Dispersible Pseudo Boehmite For Catalysts and Sol-Gel Abrasives
Pseudoboehmite is an aluminum compound with the chemical composition AlO(OH).
It consists of finely crystalline boehmite. However, the water content is higher than in boehmite.
Pseudo-boehmite is white powder with high purity, odorless, tasteless,,low pile, large pore volume, high specific surface,good
compatibility, excellent gelation and strong caking property. It can be easily decentralized and soluble in the acid and alkali
solution. It can become highly active alumina after low-temperature roasting and dehydration.
In catalysts, Pseudoboehmite with high density and gelling grade is mainly used as binder for FCC catalysts and adsorbents,also
a raw material for activated alumina.It is a binder of cracking catalyst for semi-synthetic rare-earth Y molecular sieve, a binder
in aluminum silicate refractory fiber, a catalyst in making ethylene by alcohol dehydration and in making epoxy ethane.It also
can be used as raw material for activated alumina and other aluminates.
Lower density Pseudoboehmite of partical dispersibility and lower sodium oxide is mainly used as catalyst carrier in
petrochemical and environmental protection industries, such as hydrogenation catalyst, methanation catalyst and motor tail
gas catalyst carrier.
In abrasives, these boehmites are nano-sized in the dispersed phase, exhibit a unique combination of purity, consistency and
dispersibility that make them excellent materials for use in colloidal applications, and in applications such as sol-gel ceramics,
refractory materials, rheology control and surface frictionizing. The unique microstructure, composed of extremely uniform,
sub-micron crystals, is designed to fracture conchoidally when stressed. The combination of the grit’s sharpness and structure
allows for an aggressive cutting and long-lasting ceramic grain ideal for use in organic and vitrified bond-systems.
Typical Property Product Code
SPV-LNa MPV-LNa LPV-LNa LPV-UHP
Chemical Al2O3 % 65-70 68-70 68-72 68-72
Composition Na2O % <0.10 <0.01 <0.05 <0.01
SiO2 % <0.20 <0.01 <0.15 <0.01
Fe2O3 % <0.01 <0.01 <0.01 <0.01
LOI % 30-35 30-32 28-30 28-30
Physical Peptization % >95 >95 ～20 ～20
Composition Loose Bulk Density g/ml 0.6-0.7 0.5-0.6 0.2-0.3 0.2-0.3
Particle Size(D90) μm <20 <18 <15 <15
Surface Area mm2/g >250 >230 >300 >300
Pore Volume ml/g 0.3-0.4 0.5 0.9-1.1 0.9-1.1
Crysstallite Size nm 3.5-5 4-6 7-10 7-10
Standard Purity: SPV-LNa LPV-LNa
High Purity: MPV-LNa LPV-UHP
Raw Material for
Alumina Adsorbents and Alumina Catalysts Support