The test results document summarizes the performance of Hi-Pon 50-01 polyurethane top coat in various tests. The coating passed bending, abrasion resistance, fire propagation, carbon dioxide diffusion, pencil hardness, cross-cut adhesion, impact, salt spray, humidity, chemical resistance, pull-off adhesion, accelerated weathering, and crack bridging tests. The results were based on testing with white color using a primer and two top coats applied to the specified dry film thicknesses on test panels prepared with sand blasting.

Uploaded by

janaka
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
265 views1 page

50-01 Test Report

The test results document summarizes the performance of Hi-Pon 50-01 polyurethane top coat in various tests. The coating passed bending, abrasion resistance, fire propagation, carbon dioxide diffusion, pencil hardness, cross-cut adhesion, impact, salt spray, humidity, chemical resistance, pull-off adhesion, accelerated weathering, and crack bridging tests. The results were based on testing with white color using a primer and two top coats applied to the specified dry film thicknesses on test panels prepared with sand blasting.

Uploaded by

janaka
Copyright
© © All Rights Reserved
We take content rights seriously. If you suspect this is your content, claim it here.
Available Formats
Download as PDF, TXT or read online on Scribd
You are on page 1/ 1

TEST RESULTS

HI-PON 50-01 POLYURETHANE TOP COAT

Ref : Test Result/TR-073


Established: 08 Jul 14
Updated: 24 Jun 20

Test Items Test Methods Results


ASTM D522
Bending Test* Method A Passed 4 mm
Mandrel Diameter (mm)
ASTM D4060

Abrasion Resistance* Abrasive Type: CS10 50

weight loss (mg/1000 cycles)

BS 476 Part 6 Index of performance (I): <12


Fire Propagation
(Certified by TUV SUD PSB) Sub-index performance (i1): <6
BS 476 Part 7
Surface spread of Flame Class 1
(Certified by TUV SUD PSB)
EN ISO 1062-2
Diffusion equivalent air layer
Carbon Dioxide Diffusion Method A (Gravimetric)
thickness, R > 50 m
(Certified by TUV SUD PSB)
EN ISO 7783-2
Water Vapor Transmission < 5.0 g/m2/24 Hrs
(Certified by Setsco)
ASTM D3363
Pencil Hardness Passed H
(Uni Pencil)

ISO 2409
Cross-cut Adhesion Grade 0
(3mm blade)

Impact Test ISO 6272 Passed 5J


Salt Spray Test ISO 9227 Passed 1000 hours
(5% NaCl)
Humidity Test ISO 6270 Passed 1000 hours
Chemical Resistance ISO 2812-1
(Spot Test) 10% H2SO4 Solution Passed 168 hours
10% NaOH Solution Passed 168 hours
Pull-off Adhesion Test (PAT) ISO 4624 Minimum 5 MPa

Accelerated Weathering ISO 16474-3


QUV A Gloss Retention, 60° at Passed 80% Gloss Retention
minimum 1500 Hrs

BS EN 1062-7:2004
Crack Bridging Ability Method A: Continuous ≥ 0.4 mm
Opening of Crack

REMARK:
1. Above results were based on White Colour. Results may vary marginally from colour to colour.
2. Surface Preparation before testing: Sand blasting to Sa. 2.5
3. Paint system on which test was performed: 1 coat of 100 µm (DFT) Hi-Pon 20-04 STE 80
2 coat of 50 µm (DFT) Hi-Pon 50-01 Polyurethane Top Coat
4. Test item with (*) performed with 1 coat of 60 µm (DFT) Hi-Pon 50-01 Polyurethane Top Coat

NIPPON PAINT (SINGAPORE) CO PTE LTD


1, First Lok Yang Road, Jurong, Singapore 629728. Tel: 6268 5355 Fax: 6264 1603
Co Reg No. 196200138N
www.nipponpaint.com.sg

A MEMBER OF THE NIPSEA GROUP

DISCLAIMER:
The above information is given to the best of Nippon Paint’s knowledge and practical experience. It has been compiled based on data
obtained under laboratory test conditions. Actual performance will depend upon the conditions in which the product is used. Users may
consult with Nippon Paint on the general suitability of the product for their needs and specific application practices though it remains
each user’s responsibility to determine the suitability of the product for the user’s particular use. Nippon Paint does not and cannot
warrant the results which the user may obtain by using the product. In no event will Nippon Paint be liable to the user for any kind of loss
(whether direct or indirect) even if Nippon Paint was previously advised of it.

You might also like