WELDING PROCEDURE QUALIFICATION RECORD (WPQR)
N. 18VE0048PO2\A
Manufacturer ITAQUA Srl - Trieste (TS)
WPQR No. 02\2018 Dated 13/03/2018
Manufacturer’s welding procedure (WPS) No. 02\2018 Dated 22/01/2018
RANGE OF APPROVAL
Welding process 131 Type Partly mechanized
Joint type Plates and Pipes FW
Single/Multiple pass Multiple
Parent material group(s) 23.1 to 23.1; all subgroups in group 22 and their combination ISO/TR 15608
Parent material thickness (mm) Butt Joint = N.A. Fillet Joint t1 = 3 to 30 t2 = 3 to 30
Throat thickness (mm) No restriction
Weld deposit thickness (mm) N.A.
Outside diameter (mm) Over 45 mm(*)
Filler metal Solid wire UNI EN ISO 18273 AlMg4,5 S Al5183 UNI EN 1011-4 group 5
Shielding gas (ISO 14175) I1 Backing gas (ISO 14175) With and without
Type of welding current Pulsed EP Heat input Kj/cm All
Welding position All positions except for PG and J-L045
Preheat min. (°C) +50 Interpass temp. Max. (°C) +200
Post weld heat treatment / Ageing None
Other information (*) Diameter limited to max. 180 mm , when Rina Rules apply
Welders name Cisic Ivica Stamp No. CI
Welding test conducted by ITAQUA Srl - Trieste (TS)
Mechanical test conducted by METALSERVICES srl Laboratory test No. 18.109
At presence of RINA Surveyor L. Mantovan
We certify that statements in this certificate are correct and that the test welds were prepared, welded and tested in accordance
with the requirements of UNI EN ISO 15614-2: 2006 Standard.
Requirements of RINA Rules for the Classification of Ships are also met.
Issued at: Genova on 13 March 2018
RINA Services S.p.A.
WPQR15614 WPQR ISO 15614-2_2006 rev. 1 Page 1/4
Certificate No. 18VE0048PO2\A
JOINT DETAILS AND WELDING SEQUENCES
PLATE TO PIPE FILLET WELD IN MULTI PASS
Filler metal Filler metal Travel Heat input
Pass Process Amps Volt Other
diam. (mm) classification speed (kJ/cm)
No.
(cm/min)
1 131 1,2 Al5183 218 28,5 32,6 9,1 -
2 131 1,2 Al5183 216 25,8 48,4 5,5 -
3 131 1,2 Al5183 232 26,8 43,5 6,9 -
Dx t2
t1
PARENT MATERIAL
Material specification EN 573
Type or grade Lega 6082 T6
Group(s)/Subgroup(s) No. (ISO/TR 15608) t1= 23.1; t2= 23.1
Thickness (mm) t1= 15; t2= 15 Throat thickness (mm) N.A.
Diameter (mm) 90
Branch connection angle N.A.
Other -
WELDING CONSUMABLES
Process 131
Trade name(s) SAFRA S AL5183
Specification UNI EN ISO 18273
Classification / designation Al Mg 4,5Mn0,7 A
UNI EN 1011-4 grouping 5
Size (mm) 1,2
Deposited metal thickness
Groove N.A.
Throat 7,5 mm
Flux trade name N.A.
Consumable insert N.A.
Other -
WPQR15614 WPQR ISO 15614-2_2006 rev. 1 Page 2/4
Certificate No. 18VE0048PO2\A
GAS
Gas Mixture Flow rate (l/min.)
Shielding Ar 99,99% 17
Trailing
Backing
POSITION
Welding position PB
Other -
PREHEAT POSTWELD HEAT TREATMENT
Preheat temperature +50°C Temperature None
Interpass temperature +200°C Time -
Other - Other -
ELECTRICAL CHARACTERISTICS
Current DC EP
Ampere (range) See table Volts (Range) See table
Mode of metal transfer Pulsed EP
Tungsten electrode size and type N.A.
Other -
TECHNIQUE
Travel speed (range) See table
String or weave bead Weave
Oscillation (*) None
Method of groove/edge preparation Machining/Grinding
Interpass cleaning Grinding/Brushing
Method of back gouging N.A.
Orifice or gas cup size 18 mm
Stand off distance (*) 15-20 mm
Multiple or single pass Multiple
Multiple or single electrodes Single
Torch angle (*) N.A.
Other (*) for fully mechanized/robotic only
WPQR15614 WPQR ISO 15614-2_2006 rev. 1 Page 3/4
OTHER TEST
MACROGRAPHIC EXAMINATION Acceptable
MICROGRAPHIC EXAMINATION Acceptable
FRACTURE TEST Acceptable
NON DESTRUCTIVE EXAMINATION
VISUAL EXAMINATION Acceptable
RADIOGRAPHIC EXAMINATION Not required
PENETRANT TEST Acceptable
MAGNETIC PARTICLE Not required
ULTRASONIC TEST Not required
Issued at: Genova on 13 March 2018
RINA Services S.p.A.