Thermoplastic

Polyurethane Elastomers (TPU)

Elastollan® – Product Range
Elastollan®

Elastollan® is the brand name for thermoplastic polyurethane (TPU)

from BASF. It stands for maximum reliability, consistent product
quality and cost efficiency. Elastollan® can be extruded into hoses,
cable sheathing, belts, films and profiles, and can also be pro-
cessed using blow molding and injection molding technologies.
Over the last few decades, the numerous benefits of Elastollan® in
all its forms – aromatic or aliphatic, very soft or glass fiber-rein-
forced, flame retardant or highly transparent – have been clearly
demonstrated across every sector of industry.

This extensive product portfolio, which makes use of a variety of

raw materials and formulations, is the starting point for successfully
bringing innovative customer projects to fruition.

We thrive on creative ideas and complex challenges – come and

talk to us!
Elastollan®

Nomenclature and Portfolio 04

11 Series 06
12 Series 08
C Series 10
B Series 12
BCF Series 14
500 Series 16
A Series incl. HPM (aliphatic) 18
L Series 20
FHF Series 22
HFFR / FR Series 24
Food Contact Series 26
HPM Series (aromatic) 28
R Series 30
Special Products 32
N / BMB Series 34
Infinergy® 36
Masterbatches / Additives 38
4 ELASTOLLAN®
Nomenclature

Nomenclature

Elastollan® 11 85 A 10 W 000

Elastollan® Series Shore Hardness Granule Shape Lubricant Additives Additives

The registered trade The letter or number
mark of BASF for characterizes the Shore Hardness A 1 = cylindrical or 0, 1 = no added ESD = electronic 000 = natural
thermoplastic polyol base (45-98) lentil-shaped lubricants sensitive devices
polyurethane
B, BCF, C, 5, 6, 7, Shore Hardness D 5 = diced granules 2, 3, 5, 9 = added FC = food contact
Elastollan® 8, 9 = (47-83) lubricants
FHF/HFFR/FR =
A and L polyester base
flame retardant.
stand for aliphatic
11, 12, 13, 15 = halogen-free
thermoplastic
polyurethanes polyether base
HPM = high perfor-
R = glass fiber­ mance material
Infinergy®
reinforced
M = mat surface
Elastollan® N
stands for bio-based SP = special product N = non- stabilized
thermoplastic
EXP = Experimental
polyurethanes P/W = contains
Grade*
plasticizers
Elastollan BMB
®

stands for bio-mass- Q = compounds

balance based
thermoplastic T = approved for
polyurethanes drinking water
applications

TSG = TPU for

expansion

U = UV-stabilized

* see reverse
 ELASTOLLAN®
Portfolio 5

Portfolio

Product Range Chemistry Shore Hardness* Range Properties

excellent hydrolysis resistance, cold flexibility,

11 Ether 50 A - 75 D
resistance to microorganisms

highly transparent, excellent hydrolysis resistance,

12 Ether 86 A - 83 D
cold flexibility, resistance to microorganisms

water-vapor permeable, good tear propagation strength,

13 Ether 85 A - 90 A
very good mechanical properties

excellent mechanical properties, very good damping behavior,

C Ester 80 A - 73 D
good rebound, very good wear resistance

very good mechanical properties, good cold flexibility,

B Ester 82 A - 64 D
good wear resistance

very good wear resistance and low-temperature flexibility, excellent

BCF Ester 45 A - 70 D processing behavior especially in injection molding, good compres-
sion set

500 Ester 60 A - 61 D good mechanical properties, good abrasion resistance

600 Ester 85 A - 50 D transparent, good damping behavior and rebound

excellent mechanical properties and chemical resistance, outstanding

700 Ester 85 A wear resistance, good damping characteristic and high resilience
performance

800 Ester 80 A - 90 A very good transparency, good abrasion resistance

Ether or ester
A 65 A - 55 D color-fast, non-yellowing, hydrolysis-resistant (ether)
aliphatic

Ether or ester
L 75 A - 60 D color-fast, long-term UV-stability
aliphatic

Ether flame non-halogen-based flame retardant, outstanding mechanical proper-

FHF, HFFR, FR 75 A - 54 D
retardant ties, excellent hydrolysis resistance, resistance to microorganisms

Food Contact general suitability for food contact applications in FDA and and EU
Ester or ether 70 A - 75 D
(FC) regulated markets (see Food Contact Information)

very good damping behavior and rebound, high temperature

HPM Ester 60 A - 55 D resistance, improved setting behavior, good demolding properties,
color-fast, soft touch

E-Modul glass fiber-reinforced, very high stiffness, low thermal expansion

R Ester-reinforced
1000 - 14000 MPa coefficient, low shrinkage, very good impact resistance

biobased, excellent mechanical properties, durable, flame retardant

N bio-based Ether 85 A - 95 A
possible, good media resistance

based on biomass balance approach; saving of fossil raw materials,

BMB Ether 70 A - 95 A reduction of greenhouse gases, identical product quality and
-properties

expanded, predominantly closed-cell foam particles made of

Infinergy®
thermoplastic polyurethane (E-TPU)

*incl. plasticized products

6 ELASTOLLAN®
11 Series

Elastollan® 11 Series
Thermoplastic polyether polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set 23 °C / 72 hours % DIN EN ISO 815-1
Compression set 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact resistance (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact resistance (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set 23 °C / 72 hours % DIN EN ISO 815-1
Compression set 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact resistance (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact resistance (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
11 Series 7

Excellent hydrolysis resistance

Cold flexibility
Resistance to microorganisms
Other UV stabilized products are available

SP 1150 A SP 1155 A
19 P 12 PU 1160 A 13 P 1160 A 10 P 1170 A 10 1175 A 13 U 1175 A 10 W 1180 A 10 1185 A 10 W 1185 A 10
50 54 60 63 71 74 75 80 83 87
36
1.08 1.08 1.06 1.07 1.08 1.09 1.14 1.11 1.16 1.12
22 22 27 26 30 41 40 45 40 45
1000 800 850 950 850 700 700 650 700 600
0.6 1.0 1.0 1.5 1.5 2 2 2.5 2.5
1.3 2.5 2.5 3.5 4 4 4.5 6 6
3.4 4.5 4.5 6.3 7 8 8 8 10

30 30 40 40 45 40 40 55 50 70
50 45 70 45 45 50 45 30 55 35
48 25 25 20 20 20 25 20 25
75 40 39 35 40 45 35 45
20 28 30 30 32
900 750 700 700 600
nb nb nb nb nb
nb nb nb nb nb
V0 / V2 HB V2 HB

1185 A
12 WM 1185 A 55 U 1185 A 10 M 1190 A 10 1195 A 55 U 1195 A 10 1154 D 10 1160 D 50 1164 D 53 U 1174 D 11
87 87 88 92 96
39 39 42 43 48 53 60 63 75
1.13 1.12 1.11 1.13 1.15 1.15 1.17 1.18 1.18 1.2
30 50 45 50 50 55 50 50 45 65
650 480 600 550 500 500 450 400 350 380
4 3 3.5 5 6 6 11 13 17 25
7 7 7 9 10 10 15 19 25 30
10 10 12 16 18 18 38 41 44 45
150 200 260 560
55 65 60 85 100 100 150 170 185 220
65 35 60 35 25 35 30 29 30 22
25 20 35 25 30 30 40 40 50
43 40 45 45 45 45 50 50 55
30 30 35 37 37 35 35 35
600 650 600 500 500 450 450 400
nb nb nb nb nb nb nb nb
nb nb nb nb nb 18 16 5
V2 HB HB
8 ELASTOLLAN®
12 Series

Elastollan® 12 Series
Thermoplastic polyether polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
12 Series 9

Highly transparent
Excellent hydrolysis resistance
Cold flexibility
Resistance to microorganisms

1285 A 10 U 1290 A 12 1295 A 13 U 1298 A 13 U 1250 D 13 U 1254 D 13 U 1260 D 13 U 1264 D 13 U

86 90 95
46 50 54 57 61 64
1.12 1.12 1.15 1.16 1.16 1.17 1.18 1.18
36 45 59 60 57 60 45 50
710 650 560 460 450 470 350 350
2.5 4 6 9 10 17 14 17
6 7 11 16 17 23 23 25
9 11 18 28 29 35 37 35
60 90 120 160 225 310
60 70 116 130 153 165 165 170
43 45 32 25 30 30 40 40
25 25 28 26 42 45 43
40 45 45 45 54 52 53
50 53 51 46
550 520 500 450
nb nb nb nb nb nb
160 171 17 14 13 12

1278 D 11 U 1283 D 11 U

77 83
1.2 1.22
50 67
350 170
29 56
33 47
43
808 2000
220 310
40 80
72 79
60 94

nb 8.7
10 8.4
HB
10 ELASTOLLAN®
C Series

Elastollan® C Series
Thermoplastic polyester polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
C Series 11

Outstanding mechanical properties

Very good damping behavior
Good rebound
Very good wear resistance

C 78 A 10 C 80 A 10 C 85 A 10 C 85 A 13 C 85 A 55 C 88 A 10 C 90 A 13 C 90 A 55
80 82 87 87 87 88 93 93
36 36 36 37 40 41
1.18 1.19 1.19 1.19 1.19 1.19 1.2 1.2
50 50 50 50 50 50 47 55
650 650 650 650 650 600 640 550
2 3 3 3 3 3.5 5.5 7
4 5 6 6 6 6 8.1 9
8 9 10 10 10 13 11.4 15

60 65 70 70 70 75 102 95
30 30 30 30 30 30 39 25
25 25 25 25 25 25 21 25
35 35 35 35 35 40 37 40
35 35 38 38 38 38 40 40
650 650 650 650 650 650 550 550
nb nb nb nb nb nb nb nb
nb nb nb nb nb nb nb nb
HB HB HB HB

C 95 A 10 C 95 A 55 C 98 A 10 C 59 D 53 C 60 D 53 C 64 D 53 C 74 D 50
96 96
47 47 52 57 60 62 73
1.21 1.21 1.22 1.23 1.23 1.23 1.25
55 55 50 50 50 50 45
550 550 550 500 450 400 350
8 8 11 12 16 17 28
11 11 14 17 20 24 30
22 22 26 30 35 35 35
160 250 330 390 730
120 120 130 160 180 200 240
30 30 30 30 30 30 20
30 30 30 30 40 40 40
45 45 50 50 50 55 60
40 40 40 43 43 43 45
500 500 550 480 450 420 380
nb nb nb nb nb nb 120
nb nb 25 12 8 7 4
HB HB HB HB HB
12 ELASTOLLAN®
B Series

Elastollan® B Series
Thermoplastic polyester polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
B Series 13

Very good mechanical properties

Good cold flexibility
Good wear resistance

B 80 A 15 B 85 A 10 B 85 A 15 B 90 A 11 B 90 A 15 B 95 A 15 B 98 A 15
82 83 83 92 91 96
42 48 50
1.19 1.2 1.2 1.21 1.21 1.22 1.22
50 55 55 35 55 55 55
600 600 600 550 550 550 500
2 2 4 8 8
5 4 7 11 12
15 15 20 20 30
20 140
85 75 75 93 90 100 130
35 35 35 30 30 25
20 25 26 25 30 35
30 35 38 40 40 45
40 40 40 40 40
600 600 550 500 500
nb nb nb nb nb
nb nb nb 200 18

B 60 D 11 B 60 D 15 B 64 D 11

60 60 64
1.23 1.23 1.24
55 55 55
500 500 450
13 13 17
16 16 19
30 30 35
240 240 320
150 150 180
25 25 25
35 35 35
45 45 50
40 40 40
450 450 400
nb nb nb
10 10 8
14 ELASTOLLAN®
BCF Series

Elastollan® BCF Series

Thermoplastic polyester polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
BCF Series 15

Very good wear resistance and low-temperature flexibility

Excellent processing behavior, especially in injection molding
Good rebound

BCF 55 A BCF 55 A BCF 65 A

BCF 45 A 12 P BCF 50 A 12 12 P TSG 12 PM ESD BCF 65 A 12 P 12 P ESD BCF 70 A 10 P
48 50 55 54 64 63 70

1.18 1.20 1.18 1.18 1.19 1.18 1.19

28 22 18 30 25 30 30
1210 1100 1250 1100 1000 1100 900
43 35 40 40 45 45
49 80 50 55 60 60

BCF 75 A 15 P BCF 80 A 15 BCF 85 A 15 BCF 90 A 15 BCF 95 A 15 BCF 64 D 15 BCF 70 D 15

73 80 85 90
48 64 70
1.19 1.21 1.22 1.22 1.23 1.25 1.26
35 40 45 45 47 40 55
900 800 700 550 560 450 310
45 60 70 85 120 200 260
60 40 30 40 35 30 40
16 ELASTOLLAN®
500 Series

Elastollan® 500 Series

Thermoplastic polyester polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
500 Series 17

Good mechanical properties

Good abrasion resistance

560 A 13 P TSG 565 A 12 P 565 A 12 ESDM 575 A 12 580 A 10 585 A 11 590 A 13

60 66 63 75 80 85 92

1.22 1.22 1.22 1.25 1.24 1.25 1.25

24 30 30 35 45 40 45
850 850 850 660 750 600 580
1.0 1.1 1.0 3
2.5 2.7 2.4 6
6.0 6.5 5.2 10
50 65 60 75 75 95 108
90 55 60 55 40 50 35
29 22 17
45 37 35

590 A 53 595 A 13 598 A 10 598 A 53 554 D 55 U 560 D 53

94
41 48 54 53 54 61
1.25 1.27 1.26 1.26 1.25 1.28
50 55 50 50 60 45
600 500 500 500 500 450
5 9 15
8 12 18.5
13 16 23
100 120 130 150 140 180
35 35 40 30 30 30
24 26 24
36 40 46
18 ELASTOLLAN®
A Series incl. HPM

Elastollan® A Series incl. HPM

Aliphatic thermoplastic polyester or -ether polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Compression set at 100 °C / 24 hours kJ /m² DIN EN ISO 179-1
Vicat softening temperature at 10 N
°C DIN EN ISO 306
and 120 °C/h (Proc. A120)

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Compression set at 100 °C / 24 hours kJ /m² DIN EN ISO 179-1
Vicat softening temperature at 10 N
°C DIN EN ISO 306
and 120 °C/h (Proc. A120)

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
A Series incl. HPM 19

Color-fast
Non-yellowing
Hydrolysis resistant (ether)
Soft touch

Aliphatic Polyester Aliphatic Polyester HPM

A C 85 A 12 LP 9277 10 LP 9307 10 A C 65A 12 HPM A C 70 A 10 HPM A C 55 D 10 HPM

82 68 79 64 68
56
1.14 1.17 1.18 1.17 1.17 1.25
18 14 14 7 14 31
750 1300 1080 1640 1300 690
1.2 1.6 17
2.1 2.8 17
3.3 4.5 17
50 40 45 33 40 130
40 450 350
36 25 22 30 25 30
39 35 30 40 35 45
50 45 50

70 90

Aliphatic
Polyether HPM
A 1190 A 12 HPM
90

1.11
16
850

50
120
20 ELASTOLLAN®
L Series

Elastollan® L Series
Aliphatic thermoplastic polyester or -ether polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
L Series 21

Superior transparency
Long-term UV-stability
Color-fast

Aliphatic Ethers
L 1185 A 10 L 1160 D 12 L 1275 A 10
85 70
56
1.08 1.09 1.08
50 40 35
430 430 500
3 9 1
5 11 2.5
11 16 6
70 70 42

Aliphatic Esters
L 785 A 10 L 787 A 10 L 790 A 10 L 795 A 10 L 760 D 10
86 87 90 95
60
1.13 1.13 1.13 1.13 1.14
50 45 45 50 45
500 500 450 450 400
2
4 9 8 11
10
65
22 ELASTOLLAN®
FHF Series

Elastollan® FHF Series

Flame retardant polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Burning behavior (depending on wall thickness) UL 94

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
FHF Series 23

Flame retardant halogenfree

Outstanding mechanical properties
Excellent hydrolysis resistance
Resistance to microorganisms

1177 A 10 FHF 1185 A 10 FHF 1190 A 10 FHF 1191 A 10 FHF 1192 A 10/11 FHF 1198 A 10 FHF
77 89 90 91 91
37 53
1.2 1.23 1.25 1.27 1.25 1.26
22 35 25 25 17 27
800 600 550 600 550 490
1.9 3.5 5 5 9
4.6 8 8 10 11
5.7 13 11 12 15

53 60 60 65 55 85
75 35 30 40 80 37
25 26 24 29
45 43 43 50
9 20 15 9
890 600 640 570
nb nb nb / nb
120 46 17 / 9
V0 V0 V0

1147 D 10 FHF 1154 D 10 FHF 3095 A 10 FHF

94 96
48 58
1.29 1.27 1.29
13 30 24
400 400 550
7 13
9 19
10 33
160
60 110 96
54 30 60
29 30 23
50 45 35
7 20 21
270 400 580
nb 50
21 3
V0 / V2
24 ELASTOLLAN®
HFFR / FR Series

Elastollan® HFFR / FR Series

Flame retardant polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
E-modulus from tensile test MPa DIN EN ISO 527-2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
HFFR / FR Series 25

Flame retardant halogenfree

Outstanding mechanical properties
Excellent hydrolysis resistance
Resistance to microorganisms

1185 A 10 HFFR SP 3092 A 10 HFFR SP 3093 A 10 HFFR

86 95 93
52
1.42 1.62 1.51
23 15 26
580 400 390
3.6 8
6 7
7.8 7
60
55 42 50
220
12 11 17
750 430 570

1176 A 10 FR 1183 A 10 FR 1188 A 10 FR 1192 A 10 FR 1193 A 10 FR 3096 A 10 FR

76 83 88 92 93 96
1.16 1.17 1.18 1.2 1.25 1.26
34 21 36 32 11 23
710 700 510 500 490 550
40 41 55 60 53 98
70 118 65 75 170 64
26 ELASTOLLAN®
Food Contact Series

Elastollan® Food Contact Series

Thermoplastic polyether or -ester polyurethane elastomer

Property Unit of Measurement Test Procedure 1170 A 10 FC 1180 A 10 FC

Hardness Shore A DIN ISO 48-4 (3s) 71 80
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A 1.08 1.11
Tensile strength MPa DIN 53504-S2 30 45
Elongation at break % DIN 53504-S2 850 650
Stress at 20 % elongation MPa DIN 53504-S2 1.5 2
Stress at 100 % elongation MPa DIN 53504-S2 3.5 4.5
Stress at 300 % elongation MPa DIN 53504-S2 6.3 8
Tear strength kN /m DIN ISO 34-1.B(b) 45 55
Abrasion mm³ DIN ISO 4649-A 45 30
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1 20 25
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1 39 45
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2 20 30
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2 900 700
Notched impact strength (Charpy) +23 °C kJ /m² nb nb
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m² nb nb

Property Unit of Measurement Test Procedure C 80 A 10 FC C 85 A 10 FC

Hardness Shore A DIN ISO 48-4 (3s) 82 85
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A 1.19 1.19
Tensile strength MPa DIN 53504-S2 50 40
Elongation at break % DIN 53504-S2 650 550
Stress at 20 % elongation MPa DIN 53504-S2 3
Stress at 100 % elongation MPa DIN 53504-S2 5
Stress at 300 % elongation MPa DIN 53504-S2 9
Tear strength kN /m DIN ISO 34-1.B(b) 65 65
Abrasion mm³ DIN ISO 4649-A 30
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1 25
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1 35
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2 35
Elongation at break after storage in water at 80 °C for 42 days % DIN 53504-S2 650
Notched impact strength (Charpy) +23 °C kJ /m² nb
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m² nb

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
Food Contact Series 27

B
 asic suitability for food contact applications
in FDA and EU-regulated markets (see food contact information)

1185 A 10 FC 1190 A 10 FC 1195 A 10 FC 1198 A 10 FC 1154 D 10 FC 1164 D 11 FC 1174 D 11 FC

87 92 96
36 42 48 52 53 69 75
1.12 1.13 1.15 1.17 1.17 1.18 1.2
45 50 55 50 50 50 65
600 550 500 420 450 350 380
2.5 5 6 9 11 16 25
6 9 10 15 15 25 30
10 16 18 28 38 45 45
70 85 100 130 150 190 220
35 35 35 25 30 30 22
25 25 30 35 40 40 50
45 45 45 50 50 50 55
32 35 37 35 35 35 35
600 600 500 450 450 400 400
nb nb nb nb nb nb nb
nb nb nb 190 18 12 5

C 90 A 10 FC C 95 A 10 FC C 98 A 10 FC B 95 A 11 FC 685 A 10 FC 695 A 10 FC 880 A 13 N 890 A 10 FC 991 A 10 FC

93 96 86 77 91 91
42 47 52 53 50
1.2 1.21 1.22 1.21 1.21 1.22 1.2 1.22 1.22
45 55 50 55 55 45 40 45 45
550 550 550 550 600 550 700 540 560
7 3 6 1.8 6
9.5 10 5.5 10 4.2 10
22 10.8 7.6 23
102 120 130 100 75 100 60 106 95
38 30 30 30 35 35 35 46 36
30 25 32 32
40 40 54 43

nb nb
nb 200
28 ELASTOLLAN®
HPM Series

Elastollan® HPM Series

Aromatic thermoplastic polyester or -ether polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Compression set at 100 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Vicat softening temperature at 10 N
°C DIN EN ISO 306
and 120 °C/h (Proc. A120)

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Compression set at 100 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 21 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Vicat softening temperature at 10 N
°C DIN EN ISO 306
and 120 °C/h (Proc. A120)

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
HPM Series 29

Very good damping behavior and rebound

High temperature resistance
Improved setting behavior
Good demolding properties

C 60 A 15 HPM C 65 A 15 HPM C 70 A 15 HPM C 75 A 15 HPM C 85 A 15 HPM C 90 A 15 HPM C 95 A 15 HPM

63 67 71 75 85 91 95

1.17 1.18 1.18 1.18 1.2 1.21 1.23

20 37 40 42 45 45 50
1000 950 900 900 750 600 550
0.9 1.5 1.5 2 3.5 4 8.4
1.5 2 2.5 3.5 6 8 12
2 4 5 6 11 13 16
40 44 45 50 70 80 110
98 55 50 50 40 45 21
25 25 25 25 20 20 20
43 37 35 35 30 29 32
60 55 50 35 50 43 50
20 35 30 35 35 38 46
1100 900 850 800 800 740 650
nb nb nb nb nb nb nb
nb nb nb nb nb nb nb

70 80 90 100 120 152 170

785 A 10 HPM 754 D 15 HPM 1175 A 15 HPM 3090 A 10 HPM

85 73 92
55
1.18 1.24 1.11 1.23
46 35 30 49
690 440 580 510
3.5 13 1.5
6 17 3
11 19 7
69 161 38 97
43 21 35 48
18 25 15
27 36 28
50 42 55
40 55
750 550
nb nb nb
nb nb nb

118 151
30 ELASTOLLAN®
R Series

Elastollan® R Series
Glass fiber-reinforced thermoplastic polyurethane elastomer

Property Unit of Measurement Test Procedure

E-modulus from tensile test MPa DIN EN ISO 527-2
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength (sample grade 1A) test speed 50 mm /min MPa DIN EN ISO 527-2
Elongation at break (sample grade 1A) test speed 50 mm /min % DIN EN ISO 527-2
Glass fiber content %
Impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Impact strength (Charpy) -30 °C kJ /m²
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
HDT determination at 1.8 MPa °C DIN EN ISO 75-2/A
HDT determination at 0.45 MPa °C DIN EN ISO 75-2/B
Average linear thermal expansion coefficient between 23 °C and 80 °C 10-6∙K-1 ISO 11359-2
Color
Burning behavior (depending on wall thickness) UL 94

Property Unit of Measurement Test Procedure

E-modulus from tensile test MPa DIN EN ISO 527-2
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength (sample grade 1A) test speed 50 mm /min MPa DIN 53504-S2
Elongation at break (sample grade 1A) test speed 50 mm /min % DIN 53504-S2
Glass fiber content % DIN 53504-S2
Impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Impact strength (Charpy) -30 °C kJ /m²
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
HDT determination at 1.8 MPa °C DIN EN ISO 75-2/A
HDT determination at 0.45 MPa °C DIN EN ISO 75-2/B
Average linear thermal expansion coefficient between 23 °C and 80 °C 10-6∙K-1 ISO 11359-2
Color
Burning behavior (depending on wall thickness) UL 94

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
R Series 31

Glass fiber-reinforced
Very high rigidity
Low thermal expansion coefficient
Low shrinkage
Very good impact strength

R 1000 R 1001 R 2000 R 2006 R 3000 R 3001 R 6000 R 14000

1000 300 2000 2000 2800 3000 6400 14000
60 50 67 64 73 75
1.36 1.27 1.37 1.35 1.38 1.32 1.4 1.65
50 30 65 65 80 65 114 210
40 65 25 20 10 25 7 3
20 10 20 20 20 15 26 50
nb nb 140 130 120 100 84 50
130 160 110 80 70 70 67 40
70 70 50 40 30 30 21 14
20 30 10 10 10 6 12 12
114 65 115 120 126 110 124
145 125 138 150 162 155 166
20 28 20 20 20 30
natural natural natural black natural black natural natural
HB HB HB

R 2600 FHF R 4000 FR

2700 3900
67 76
1.39 1.24
35 42
6 8
15
63 46
65 37
18 12
11 7
129
139

natural
V0/V2 HB/V0/V2
32 ELASTOLLAN®
Special Products

Elastollan® Special Products

Thermoplastic polyether or -ester polyurethane special product

Property Unit of Measurement Test Procedure

Applications

Hardness Shore A DIN ISO 48-4 (3s)

Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²

Property Unit of Measurement Test Procedure

Applications

Hardness Shore A DIN ISO 48-4 (3s)

Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²

For more detailed information, please refer to the product information and processing guidance.
 ELASTOLLAN®
Special Products 33

1385 A 12 1390 A 12 SP 806 10 SP 883 10 1598 A 10 FC

ether base with extremely ether base with extremely

ether base with excellent
high water-vapor high water-vapor ether base for opaque films ester base for opaque films
burst behavior
permeability permeability

85 90 87 85
43 56
1.21 1.22 1.12 1.19 1.15
35 44 45 42 47
850 720 550 630 500
2.5 5 2.5 2
4.6 8 6 5 14.5
12 12 105
45 65 60 72 125
70 70 30 40 35
26 26 22 25
46 43 37 50
nb nb nb
nb nb nb

785 A 10 A C 70 D 10 QAFHF 1160 D 10 QA1

ester base with excellent
special aliphatic flame
wear resistance and hydro- special thermoplastic
retardant thermoplastic
lysis resistance, as well as polyether polyurethane
polyester polyurethane
good damping and rebound elastomer compound
elastomer compound
behavior
89
42 71 59
1.17 1.12 1.14
50 34 52
620 280 380

85 187 149
35
25
35
34 ELASTOLLAN®
Series N and BMB

Elastollan® Series N and BMB

Bio- or biomass balance (BMB-) based thermoplastic polyether
polyurethane elastomer

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Biobased carbon content (% total organic carbon) % ASTM D 6866

Property Unit of Measurement Test Procedure

Hardness Shore A DIN ISO 48-4 (3s)
Hardness Shore D DIN ISO 48-4 (3s)
Density g /cm³ DIN EN ISO 1183-1-A
Tensile strength MPa DIN 53504-S2
Elongation at break % DIN 53504-S2
Stress at 20 % elongation MPa DIN 53504-S2
Stress at 100 % elongation MPa DIN 53504-S2
Stress at 300 % elongation MPa DIN 53504-S2
Tear strength kN /m DIN ISO 34-1.B(b)
Abrasion mm³ DIN ISO 4649-A
Compression set at 23 °C / 72 hours % DIN EN ISO 815-1
Compression set at 70 °C / 24 hours % DIN EN ISO 815-1
Tensile strength after storage in water at 80 °C for 42 days MPa DIN 53504-S2
Elongation at break after storage in water at 80 °C for 21 days % DIN 53504-S2
Notched impact strength (Charpy) +23 °C kJ /m²
DIN EN ISO 179-1
Notched impact strength (Charpy) -30 °C kJ /m²
Biobased carbon content (% total organic carbon) % ASTM D 6866

For more detailed information, please refer to the product information and processing guidance.

* see reverse
 ELASTOLLAN®
Series N and BMB 35

Based on renewable resources

Identical material properties to those of equivalent
fossil-based products

Biomass balance based Polyether

BMB 1170 A 10 BMB 1185 A 10 BMB 1195 A 10
71 87 96
36 48
1.08 1.12 1.15
30 45 55
850 600 500
1.5 2.5 6
3.5 6 10
6.3 10 18
45 70 100
45 35 35
20 25 30
39 45 45
20 32 37
900 600 500
nb nb nb
nb nb nb

Bio-based Polyether
EXP N 1185 A 10 001* EXP N 1190 A 10 FHF*
87 90

1.12 1.25
45 28
600 550

70 60
35 30

57 50
36 ELASTOLLAN®
Infinergy®

Infinergy®
Expanded thermoplastic Polyurethane (E-TPU)

Property Unit Test Specification

Buld density (Beads) kg/m³
Particle weight of 50 beads g
Color
Molded density
10 mm test plate kg/m³ DIN EN ISO 845
20 mm test plate kg/m³ DIN EN ISO 845
Tensile strength* MPa According to DIN EN ISO 1798°
Elongation at break* % According to DIN EN ISO 1798°
Compressive stress** kPa
at 10 % strain According to DIN EN ISO 844°°
at 25 % strain According to DIN EN ISO 844°°
at 50 % strain According to DIN EN ISO 844°°
Rebound** % DIN 53512
Compression set (50 % /22 h /23 °C /24 h Relaxation)** % DIN EN ISO 1856 (Method C)
Dimensional stability under heat*. after anneling (4 h 70 °C) % According to DIN ISO 2796
Linear change in size after 4 days additional storage at 60 °C
Linear change in size after 4 days additional storage at 110 °C

For more detailed information, please refer to the product information and processing guidance.

* Meassured form 10 mm test plate

** Meassured form 20 mm test plate
° Deviating specimen (150 * 25.4 * 10 mm)
°° Deviating test speed (20 mm/s)
1
Molded without crack steam (max. Pressure 1.95 bar, max. cycle time 4.5 min)
2
Molded with crack steam (max. Pressure 1.3 bar, max. cycle time 3.5 min)
3
Molded with crack steam (max. Pressure 1.3 bar, max. cycle time 3 min)
 ELASTOLLAN®
Infinergy® 37

32-100 U101 100 HD1 X1125-130 U2 230 BLACK2 200 MP3

110 ± 15 140 ± 15 130 ± 10 130 ± 10 150 ± 10
5.6 ± 9.4 5.4 ± 8.6 5.7 ± 7.1 5.7 ± 7.1 2.4 ± 3.6
white white white black white

220 300 270 260 340

230 290 250 240 300
0.9 0.9 1.1 1.2 1.1
134 118 195 220 125

43 55 24 25 29
112 167 76 77 94
261 433 246 241 329
> 57 > 57 > 67 > 67 > 67
<8 <6 < 14 < 16 <5
< 2.5 < 5.0 < 3.5 < 2.5 < 2.0
< 1.0 < 0.5 < 0.5 < 0.5 < 0.5
< 4.5 < 5.5 < 6.0 < 4.5 < 4.0
38 ELASTOLLAN®
Masterbatches / Additives

Masterbatches / Additives
BASF also offers a selected range of Elastollan® TPU-based additives (masterbatches). The range is generally divided
into processing agents, e. g. mold release agents, functional additives such as crosslinkers or stabilizers, and color
masterbatches for coloring the base polymer.

Color Corresponds to RAL Conc

Mold release agent:
Yellow 1021 / 1018 133 F Conc 950/1 – can be used for both polyether
and as well as polyester-based Elastollan® grades
1012 138
Conc 978 – can be used for both polyether and
1021 139 as well as polyester-based Elastollan® grades
Orange 2004 201 F
especially for low viscosity grades
Conc V 2871 – suitable for both polyether and
2003 202 F / 1 polyester-based as well as polyester-based
Red 3000 315 F Elastollan® grades especially for low-viscosity
grades
Dark blue 5015 530 / 1
Conc 2907 – can be used for both polyether-
5015 530 / 4 and polyester-based as well as polyester-based
Elastollan® grades with improved sliding friction
Green 6028 602 / 1
properties (extrusion)
6001 618 / 1 Conc 2913 – can be used for polyether-based
Gray 7000 704
Elastollan® grades with reduced efflorescence
behavior
7032 718

Black 9005 917 / 3 Crosslinker concentrates to improve the com-

pression set and temperature resistance:
9005 917 / 4
X-Flex 2905 – bi-functional crosslinker
White 9010 955 X-Flex 2909 – bi- and tri-functional crosslinker
Extract from the Elastollan® portfolio of color masterbatches and additives
Abrasion improver:
Conc V 2881/1 – especially for expanded
­Elastollan®
Conc 2821/2 – for improved sliding friction
and reduced abrasion
 ELASTOLLAN®
Masterbatches / Additives 39

80 76.4
Degree of yellowness [YI]

70 66.3
1195 A 15
60
1195 A 15 + 4 % Conc 2877
50
40
33.2
30
19.5
20 17.8
13.3
9.6
10
3.7
0
0 100 300 500

Exposure time [h]

Influence of conc 2877 on the degree of yellowness as a

function of exposure time

UV stabilizers:
Conc 2876 – for polyester-based Elastollan® grades
Conc 2877 – for polyether-based Elastollan® grades
Conc 2926 – for polyether-based Elastollan® grades

Laser marking:
Conc V 2804 B – antimony-free additive
Conc 2918 – based on encapsulated antimony with
improved contrast properties

Blowing agent:
Conc V 2893 – Chemical blowing agent – can be used in
combination with physical blowing agent
Conc V 2894, Conc 2919 – Physical blowing agent

Other:
Conc 926 – matting agent for extrusion
Conc V 2464 – X-ray contrast agent
Conc 2908, Conc 2925 – for antistatic equipment
Selected product literature:

Thermoplastic Polyurethane Elastomers (TPU) – Think, create, Elastollan®

Elastollan® – Material Properties
Elastollan® – Processing Recommendations

Elastollan® Experimental Grade (EXP):

Elastollan® EXP grades are newly developed products or variations of existing commercial products that are in an experimental phase regard-
ing the evaluation of applicability, workability or new properties. Modifications of the product to improve properties must be expected without
prior information. After the evaluation phase, a decision is made as to whether the product will be commercialised under a new trade name.

3D Printing Applications and Hazards

3D printing is becoming a popular method for rapid prototyping. Please note that 3D printers use very different process mechanisms and that
emission of hazardous vapors and gases during the printing process is possible depending on the process parameters used. Furthermore,
it is possible that hazardous substances are used or generated during 3D printing with regard to skin contact. Against this background,
we strongly advise against the use of our products for private 3D printing processes. However, as the printing processes are manifold and
beyond our detailed knowledge, BASF Polyurethanes GmbH cannot give you any recommendations, detailed instructions or concrete mea-
sures for a safe handling of of our products in the 3D printing process. This is the sole responsibility of the user who markets or uses our
products in 3D printing applications.

Note
The data contained in this publication are based on our current knowledge and experience. In view of the many factors that may affect
processing and application of our product, these data do not relieve processors from carrying out own investigations and tests; nei-
ther do these data imply any guarantee of certain properties, nor the suitability of the product for a specific purpose. Any descriptions,
drawings, photographs, data, proportions, weights etc. given herein may change without prior information and do not constitute the
agreed contractual quality of the product. It is the responsibility of the recipient of our products to ensure that any proprietary rights
and existing laws and legislation are observed. ( September 2022 )

Further information on Elastollan® can be found on the

Internet:
® = egistered trade mark of BASF SE

www.elastollan.com

Please visit our websites:

www.plastics.basf.com
www.plastics.basf.de

If you have technical questions of the products,

please contact the Elastollan®-Infopoint:
PMEI 2203 RE