TECHNICAL DATA SHEET

UK / TDS / RM / Zinc+PVC Zinc / Rev: 01, July 07

RENO MATTRESSES
ZINC GALVANISED & PVC-ZINC GALVANISED
The Reno Mattress is a structure made of 6x8 or 8x10
hexagonal double twisted wire mesh type as per BS EN10223-
3 (Fig. 1 and 2). Reno Mattresses are filled with stones at the
project site to form flexible and permeable, monolithic Lid
structures such as river bank protection and channel linings for
erosion control.
The steel wire used to manufacture the mattress is heavily Zinc
coated soft temper steel. A PVC coating is then applied to Diaphragm
provide added protection for use in aggressive environments
where soil or water are acidic: in salt or fresh water, or
wherever the risk of corrosion is present. The PVC coating has
a nominal thickness of 0.50 mm. The standard combinations of
mesh and wire are shown in Tab. 2.
In order to reinforce the structure, all mesh panel edges are H
selvedged with a wire having a greater diameter (Tab. 3). L
Reno mattresses are divided into uniformly partitioned cells by
internal diaphragms. W
Dimensions and sizes of Reno Mattresses are shown in Tab. 1.
Wire
All tests on wire are performed prior to manufacturing the
mesh.
1. Tensile strength: the wire used for the manufacture of Figure 1
gabions have a tensile strength between 350-500 N/mm²
according to BS EN10223-3. Wire tolerances (Table 3) are
in accordance with BS EN10223-3.
2. Elongation: Elongation is greater than 10%, in accordance
with BS EN10223-3. The tolerance on the opening
3. Zinc galvanised coating: the minimum quantities of Zinc of mesh ‘D’ being the
shown in Table 3 meet the requirements of BS EN10244-2. distance between the axis of
Class A. two consecutive twists, is
4. Adhesion of Zinc: the adhesion of the Zinc coating to the according to BS EN10223-3
D
wire is such that, when the wire is wrapped six turns around
a mandrel having four times the diameter of the wire, it
does not flake or crack when rubbing it with the bare

P.V.C. (Polyvinyl Chloride) Coating

The technical characteristics and the resistance of the PVC to
ageing meet the relevant standards. The main values for the
PVC material are as follows: Figure 2

• The initial property of the PVC coating are in compliance with

ASTM A975-97 section 8.2.
• The PVC polymer has a minimum durability of 60 years when
tested in accordance with UL 746B Polymeric Material Long
Term Property Evaluation for heat aging test.

Lacing Operations
Lacing operations to assemble and connect Reno Mattress
units are made by using lacing wire specified in Table 2 and
described in Fig. 3.

Zinc galvanised or Stainless steel ring fasteners may be used

instead of lacing wire for Zinc galvanised coated mattresses or
PVC Zinc galvanised coated mattresses respectively. (Fig. 4
and Fig. 5). Wire for PVC Zinc coated rings are in accordance
with BS EN10223-3 & BS EN 10244-2. Stainless steel rings for
PVC coated mattresses are in accordance with ASTM A975
section 6.3.

Spacing of the rings shall be in accordance with ASTM A975

Table 2, Panel to Panel connection, Pull-Apart Resistance. Channel lined with Reno Mattresses

Page 1 of 2
 Maccaferri reserves the right to amend product specifications without notice and specifiers are
requested to check as to the validity of the specifications they are using.

1. Table of sizes for Reno Mattresses 2. Standard Mesh-Wire

Available mesh/wire Selvedge Lacing
Length (L) m Width (W) m Height (H)m Mesh Mesh Wire
size Type D (mm) Wire Wire
Tolerance (mm)
(mm) (mm)
3 2 0.17 PZ6/2.0
6 2 0.17 PZ6/2.0 6x8/ +16%
60 2.00 2.40 2.20
3 2 0.23 PZ6/2.0 Zinc+PVC - 4%
6 2 0.23 PZ6/2.0
3 2 0.30 PZ8/2.4 8x10/ +16%
80 2.40 3.0 2.20
6 2 0.30 PZ8/2.4 Zinc+PVC - 4%
3 2 0.50 PG8/2.7*
6 2 0.50 PG8/2.7* 8x10/ +16%
80 2.70 3.4 2.20
* These units are available in Galfan PVC coated as standard. Galfan+PVC - 4%
All sizes and dimensions are nominal.
Tolerances of ± 5% of the width, height, and length of the
gabions shall be permitted. 3. Standard wire diameters
Wire Diameter ø mm 2.0 2.2 2.4 2.7 3.0 3.4
Assembly and installation
Lacing operations can be made by using lacing wire or Wire Tolerance (±) ø mm 0.05 0.06 0.06 0.06 0.07 0.07
stainless steel fasteners. With stainless steel fasteners, the Min. Galvanising g/m 2
215 230 230 245 255 265
ring can be placed using automatic or manual tools (Fig. 5.).
The maximum spacing of the fasteners is determine by ASTM
A975 Table 2, Pull Apart Resistance test. For full details please
Quantity Request
When requesting a quotation, please specify:
see the Reno Mattress Product Installation Guide.
• No. of units,
• size of units (length x width x height, see Fig.1),
• type of mesh,
• type of coating.
EXAMPLE: No. 100 Reno Mattresses 3x2x0.17m - Mesh type
Lacing wire Rings 6x8 - Wire diameter 2.0 mm - PVC-Zinc.
Max
Max 200 mm
80-120 mm

1. Pliers
2. Pliers with

1 2 3 A nipper
3. Nipper

Figure 3

Open Closed
20 mm

Pneumatic

B
19

Spenax
tool
Nominal overlap of
50 mm
44
25 mm after closure
Figure 4 Figure 5

Maccaferri Ltd - Head Office Area offices

7600 The Quorum, Perth:
Oxford Business Park, North, T: 01738 621317 F: 01738 442283 E: [email protected]
Garsington Road, Oxford, OX4 2JZ Belfast:
Tel: 01865 770555 T: 028 9026 2830 F: 028 9026 2849 E: [email protected]
Fax: 01865 774550 Dublin:
Email: [email protected] T: 01 885 1662 F: 01 885 1601 E: [email protected]
Web: www.maccaferri.co.uk Web: www.maccaferri.ie Oxford, Perth, Belfast
Page 2 of 2