WPS 141-111 P460QH To Same

The document is a Welding Procedure Specification (WPS) that specifies the parameters for welding a V-groove butt joint between pieces of steel that are 40mm thick. It lists the welding processes, materials, positions, parameters such as current, voltage, and wire feed speed. The joint will be welded in two passes using processes 141 and 111 with filler metals of the appropriate classifications. Upon completion, the weld will undergo post-weld heat treatment at 570C for 2 hours to relieve stresses.

Uploaded by

akisdassas
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOC, PDF, TXT or read online on Scribd
639 views1 page

WPS 141-111 P460QH To Same

The document is a Welding Procedure Specification (WPS) that specifies the parameters for welding a V-groove butt joint between pieces of steel that are 40mm thick. It lists the welding processes, materials, positions, parameters such as current, voltage, and wire feed speed. The joint will be welded in two passes using processes 141 and 111 with filler metals of the appropriate classifications. Upon completion, the weld will undergo post-weld heat treatment at 570C for 2 hours to relieve stresses.

Uploaded by

akisdassas
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as DOC, PDF, TXT or read online on Scribd
You are on page 1/ 1

MOODY HELLAS S.A.

21 Elvetias Str., Agia Paraskevi, GR 15342, Athens


Tel.: +30 -210-6009040 Fax: +30-210-6009091,
e - mail: [email protected], www.moodyhellas.gr

QSF-ID-24 Certificate No.:ΧΧΧΧΧΧΧ/000.319.473


REV. 03 Date: ΧΧ/05/2023

Welding Procedure Specification (WPS)


According to EN ISO 15609-1:2004 Code Specification
WPS No.: XXXXXX/00.319.473 Test body No. : 0656
WPQR No.: XXXXXXX/00.319.473 Method of Preparation and Cleaning : Brushing &/or Grinding
Manufacturer: SALONICA CONSTRUCTIONS S.A Parent Material Designation: EN10222-4 : P460QH to P460QH
Welding Process : 141+111 Material Thickness (mm): 40
Joint Type and Weld Type: V-Groove, Butt Outside Diameter (mm): 340
Weld preparation & details Welding Position: 141: PA, 111: PA
Joint Design Welding Sequence

35° ±2.5°

T =40 2-3

2-3

Welding Details

Size of Type of Wire Travel Heat Run Mode of


Filler Metal Current Voltage Current / Feed Speed Input Thick Metal
Run Process
(Φ mm) A V Polarity Speed mm/s J/mm mm Transfer
mm/min
1 141 2.40 90-100 10-12 DC SP 1.0 630 2
2,3 141 2.40 100-110 10-12 DC SP 1.2 580 2/2
XX 111 2.50 80-100 22-23 DC RP 2.0 810 Tbd
XX 111 3.25 110-130 22-23 DC RP 2.0 1080 Tbd
XX 111 3.25 120-140 24-25 DC RP 2.2 1110 Tbd
Filler Metal Class. and trade name : 141: ISO 16834-A (EN 12534): W 55 6 Mn3 Ni1Mo (BOHLER NiMo 1-IG)
: 111: ISO 18275-A (EN 757): E55 6 1NiMo B 4 2 H5 (BOHLER – FOX EV65)
Any Special Baking or Drying : No Other Information ** :
Gas Flux: - shielding : 141: ISO 14175 (EN 439): I1 141 consumable Heat No: XXXXXX
- backing :- 111 consumable Heat No: XXXXXX
Gas Flow Rate - shielding : 6 lit/min 111 consumable Heat No: XXXXXX
- backing :- Distance contact tube/work piece: 10mm
Tungsten Electrode Type / size : EWTh 2% , Ø 2.4 mm Torch angle: 141: ~ 90° , 111: 75° ÷ 90°
Details of back Gouging / Backing :- Orifice or gas cup size: 141: #6
Preheat Temperature : 80°C Single / Both sides: Single
Interpass Temperature : 250°C String/Weave: String & Light Weave
Post Weld Heat Treatment and / Ageing : Yes
Time, Temperature, Method : 570°C for 2 hours Examiner or test body
Heating and Cooling Rates * : Heating: 55°C/hr (above 300°C) MOODY S.A.
* if required Cooling: 55°C/hr(down to 300°C) Date of issue : xx/05/2023

Manufacturer’s signature and date Inspector’s name and signature

THIS INSPECTION HAS BEEN CARRIED OUT TO THE BEST KNOWLEDGE AND ABILITY AND OUR RESPONSIBILITY IS LIMITED TO THE EXERCISE OF DUE CARE. ΑND THE RESULTS CONCERN ONLY THE ITEMS
INSPECTED. THIS CERTIFICATE IS NOT INTENDED TO RELIEVE THE PARTIES CONCERNED FROM THEIR CONTRACTUAL OBLIGATIONS.
THE PRESENT REPORT CAN ONLY BE REPRODUCED IN ITS WHOLE ENTITY AND AFTER THE APPROVAL OF THE INSPECTION BODY AND THE CLIENT

Page 1 of 1