Technical data sheet
Thick-film zinc repair
compound
LZ-09
Zinc repair compound, light silver, 1-component.
Application For repairing flaws on hot-dip galvanised steel parts,
moreover for galvanised surfaces damaged by grinding or
welding, and for non-galvanised small steel parts, that are
to be matched to galvanized constructions.
Note According to the requirements of standard DIN EN ISO
1461 edition 2022-12 and DIN EN ISO 3549.
Properties • excellent corrosion protection
• different colour shades
• easy application
• best praxis
• high Zinc content
Delivery sizes 100 ml
250 ml
500 ml
1,0 l
2,5 l
5,0 l
12 kg
Colour shades Available in 6 different shades from light to dark, see
ReiColor colour chart no. 6.
Product types LZ-09.00.0000.0 light
LZ-09.00.0001.1 light
LZ-09.00.0002.1 middle
LZ-09.00.0004.1 middle
LZ-09.00.0008.1 dark
LZ-09.00.0016.1 dark
Gloss level matt
Application rate approx. 8 m²/l
Density approx. 1,2 kg/l
Storage stability / shelf-life Min. 3 years at room temperature and dry storage
.
Thick-film zinc repair compound LZ-09 Page 1 of 3
Technical data sheet
Working instruction Stir thoroughly before use.
Substrate preparation Bottom chord clean thoroughly before applying.
Thoroughly remove loose parts such as rust, white rust,
scale, carbon black, grease and other contaminations.
Application method Undiluted mainly by brushing and rolling.
Application temperature The temperature of the zinc bottom chord should be
between +5°C and approx. + 50°C. Especially at deep
temperatures it is to be paid attention to the cool zinc
surfaces neither being covered with condensate nor with
frozen dew. Otherwise there might arise spallings after
overpainting the surface.
In case of very high temperatures the dissolvents flash off
too quickly due to the hot surface. As a consequence
further processing of LZ 09 is not possible any more.
Solvents ReiColor VE-50, ReiColor VK-30 or ReiColor VK-80
Dry film thickness 100 µm per application
Drying method air drying
Dust dry after approx. 1 hour.
Recommended drying time: over night.
Over-paintable after complete drying, e.g. with ReiColor LZ-80, ReiColor
ZY-20, ReiColor ZL-22
Safety instructions VOC Cat. A/i, 500 g/l (2010).
This product contains 500 g/l VOC max.
Hazard notes Please observe technical data sheet and safety data sheet
before use.
Data base: All technical information in this data sheet is based on laboratory tests and may deviate from
values actually resulting from practical use.
Disclaimer: The above data are based on our present knowledge and experience provided that the material is
stored properly and applied appropriately. The data are exclusively intended to describe the products and do
not constitute warranted properties in any legal sense. We reserve the right to make changes to product
specifications at any time. Our technical advice - whether verbal, in writing or by way of trials - is given in good
faith but without warranty, and this also applies where proprietary rights of third parties are involved. Our
advice does not release the customer from the obligation to verify the information currently provided -
especially that contained in our safety data and technical information sheets - and to test our products as to
their suitability for the intended processes and uses. The application, use and processing of our products and
the products manufactured by you on the basis of our technical advice are beyond our control and, therefore,
entirely your own responsibility. Our products are sold in accordance with the current version of our General
Conditions of Sale and Delivery.
The current version of the technical data sheet with the newest release date is available on our
homepage www.reicolor.de/Produkte. With the publication of a new edition of this technical data sheet
all information in previous data sheets is no longer valid.
Thick-film zinc repair compound LZ-09 Page 2 of 3
Technical data sheet
Reicolor Chemie-GmbH
Werkstraße 21
D-90518 Altdorf b. Nürnberg
Tel.: +49(0)9187/97 03-0
http://www.reicolor.de Release date: 16.01.2023
Thick-film zinc repair compound LZ-09 Page 3 of 3