1600T Lab Test by EC 29 July 2016

Exceed Consulting conducted abrasion testing on one wear sample submitted by Alloy Steel International in accordance with ASTM G65. The sample, identified as Arcoplate 1600T, underwent dry sand abrasion testing using a rubber wheel. The test results showed an average mass loss of 0.0312 grams and average volume loss of 4.1 cubic millimeters. The wear scar was determined to be even. Exceed Consulting prepared the report detailing the testing procedure and results for the client.

Uploaded by

Yudi Bahrain
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
79 views3 pages

1600T Lab Test by EC 29 July 2016

Exceed Consulting conducted abrasion testing on one wear sample submitted by Alloy Steel International in accordance with ASTM G65. The sample, identified as Arcoplate 1600T, underwent dry sand abrasion testing using a rubber wheel. The test results showed an average mass loss of 0.0312 grams and average volume loss of 4.1 cubic millimeters. The wear scar was determined to be even. Exceed Consulting prepared the report detailing the testing procedure and results for the client.

Uploaded by

Yudi Bahrain
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 3

EXCEED CONSULTING (WA) PTY LTD

OFFICE & WORKSHOP POSTAL ADDRESS


Unit 8, 7 Prindiville Drive PO BOX 1684
WANGARA WA 6065 WANGARA DC 6947

Phone (08) 9409 6965 Mobile 0407 770 551


Facsimile (08) 9409 5967

Web: www.exceedconsulting.com.au
ABN: 86 107 401 632 Email: [email protected]

Report No: EXC16 – 161


Client: Alloy Steel International
Attention: Mr M Perry
Order: 73556P
Date: 29 July 2016
Subject: ASTM G65 Abrasion Testing of One Wear Sample

1.0 INTRODUCTION

One wear samples were submitted for abrasion testing in accordance with ASTM
G65.

2.0 PROCEDURE

2.1 Identification

The following identification was assigned to the samples submitted:

Exceed ID Client ID

EXC16 – 161/1 Arcoplate 1600T

2.2 Wear Testing

Dry sand abrasion testing was conducted in accordance with ASTM G65
Method A.

Materials Engineering – Materials Selection – Failure Analysis – Visual Inspection – Specialist Testing & Inspection Services
Report No: EXC16 – 161 Page 1 of 3 Revision: C
3.0 RESULTS

3.1 Wear Testing

3.1.1.1 EXC16 – 151/1

Dry Sand / Rubber Wheel Test


ASTM G65 Procedure A
Test Data
Material: Arcoplate 1600T Wheel Diameter: 228 mm
Wheel Width: 12.7 mm
Wheel Hardness: 60 A
Surface Preparation: As received

Specimen Number 1 2 3 Average Result


Test Load, N 130 130 130
Wheel Speed, RPM 200 200 200
Wheel Revolutions 6000 6000 6000
Sand Flow Rate g/min 350 350 350
Mass Loss, g 0.0285 0.0335 0.0315 0.0312
Volume Loss, mm 3
3.8 4.5 4.2 4.1
Wear Scar Even Even Even

R J Dunning A Dunning
B App Sc (Met) MIE Aust C P Eng CMP Adv. Dip. Metallurgy
Materials Engineer

---------- End of Report ----------

This report has been prepared using the information and samples supplied by the customer. The report
shall not be reproduced except in full. Samples which have been supplied to Exceed Consulting for
the purpose of this investigation will be retained for a period of 1 month from the date of this report.
Should the client wish the samples to be returned or to be retained please advise of the retention
requirements in writing

Materials Engineering – Materials Selection – Failure Analysis – Visual Inspection – Specialist Testing & Inspection Services
Report No: EXC16 – 161 Page 2 of 3 Revision: C
Figure 1: Wear scar of EXC16 – 161

Materials Engineering – Materials Selection – Failure Analysis – Visual Inspection – Specialist Testing & Inspection Services
Report No: EXC16 – 161 Page 3 of 3 Revision: C