ENJOY A BONDING WORLD
®
Lushan AR493 Lushan, one of the most innovative technological
enterprises in China, is committing to bonding a more
- Maleic Anhydride Grafted
wonderful world with the power of chemistry R&D
technology.
Polyolefin Elastomer
Description
Lushan® AR 493 for nylon toughener is a maleic anhydride grafted polyolefin elastomer, with a
very low residual maleic anhydride monomer, no irritating odor when using. Because of its good
response compatibility, elastomer dispersed in PA matrix rapidly to form the fine dispersed
elastomer phase and the combined closely two-phase interface structure, thereby it can be used
for enhancing the toughness of nylon.
Technical Properties
Item Value Method
Appearance Natural color or light yellow granule Visual
Density 0.87 g/cm3 ASTM D792
MI (190 °C / 2.16 Kg) 0.2 g/10min ASTM D1238
Melting Point (DSC) 61 °C ASTM D3418
Grafting Ratio H* Lushan Method
Hardness (Shore A) 67 ASTM D2240
*Grafting Ratio: H ≥ 1.0wt%, M ≥ 0.5wt%. These are typical properties and not intended as
specification.
Application
As impact modifier for toughening Nylon products like PA6, PA66 and etc.
Improve the impact resistance, cold resistance, lower water absorption of nylon products.
For PA / PE or other PA base filled compounds.
Guangzhou Lushan New Materials Co., Ltd No. 22, Pubei Road, Huangpu, Guangzhou 510530, China
Tel.: +86-20-82266153 Fax: +86-20-8226-6105 [email protected] www.cnlushan.com
ENJOY A BONDING WORLD
Features & Performance
Figure 1: IR spectrum contrast between AR493 and POE.
POE
AR493
Table 1: Used for Nylon 6 strengthening and toughening.
Item PA6+30%GF PA6+30%GF+5%AR493
Tensile strength (MPa) 142 139
Bending strength (MPa) 161 154
Elongation at break (%) 23 28
Notch impact strength (kJ/m2) 9.8 19.5
These are typical properties and not intended as specification.
Table 2: Used for Nylon 66 strengthening and toughening.
PA66+30%GF+5% PA66+30%GF
Item PA66+30%GF
AR493 +10%AR493
Tensile strength (MPa) 160 146 120
Bending strength (MPa) 242 210 175
2
Notch impact strength (kJ/m ) 9 14 24
These are typical properties and not intended as specification.
Packaging & Storage
Packed in 25kgs paper-plastic bag lined with polyethylene film bag.
Store in dry, cool and ventilated environment; avoid exposure to water & strong light.
Securely wrap the unused.
Shelf Life: one year.