MasterSeal® 588
An elastomeric, cement based waterproof coating for concrete and masonry
DESCRIPTION PACKAGING AND COLORS
MasterSeal 588 powder is a blend of Portland MasterSeal 588 is supplied in 35 kg unit (25 kg
cements, selected silica sands and modifying Powder + 10 kg Liquid, mix ratio 1:1) and available
agents. When mixed to a slurry consistency with in Grey and White.
MasterSeal 588 liquid, an acrylic polymer
emulsion, it can be easily applied by brush or TYPICAL PROPERTIES*
roller. It cures to give an elastomeric flexible
membrane. Wet density 1.68 kg/l
Tensile Strength ASTM D412
MasterSeal 588 must be reinforced with mesh Air cured @ 28 days > 0.7 N/mm²
across all construction joints and cracks. The Water cured @ 28 days > 0.5 N/mm²
reinforcing mesh may be either 100% virgin Elongation ASTM D412
polypropylene or an alkali resistant glass-fibre Air cured @ 28 days > 37%
mesh depending on which particular enhanced Water cured @ 28 days > 30%
tensile properties are required, please consult your Water Resistance DIN 1048 7 bar
local BASF Technical Service Representative for Water Absorption ASTM C642-15 < 1.5%
Liquid water permeability Class W3
further advice on the correct selection of mesh. BSEN 1062-3 2008
Static crack bridging EN 14891 A.8.2 >1.5 mm
TYPICAL APPLICATIONS Dynamic crack bridging ability >1mm
For waterproofing of water-retaining structures BSEN 1062-7 2004 @ 20000 cycles
which may be subject to movement. Freeze-Thaw resistance No failure
ISO DIN 4846.2 / EN 13687-1
To protect concrete from water, carbonation Carbon dioxide permeability Class C1
and deicing salts. BS EN 1062-1
Suitable for internal and external use, against Adhesion Strength (concrete) > 0.8 N/mm²
positive and negative water pressure. @ 28 days EN 1542
Suitable for use in wet area waterproofing Maximum particle size 300 microns
where tiles are to be installed directly on top of ASTM E 2651-10
the membrane using a proprietary tile Pot life Approx. 60 min
Drying time Approx. 360 min
adhesive.
Can be applied to damp substrates.
Thin layer application. APPLICATION GUIDELINES
Equipment to be cleaned simply with water.
For waterproofing of swimming pools. SUBSTRATE PREPARATION
The surface to be coated must be clean and
ADVANTAGES sound. Remove all traces of formwork, release
Retains flexibility when submerged agents, previous coatings, laitance, organic growth
Good chemical resistance against soft water, and any other contaminants that may affect the
domestic waste water, manure or other liquids bond adversely. Suitable cleaning methods include
moderately aggressive to mineral substrates ultra high-pressure water jetting, grit blasting and
Withstands occasional foot traffic grinding. Aggressive percussive methods such as
Freeze-thaw resistant scabbling or scarifying are not recommended
Water vapour permeable unless followed by grit blasting, wire bushing or
CO2 barrier high-pressure water jetting. After the above
Non-toxic, suitable in contact with drinking treatment, surfaces must be thoroughly rinsed with
water clean potable water to remove all dust and loose
Simple and fast method of treating cracks and particles.
joints Cracks bolt holes and large surface defects must
Quick and easy brush or roller application be cut out and filled solid with MasterSeal 590 or
one of the MasterEmaco range of repair material.
MasterSeal® 588
Small blowholes in the concrete should be filled HEALTH AND SAFETY
with a thixotropic mix of MasterSeal 588 Powder MasterSeal 588 Powder is cement based and
with reduced liquid content. may be irritating to the skin and eyes. Gloves and
eye protection should be worn. The use of dust
CURING masks is recommended.
Under hot or excessive drying conditions adequate MasterSeal 588 Liquid should not be ingested,
protective shielding should be foreseen. accidental splashes of the material to the skin or
eyes should be immediately washed off with clean
In cold, humid or unventilated areas it may be water. In the event of prolonged irritation, seek
necessary to leave the application for a longer medical advice.
curing period. MasterSeal 588 needs to cure
under dry-air conditions. Additional heating and/or MasterSeal 588 contains no solvent, safe to
ventilation can assist proper curing. NEVER use handle and use approved for contact with potable
dehumidifiers during curing periods. water. For further information refer to the material
safety datasheet.
COVERAGE / YIELD
Approx. 1 L / m² / coat @ 1 mm thickness 2 layers QUALITY AND CARE
recommended. All products originating from BASF’s Dubai, UAE
An additional 0.5 kg/m² is required when facility are manufactured under a management
embedding BASF approved mesh. system independently certified to conform to the
Yield requirements of the quality, environmental and
Approx. 20.83 L / 35 kg unit. occupational health & safety standards ISO 9001,
ISO 14001 and ISO 45001.
STORAGE AND SHELF LIFE * Properties listed are based on laboratory controlled tests.
Part A (powder): Shelf life is 12 months from date
of manufacturing in unopened original bags. ® = Registered trademark of the BASF-Group in many countries.
Product must be kept out of direct sunlight, in a
dry, cool place, stored clear of the ground on
pallets. Avoid excessive compaction.
Part B (liquid): Shelf life is 12 months from the
date of manufacturing in unopened original
containers.
Product must be kept out of direct sunlight and in a
dry, cool, preferably air-conditioned warehouse
below 35ºC temperature. Store clear of the ground
on pallets. Do not stack pallets.
BASF_CC-UAE/Sl_588_03_19/v6/09_19/v7/07_20/v8/09_20/v9/11_20
The technical information and application advice given in this BASF publication are based on the present state of
STATEMENT OF our best scientific and practical knowledge. As the information herein is of a general nature, no assumption can be
RESPONSIBILITY made as to a product's suitability for a particular use or application and no warranty as to its accuracy, reliability or
completeness either expressed or implied is given other than those required by law. The user is responsible for
checking the suitability of products for their intended use.
Field service where provided does not constitute supervisory responsibility. Suggestions made by BASF either
NOTE orally or in writing may be followed, modified or rejected by the owner, engineer or contractor since they, and not
BASF, are responsible for carrying out procedures appropriate to a specific application.
BASF Construction Chemicals UAE LLC
P.O. Box 37127, Dubai, UAE
Tel: +971 4 8090800, Fax: +971 4 8851002
www.master-builders-solutions.basf.ae
Disclaimer: the LRQA mark relates to
certified management system and not to the
product mentioned on this datasheet