tensile test, as specie’ In DIN EN 10002 Part 1; 49) a flattening test, as specified in DIN EN 10293: «@) a drift expanding test, as specified in DIN EN 10234. Fiattening and ofift expanding tests shall only be carried ‘out on annealed or normalized tubes made of the steel ‘grades listed in table 2 i testing doos not adversely affect the tube diameter and wall thickness. ‘Subject to agreement, a type 2.2 inspection document in ‘compliance with DIN 50049 shail be issued. ‘Additional tests snail be subject to agreement. They are relevant for quality grade C steels.DIN*ENGLISH 239%*PTx2 94 MM 279444b 0038563 753 Ml 10.2 Tubes to be supplied with inspection document (quality grade C) ‘Should a DIN 50049 inspection certificate be required for quality grade C stee! tubes, this shal be agreed upon at the time of ordering. The order shall state the type of document requested and the name the testing agoncy if the inspaction 's carried out by a third party Tubes shall be tested at the manufacturer's works. Produc- tion shall not be unduly disturbed if inspection is cared out by experts who are not employed by the manufecturer 10.2.1 Scope of testing ‘Tubes shall be tested by batches. For dotalls, soe table 9 For the purpose of testing, tubes shall be divided according to steel grade, tinal supply condition and size, nto batches each comprising 200 units. Remainders of up to 20 units may be dietnbuted unitormly acrose the other Datchas, Femainders ranging {rom 20 to 200 units and consignments of less than 200 units being considered a whole batch, 10.2.2 Procedure Ail tests shail De carried out at ambient temperature. 40.2.2:1 Tensile toot ‘The tensile test shall be carried out as specified in DIN EN 10002 Part 1. 10.2.2.2 Flattening test ‘The ftattoning test shall be carmied out, as specified in DIN EN 10233, on annealed and normalized tubes, the wall thickness of which s less than 1596 of the outside diam- eter. The test pleces or tube ends shall be flattened until a specified distance between platens, H, is reached. This distance, in mm, is to b@ calculated on the basis of the following equation: y -fteheT 7 oD where. Tis the wall thickness, in mm: D_ 1s the outsice diameter of tne tube, n mm: € {is a constant, which is 0,09 for steel grades ‘St 30 and St 35, and 0,07 for steel grades St 45 and St62. ‘After testing, the samples shall be inspected for cracks. Table 8: Percentage expansion Percentage expansion for a Stee! grade | "M8! SUPP | wall thickness, in mm, of upto4 | above s 313051 20 16 St30A1 | Nonmalizes | 20 15 stas_ for 18 2 tas annealed 8 10 st52 6 10 Copyright by the DIN Deutsches Intl Pur Normung KV Hed Sep 14 09:15:37 2005 DIN 2991 Part2 Pages 10.2.2.3 Dnt expanding test Tne orit expanaing test snail be conductea until ine max!- ‘mum expansion specified in table Bis reached. It shal be Cartied out, as described in DIN EN 10234, on annealed ‘and normalized tubes with a maximum outside diameter of 150mm and a wall thickness of up to 9 mm. ‘Attor ecting, tho camples shall be inapeoted for oracke. 10.2.2.4 Moasurement of surface roughness ‘The surface roughness shall be measured axially by using electric stylus instruments as specified in DIN 4768. 0.2.2.5 Dimensional check ‘The tube dimansions shall be measured with niques. ‘The type and scope of the dimensional checking of tubes of length shall be subject to agreement table tech- 10.2.2.6 Surface inspection ‘The appearance of the outer and, if possible, inner tube ‘surtace shall be examined visually under appropriate light- ing conditions by an ingpector having normal vision. agreed, another method of checking the appearance may hha aise ‘The type and scope of surface inspection of tubes of exact length shall be subject to agreement. 10.2.2.7 Leak tightness test ‘The tubes shall be tested for leak tighiness by using appro~ priate non-destructive test methods (e.g. eddy current {esting in accordance with Stah/-Eisen-Prifolat (iron and ‘steal testing epectication) 1926"), 10.2.0.6 Non-deotructive testing If freedom from imperfections is of particular significance, eddy current testing as specified in PRP 02-74 may be car- Tied out, primariy to detect transverse defects. The ultra- sonic test, as specified in StaMi-Eisen-Profolatt 1915, is Usually conducted to detact longitudinal detects 10.2.3 Retests 0.2.9.1 Tubes not satisfying the requirements when tested as specified n subclauses 10.2.2.1 to 10.2.2.3 shall bbe rejected. Two further tubes shall be taken rom the batch ‘concemed in place ofthe rejected sample tube and submit- ted for testing. If one of these two tubes does not fulfil the requirements, vie entire Darcn sna De Consigered not to comply with the standard 10.2.3.2 Ifthe detects or deficiancies established can be made good by means of heat treatment or other suitabh ‘measures, the supplier shall be given the opportunity to present a batch which was rejected for renewed accept- ance inspection. If the test pieces stil fall to satisfy the Fequirements, the entire batch shall be considered not to ‘comply with the standara 10.3 Inspection documents ‘The inspection documents to be issued shall comply with DIN 50049,DINKENGLISH 23924PT#2 94 MM 279444b 0036562 bIT Page6 DIN2301 Part2 Table@: Scope of testing ho] Type of test or inspection | °%,Su0- Scope of testing?) Responsible fr tectng 1 | Tensie test 10.221 | One esl pecs, laken Kom ove sample tube per | Subject to agreement. fateh 2 | Fitting west 1022.22 | One esi pace taken alone ond ofcample te | Subject fo agreement Spoctes under tem No. Dat oxpancng wat | 1022.8 | One tex pice taken at one end of ample ube | Subject to agreoment specitied under item No. 1. 4 | Measurement of surface | 10.2.2.4 | If agreed upon, one test piece taken from one | Manufacturer roughness sample tube specified under iter No.1 5 | Dimensional check 102.25 | All tubes. ‘Subject to agreement 6 | Surface inspaction 10.22.6 | a tubes. ‘Subject to agreement 7 | Leak tantness test 1022.7 | agreed, all tubes Manufacturer @ | Non-dostructive test 02.2.8 | W agreed, all tubes Manufacturer 7) Applies to random lengths and multiples of cut and exact lengths. 11 Quality grade C ‘Table 10: Special requirements (examples) Line ‘Special requirement Features and/or technical devary conditions 7 | Stee! grades other than speci’ | As specified n DIN 1651, DIN EN 10025, DINEN 10089 Parts t and 2, or fied in table 1 BIN 17240. 2 _| Tubes for pipelines. ‘As specified in DIN 1628, DIN 1690, or DIN 2445 Part 2 ‘3 | Other geometry and surface. | Tubes with an outside clameter smaner than 4mm an greater than 260 mm. with a non-circular cross section, subject to other tolerances than those specified in DIN 2391 Part 1, other tolerance positions or special Tequirements regarding the surface condition, straightness end squareness of pipe ends. 4 | Final supply concition other | Tempered; annealed to obtain specie microstructure. than specified in table 4. | Other mechanical properties. __| Deviations regarding the mechanical properties specified in table 5. 42. Marking 13 Bundling ‘A durable tag, containing the following information, shallbe The type of bundling shall be subjact to agreement. securaly attached to each bundle: ) the manufacturer's mark; ») the relevant standard (technical delivery condition) and quality grad ©) steel grade, in compliance with table 1; 14 Complaints 4) tna final snl eondton, i accordance wih t& yarany claims may ont bo alaod i baced onthe techni le; cal delivery conditions specified here or on any further «) the dimensions: agreement. - Y tans f) the inspector's mark, where tubes are suppiea win The purchaser shall glve the supplier the opportunity ot an ingpestion document. judging whether the complaints justified, by submitting the Further markings shal be suibject to agreement. tube objected to and sampies of the other tubes supplied. Copyright by the DIN Deutsches Inti Pur Normung KV Hed Sep 14 09:15:37 2005DIN¥ENGLISH 239%"PTx2 94 MM 279444b 0038563 526 Ml DIN 2391 Part2 Page7 Standards and documents referred to DIN 1630 DIN 1651 DIN 2991 Part 1 DIN 2485 Part 2 IN 4768 DIN 8528 Part 1 DIN 7121 DIN 17124 DIN 17172 DIN 17173 IN 17175 DIN 17178 DIN 17204 bin 17210 DIN 17458 DIN 50049 DIN 50960 Part 1 DIN EN 10002 Part 1 DINEN 10025 DIN EN 10027 Part + DIN EN 10027 Part2 DIN EN 10089 Part + DIN EN 10083 Part2 DIN EN 10.292 DIN EN 10234 ‘Stahi-Eisen-Prafblatt 1915") ‘Stahi-Eisen-Profblatt 1928 PRP 02-74") ‘Seamless, cheulir, unalloyed steel pipes subject o special requirments; Ueclmival delivery cconditir High performance seamiess, circular, unalloyed stee! tubes; technical delivery conditions Free cutting steel; technical delivery conditions ‘Seamless precision steel tubes; dimensions ‘Seamless precision stee! tubes subject to fatigue loading, rated fora pressure of 64 to 400 bar Determination of surface roughness parameters R,, R,, and Ry, using electric styk monte; conospte and meacuring conditions ‘Weldabilty of metalic materials; concepts ‘Seamless circular steel stubes for structural stee\work; technical delivery conditions ‘Seamless circular fine grain steel tubes for structural steelwork; technical delivery conditions ‘Steel pipes for conveying combustible liquids and gases; technical delivery conditions ‘Seamless circular tudes made from steel with low temperature toughness; technical delivery conditions Seemiess tubes with elevated temperature propertioe; technical delivery conditions ‘Seamless circular fine grain steel tubes subject to special requirements; technical delivery conditions ‘Seamless circular tubes made trom steels for quenching and tempering; technical detivery conditions, ‘Case hardening steel; technical delivery conditions Seamless circular austenitic stainless steel tubes cubject to special requirements; technical delivery conditions Inspection documents for the delivery of metalic products Electroplated and chemically applied coatings; designation and information in technical ‘documentation ‘Toneilo testing of metalic materiale; method of test at ambient temperature (including Amend- ment AC 1:1380) Hot rolled unalloyed structural steel products; technical delivery conditions (including ‘Amendment At:1293) Designation systems for steel; steel names and principal symbols, Designation systems for steel; numerical system ‘Quenched and tempered steels; technical devery conditions for special atest ‘Quonched and tempered steels; technical delivery conditions for unaloyed quality steets Lotallie material; the: flattening tast Metallic materials; tube; drift expanding test Uttraschalprifung auf Langsfenler von Rohren aus warmfeston Stahien (Utrasonic testing for longitudinal imperfections in steel tubes with elevated temperature properties) -Elektromagnetische Prifung von Rohren zum Nachwels der Dichtheit (Eddy current testing of tubes for leak tightness) Prifelat for dle Wirbelstromprofung von Prézisionsstahlrohren (Specification regarding the ‘eddy current tasting of seamless precision steel tubes) instru Other relevant standard DINEN 10021 General technical delivery conditions for steel and iron products Previous editions DIN 2391 Part 2: 1940-06, 1957-11. 1967-07. 1981-07. >) Obianabie trom Fachvereinigung Prazisionsronrwerke e.v. Posttach 30 03 64, D-40403 Dusseldort. ~) Obtainable trom Voriag Stahicisen mbH, Posttach 10.61 64, D-40042 Dasseldort Copyright by the DIN Deutsches Inti Pur Normung KV Hed Sep 14 09:15:37 2005DINKENGLISH 23924PT#2 94 MM 2794445 OO38Sb4 4b2 Ol Pages DIN 2391 Pat? Amendments In.comparsson wan the July 1981 edtion, this standard has been revisud i fur ar substance and Une following amendments made: ‘) Quality grade 8 has been dropped and grades A and C redefined. ») The outside diameter, the Inside diameter and the wal thickness have been referred to as D, D,, and T, respectively, and the order details changed accordingly. ©) The use of SM steel and unkilea casted stee! 1s no longer specitiea ror precision steel tubes. 1) Grade C tubes may be made from other steels if these are sultable (ct. table 1) «@) In table 2 the maximum permissible P and & contents were brought into ine with the etate of the art and the adiition, ‘of further alloying elements specified. {table covering permite deviations of he produ! anaiis rom he specie ase aaj as been includ {) The BKS ‘cold formed and stress-rellet annealed’ condition has been included and the descriptions provided for the ‘other final supply conditions amended. hn) Mechanical properties of tubes in the BKS condition have been specified and the minimum values regarding the tensile strength for BK and BKW conditions increased. |) The specifications for surface appearance have been completely revised. |). With regard to deviations from straightness, a distinction has been made between localized deviations and deviations ‘tony the entire tube length, kk) Random lengths have been limited to a range between 4m and 7 m. 1) The requirements for tube ends have been amended. im) Specifications regarding divergence between the quantity ordered and the actual consigament now apply to orders, for exact lengths only 1) Leak tightness tests are no longer specified for qualily grade A tubes. if delivery conditions require leak tigntness, tubes shall be supplied in quality grade C. 16) A table covering the ecope of tasting hae bean included (et. table 9) 8) Th esirements roaring he periomance of est pipes submited to attening an ct expanding tests have been amended q) The procedures regarding surface roughness measurement, dimensional checks and surface inspections, as well as leak tightness tests and non-destructive testing have been altered. International Patent Classification F 18 L 009/02 Gor B02130 @.01 Noss/20 Copyright by the DIN Deutsches Init Pur Normung KV Hed Sep 14 09:15:36 2005