Data sheet

ACH9019

SEALED NICKEL METAL HYDRIDE

RECHARGEABLE CELLS & BATTERIES

1. SCOPE
This specification governs the performance of the following Enix Energies Nickel-Metal Hydride Cell and its
stack-up batteries.
Cell size : 1,2V
IEC designation : HR6

The data involving nominal voltage and the approximate weight of stack-up batteries shall be equal to the
value of the unit cell multiplied by the number of unit cells in the battery. For example, a stack-up battery
consists of 1 unit cells:
Nominal Voltage of unit cell = 1.2V
Thus, nominal voltage of stack-up battery = 1.2V×1 = 1,2V

2. RATINGS.

Type Rechargeable Nickel Metal Hydride Cylindrical Cell

Nominal Voltage 1,2V
Nominal Capacity 2000 mAh
Minimum Capacity 1900 mAh when discharged at 0.2C to 1.0V at 20
Standard Charge 200 mAh (0,1C) for 16 hrs at 200C
Charge termination control recommended : 950 mAh
Fast Charge Control parameters: -△V = 0-5mV
0
DT/dt** : 0.8 C/min(0.5 to 0.9C) // 0.8-1/min
Trickle Charge 57 mAH (0.03C)～ 95 mAh (0.05C)
Service Life ＞500 cycles (IEC standard)
Continuous Overcharge 190 mAh maximum current for 1 year
Internal Resistance Average 50 mΩ upon fully charged at 1000HZ
Max. Charging Voltage 1,5V at 190 mAh charging
Discharge Cut-off Voltage 1V
Max. Discharging current 5700 mAh ( 3C)
Standard Charging : 0 to 45℃
Ambient Temperature Range Fast Charging : 10 to 40℃
Discharging : -20 to 60℃

Temperature range for storage: Within 1 year : -20 to 35℃

﹪)
(Humidity: 65 ± 20﹪ Within 6 months : -20 to 35℃

05/12/2007 ACH9019 Page 1

 Data sheet

3. PERFORMANCE

Unless otherwise stated, tests should be done within one month of delivery under the following conditions:

Ambient Temperature, Ta : 20±50C

Relative Humidity : 65±20%

Standard Charge/Discharge Conditions:

Charge : 190 mAh (0.1C)×16hrs
Discharge : 380 mAh (0.2C) to 1.0V/cell

Test Unit Specification Conditions Remarks

Up to 3 cycles are
Capacity mAh ≥1900 Standard Charge/Discharge
allowed

Open Circuit Within 1hr after standard

V ≥1,25 Unit cell
Voltage (OCV) Charge
Internal
mΩ ≤50 Upon fully charge (1kHz) Unit cell
Impedance (Ri)
Standard charged, stored for 6
85 % capacity min. months below 20°c, then standard
discharge to 1,0V
Self - discharge mAh
Standard charged, stored for 1 year
80 % capacity min. below 20°c, then standard
discharge to 1,0V
No leakage or 190 mAh (0.1C) charge
Over-charge N/A
explosion for one year

After discharge, be
Over-discharge N/A conducted with constant 80% original capacity
load resistor 8 for 3 days.

Accelerated Cycle Charge : 400mA (0.2C) Cycling Charging

Life Discharge: 400mA(0.2C) Cutoff condition:
Cycle ≥200 To 1.0V/cell -∆V=5-10mV/cell or
End-of-life: 80% nominal Timer Cutoff=105%
Capacity. Of input capacity

Change of voltage :
Standard charge. Then leave
Should be under
for 24 hours, check cell
0,02 V/ cell
before/after vibration.
Vibration Resistance N/A Unit cell
Change of
Amplitude:1.5mm
impedance :
Should be under Vibration:3000CPM
5 milli-ohm/cell.

Test conditions :

Cycle No. Charge Rest Discharge

1 0.1C×16hrs none 0.25C×2hs20mins
2 - 48 0.25C×3hrs none 0.25C×2hs20mins
49 0.25C×3hrs none 0.25C to1.0V/cell
50 0.1C×16hrs 1-4hr(s) 0.2C to1.0V/cell
Cycles 1 to 50 shall be repeated

05/12/2007 ACH9019 Page 2

 Data sheet

4. CONFIGURATION, WEIGHT, DIMENSIONS AND PACKING

Please refer to the attached drawing

Battery
Dimension (mm) 50,5 x 14,5
Typical weight 27 g.

Blister
Dimension (mm) 130 x 104
Typical weight 10g.
Typical weight (with batteries) 120g.

Packing
1 blister = 4 batteries
1 box = 12 blisters
1 carton = 12 box

5. EXTERNAL APPEARANCE
The cell/battery shall be free from cracks, scars, breakage, rust, discoloration, leakage or deformation.

6. WARRANTY
One (1) year limited warranty against workmanship and material defects.

7 .CAUTION
1. Reverse charging is not acceptable.
2. Charge before use. The cells/batteries are delivered in an uncharged state.
3. Do not charge /discharge with more than the specified current.
4. Do not short circuit the cell/battery. Permanent damage to the cell/battery may result.
5. Do not incinerate or mutilate the cell/battery.
6. Do not solder directly to the cell /battery.
7. The life expectancy may be reduced if the cell/battery is subjected to adverse conditions like: extreme temperature, deep cycling,
and excessive overcharge/ over discharge.
8. Store the cell/batteries uncharged in a cool dry place.
9. Keep away from children. If swallowed, contact a physician at once.
10. Air ventilation should be provided in the plastic case of batteries, otherwise it may have a risk of generating gas inside them
(oxygen gas, hydrogen gas) resulting explosion triggered by fire sources.

nx - ready with discharge at 150mAh

1,5
Tension(v)

Precharged capacity
0,695Ah
1
Capacity after charge
0,5 0,790Ah

0
0 1 2 3 4 5 6
Test_Time(h)

05/12/2007 ACH9019 Page 3