Polypropylene Homopolymer Woven Sacks
Product Description: Recommended Applications:
PP Homopolymer 1030RG is recommended for
PP Homopolymer 1030RG is a natural colored
stretched tapes of Woven sacks like
grade produced by the latest Spheripol II
Fabrics for general packaging
Technology with following features:
Cement & polymers packaging
Exceptional processability
Food grains packaging
Low water carry over
Technical Datasheet
Carpet packing
Good balance of tenacity & elongation
Typical Properties:
Tested Properties Test Method UOM Values*
Resin Properties
0
Melt Flow Index (230 C & 2.16 Kg) ASTM D 1238 gm/10 min 3.3
o 3
Density @ 23 C ASTM D 1505 gm/cm 0.90
Mechanical Properties
Tensile Strength @ Yield (50 mm/min) ASTM D 638 MPa 35
Elongation @ Yield (50 mm/min) ASTM D 638 % 12
Flexural Modulus (1.3 mm/min) ASTM D 790 MPa 1550
o
Notched Izod Impact Strength @ 23 C ASTM D 256 J/m 50
Thermal Properties 2
Heat Deflection Temperature (0.46 N/m ) ASTM D 648 o C 95
ASTM D 1525 o C 156
* Typical values not to be construed as specification limits. Values may change without any prior notice.
* Mechanical properties tested on specimen molded as per ASTM D 4101 and conditioned as per ASTM D 618.
o
Recommended Processing Temperature: 170 – 230 C
Packaging Information:
This material is packed and available in raffia bags with net content of 25.0 Kg only. The raffia bags used conforms to the minimum strength requirements of BIS,
however, customer shall take due care while handling the bag. Prolonged exposure of these bags to sunlight may deteriorate the bag’s performance and cause
spillage and wastage. IOCL does not warranty loss of material due to poor material handling practices.
Regulatory Information: Storage & Handling:
Product
PP Homopolymer 1030RG shall meet the requirements stipulated Prevent PP Material from direct exposure to sunlight & heat to avoid quality
in IS 10910 on 'Specification for Polypropylene and its Copolymers deterioration. The storage location should be dry, dust free and the Storage
o
for safe use in contact with Foodstuff, Pharmaceutical & Drinking temperature should not exceed 50 C. Non - compliance to these precautionary
water'. The grade and Additives incorporated in this grade shall measures can lead to degradation of the product causing Color changes, Odor &
meet the positive list of constituents as prescribed in IS 10909. inadequate product performance. It is advised to process PP material within 06 months
The Grade and the additives incorporated in it will also comply with after delivery.
the FDA: CFR Title 21,177.1520, Olefin Polymers.
Disclaimer: IOCL assumes no liability whatsoever in respect of application, processing or any use made of the aforementioned information or products, or any consequence thereof. No liability whatsoever shall attached to
any of the IOCL companies for any infringement of the rights owned or controlled by a third party in intellectual, industrial or other property by reason of application, processing or use of the afore-mentioned information or
products by the user.
00-12/13