Datasheet EFPE 1001

This product is a calcium carbonate master batch containing 80% calcium carbonate, polyethylene resin, and additives. It is manufactured using modern extrusion technology to achieve a very fine and uniform dispersion without agglomeration, providing smooth surfaces and good gloss. Technical analysis shows the product has a melt flow rate of 0.5 g/10min at 190°C/2.16kg and 4.0 g/10min at 190°C/5kg, with a melt temperature of 110°C and bulk density of 1.22 g/cm3. It can be used at 5-30% and processed from 140-280°C.

Uploaded by

Mỹ Hạnh Bùi
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
419 views1 page

Datasheet EFPE 1001

This product is a calcium carbonate master batch containing 80% calcium carbonate, polyethylene resin, and additives. It is manufactured using modern extrusion technology to achieve a very fine and uniform dispersion without agglomeration, providing smooth surfaces and good gloss. Technical analysis shows the product has a melt flow rate of 0.5 g/10min at 190°C/2.16kg and 4.0 g/10min at 190°C/5kg, with a melt temperature of 110°C and bulk density of 1.22 g/cm3. It can be used at 5-30% and processed from 140-280°C.

Uploaded by

Mỹ Hạnh Bùi
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

PRODUCT INFORMATION AND DATA SHEET

PRODUCTION NAME: FILLER MASTER BATCH


PRODUCT GRADE: EFPE 1001

About Product
This product is a Calcium Carbonate master batch. It is manufactured in a twin screw extruder
machine using the most modern technology.
General Description
This product contains CaCO3, PE resin and additives. It is suitable for blowing film, extrusion,
etc. This product has very fine dispersion that guarantees free agglomeration, bringing to the
end product more gloss and smooth surface.
Technical Analysis
Physical Property
Items Test method Value Unit
Calcium Carbonate (CaCO3) content ASTM D 5630 80 wt%
Melt Mass-Flow Rate (190oC/2.16kg) ASTM D 1238 0.5 g/10min
Melt Mass-Flow Rate (190 C/5kg)o
ASTM D 1238 4 g/10min
Melt Temperature (DSC) 110
o
C
Bulk density ASTM D1895 1.22 g/cm3
Particle size of CaCO3 Powder D50 Malvern 3 µm
Moisture ASTM D6980 < 0.08 wt%

Properties:
Appearance (Surface color): White
Additives: Dispersion agent, processing aid
Processing temperature: 140 – 280oC
Usage rate: 5 - 30 %
Pellet Size: 3x3 (±0.3) mm
Packaging: 25 kg per PE/PP bag (or 1250kg/jumbo bag)
Storage: Keep at dry condition

Caution:
- This product information is based on our general experience and does not constitute a specification. Since many
factors affect the use of our products, no warranty is given or implied with respect to this information or patent
infringement. We do not accept liability for any loss or damage arising from the use of this information. All sales
are subject to our Standard Terms and Conditions of Sale.