BUREAU OF INDIAN STANDARDS
BIS, Patna Branch Laboratory (PBL) ULR No. :
DOC No. : Bureau of Indian Standards, Patliputra Industrial
Telephone : 9955998957 Estate, Patna - 800013, Patna, Patna, Bihar, India -
FAX : - 800013
E-Mail :
[email protected] BO Code : NOBO
Test REPORT AS PER : IS 1786 (2008)
QR Code/Barcode : 100000493932
REPORT NO : NOBO/70269/20231020/MS/9_1 DATE : 30 Nov, 2023
PART A. PARTICULARS OF SAMPLE SUBMITTED
a) Customer Name & Address : -
b) Nature of sample : MS
c) Grade/Variety/Type/Class Size etc : Type / Size / Grade / Variety : Size 10mm TMT,
Type / Size / Grade / Variety : Grade Fe 550
d) Declare values, if any : --
e) Batch No. & Date of Manufacture : AS/153/
f) Quantity : 6 nos x 1 mtr
g) Date of Receipt : 06 Nov, 2023
h) BIS Seal : Verified by Sample Cell
i) IO's Signature : Verified by Sample Cell
j) Any other Information / Expiry Date, If any : /
k) Date of Commencement of Testing : 14 Nov, 2023
l) Date of Completion of Testing :
m) Section Code : 23MAD18N
n) Section Report No. : 23MAD18N_1
o) Report Type : New
p) Reference Report No. :
q) Remarks :
GAURAV MEENA
OIC SAMPLE CELL
(Authorized Signatory)
Authorized on: 30 Nov, 2023 16:36 PM
1. This report, in full or in part, shall not be published, advertised, used for commercial purpose or any legal action,
unless prior permission has been ecured from the Director General, Bureau of Indian Standards . This report Is
intended for "BIS CERTIFICATION MARKS PURPOSE ONLY"
2. This test report is ONLY FOR THE SAMPLE TESTED.
This is a Computer Generated Report.
Page 1 of 5
Section Report No. : 23MAD18N_1 IS 1786 (2008)
PART B. SUPPLEMENTARY INFORMATION
1. Reference to sampling procedure, wherever applicable. No
2. Supporting documents for the measurements taken and results derived like graphs, No
table sketches and or photographs as appropriate to test report, if any.
3. Deviation from the test methods as prescribed in relevant ISS/Work instruction, if any. No
3. NABL Report required ? No
DEEPAK PATRA
OIC Mechanical
(Authorized Signatory)
Authorized on: 30 Nov, 2023 15:42 PM
This is a Computer Generated Report.
Page 2 of 5
Section Report No. : 23MAD18N_1 IS 1786 (2008)
PART C. TEST RESULT
S.No. Clause No Parameter - Test Description Min Max Unit Result/
Table No. Method of test Limit Limit Observation
Sl. No
1 Cl. 5 Cl.5 Mean area of mm²/mm 1.2 - mm²/mm 2.12
ribs/unit length (Ar),
2 Cl. 5 Cl. 5 - Mean mm²/mm 0.4 - mm²/mm 2.12
projected area of
transverse ribs (1/3
of Ar)
3 Cl. 6.1 Nominal Size mm - - - 10 mm declared
4 Cl. 7.2 Table -2 Nominal Mass kg/m - - - Spe req(kg/m): 0.617
-8% Result: 0.5947
5 Cl. 8.1 Table 3 Yield Stress (YS) N/mm² 550.0 - N/mm² 665.787
6 Cl. 8.1 Table 3 Tensile Strength (TS) N/mm² 585.0 - N/mm² 776.399
7 Cl. 8.1 Table 3 TS/YS ratio Ratio - - - Spe Req: Greater
than or equal to 1.06
Result: 1.166
8 Cl. 8.1 Table 3 Elongation, % 10.0 - % 17.82
percentage
9 Cl. 9.3, Table 4 Bend Test The bend test shall - - - Satisfactory
be performed in
accordance with the
requirements of IS
1599. The test piece,
when cold, shall be
doubled over the
mandrel by
continuous pressure
until the sides are
parallel. The
specimen shall be
considered to have
passed the test if
there is no rupture or
cracks visible to a
person of normal or
corrected vision on
the bent portion.
10 Cl.9.4 & Cl. 9.4.1 Rebend test The test piece shall - - - Satisfactory
be bent to an include
angle of 135 degrees
using a mandrel of
appropriate
diameter. The bent
piece shall be aged
by keeping in boiling
water (lOO°C) for 30
min and then allowed
to cool. The piece
shall then be bent
back to have an
included angle of
157.5 degrees. The
specimen shall be
considered to have
passed the test if
there is no rupture or
cracks visible to a
person of normal or
corrected vision on
the rebent portion.
11 Cl 5 Deformations and Requirement For - - - Test Not Applicable
Surface Bond
Characteristics
Page 3 of 5
DEEPAK PATRA
OIC Mechanical
(Authorized Signatory)
Authorized on: 30 Nov, 2023 15:42 PM
This is a Computer Generated Report.
Page 4 of 5
Section Report No. : 23MAD18N_1 IS 1786 (2008)
PART D. REMARKS
DEEPAK PATRA
OIC Mechanical
(Authorized Signatory)
Authorized on: 30 Nov, 2023 15:42 PM
This is a Computer Generated Report.
Page 5 of 5 End of Report