GURU GOBIND SINGH POLYTECHNIC, NASHIK

SEM-II APPLIED CHEMISTRY (22202)

MCQS FOR FINAL ONLINE EXAM

1. METALLURGY,CEMENT,LIME,REFRACTORIES
Sr No Question Option A Option B Option C Option D ANSWER
In a Blast furnace the temperature range in Zone 300 Degree 1000 Degree 1300 Degree 1500 Degree 300 Degree
12 d
of reduction is _______ Celsius to 1000 Celsius to 1300 Celsius to 1500 Celsius to 2000 Celsius to 1000
In smelting process _______ is used as a
16 d carbon zinc aliminium flux carbon
reducing agent.
Identify the concentration process of ore from magnetic Froth flotation Froth flotation
19 d roasting calcination
the given figure separation process process
Slag is an fusible material formed by
26 d Flux + ore Flux + mineral Flux + gaunge Flux + metal Flux + gaunge
combination of...
Name the Furnace which is 30 to 40 meters in Reverberatory
29 d Blast furnace Muffle furnace Heating Furnace Blast furnace
Height & is heated by hot air coming from twyer Furnace
The method of refining of a metal involving use
38 d Liquation ELectrorefining Distillation Poling Poling
of a green log of wood is ______
Name the refining method used for Low melting
39 d Liquation ELectrorefining Distillation Poling Distillation
point & volatile metals .
The concentration process of ore based on the gravity
54 d roasting calcination froth floatation froth floatation
principle of difference in wetting characteristics separation
Reverberatory Bessemer
56 Smelting process is carried out in ....... d Muffle furnace Blast furnace Blast furnace
furnace converter
The Molten Iron obtained from Blast furnace is
90 d Pure Iron pig Iron wrought Iron Blister Iron pig Iron
called ....
\"a\", \"b\" and \"c\" in the given figure a.zone of a.zone of fusion , a.zone of a. zone of heat a.zone of
91 d
represents____. reduction , b. b. zone of heat reduction , absorption , reduction , b.
linings of purifying of linings of
110 Refractory materials are used in........ d binding of metals alloying
furnaces. metal furnaces.
The zone of Heat Absorption in Blast furnace has 300 Degree 800 Degree 1300 Degree 1500 Degree 800 Degree
14 d
temperature range _______ Celsius to 1000 Celsius to 1300 Celsius to 1500 Celsius to 2000 Celsius to 1300
The zone of Fusion in blast furnace has 300 Degree 1000 Degree 1200 Degree 1500 Degree 1200 Degree
15 d
temperature range __________ Celsius to 1000 Celsius to 1300 Celsius to 1500 Celsius to 2000 Celsius to 1500
d CaO SiO2 CaCl2 SiO3
...........used as flux in blast furnace
d A-1, B-2, C-3 A-2, B-1, C-3 A-2, B-3, C-1 A-3, B-2, C-1
Match the pair
headd
Region of blast furnace at diameter of funcace become maximum isbody bosh
known as ------- hearth

d Liquiation Distillation Poling Electrorefining

Lead [Pb] and Tin [Sn] refined by ------- method
 d
Zinc [Zn] and Mercury [Hg] refined by ------- method Liquiation Distillation Poling Electrorefining

d Liquiation Distillation Poling Electrorefining

If impurity has strong affinity toward oxidation then we perform ------- refining method
d
pure metal converts into extra pure metal known as Reduction
---------- Crushing Refining pulverization

d Liquiation Distillation Poling Electrorefining

identify
d Liquiation Distillation Poling Electrorefining
identify
d Liquiation Distillation Poling Electrorefining
identify
d concentration calcination smelting pulverization
------ process takes place in blast furnace
300 Degree 800 Degree 1200 Degree 1500 Degree
d
Maximum temperature of blast furnaces reaches upto ------ Celsius Celsius Celsius Celsius
d dross sludge slag flux
impurity stuck on slopping surface of hearth in liquiation process of refining is known as --------
Haematite ore is physically concentrated froth flotation gravity calcination gravity separation
20 d Roasting process
by............... process separation process process
The mineral from which metal is extracet
24 d ore flux slag gaunge ore
economically & profitably is called as....
During extraction of metal ,the earthy impurities
25 d minreals gaunge slag flux gaunge
present in ore are called as.....
The device which is used for heating purpose,
27 d Burner furnace Vessel container furnace
during extraction of metals is called________
Name the process of physical concentration of Gravity Magnetic Gravity
31 d Froth flotation Reduction
ore, which is based on the principle of difference separation Separation separation
Name the process of physical concentration of Gravity Magnetic Magnetic
32 d Froth floatation Reduction
ore, which is based on the principle of difference separation Separation Separation
Name the process used for the physical Gravity Magnetic
33 d Froth flotation Reduction Froth flotation
concentration for Sulphide ores. separation Separation
Physical concentration of sulphide form of ore is gravity
34 d froth flotation roasting calcination froth flotation
done by __________ method. separation
35 The ore of iron is ______ d tinstone haematite galena bauxite haematite
The process of heating the ore in the presence of
36 d Calcination Reduction Roasting Smelting Roasting
Excess of air to a temperature below its melting
The chemical concentration of sulphide ore of Electrolytic
37 d Smelting calcination roasting roasting
copper is done by ___________. reduction
Identify the process of concentration of ore on Gravity magnetic Gravity
139 d calcination roasting
the basis of density separation separation separation
Identify the process of concentration of ore with froth flotation Magnetic gravity Magnetic
147 d calcination
electromagnetic roller process separation separation separation
160 Fe2O3 IS Chemical formula of d Magnetite Limonite Azurite Haematite Haematite
froth flotation gravity
171
Tinstone ore is physically concentrated by...…d process separation magnetic
Roasting process
 Ore and Mineral and
172 d
In magnetic separation method magnets are used toMineral and ore
separate _ _ _impurity metal
Ore and flux

173 d Calcination Concentration Roasting Reduction

Heating of an ore in presence of air/oxygen known as _____*
174 d Calcination Concentration Roasting Reduction
Heating of an ore in absence of air/oxygen known as _____*
Among the given ores, which one is NOT
175 d Copper pyrite Haematite Malachite Cuprite
a ore of copper? *
176 d CO2 CO SO2 SO3
Removal of volatile impurity in Roasting _ _ _ _ _
Froth flotation Gravity Magnetic Roasting
177 d
method is exclusively used only when pure ore is magnetic
process and impurity is non magnetic
separation separation process
178 d
Removal of volatile impurity in Calcination _ _ _ _ _ CO2 CO SO2 SO3

179 d Calcination
If Carbonate ores converts into oxide ores, then method is_ _ _ _ Concentration Roasting Reduction
Froth flotation Gravity Calcination Roasting
180 d
Iron pyrite FeS2 , Copper pyrite CuFeS2 , Galena PbS ore is physically
process concentrated
separation by...…
process process
181
If Sulphide ores converts into oxide & Sulphated ores,Calcination Concentration
then method is_ ___ Roasting Reduction

182 d Haematite Iron Pyrite Limonite Bauxite

Out of which is not ore of Fe
183 d
The naturally occurring substance from which metalMineral Ore
can be extracted economicallyGangue Flux
is known as...…..
Crushing& Crushing& Crushing& Concentration,
184 Correct sequence of metallurgy process is d
Pulverization, Pulverization, Pulverization, Crushing&
The naturally occuring substance from which
1 d Mineral Ore Gangue Flux Ore
metal can be extracted economically is known
The Percentage of carbon in medium carbon
2 ALLOY 1.5 to 2.5 % 0.05 to 0.03 % 0.3 to 0.6 % 0.6 to 1.3 % 0.3 to 0.6 %
steel is.....
The Percentage of Carbon in low carbon steel
3 ALLOY 0.05 -0.3 % 0.60% 0.6-0.8% 0.3-0.6% 0.05 -0.3 %
is......
The percentage of carbon in High carbon steel
4 ALLOY 0.3-0.6% 0.6-1.5% 1.5 to 2.5 % 0.6-0.8% 0.6-1.5%
is.....
Name the property of metal by virtue of which it
5 pr Malleability Ductility Hardness Brittleness Ductility
can be drawn into wire .
Fusible mass called slag is formed on reaction
6 D mineral and flux ore and flux gangue and flux metal and flux gangue and flux
between.......
Wood\'s metal is used for making safety plugs of highly resistant
8 ALLOY hard and tough highly magnetic easily fusible easily fusible
pressure cookers, sprinklers, fire alarms because to surface wear
Aluminium and
9 Tinman Solder is the alloy of.... ALLOY Lead and Tin Copper and TIn Zinc and Tin Lead and Tin
Tin
A type of steel is called Stainless steel because of high corrosion high corrosion
10 ALLOY boiling point appearence melting point
it\\\'s ..... resistance resistance
-------------- is generally made up of from high
11 ALLOY wires hammer rolled sheets condenser tubes hammer
carbon steel .
13 optiona o
 Reduction of iron extraction of research facility research facility
17 Muffle furnace is used for the purpose of .... mf refining of metal
ores copper in laboratories in laboratories
The desired temperature in the Muffle furnace is electrical heating using coke as electrical heating
18 mf hot blast of air Bunsen burner
attained by heating with...... coil fuel coil
1- c, 2-ca, 3-d, 4-
21 1- a, 2-c, 3-b, 4-d o 1- d, 2-c, 3-a, 4-b 1- b, 2-a, 3-c, 4-d optionb
b
22 1- d, 2-a, 3-b, 4- c o 1- b, 2-c, 3-d, 4- a 1- c, 2-b, 3-a, 4-d 1- a, 2-b, 3-d, 4-c optiona

23 1-d, 2-b, 3-c, 4-a o 1-a, 2-b, 3-c, 4-d 1-d, 2-a, 3-b, 4-c 1-b, 2-a, 3-c, 4-d optionc
Name the furnace which is oven like and is Reverbratory
28 mf Blast furnace Muffle furnace Heating furnace Muffle furnace
heated by external source of current. furnace
Reverbratory
30 Name the given furnace. mf Muffle furnace Blast furnace Heating furnace Muffle furnace
furnace
40 Chemical formula of cuprite ore is Cu Cu2O CuO CuFeS2 FeO Cu2O
cuprous Sulphide cupric Sulphide + cuprous Sulphide cupric Sulphide + cuprous Sulphide
41 Copper matte is a mixture of.... Cu
+ Ferrous Ferrous Sulphide + Ferric Sulphide Ferric Sulphide + Ferrous
During the extraction of Copper from Copper
42 Cu Smelting Bessemerisation Poling Electrorefining Bessemerisation
pyrite ore, the most important step in which
During electro-refining of copper the pure Cathode electrolytic Cathode
43 Cu Anode electrode Anode Mud
copper metal is obtained from..... electrode solution electrode
The property of metal by virtue of which it can
44 pr Ductility Malleability Toughness Hardness Malleability
be hammered into sheet is known as ....
Hardness is the property of metal/alloy to resist Breaking & Shocks &
45 pr Wear & Abrasion castability Wear & Abrasion
.... cracking vibrations
46 1-a, 2-c, 3-d, 4- b o 1-c, 2-d, 3-b, 4- a 1-b, 2-a, 3-c, 4- d 1- d, 2-b, 3-a, 4-c optionb

47 1- b, 2-a, 3-d, 4-c o 1- a, 2-c, 3-b, 4-d 1- c, 2-a, 3-d, 4-b 1- d, 2-a, 3-b, 4-c optiona
copper +tin +
48 Brass is an alloy of __________ ALLOY copper + tin copper + zinc zinc + tin copper + zinc
zinc
The alloying element which increases the tensile
49 ALLOY Carbon Silicon Magnesium Chromium Carbon
strength of pure Iron is_______---
The alloying element which increases the tensile
50 ALLOY Carbon Silicon Magnesium Chromium Carbon
strength of iron is------------
51 #NAME? o Brass duralumin woods metal tinmanns solder woods metal

52 #NAME? o Carbon Dioxide Iron oxide Copper oxide Nitrogen oxide Iron oxide
Otto Hofmann's Bomb Fractional Bomb
53 Identify the given figure- o Combustion tube
oven Calorimeter distillation Calorimeter
The sulphide ores are concentrated by froth difference in difference in difference in difference in difference in
55 d
flotation as it is based on the principle of........ densities of ore wetting magnetic preference to get wetting
Compression method for preparation of alloy Simultaneous melting the Reduction of one mixing mixing
57 ALLOY
involves..... deposition of metal and adding metal ore in component in component in
Name the method for preparation of alloy in Electrodepositio Reduction Compression
58 ALLOY Fusion method Fusion method
which the metals are heated to their melting n method method method
 Name the method of preparation of alloy in Electrodepositio Compression Reduction Compression
59 ALLOY Fusion method
which a mixture of two or more powdered n method method method method
The method used for the preparation of Wood\'s Electrodepositio Reduction Compression Compression
60 ALLOY Fusion method
metal is ______ n method method method method
__________ method is used for the preparation Electrodepositio
61 ALLOY Fusion Reduction Compression Fusion
of Brass and Bronze alloy. n
The ingredient used as binder in concrete
62 cement gravel cement water sand cement
mixture is ??.
75 The chemical formula of Lime is________ lime CaO CaO
A self healing material used to enhance
64 cement portland cement lime refractories biocement biocement
durability of building structure is _______
The process of hardening & setting of Hydraulic hydration & hydration &
65 cement oxidation carbonation decomposition
cement is due to_______ reaction hydrolysis hydrolysis
The process of hardening & setting of lime is due Hydration &
66 cement Decomposition Reduction Carbonation Carbonation
to?.. hydrolysis
Rapid hardening
67 #NAME? cement ordinary cement Portland cement Biocement Biocement
cement
------------------ cement provide chemical Rapid hardening
68 cement Portland cement ordinary cement white cement Portland cement
resistance ,to be used for construction of water cement
Rapid Hardening cement can be used for interior facing of Beams &
69 cement water dam pavement Beams & columns
construction of........ walls columns
70 #VALUE! 0 Calcium Oxide Aluminium Oxide Carbon dioxide Iron Oxide Carbon dioxide
On mixing cement & water a hard rigid mass is Clinker of Hardening of Setting of Hardening and
71 cement Setting of cement
formed due to initial gel formation which is cement cement cement setting of
On mixing cement & water ,a hard rigid mass is Hardening of clinkering of Setting of slaking of Hardening of
72 cement
formed which gradually changes into compact cement cement cement cement cement
Name the cement which is used as Eco-
73 cement coloured cement portland cement Bio -cement white cement Bio -cement
construction Material.
From the following, which statement is incorrect it is eco- it increases it is very efficent it evolves large it evolves large
74 cement
for bio cement ? contruction compressive compared to amount of amount of carbon
calcium
78 Slaked lime is formed when lime is mixed with?.. lime water carbondioxide air water
carbonate
cause cement to control initial lower clinkering give strength to cause cement to
138 If lime is added in excess quantity ,it will.......... lime
expand and setting time. temperature cement expand and crack.
148 Lime is prepared by _____________ lime Calcination Calcination
The cementing action of lime depends on the
152 lime hydrolysis hydration carbonation evaporation carbonation
rate of____________
From the following, which statement is not true it should be it should be it should be it should be it should be
79 rf
for Refractories. chemically stable physically stable thermally mechanically thermally
80 An alloy used in making parts of aeroplane is..... ALLOY Brass Duralumin stainless steel Gun metal Duralumin

81 An alloy used as casting for dental work is.... ALLOY Tinman's solder Brass Duralumin Wood's metal Wood's metal
Purification of copper is done by.............process
82 Cu Liquation Electrolysis Distillation Aluminothermic Electrolysis
to get high purity metal.
 Refractories are materials which have the High
83 rf High moisture High Resistance High pressure High temperature
property to withstand ..... temperature
84 CuFeS2 IS CHEMICAL FORMULA Cu Copper glance Azurite Cuprite Copper pyrite Copper pyrite

85 Acidic refractories contains____ rf Graphite MgO

Among the following, ________ is a Basic
86 rf CaO CaO
refractory.
87 The porosity of a good Refractory should be.... rf low High medium very high low
Refractory should possess the ability to be Fused at
88 rf conducting isolating isobaric isolating
perfectly --------- conditions of
154 Lime is also used as ____________in metallurgy. lime reducing agent flux oxidising agent retarder flux
Iron metal is used of making heavy machines due
92 pr Ductility Hardness mellability brittleness Hardness
to the property of ......
The refractoriness of refractory materials should
93 rf High low moderate None of these High
be....
Refractoriness is the ability of refractory material
94 rf pressure moisture heat reactivity heat
to withstand high________
Among the following------------- is not a neutral
95 rf Aluminium oxide Graphite Zirconia Chromite Aluminium oxide
refractory.
In which of the following application gypsum is Reduction of Thermal
96 cement Plastering of wall Slaking of lime Plastering of wall
used. metal expansion of
Name the type of steel used for making cutting Medium carbon
97 ALLOY low carbon steel High carbon steel Mild steel High carbon steel
tools. steel
The steel used for making axle shafts ,gearing Medium carbon Heat resistance Medium carbon
98 ALLOY low carbon steel High carbon steel
plates are.... steel steel steel
The low melting point alloy of tin and lead is
99 ALLOY brass woods metal bronze tinmann's solder tinmann's solder
______
The melting temperature of refractory material
101 rf Below Above Equal Moderate Above
should be well----------the operating temperature
102 _____ is an example of neutral refractory. rf Bauxite Magnesite quartz dolomite Bauxite
On the basis of chemical composition Acidic , basic , oxide, sulphide, ferrous and non High refractory Acidic , basic ,
103 rf
refractories are classified as___________ neutral carbonate ferrous and Super neutral refractory
The example of Acidic refractory materials is Magnesium
104 rf calcium oxide Silica Chromite Silica
........... oxide
Basic refractories are made up of basic material
105 rf Alumina Fire clay Silicon Carbide Quartz Alumina
such as...........
106 optiona o
From the following-------------- is the example of
107 rf Alumina Magnesia Zirconia Bauxite Zirconia
neutral refractory.
large size
108 A good refractory should have ________ rf Low porosity Medium porosity High porosity Low porosity
porosity
The effect of high porosity on the Refractory decrease in its increase in the has no effect on increases the life decrease in its
109 rf
is...... density and resistance to it. of refractory density and
 The sudden change in operating temperature in increase in load increase in high electrical
111 rf thermal spalling thermal spalling
a refractory causes ______ bearing strength porosity conducitivity
The effect of high temperature on the shape and contract at high expand at high deform at high remain stable at remain stable at
112 rf
size of refractory material is it ________ temperature temperature temperature high high temperature
Alumina and
113 #NAME? o Alloys Metals cement Alumina and silica
silica
Refractory materials are used in chemical they are highly they are high electrical they are
114 rf high porosity
industries that require high temperature for chemically active chemically inert conductivity chemically inert
The load bearing capacity of refractory should Depending on
115 rf High Low Constant. High
be......... temperature.
On alloying gold and silver with copper, it
116 ALLOY tensile strength weldability softness hardness. hardness.
increases their ________________
The melting point of an alloy is lower than the alloying element alloying element alloying element alloying element alloying element
117 ALLOY
pure metal because...... has low melting acts as impurity is in high is non metal. acts as impurity
Cut into any to have good to resist to resist shocks Cut into any
118 Machinability is the ability of metal to ......... pr
desired shape fluidity deformation or vibration. desired shape
The property by virtue of which metal gets a
119 pr Castability Brazing malleability Specific gravity Castability
desired shape by pouring a molten metal into a
The process of joining two or more metals by
120 pr Welding melting alloying brazing brazing
using non ferrous alloy between them is known
The property which describes the heaviness or Fatigue
121 pr Toughness Refractoriness Specific gravity Specific gravity
lightness of the metals is known as........... resistance
The ability of metal to resist weakening and Fatigue
122 pr Tensile strength Brazing Stiffness Fatigue resistance
structural damage by repeatedly applied loads is resistance
An ability of An ability to An ability to An ability to An ability of
123 Hardness of metal is__________ pr
metal to resist carry load deform under resist shocks or metal to resist
resist permanent carry load deform under resist shocks or resist shocks or
124 Toughness is an ability of a metal to ------------ pr
shape change or without breaking pressure. vibrations. vibrations.
An ability of An ability to An ability to An ability to An ability to carry
125 Tensile strength is----------- pr
metal to resist carry load deform under resist shocks or load without
The ability of substance to absorbs or release Specific
126 pr Specific gravity Specific heat Specific density Specific heat
energy is ---------- resistance
Fatigue occurs when the material is subjected to weakening and increase in weakening and
127 pr low density solidification
repeated loading and unloading which structural stiffness structural
high melting high tensile low melting Low corrosion low melting
128 Wood\'s metal has...... ALLOY
point strength point. resistance point.
Name the furnace in which heating is done by Reverberatory
129 d Blast Furance Muffle Furnace Retort Blast Furance
Blast of Hot air. furnace
An alloy of iron, ------- is preferred over pure Iron
130 ALLOY steel Aluminium Copper Tin steel
for machines construction.
For making rivets, bolts and nails which of the
131 ALLOY High carbon steel Tinman's solder low carbon steel Wood's metal low carbon steel
following alloy is used ?
a)-iii ,b)-iv , c)- ii) a)-iii , b)-i , c)- ii) a)-i b)-iv c)- iii) d)-
132 a)-ii , b)-iv, c)- i) , d)- iii) o optionb
,d)- i) ,d)- iv) ii)
Medium carbon
133 #NAME? ALLOY Duralumin low carbon steel High carbon steel High carbon steel
steel
134 Select the ferrous alloy among the following- ALLOY Tinman's solder Duralumin Brass Stainless steel Stainless steel
 The chemical ingredient of cement which
135 cement Alumina lime silica iron oxide iron oxide
provides colour to the cement is
lower the controlling initial controlling initial
136 The function of Gypsum in cement is to......... cement giving strength provide colour.
clinkering setting time of setting time of
Identify the component which when added in
137 cement Iron oxide Alumina Lime Silica Silica
excess amount in cement causes slow setting of
155 Slaking of lime is................ reaction lime Endothermic Exothermic Sublimation Reduction Exothermic
The presence of tricalcium silicate in the cement hardens cement causes cement to generates less lowers clinkering hardens cement
140 cement
________________ readily expand and heat of temperature of readily
The presence of iron oxide in the provides colour hydrates the causes initial generates more provides colour
141 cement
cement_______________ to the cement cement slowly. setting of heat of to the cement
to cause initial
The effect of tricalcium aluminate in cement provide colour to harden the generate less to cause initial
142 cement setting of
is___________ the cement cement slowly. heat of hydration setting of cement
cement
Most of the heat liberated during hydration of tetra calcium dicalcium tricalcium tricalcium
143 cement dicalcium silicate
portland cement is due to _______ aluminoferrite aliuminate aluminate aluminate
Tricalcium silicate develops strength in cement
144 cement 28 7 2 1 7
in___________days
decrease
prolong decrease heat of reducing curing prolong
145 Gypsum is added to cement to______________ cement strength after
hydration. hydration time hydration.
hydration
Chemical formula of gypsum is
146 cement CaSO4,2H2O CaSO4,2H2O
________________
________ is used for water purification, refining
156 lime cement Lime duralumin brass Lime
of sugar and in refractories.
157 Reaction of quick lime and water is called…… lime Cementing Slaking Hardening Setting Slaking
The lime having maximum percentage of CaO in
63 lime dolomite lime lean lime fat lime hydraulic lime fat lime
it is _______
151 optionb o
Greater than
76 The Percentage of \"CaO\" in Fat lime is?? lime 60-70% 70-80% Less than 50% Greater than 90%
90%
Quick hydraulic eminently poor hydraulic eminently
77 One of the type of hydraulic lime is _________ lime fat hydraulic lime
lime hydraulic lime lime hydraulic lime
A Mason has to Plaster the walls ,he will select feebly hydraulic
89 lime Fat lime poor lime Hydraulic lime Fat lime
which type of lime for this work? lime
149 Percentage of Calcium oxide in Fat lime is....... lime 70-80 % 60-70 % 80-90 % 95-98 % 95-98 %

----------------- contains 60-70 % CaO and 30-40 %

150 lime Fat lime Lean Lime Dolomite lime Hydraulic lime Dolomite lime
MgO
 Name the lime that has high percentage of clay Eminently Moderately Eminently
153 lime feebly hydraulic Dolomite
in it. hydraulic lime hydraulic lime hydraulic lime
The process of heating the ore strongly in the Aluminothermic
158 d Calcination Roasting Smelting Calcination
absence of air is known as................ process
Hardness of Gold can be increased by alloying it
159 ALLOY Cu Mg Ca Al Cu
with ______
Among the given ores, which one is NOT a ore of
161 Cu copper pyrite haematite malachite cuprite haematite
copper?
162 CuFeS2 IS CHEMICAL FORMULA Cu Copper glance Malachite Copper pyrite optionc Copper pyrite
Ferrous alloys are those alloys which contain
163 ALLOY Copper Iron Lead Aluminium, Iron
base metal as...
164 Non-Ferrous alloys is... ALLOY carbon steel Stainless Steel Duralumin Steel Duralumin
corrosion
165 Alloys are made to lower the ...... of metal. ALLOY tensile strength melting point toughness melting point
resistance
The role of gypsum added in cement is to control Hardening & Hardening &
166 cement softening setting only hardening only
the rate of ??. setting setting
Magnesium
The type of refractories that are NOT attacked by carborundum or carborundum or
167 rf alumina Silica oxide or Calcium
acidic or basic material are made up of ______ chromite chromite
oxide
A good refractory should have following high load bearing high electrical high chemical high load bearing
168 rf high porosity
property__________ strength conductivity reactivity strength
Refractories of low thermal conductivity are
169 rf Blast furnace Muffle furnace Retorts Recoperators Blast furnace
mostly used in
The amount of heat per unit mass required to
Specific
170 raise the temperature of substance by one pr Specific gravity Specific heat Specifi density Specific heat
resistance
degree Celsius is known as...........
291 both (A) and (B) O optiona