PRODUCT DATA SHEET
Sikalastic® HLM 5000 R SL
(formerly MSeal HLM 5000 R)
Self-levelling, Liquid cold-applied waterproofing membrane system
DESCRIPTION
CHARACTERISTICS / ADVANTAGES
Sikalastic® HLM 5000 R SL is a single component, mois-
ture curing, pure polyurethane based waterproofing • Waterproof - Protects structure from water penetra-
membrane that cures by reaction with atmospheric tion
moisture to form a tough membrane. • Elastomeric - Permits nominal expansion and con-
Sikalastic® HLM 5000 R SL protects structures from traction of the structure
water penetration while remaining flexible to handle • Low Temperature Flexibility – Wide service temper-
the nominal expansion and contraction of substrates. ature, suitable for all climates
• Single Component – No complex mixing & easy to
USES use
• Cold Applied & Seamless – Eliminates lapping, seam-
Waterproofing for ing and precutting
▪ Flat and slope concealed roof structures • Root resistant - Suitable for planter box and green
▪ For podium and green roof roof
▪ Balconies, planter box and parking garages
▪ Above grade between two cources of concrete or APPROVALS / STANDARDS
mansory of cavity wall
▪ Exterior below grade on concrete and mansory ▪ Comply with ASTM C 836, among that crack bridge
test temperature adjusted at -20°C;
▪ VOC report by following ISO 11890-2;
▪ VOC Emission by following CDPH/EHLB/Standard
Method Version 1.2 - California Specification, report
No. 24436443a 001
▪ Water vapor transmission and water vapor permeab-
ility per ASTM E 96
▪ Root resistant CEN/TS 14416:2014
PRODUCT INFORMATION
Chemical base Aromatic polyurethane
Packaging 22.5 kg in big open mouth pail
25 kg in small open mouth pail
Colour Black color
Shelf life 9 months from date of production
Storage conditions The Product must be stored in original, unopened and undamaged sealed
packaging in dry conditions at temperatures between +5 °C and +35 °C. Al-
ways refer to packaging. Refer to the current Safety Data Sheet for inform-
Product Data Sheet
Sikalastic® HLM 5000 R SL
August 2025, Version 03.01
020915205000000128
1/4
ation on safe handling and storage.
Density ~ 1.55 kg/L
Volatile organic compound (VOC) con- 116 g/L ISO 11890-2:2013
tent
Solid content by weight ≥ 88%
Shore A hardness 62 ASTM D 2240:2015
Tensile strength ≥2.0 MPa ASTM D 412:2016
Elongation at break ≥ 500% ASTM D 412:2016
Tensile adhesion strength ≥ 1.2 MPa (self-primer on standard concrete) ASTM D 7234:2021
Tear strength ≥ 15 N/mm ASTM D 624:2020
Crack bridging ability Pass 3.2mm at -20°C for 10 cycles ASTM C 1305:2016
Water tightness 0.30 MPa, no penetration ASTM D 5385:2014
Water absorption ≤5% ASTM D 570:1998
Flexibility at low temperature No crack at -35°C ASTM D 1970:2021
APPLICATION INFORMATION
Consumption DFT Coverage
1mm Approx 1.7-1.8 kg/sqm in 2 coats
1.5mm Approx 2.5 -2.6 kg/sqm in 2 coats
Note : The above consumption data for Sikalastic® HLM 5000 R SL is theor-
etical and does not consider any additional material due to surface poros-
ity, surface profile,variations in level, wastage or any other variations. Ap-
ply product to a test area to calculate the exact consumption for the spe-
cific substrate conditions and proposed application equipment.
Primer (Optional ,recommended for Use Sikalastic® HLM 5000 R SL self
porous substrates) diluted with 5% xylene as solvent
Product temperature Minimum 5 °C
Maximum 35 °C
Ambient air temperature Minimum 5 °C
Maximum 40 °C
Relative air humidity Minimum 20%
Maximum 85%
Dew point Beware of condensation. Substrate temperature during application must
be at least +3 °C above dew point.
Substrate temperature Minimum 5 °C
Maximum 35 °C
Substrate moisture content Substrate Test Method Moisture Content
Cementitious Calcium carbide meth- ≤ 4 % (for self - primer)
Substrate od Or refer to selected ap-
(CM-method) proved primer PDS
No rising moisture (ASTM D4263, polyethylene sheet)
The substrate must be visibly dry with no standing water.
Product Data Sheet
Sikalastic® HLM 5000 R SL
August 2025, Version 03.01
020915205000000128
2/4
Waiting time / Overcoating Ambient temperature Relative humidity Minimum
+10 °C 50 % 24 h
+20 °C 50 % 12 h
+30 °C 50 % 8h
Times are approximate and will be affected by changing ambient condi-
tions particularly temperature and relative humidity.
BASIS OF PRODUCT DATA such as blow holes and voids. Note Suitable methods
for surface preparation are high-pressure water jetting
All technical data stated in this Product Data Sheet are or abrasive blast cleaning. If using other pre-treat-
based on laboratory tests. Actual measured data may ments such as scarifying and milling, subsequently use
vary due to circumstances beyond our control. water jetting or blast cleaning to eliminate the remain-
ing structural faults, remove cement laitance, and
achieve an open and sound textured surface.
ECOLOGY, HEALTH AND SAFETY 5. Repair and fill blow holes and voids using appropri-
User must read the most recent corresponding Safety ate products from the SikaTop®, Sika MonoTop®, Sika-
Data Sheets (SDS) before using any products. The floor®, Sikadur® and Sikagard® range of materials.
SDSprovides information and advice on the safe hand- 6. Remove dust by industrial vacuuming equipment.
ling, storage and disposal of chemical products and 7. To confirm adequate surface preparation and adhe-
contains physical, ecological, toxicological and other sion of the Product , carry out a small trial before full
safety-related data. application together with adhesion tests as required.
MIXING
APPLICATION INSTRUCTIONS
IMPORTANT
EQUIPMENT The Product is supplied ready to use.
Prior to application mix for at least 2 minutes using an
Select the most appropriate equipment for all applica- electric single-paddle mixer (300 to 400 rpm) until the
tions required for the project. liquid and all coloured pigment has achieved a uni-
form colour.
SUBSTRATE PREPARATION EQUIPMENT
▪ Grinding equipment APPLICATION
▪ Manual or mechanical wire brushes
▪ High-pressure power washer Strictly follow installation procedures
▪ Industrial vacuuming equipment Strictly follow installation procedures as defined in
For other types of preparation equipment, contact Method Statements, application manuals and working
Sika Technical Services. instructions which must always be adjusted to the ac-
tual site conditions.
MIXING EQUIPMENT
▪ Electric single-paddle mixer (300 to 400 rpm) COATING
APPLICATION EQUIPMENT Always begin application with detailing (corners, up-
▪ Trowl stands, joints) before installation of the main horizont-
▪ Brush al surfaces.
▪ Airless spray equipment 1.Apply Sikalastic® HLM 5000 R SL as self-primer
evenly over the surface with trowel or airless spray
equipment first then roller to evenly. If taking other
SUBSTRATE PREPARATION primer please follow application guidance.
2. Apply first layer bodycoat in trowel or airless spray
Penetrations and structural joints equipment. Note Maintain a "wet edge" during applic-
Sika Joint Sealing Solutions must be used for connec- ation to achieve a seamless finish.
tions around penetrations and for construction joints. 3. For reinforced membrane lay the Sika® Reinforce-
CONCRETE OR CEMENTITIOUS SCREEDS ment onto the wet base coat. Note The reinforcement
1. Substrate must be sound with a minimum tensile fibres must be fully encapsulated within the base coat.
adhesion strength of 1.5 N/mm2,clean, dry and free of 4. Within overcoating time, apply second layer of the
all contaminants such as dirt, oil, grease, coatings, lait- product evenly over the surface with trowel or airless
ance, surface treatments and loose friable material. spray equipment. Note Maintain a "wet edge" during
2. New concrete must be cured for at least 28 days application to achieve a seamless finish.
and have a tensile strength > 1.5 N/mm2. 5. The coating must be continuous, pore free and to
3. IMPORTANT The final texture of the substrate must the required surface finish.
be open-textured and gripping. Prepare cementitious Protect from rain
substrates mechanically using abrasive blast cleaning, After application, protect the Product from heavy rain
planing or scarifying equipment to remove cement or rain showers until dry to prevent surface damage.
laitance. No application on rising moisture
4. Remove weak concrete and fully expose defects Do not apply on substrates with rising moisture.
Product Data Sheet
Sikalastic® HLM 5000 R SL
August 2025, Version 03.01
020915205000000128
3/4
CLEANING OF TOOLS
Clean all tools and application equipment with Sika®
Thinner C immediately after use. Hardened material
can only be removed mechanically.
LEGAL NOTES
The information, and, in particular, the recommenda-
tions relating to the application and end-use of Sika
products, are given in good faith based on Sika's cur-
rent knowledge and experience of the products when
properly stored, handled and applied under normal
conditions in accordance with Sika's recommenda-
tions. In practice, the differences in materials, sub-
strates and actual site conditions are such that no war-
ranty in respect of merchantability or of fitness for a
particular purpose, nor any liability arising out of any
legal relationship whatsoever, can be inferred either
from this information, or from any written recom-
mendations, or from any other advice offered. The
user of the product must test the product’s suitability
for the intended application and purpose. Sika re-
serves the right to change the properties of its
products. The proprietary rights of third parties must
be observed. All orders are accepted subject to our
current terms of sale and delivery. Users must always
refer to the most recent issue of the local Product
Data Sheet for the product concerned, copies of which
will be supplied on request.
Sika India Pvt. Ltd. Contact:
620, Diamond Harbour Road Phone: +91 33 2447 2448
Commercial Complex II Fax: +91 33 2397 8688
Kolkata - 700 034
[email protected]West Bengal, India www.sika.in
SikalasticHLM5000RSL-en-IN-(08-2025)-3-1.pdf
Product Data Sheet
Sikalastic® HLM 5000 R SL
August 2025, Version 03.01
020915205000000128
4/4