Chang Chun Plastics CO., LTD

This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

Uploaded by

ChunYenHuang
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
214 views2 pages

Chang Chun Plastics CO., LTD

This document provides information on product CCP PBT 5515F-200, a 15% glass fiber reinforced flame retardant thermoplastic polyester resin. It lists key details such as the manufacturer, product description, characteristics, physical and mechanical properties, thermal properties, flammability ratings, electrical properties, and processing guidelines for injection molding. The product is halogen and antimony free with a density of 1.4 g/cm3, flexural strength of 125 MPa, melting temperature of 225°C, and achieves a V0 rating under UL94 testing at 0.8mm thickness.

Uploaded by

ChunYenHuang
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 2

CHANG CHUN PLASTICS CO., LTD.

NO. 301, SONGKIANG ROAD, 7TH FL.,TAIPEI, 10477 TAIWAN


TEL : 886-2-2503-8131 (REF) FAX : 886-2- 2501-8018

CCP PBT 5515F-200


THERMOPLASTIC POLYESTER RESIN

Product Description
PBT 5515F-200 is a 15% glass fiber reinforced and flame retardant injection molding grade.
(Halogen and Antimony Free)
Characteristics
Processing ‧Injection Moulding
Deliver form ‧Pellets
Additives ‧Glass fiber, Flame retardant, Modifier
Physical properties Value Unit Test Method
Density 1.4 g/cm3 ISO 1183
Moulding shrinkage, parallel 0.3-0.6 % ISO 294-4, 2577
Moulding shrinkage, normal 0.9-1.2 % ISO 294-4, 2577
Moisture 0.2 % ISO 62
Mechanical properties Value Unit Test Method
Stress at break 80 MPa ISO 527-1/-2
Strain at break 3.0 % ISO 527-1/-2
Flexural Strength 125 MPa ISO 178
Flexural Modulus 5300 MPa ISO 178
Charpy impact strength – notched
ISO 179/1eA
23℃ 7.5 kJ/m2
Thermal properties Value Unit Test Method
Melting temperature, 10℃/min 225 ℃ ISO 11357-1/-3
Heat deflection temperature under load ISO 75-1/-2
1.80 Mpa 195 ℃
0.45 MPa 215 ℃
Flammability Value Unit Test Method
Flammability acc. to UL94, 0.8mm V0 - UL 94
Electrical properties Value Unit Test Method
Dielectric strength, 2mm 24 kV/mm ATSM D149

Revised: 2020-09-22
CHANG CHUN PLASTICS CO., LTD.
NO. 301, SONGKIANG ROAD, 7TH FL.,TAIPEI, 10477 TAIWAN
TEL : 886-2-2503-8131 (REF) FAX : 886-2- 2501-8018

CCP PBT 5515F-200


THERMOPLASTIC POLYESTER RESIN

Volume resistivity >1013 Ω*m IEC 60093


Surface resistivity 1013 Ω IEC 60093
Comparative tracking index 450 V IEC 60112
Injection molding
Pre-drying : 120℃, 5hours or longer
140℃, 3hours or longer
Processing moisture content : =< 0.04%
Resin temperature : 240~270℃
Mold temperature : 40~80℃
These property values are typical values obtained under varying conditions prescribed by certain standards and
test methods and therefore are not the minimum values of the material specifications.

Revised: 2020-09-22