Technical Parameters of
Product
UV3311
Specific gravity
1.10
@25℃
Viscosity@25℃,
mPa.s(cp)
300 200-400
Brookfield RVT
1#rator @20rpm
Flash
>77
point(TCC),℃
Crack under force
The liquid adhesive was applied to the
medical-grade polycarbate square rods that had
been bent first to produce different stress levels.
The dimensions of the rods were 64mm× 13mm ×
3mm. Record the time when the crack lines are
produced or when they are cracked by force.
Crack under force, ASTMD
＞15mins
3929 7N/mm2 (1000psi)
Crack under force, ASTMD
3-4mins
3929 12N/mm2 (1750psi)
Typical curing performance
The product will solidify when exposed to
ultraviolet light and/or visible light of sufficient
intensity. To fully solidify the surface exposed to
the air, the purple outer light at 220-260nm will
accelerate the de-bonding and solidification of the
Material properties before surface. The curing speed and the final curing
depth are determined by the light intensity, the
curing spectral distribution of the light source, the
Typical Range exposure time and the light transmittance of the
value bonded materials.
Chemical type Allyl ester Note: The ultraviolet light intensity mentioned here
urethane was measured using an OAI 306 ultraviolet light
Appearance Transparent intensity measuring instrument at 365nm.
liquid Fixed time period
Description
The data in this article were obtained under laboratory conditions. Due
to the differences in the conditions of use, users should refer to these data
and conditions of use for analysis and testing. Ltd. does not guarantee the
sale of Joinbond New Material Technology Co., Ltd. products or the use of
Joinbond New Material Technology Co., Ltd. products under specific
operating conditions, and does not assume any responsibility for direct,
indirect or accidental damages.
If you encounter any problems in the process of use, you can contact the
technical service department of Joinbond New Material Technology Co.
Technical Parameters of
Product
UV3311
Two 1-cm-long polycarbamate and PVC Lamp bulb type: Metal halogen lamp
samples were overlapped onto one piece, with
an overlap length of 13mm and a gap of
0.5mm between the adhesive layers. They were
solidified under the illumination of a light
source. The time during which the lap joint can
withstand a weight of 3 kilograms for 10
seconds without breaking is the fixed time.
Fixed time, Ultraviolet light
second intensity mW/cm2
Types of lamps 30 50
Metal halogen Bulb type: Fusion D lamp
＜5
lamp (doped)
Fusion H&V
＜5
lamps
Fusion D lamps ＜5
The relationship between curing
depth and ultraviolet light
intensity
The following figure shows the relationship Bulb type: Fusion H lamp
between the depth of curing and the curing
time tested by a PTFE mold with a straight
diameter of 15mm under ultraviolet light
irradiation ranging from 30 mW/cm2 to
100mW/cm2.
When the test samples were exposed to 50 and
100 mW/cm2 purple outer line irradiation (V
lamp) and cured for 30 seconds, the curing
depth exceeded 13mm. Make the curing
properties obtained by illumination with
Description
medium-pressure mercury
The data in this article lamps
were obtained underand Fusion
laboratory H Due
conditions.
to the differences in the conditions of use, users should refer to these data
lamps similar.of use for analysis and testing. Ltd. does not guarantee the
and conditions
sale of Joinbond New Material Technology Co., Ltd. products or the use of
Joinbond New Material Technology Co., Ltd. products under specific
operating conditions, and does not assume any responsibility for direct,
indirect or accidental damages.
If you encounter any problems in the process of use, you can contact the
technical service department of Joinbond New Material Technology Co.
Technical Parameters of
Product
UV3311
conducted under the tensile die. The shear test
Typical properties of the cured sample was cured for 80 seconds with a metal
halogen lamp at a light intensity of
material 30mW/cm2.
When illuminated with a metal halogen lamp Initial strength, N/mm2 5
equipped with a glass filter at a light intensity of (psi) (750)
30 mW/cm ², it solidifies for 80 seconds. Classic environmental resistance
Physcial properties performance
Breaking tensile N/mm2 23 Test method: ASTMD3163
strength (psi) (3300) Substrates:Polycarbamate, with an interlayer gap
% Fracture elongation rate, ASTM 265 of 0.5mm
D882 Curing process: Use a metal halogen lamp to
Modulus, ASTM N/mm2 669 cure for 80 seconds under a light intensity of
D882 (psi) (97000) 30mW/cm ².
Hardness(Shore D) 64 Cautions:
Hygroscopicity, ASTM D570, % in 5.36
This product should not be used in pure
boiling water for 2 hours
oxygen and/or oxygen-rich environments, nor
Refractive index, ND 1.50
should it be used as a sealing material for
Electrical performance
chlorine gas or other strongly oxidizing
Dielectric constant and loss, ASTM D150
substances.
constant Return loss
For safety precautions regarding this
@100Hz 4.556 0.0473
product, please refer to the Material Safety
@1kHz 4.408 0.0201
Data Sheet (MSDS) of JoinBond Company.
@1MHz 4.023 0.0310
Bulk electrical resistance rate, 8.4×1014 Storage conditions
ASTM D149,.cm
Unless otherwise specified, the storage
Surface electrical resistance 1.0×1015
conditions for this product should be kept in a
rate,ASTMD149，
cool and dry place within the temperature
Dielectric intensity ， ASTM 31
range of 8 to 28 ° C (46 to 82 ° F), and stored
D257，kV/m
in the original package. If this product is stored
Material properties after curing
at 8 to 18 degrees Celsius, it will be more
According to ASTM D3163, the shear strength
desirable. To avoid contaminating the unused
test of the polycarbate lap shear test sample with
glue, no glue should be poured back into the
a 0.5mm gap between the rubber layers was
original package.
Description
The data in this article were obtained under laboratory conditions. Due
to the differences in the conditions of use, users should refer to these data
and conditions of use for analysis and testing. Ltd. does not guarantee the
sale of Joinbond New Material Technology Co., Ltd. products or the use of
Joinbond New Material Technology Co., Ltd. products under specific
operating conditions, and does not assume any responsibility for direct,
indirect or accidental damages.
If you encounter any problems in the process of use, you can contact the
technical service department of Joinbond New Material Technology Co.