- 1. PROJECT REPORT A MINI PROJECT REPORT ON POLYMER CONCRETE Submitted in partialfulfilment of the Requirementsfor the award of Degree of Bachelor of Technology in Civil Engineering SUBMITTED BY: SUBMITTED TO: VIKASH TOMAR Er.PARMIT SHARMA 2000040000024 DR. APJ ABDUL KALAM TECHNICAL UNIVERSITY,LUCKNOW Department of Civil Engineering
- 2. RAJA BALWANT SINGH ENGINEERING TECHNICAL CAMPUS,AGRA RBS ENGINEERING TECHNICAL CAMPUS BICHPURI, AGRA DEPARTMENT OF CIVIL ENGINEERING CERTIFICATE This is to certify that Mr. VIKASH TOMAR S/O Mr. SHIV KUMARSINGH TOMAR of B. Tech Civil Engineering 3rd year Roll No. 2000040000024 has Completed / partially completed / not completed his / her Project during the academic year 2022-23. ITVV Coordinator Head of the Department
- 3. ACKNOWLEDGEMENT It gives me a great sense of pleasure to represent the report of the B. Tech , Mini project undertaken during B. Tech 3rd year. I owe special thanks gratitude to Er. Parmit Sharma and place for his support and guidance throughout the project. His sincerity, throughout the perseverance has been a constant source of inspiration for me. We also do not like to miss the opportunity to acknowledge the contribution of all the Department for their kind assistanceand cooperation during the training. Signature: Name : VIKASH TOMAR Roll No. : 2000040000024 Date :
- 4. ABSTRACT As part of curriculum, and for the partial fulfilment of the requirementsfor completion of B.TECH degree from Raja Balwnat Singh Engineering Technical Campus, I VIKASH TOMAR working on a mini project .The report consistsof brief study and description of methods, techniques,procedures used at the mini project. The report contains my different and amazing experience in making of my mini project. All the contentsare broadly explained and it is constructedfrom the experience of my project. In the opening content I have given details of the project background including its mission. The contentsare written in such a manner which give details of the project so that the reader can easily know and access the my project. In the second contentI have explained my overall project familiarity in the last time. This contentis the main content that I have recorded and it contains overall work I have been executing.
- 5. POLYMER CONCRETE SUBMITTED BY: VIKASH KUMAR CIVIL ENGINEERING(3RD YEAR) R B S ENGINEERING TECHNICAL CAMPUS
- 6. INTRODUCTION • Concrete is a composite material that contain cement, water, coarse aggregate and fine aggregate. • The resulting material is stone like structure which is formed by the chemical reaction of cement and water. • Some of the reasons are its simplicity in preparation, the easily availability and low cost of its ingredients, and above all, the satisfactory properties • of its structure.
- 7. INTRODUCTION • Concrete strength is much influenced by the porosity of hardened concrete. • Any reduction in porosity add its strength to the cement. • Polymer concrete is a part of group of concrete that use polymer to supplement or replace cement as a binder.
- 8. BENEFITS • Fire and Heat resistance. • It has thinner application. • Less chalking at outdoor exposure. • Abrasion resistance • It has temperature stablity.
- 9. TYPES OF PC There are two types of Polymer concrete: • Polymer Impregnated Concrete • Polymer Cement Concrete
- 10. POLYMER IMPREGNATED CONCRETE • This concrete is produced by port land cement by impregnated with monomer and subsequently polymerized in situ. • The cement is cast and cured normally and then concrete product gets hardened and dried , air from its voids is removed from voids under partial vaccum and a low viscosity monomer is diffused through the pores of the concrete. Then concrete is finally undergoes polymerization by radiation or heat therapy.
- 11. POLYMER CEMENT CONCRETE This cement is produced by integrating an emulsion of polymer or monomer in portland cement concrete. The ingredient consisting of cement, aggregates and monomer is mixed with water and the monomer is polymerized after placing the concrete into forms. This concrete can be used in marine works.
- 12. ADVANTAGES • Improve workability, strength and adhesion. • Chemical resistance, impact resistance and abrasion resistance. • Increased permeability and reduced absorption.
- 13. APPLICATIONS • Nuclear power plants • Roads • Kerbstones • Precast slabs for bridge desks • Sewage works
- 14. APPLICATIONS 1. Marine works 2. Prefabricated structured elements 3. Prestressed concrete 4. Food processing buildings 5. Waterproofing of buildings