STRUCTURAL ENGINEERING DIVISION

Test Floor Laboratory

Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202

Ref: CED/TFL/01/29432-443 Dated: 12-01-18

To,
RE (Reach-3)
MMP Peshawar
(Peshawar Sustainable Bus Rapid Transit Project Reach-III)

Subject: - CALIBRATION OF PRESSURE GAUGE (ARK: TFL/01/29432)

Reference to your Letter No. RE/MMP/RH-03/BRT-PDO/03, Dated:

23/11/2017 on the subject cited above. One Pressure Gauge (EN837-I) as received by us
has been calibrated. The results are tabulated as under:

Total Range : Zero - 15000 (Psi)

Calibrated Range : Zero - 7000 (Psi)

Pressure Gauge Reading (Psi) 1000 2000 3000 4000 5000 6000 7000

Calibrated Load (kg) 15000 28200 42000 56000 69200 84400 98000

Calibrated Pressure (Psi) 1077.50 2025.70 3017.00 4022.67 4970.87 6062.73 7039.67

The Ram Area of Calibration = 198 cm2

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Quality Manager
Typsa-Asian Jv
Passenger Terminal Expansion Project at Allama Iqbal International Airport (AIIAP), Lahore –
Car Parking Package (Mughal Steel)
Reference # CED/TFL 29433 (Dr. Aqsa) Dated: 12-01-2018
Reference of the request letter # TYPSA-PK-858-16 Dated: 11-01-2018

Tension Test Report (Page -1/1)

Date of Test 12-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual
(inch)

(inch)
(#)

(kg) (kg)

1 0.377 3 0.376 0.11 0.111 3800 4800 76200 75630 96200 95600 0.90 11.3

2 0.365 3 0.370 0.11 0.107 3800 4800 76200 78030 96200 98600 0.90 11.3

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Resident Engineer
The Islamia University of Bahawalpur
Construction of Overhead Water Reservoir & Pump House of IUB Sub Campus at Rahim Yar
Khan

Reference # CED/TFL 29434 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # 70/Engg Dated: 11-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load

Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.417 3/8 0.395 0.11 0.123 5300 6000 106200 95270 120300 107900 0.80 10.0

2 0.420 3/8` 0.396 0.11 0.123 5200 6000 104200 92910 120300 107200 0.80 10.0

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and two samples for bend test

Bend Test
3/8" Dia Bar Bend Test Through 180º is Satisfactory
3/8" Dia Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202

To,
Resident Engineer
ACE (Pvt) Ltd
Construction of Administration Block & Appartment New Campus of GCU at KSK Campus –
Package-3
Reference # CED/TFL 29435 (Dr. Ali Ahmed) Dated: 12-01-2018
Reference of the request letter # RE/ACE Arts/GCU/ECC/188 Dated: 10-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load

Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.434 3/8 0.403 0.11 0.128 4600 6000 92200 79510 120300 103800 0.90 11.3

2 0.427 3/8 0.400 0.11 0.126 4800 6200 96200 84240 124300 108900 1.00 12.5

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
3/8" Dia Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
M/S Ittefaq Building Solutions Pvt Ltd
Lahore
(Allied Bank New International Airport Islamabad)

Reference # CED/TFL 29436 (Dr. Aqsa) Dated: 12-01-2018

Reference of the request letter # IBS/ABL/ST01 Dated: 11-01-2018

Tension Test Report (Page -1/1)

Date of Test 12-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.369 3/8 0.371 0.11 0.108 3100 4800 62200 63070 96200 97700 1.20 15.0

2 0.367 3/8 0.370 0.11 0.108 3100 4800 62200 63380 96200 98200 1.20 15.0

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile test

Bend Test

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Sub Divisional Officer
Highway Sub Division Daska
(Construction of Metalled Road from Buj Arian to Bera Bazi Garan via Galotion Morr, Galotian Khurd Mohala khan own,
Galotian Chowk, Kotki Manga (Section km no. 0.00 to 3.10 Length= 3.10 km, Part-A)
Reference # CED/TFL 29437 (Dr. Ali Ahmed) Dated: 12-01-2018
Reference of the request letter # 241/D Dated: 27-12-2017

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.367 3/8 0.371 0.11 0.108 4000 5000 80200 81750 100200 102200 1.20 15.0

2 0.368 3/8 0.371 0.11 0.108 4000 4900 80200 81500 98200 99900 1.00 12.5

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
3/8" Dia Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Sub Divisional Officer
Buildings Sub Division
Shakargarh
(Re-construction of Dangerous School Buiolding GPS Jhumian Kalan Tehsil Shakargarh)

Reference # CED/TFL 29438 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # 578/Sg Dated: 19-12-2017

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load

Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.370 3/8 0.372 0.11 0.109 3700 4900 74200 75020 98200 99400 1.10 13.8

2 0.402 3/8 0.388 0.11 0.118 3300 5200 66200 61590 104200 97100 0.90 11.3

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile test

Bend Test

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Project Manager
U.C.C. (Pvt) Ltd
CAT V 188 Houses C 4 at Chashma

Reference # CED/TFL 29439 (Engr. Bilal) Dated: 12-01-2018

Reference of the request letter # UCC/STEEL/17/MOV/1283 Dated: 11-01-2018

Tension Test Report (Page -1/1)

Date of Test 12-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.371 3/8 0.373 0.11 0.109 3600 5500 72200 72770 110200 111200 1.10 13.8

2 0.372 3/8 0.373 0.11 0.109 4100 5500 82200 82720 110200 111000 1.00 12.5

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
3/8" Dia Bar Bend Test Through 180º is Satisfactory

Witness by Fiaz Hussain Khan (C. Tech (Civil) WASO)

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
M/S Defence Housing Authority.
Lahore Cantt
(Infra Dev Works of Prism-9 Pkg-III & IV Sector-C&M DHA Phase - IX)(M/S NLC)(Bashir)

Reference # CED/TFL 29440 (Dr. M Rizwan Riaz) Dated: 12-01-2018

Reference of the request letter # 408/241/E/Lab/13/311 Dated: 11-01-2018

Tension Test Report (Page – 1/1)

Date of Test 17-01-2018
Gauge length 2 inches
Description MS Pipe Steel Strip Tensile and Bend Test
Size of Strip

Yield Stress
Designation

Elongation
Yield load
X Section

Breaking

Ultimate

% Elongation
Stress
Load
Area

Remarks
Sr. No.

(inch) (mm) (mm2) (Kg) (Kg) (MPa) (MPa) (in)

1 MS Pipe 16 26.80x6.30 168.84 5000 6700 290.51 389.29 0.50 25.00

2 MS Pipe 16 26.80x6.00 160.80 5000 6200 305.04 378.25 0.60 30.00

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -

- - - - - - - - - - -
Only Two Samples for Tensile and One Sample for Bend Test

Bend Test
Strip Taken from MS Pipe 16" Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Resident Engineer
NESPAK
Signal Free Corridor from Walton Road to Lallak Chowk DHA, Lahore

Reference # CED/TFL 29442 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # 3790/103/MHK/02/44 Dated: 11-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual
(inch)

(inch)
(#)

(kg) (kg)

1 0.369 3 0.372 0.11 0.108 3800 5000 76200 77220 100200 101600 0.90 11.3

2 0.367 3 0.370 0.11 0.108 4300 5300 86200 87950 106200 108400 0.90 11.3

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Construction Manager
On behalf of CNEEC-FNEPC Jv

Reference # CED/TFL 29444-445 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # CNCEEC/NEW/LAHORE(Extn)/NESPAK/001Dated: 12-01-
2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.378 3 0.376 0.11 0.111 3500 5400 70200 69340 108200 107000 1.10 13.8

2 0.368 3 0.371 0.11 0.108 3500 5200 70200 71410 104200 106100 1.10 13.8

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory

Witness by Engr. Asad Shafiq (Jr. Engr G-8 (a) NESPAK)

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Project Manager
Ittefaq Construction Services
Construction of Apartment Building, Plot # 81, Block - C/1, Gulberg III Lahore

Reference # CED/TFL 29446 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # ICS/M.A/0 Dated: 12-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Load
Diameter/ Area Yield Stress Ultimate Stress

% Elongation
Size (in2) (psi) (psi)

Remarks
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual
(inch)

(inch)
(#)

(kg) (kg)

1 0.368 3 0.371 0.11 0.108 4000 4600 80200 81420 92200 93700 1.00 12.5

2 0.374 3 0.374 0.11 0.110 4500 5200 90200 90330 104200 104400 1.00 12.5

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile test

Bend Test

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Resident Engineer
Al-Imam Enterprises (Pvt) Ltd
Construction of Penta Square, Phase-V, D.H.A, Lahore
(AF Steel)
Reference # CED/TFL 29447-448 (Dr. Ali Ahmed) Dated: 12-01-2018
Reference of the request letter # Al-Imam/746/PS-1/DHA/LHE/451 Dated: 10-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.415 10 10.01 0.11 0.122 3400 5200 68200 61440 104200 94000 1.30 16.3

2 0.412 10 9.98 0.11 0.121 3200 5000 64200 58190 100200 91000 1.40 17.5

3 0.399 10 9.81 0.11 0.117 3100 4900 62200 58320 98200 92200 1.20 15.0

4 0.402 10 9.85 0.11 0.118 3300 5300 66200 61600 106200 99000 1.20 15.0

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only four samples for tensile and two samples for bend test

Bend Test
10mm Dia Bar Bend Test Through 180º is Satisfactory
10mm Dia Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
Ref: CED/TFL/01/29449-475 Dated: 12-01-18

To
Project Engineer – Civil
Grid Solution Pakistan (Private) limited
Procurement of 220/132kV GIS Plant, Design, Supply, Installation, Testing &
Commissioning at Ghazi Road Lahore

Subject: TESTING OF R.C.C. PIPE [ASTM-C76]

Reference to your letter No. P-60194/30, dated 12.01.2018 on the subject

cited above. Two R.C.C. Pipes as received by us have been tested. The results are

tabulated as under.

Proof load
Thickness

Ultimate
Diameter

Diameter
External

Ultimate
Nominal

Internal
Loaded
Length

Length

Stress

Stress
Proof
Total

Load
Wall
Size

Sr.
No
.
(mm) (m) (m) (mm) (mm) (mm) (Kg) (Kg) N/m/mm N/m/mm

1 225 2.371 2.270 280.00 224.52 27.74 7200 9400 138.59 180.93

2 300 2.375 2.222 405.00 310.66 47.17 12100 13500 171.96 191.86
Witness by Amjad Tufail (S.E NESPAK)

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
M/S Westcom Construction (Pvt) Limited
Lahore

Reference # CED/TFL 29450 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # Nil Dated: 12-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/ Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
(inch)
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual

(inch)
(kg) (kg)

1 0.390 3 0.382 0.11 0.114 3600 5900 72200 69300 118300 113600 0.75 9.4

2 0.395 3 0.385 0.11 0.116 3600 5900 72200 68260 118300 111900 1.10 13.8

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
GM
Professional Construction Services (Pvt) Ltd
Housing & Academic Block at Namal University Mianwali

Reference # CED/TFL 29451 (Dr. Ali Ahmed) Dated: 12-01-2018

Reference of the request letter # PCS/18/Eng-24 Dated: 12-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Diameter/
Load
Area Yield Stress Ultimate Stress

% Elongation
Size
(in2) (psi) (psi)

Remarks
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual
(inch)

(inch)
(#)

(kg) (kg)

1 0.422 3 0.398 0.11 0.124 4900 6100 98200 87020 122300 108400 1.10 13.8

2 0.427 3 0.400 0.11 0.126 4900 6100 98200 85950 122300 107000 1.20 15.0

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only two samples for tensile and one sample for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202
To,
Sub Divisional Officer
Development Sub Division
Bahawalnagar
((Rehablitation of Malik Baranch and Gajjiani Disty Construction of Fall Cum Bridge at RD
23+900)
Reference # CED/TFL 29452 (Dr. Ali Ahmed) Dated: 12-01-2018
Reference of the request letter # 01 Dated: 01-01-2018

Tension Test Report (Page -1/1)

Date of Test 15-01-2018
Gauge length 8 inches
Description Deformed Steel Bar Tensile and Bend Test as per ASTM-A615

Elongation
Yield load

Breaking
Weight

Load

Diameter/ Area Yield Stress Ultimate Stress

% Elongation
Size (in2) (psi) (psi)

Remarks
Sr. No.

Nominal

Nominal

Nominal

Nominal
(lbs/ft)

Actual

Actual

Actual

Actual
(inch)

(inch)
(#)

(kg) (kg)

1 0.383 3 0.378 0.11 0.112 2800 4200 56200 54870 84200 82400 1.00 12.5

2 0.385 3 0.380 0.11 0.113 2800 4300 56200 54520 86200 83800 1.40 17.5

3 4.285 10 1.266 1.27 1.260 26400 42000 45900 46200 72900 73500 2.10 26.3

4 4.283 10 1.266 1.27 1.259 27400 44600 47600 47980 77500 78100 2.00 25.0

- - - - - - - - - - - - - -

- - - - - - - - - - - - - -
Note: only four samples for tensile and two samples for bend test

Bend Test
#3 Bar Bend Test Through 180º is Satisfactory
#10 Bar Bend Test Through 180º is Satisfactory

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples
 STRUCTURAL ENGINEERING DIVISION
Test Floor Laboratory
Department of Civil Engineering
University of Engineering and Technology Lahore, 54890
Pakistan. Ph: 92-42-99029202

I/C Testing Laboratoires

UET Lahore, Pakistan.
Note:
1- You can See your reports On Internet in the following web site
http://www.uet.edu.pk/faculties/facultiesinfo/civil/index.html?RID=testing_reports
2. The above results pertain to sample /samples supplied to this laboratory.
3- Sealed sample / Unsealed sample / Marked sample/Signed Samples