LG MABS
TR558A
LG Chem Ltd. - Methyl Methacrylate / ABS Sunday, October 2, 2022
General Information
Product Description
Description
• Transparency, General Purpose
Application
• Electric & Electronic Products
General
Material Status • Commercial: Active
• Asia Pacific • Latin America
Availability
• Europe • North America
Features • General Purpose • High Clarity
Uses • Electrical/Electronic Applications • General Purpose
RoHS Compliance • RoHS Compliant
Appearance • Clear/Transparent
Processing Method • Injection Molding
ASTM & ISO Properties 1
Physical Nominal Value Unit Test Method
Density / Specific Gravity 2 1.11 g/cm³ ASTM D792
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) 25 g/10 min ASTM D1238
Molding Shrinkage - Flow (23°C, 3.20 mm, Injection Molded) 0.40 to 0.70 % ASTM D955
Mechanical Nominal Value Unit Test Method
3 2350 MPa ASTM D638
Tensile Modulus (23°C, 3.20 mm, Injection Molded)
3 ASTM D638
Tensile Strength
Yield, 23°C, 3.20 mm, Injection Molded 52.0 MPa
3 ASTM D638
Tensile Elongation
Yield, 23°C, 3.20 mm, Injection Molded > 5.0 %
Tensile Elongation 3 ASTM D638
Break, 23°C, 3.20 mm, Injection Molded > 15 %
Flexural Modulus 4 (23°C, 3.20 mm, Injection Molded) 2550 MPa ASTM D790
4 79.0 MPa ASTM D790
Flexural Strength (23°C, 3.20 mm, Injection Molded)
Impact Nominal Value Unit Test Method
Notched Izod Impact ASTM D256
-30°C, 3.20 mm, Injection Molded 35 J/m
-30°C, 6.40 mm, Injection Molded 35 J/m
23°C, 3.20 mm, Injection Molded 130 J/m
23°C, 6.40 mm, Injection Molded 120 J/m
Hardness Nominal Value Unit Test Method
Rockwell Hardness (R-Scale) 113 ASTM D785
Thermal Nominal Value Unit Test Method
Deflection Temperature Under Load 5 ASTM D648
1.8 MPa, Unannealed, 6.40 mm, Injection Molded 83.0 °C
UL LLC ©2022. All rights reserved.
The information presented here was acquired by UL from the producer of the product or material or original information provider. However, UL assumes no
responsibility or liability for the accuracy of the information contained on this website and strongly encourages that upon final product or material selection
information is validated with the manufacturer. This website provides links to other websites owned by third parties. The content of such third party sites is not within
www.ulprospector.com our control, and we cannot and will not take responsibility for the information or content.
Page: 1 of 2
LG MABS TR558A
LG Chem Ltd. - Methyl Methacrylate / ABS
Thermal Nominal Value Unit Test Method
Vicat Softening Temperature 91.0 °C ASTM D1525 6
RTI Elec 60.0 °C UL 746B
RTI Imp 60.0 °C UL 746B
RTI Str 60.0 °C UL 746B
Flammability Nominal Value Unit Test Method
Flame Rating UL 94
1.5 mm HB
3.0 mm HB
Optical Nominal Value Unit Test Method
Light Transmittance (3200 µm, Injection Molded) 90.0 % ASTM D1003
Haze (Injection Molded) 1.80 % ASTM D1003
Processing Information
Injection Nominal Value Unit
Drying Temperature 80 to 90 °C
Drying Time 2.0 to 4.0 hr
Rear Temperature 180 to 200 °C
Middle Temperature 190 to 210 °C
Front Temperature 200 to 220 °C
Nozzle Temperature 200 to 230 °C
Processing (Melt) Temp 200 to 230 °C
Mold Temperature 40 to 60 °C
Back Pressure 29.4 to 58.8 MPa
Screw Speed 30 to 60 rpm
Injection Notes
Minimum Moisture Content: 0.01%
Notes
1
Typical properties: these are not to be construed as specifications.
2
23°C
3
50 mm/min
4
15 mm/min
5
Edgewise
6
Rate A (50°C/h), Loading 2 (50 N)
UL LLC ©2022. All rights reserved.
The information presented here was acquired by UL from the producer of the product or material or original information provider. However, UL assumes no
responsibility or liability for the accuracy of the information contained on this website and strongly encourages that upon final product or material selection
information is validated with the manufacturer. This website provides links to other websites owned by third parties. The content of such third party sites is not within
www.ulprospector.com our control, and we cannot and will not take responsibility for the information or content.
Page: 2 of 2