UTILIZING SAWDUST AS
A SAND REPLACEMENT
AND WOOD ASH FOR
NON-BEARING WALL
TITLE: The Effect of Wood Ash as a Partial Cement Replacement Material for Making Wood-Cement Panels
AUTHOR: Viet-Anh Vu , Alain Cloutier , Benoit Bissonnette , Pierre Blanchet and Josée Duchesne
DATE PUBLISHED: 28 August 2019
METHODOLOGY FINDINGS SIMILARITIES
Wood-Cement Mixtures the wood ash does not qualify as a
( wood to binder ratio 0.35 by pozzolan ( Both studies emphasize sustainability and the
weight ) use of local materials
PH value increases.
DIFFERENCES
Test Specimens density of the samples is found to
decrease as the WA replacement
rate increases
Wood ash as a cement or binder
fraction of the ash of about 7%
Test Method dissolves in water
ORIGINALITY
increase in the heat capacity of
WCAP Used as replacement for Cement
TITLE: Utilization of Sawdust in Making Concrete Blocks: An Experimental Research on Hollow Concrete Block’s Rigidity
AUTHOR: Joefil Carl Osabel Dacorro and Tomas Jr Aquino Diquito
DATE PUBLISHED: March 12, 2022
METHODOLOGY FINDINGS SIMILARITIES
Statistical tool : Using Cross-sectional the heavier the block is, the
area formula higher its compressive
strength. Testing the compressive strength
The highest compressive
Data Gathering Procedure strength achieved among all
- Procurement of Materials Needed in Making blocks is 4.98 MPa; 2.45 MPa DIFFERENCES
Concrete for blocks incorporated with
- Pretreatment of Sawdust
- Production of Concrete Block with Sawdust as sawdust.
Fine Aggregate the compressive strength, Use as concrete blocks
- Curing of Concrete Blocks. average load, and mass of
concrete block decreases as
Testing : Compressive strength test the percentage of sawdust
replacement increases. ORIGINALITY
agree that the compressive
strength and weight of Sawdust in Concrete blocks
concrete decrease as the
percentage of sawdust
increases
TITLE: Partial Replacement of Cement with Saw Dust Ash in Concrete
AUTHOR: Dr. Ramireddy Sushmitha , B. Rohini and Japthi Sravani
DATE PUBLISHED: November 2023
METHODOLOGY FINDINGS SIMILARITIES
• Testing : (Compressive strength • The max compressive strength Both studies emphasize sustainability and the use
test, Split-tensile strenght test attained was 43.2 N/mm^2 in 28
days, when cement is replaced of local materials.
and Flexural strength test)
with 10%
DIFFERENCES
• Comparison (replaced ash SDA
concrete with conventional • The decrease in the strength can
concrete) be observed when the • Focus on the effects of Saw Dust Ash as partial
replacement percentage is replacement of cement
• Mix portion design M30 beyond 10%.
concrete
ORIGINALITY
Saw dust as a replacement of cement
TITLE: Investigation of Properties of Concrete Using Sawdust as Partial Replacement for Sand
AUTHOR: Olugbenga Joseph Oyedepo , Seun Daniel Oluwajana and Sunmbo Peter Akande
DATE PUBLISHED: 2000
METHODOLOGY FINDINGS SIMILARITIES
Concrete mix design,
Post-cracking stiffness of bamboo reinforced
casting and curing Used bamboo as reinforcement
procedure SCC slabs were lower than NC slabs
The cracking performance of bamboo
DIFFERENCES
reinforced SCC slabs in terms of number of
flexural cracks and maximum crack width is
considerably better than those made from Used as concrete reinforcement
the conventional vibrated concrete.
ORIGINALITY
Focus on replacement of concrete fiber
with bamboo fiber
TITLE: Rice husk ash as a partial replacement of cement in high strength concrete containing micro silica: Evaluating
durability and mechanical properties
AUTHOR: Seyed Alireza Zareeia,⁎ , Farshad Amerib , Farzan Dorostkarc , Mojtaba Ahmad
DATE PUBLISHED: 2017
METHODOLOGY FINDINGS SIMILARITIES
Mixture-Proportions mixtures with 25% RHA showed the
lowest ratios of water absorption
Tests : by about 4.8% at 7 days. Both ash
Compressive Strength
Tensile Strength The performance of rice husk ash in
Short-Term water concrete is of factors influencing DIFFERENCES
absorption test the amount of silica added.
Rapid Chloride Rice husk as a partial replacement of cement
permeability test Replacement with 25% rice hush
ash result in drastic enhancement
of the permeability properties of ORIGINALITY
blended concrete.
Use of rice ash husk
TITLE: EFFECT OF SAWDUST AS PARTIAL REPLACEMENT OF SAND IN CONCRETE
AUTHOR: DABAN A. MUHEDIN 1,* , SANGAR J. QADIR** , MADEH I. HAMAKAREEM* and AHMED J. HAMA
RASH*
DATE PUBLISHED: December 8, 2020
METHODOLOGY FINDINGS SIMILARITIES
Increasing the percentage of sawdust in
Mix Proportion concrete specimens led to reducing in Saw Dust
(0,5,10,15,20,25%) – Saw Dust compressive, tensile and flexural strength.
in Cement. For compressive strength, 5% replacement of
sand by sawdust, shows a satisfactory result 26 DIFFERENCES
Test : Mpa.
For compressive strength, 10% replacement
Compressive Strength Test the value would be 20.1 MPa and for 15% Saw Dust as a Partial replacement
Split-Tensile Strength Test replacement the value would be 15.9 MPa at
Flexural Strength Test 28 days.
For spitting tensile strength, 5% replacement of ORIGINALITY
sand the result would be 2.2 MPa at 28 days
For flexural strength test, 5% replacement of Used as a Partial Replacement
sand the result would be 2.4 MPa at 28 days
TITLE: Partial replacement of portland cement by bamboo ashes
AUTHOR: Anthony Nkem Ede and Joshua Olaoluwa Agbede
DATE PUBLISHED: February-2015
METHODOLOGY FINDINGS SIMILARITIES
Characterization of • The ashes are not classified • Bamboo ashes
bamboo stalk ash as pozzolanic material
Grinding because they do not meet DIFFERENCES
Analysis of the hydration of the chemical requirements
cement partially replaced of the standard.
with bamboo ash • Bamboo ashes as partial replacement of cement
Mortars with partial
replacement of cement by ORIGINALITY
bamboo ash
• Bamboo ashes