SWANCOR 901-VP

Epoxy Vinyl Ester Resins

Product Description Typical clear casting properties of cured resin
5
Property SI* US Standard Test Method
SWANCOR 901-VP is a low viscosity Bisphenol A type epoxy
Tensile Strength 80~90MPa 11,000~13,000psi ASTM D638
vinyl ester resin had been pre-promoted with cobalt-salt promoter.
5
It provides excellent corrosion resistance to a broad range of Tensile Modulus 3.2~3.5GPa 4.6~5.1 X 10 psi ASTM D638
organic and inorganic acids, alkalis, oxidizing chemicals and salt
solutions etc. It also provides very good mechanical strength such Tensile Elongation 4.5~5.5% 4.5~5.5% ASTM D638
as tensile and flexural while incorporated with reinforcement such Flexural Strength 114~138MPa 16,500~20,000psi ASTM D790
glass fiber, carbon fiber or kevlar fiber etc. The ease of use of
5
SWANCOR 901-VP makes it suitable for various fabrication Flexural Modulus 3.1~3.5GPa 4.5~5.0 X 10 psi ASTM D790
process, such as pultrusion, RTM, filament winding and vacuum Volume Shrinkage 7.5~8.0% 7.5~8.0% ASTM D2566
infusion etc. It has good heat resistance distortion temperature as
Heat Distortion o o
good as SWANCOR 901. 6 100~105 C 212~221 F ASTM D648
Temperature*

Applications Barcol Hardness 34 +/- 4 34 +/- 4 ASTM D2583

5
* SI values based on conversion.
• Chemical storage tanks, pipes, flue gas desulfurization 6
* Cure condition for HDT: 24 hours at room temperature then 2
systems (FGD), scrubbers, ducts. o
hours at 105 C.
• Corrosion resistant flooring while incorporated with
aggregates. NOTICE IN USE
• Waste water treatment systems.
• Food storage tanks and pure water system. 1. If SWANCOR 901-VP had been blended with cobalt-salt
• Marine use for yachts and boats, approved by DNV. promoters, shelf life will be shortened. SWANCOR 901-VP
must be used within three months.
Fabrication Methods 2. The gel time of SWANCOR 901-VP is affected primarily by
catalyst concentration and temperature. The variations of cure
• Can be easily applied by spray-up, pultrusion, resin transfer characteristics may be caused by the variations of catalyst,
molding (RTM), filament winding and vacuum infusion. humidity, pigment, fillers and other additives. It is
• Can be used in polymer concrete casting. recommended that the fabricators check the cure
• Can comply with US FDA regulation 21 CFR 177.2420 if the characteristics with a small quantity resin before proceeding for
resin is properly formulated and cured. bulk production.
3. SWANCOR 901-VP contains organic solvent (styrene). Keep
Typical properties of liquid resin away from heat, sparks and flames.
1 4. SWANCOR 901-VP is a potentially reactive chemical. Please
Property* Value
store it in dark and keep away from heat and direct sunshine.
Appearance Light pink 5. Containers, not completely emptied, must be closed
Solid Content (%) 51.5 +/- 1.5 immediately after use.
2
Viscosity * 250 +/- 100 cps 250 +/- 100 mPa.s

Specific Gravity 1.04 +/- 0.02 MATERIAL SAFETY AND HANDLING INFORMATION
3 4
Gel Time (min)* 20~30 min*
SKIN CONTACT:
Shelf Life (months) 3 Thoroughly wash exposed area with soap and water immediately.
1
* Measurement was obtained under 25 C.
o Remove contaminated clothing. Launder contaminated clothing
2
* LVT-#3-60rpm@25 C.
o before re-use.
3
* 55%MEKP: 1.0phr.
4
* Gel time of swancor 901-VP can be specified by customers. EYE CONTACT:
Flush with large amount of water immediately and continuously for
20 minutes, lifting upper and lower lids occasionally. Get medical
attention.

The data presented herein are believed to be accurate and reliable. We require customers to inspect and test our product before use and to satisfy
themselves as to contents and suitability for their specific applications. Information herein is to assist customers in determining whether our products
are suitable for their applications but not to be taken as a guarantee, express warranty or implied warranty of merchantability or fitness for
particular purpose, nor is any protection form any law or patent to be inferred. All patent rights are reserved. The exclusive remedy for all proven
claims is limited to replacement of our material and in no event shall we be liable for special, incidental or consequential damages.
Page：1/2 Document Code: NT26-147-E Issue Date: AUG/2009
No. 9 Industry South 6 Road, Nantou City 54066, Taiwan
SWANCOR IND. CO., LTD. Tel: +886 49 225 5420 Fax: +886 49 225 1534
E-mail: [email protected]
www.swancor.com
 SWANCOR 901-VP
Epoxy Vinyl Ester Resins
INGESTION: PACKAGE
Do not induce vomiting. Keep person warm, quiet and get medical
attention. Aspiration of material into the lungs can cause chemical Standard packing is 200 kg steel drum.
pneumonitis which can be fatal.

INHALATION:
If affected, remove individual to fresh air. If breathing is difficult,
administer oxygen. If breathing has stopped, give artificial
respiration. Keep person warm, quiet, and get medical attention.

PERSONAL PROTECTION:
Do not breathe vapors. High concentration of vapor can be
hazardous. Keep out of sewers. Eliminate all sources of ignition in
vicinity of spill or released vapor to avoid fire or explosion. For
large spills, warn public of downwind explosion hazard. Check
area with explosion meter before re-entering area. Ground and
bond all containers and handling equipment.

RESIN STORAGE

Keep away from ignition sources; flames, pilot lights, electrical

sparks, and sparking tools. NO SMOKING. Do not store in direct
sunlight. Store separate from oxidizing materials, peroxides, and
metal salts. Keep container closed when not in use. To ensure
maximum stability and maintain optimum resin properties, resins
o
should be stored in closed containers at temperatures below 25 C
o
(77 F). Copper or copper containing alloys should be avoided as
containers.

SPILLS

Eliminate all ignition sources (flares, flames, including pilot lights

electrical sparks). Persons not wearing protective equipment
should be exclude from area of spill until clean-up has been
completed. Stop spill at source, dike area of spill to prevent
spreading, pump liquid to salvage tank. Remaining liquid may be
taken up on sand, clay, earth, floor absorbent or other absorbent
material and shoveled into containers.

WASTE DISPOSAL

Destroy by liquid incineration in accordance with applicable

regulation. Contaminated absorbent should be disposed in
accordance to government regulations.

The data presented herein are believed to be accurate and reliable. We require customers to inspect and test our product before use and to satisfy
themselves as to contents and suitability for their specific applications. Information herein is to assist customers in determining whether our products
are suitable for their applications but not to be taken as a guarantee, express warranty or implied warranty of merchantability or fitness for
particular purpose, nor is any protection form any law or patent to be inferred. All patent rights are reserved. The exclusive remedy for all proven
claims is limited to replacement of our material and in no event shall we be liable for special, incidental or consequential damages.
Page：2/2 Document Code: NT26-147-E Issue Date: AUG/2009
No. 9 Industry South 6 Road, Nantou City 54066, Taiwan
SWANCOR IND. CO., LTD. Tel: +886 49 225 5420 Fax: +886 49 225 1534
E-mail: [email protected]
www.swancor.com